ASTM A297 A297M-2014 Standard Specification for Steel Castings Iron-Chromium and Iron-Chromium-Nickel Heat Resistant for General Application《通用耐热性铁-铬和铁-铬-镍钢铸件的标准规范》.pdf

1、Designation: A297/A297M 14Standard Specification forSteel Castings, Iron-Chromium and Iron-Chromium-Nickel,Heat Resistant, for General Application1This standard is issued under the fixed designation A297/A297M; the number immediately following the designation indicates the yearof original adoption o

2、r, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers iron-chromium and iron-chromium-nickel alloy castin

3、gs for heat-resistant service. Thegrades covered by this specification are general purpose alloysand no attempt has been made to include heat-resisting alloysused for special production application.NOTE 1For heat-resisting alloys used for special product application,reference should be made to Speci

4、fication A351/A351M, A217/A217M,and A447/A447M.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the

5、 two systems may result in non-conformancewith the standard.2. Referenced Documents2.1 ASTM Standards:2A217/A217M Specification for Steel Castings, MartensiticStainless and Alloy, for Pressure-Containing Parts, Suit-able for High-Temperature ServiceA351/A351M Specification for Castings, Austenitic,

6、forPressure-Containing PartsA370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA447/A447M Specification for Steel Castings, Chromium-Nickel-Iron Alloy (25-12 Class), for High-TemperatureServiceA781/A781M Specification for Castings, Steel and Alloy,Common Requirements, for Gener

7、al Industrial UseA957/A957M Specification for Investment Castings, Steeland Alloy, Common Requirements, for General IndustrialUse3. General Conditions for Delivery3.1 Except for investment castings, material furnished tothis specification shall conform to the requirements of Speci-fication A781/A781

8、M, including any supplementary require-ments that are indicated in the purchase order. Failure tocomply with the general requirements of Specification A781/A781M constitutes nonconformance with this specification. Incase of conflict between the requirements of this specificationand Specification A78

9、1/A781M, this specification shall pre-vail.3.2 Investment castings furnished to this specification shallconform to the requirements of Specification A957/A957M,including any supplementary requirements that are indicated inthe purchase order. Failure to comply with the general require-ments of Specif

10、ication A957/A957M constitutes nonconfor-mance with this specification. In case of conflict between therequirements of this specification and Specification A957/A957M, Specification A957/A957M shall prevail.4. Ordering Information4.1 The inquiry and order should include or indicate thefollowing:4.1.

11、1 A description of the casting by pattern number ordrawing (dimensional tolerances shall be included on thecasting drawing),4.1.2 Grade of steel,4.1.3 Options in the specification, and4.1.4 The supplementary requirements desired including thestandards of acceptance.5. Process5.1 Alloys shall be made

12、 by the following processes:electric-arc, electric-induction, or other approved processes.6. Heat Treatment6.1 Castings for heat-resistant service may be shipped in theas-cast condition without heat treatment. If heat treatment isrequired, the treatment shall be established by mutual agree-ment betw

13、een the manufacturer and the purchaser and shall beso specified in the inquiry, contract, or order.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.18 on Castings.Current edition approv

14、ed May 1, 2014. Published June 2014. Originallyapproved in 1946. Last previous edition approved in 2010 as A297/A297M 10.DOI: 10.1520/A0297_A0297M-14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStand

15、ards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States17. Chemical Composition7.1 Alloy

16、s shall conform to the requirements as to chemicalcomposition prescribed in Table 1.8. Repair by Welding8.1 Except for Grade HG10MNN, the composition of thedeposited weld metal shall be similar to the composition of thecasting. For Grade HG10MNN, the filler metal to be used shallbe established by mu

17、tual agreement between the manufacturerand the purchaser. All weld repairs shall be subjected to thesame inspection standards as the casting.8.2 Castings with major weld repairs shall be heat treated inaccordance with Section 6.8.3 Weld repairs shall be considered major when the depthof the cavity a

18、fter preparation for repair exceeds 20 % of theactual wall thickness, or 1 in. 25 mm, whichever is smaller,or when the extent of the cavity exceeds approximately 10in.265 cm2.8.3.1 When Supplementary Requirement S7 is specified onthe purchase order, or inquiry, major weld repairs shall besubject to

19、the prior approval of the purchaser.8.4 All other weld repairs shall be considered minor andmay be made at the discretion of the manufacturer withoutprior approval of the purchaser.TABLE 1 Chemical RequirementsAGrade/UNS NumberTypeComposition, % (max, except where range is given)Carbon Manganese Sil

20、icon Phosphorus Sulfur Chromium Nickel MolybdenumBOtherCHFJ9260319 Chromium,9 Nickel0.200.40 2.00 2.00 0.04 0.04 18.023.0 8.012.0 0.50HHJ9350325 Chromium,12 Nickel0.200.50 2.00 2.00 0.04 0.04 24.028.0 11.014.0 0.50HIJ9400328 Chromium,15 Nickel0.200.50 2.00 2.00 0.04 0.04 26.030.0 14.018.0 0.50HKJ942

21、2425 Chromium,20 Nickel0.200.60 2.00 2.00 0.04 0.04 24.028.0 18.022.0 0.50HEJ9340329 Chromium,9 Nickel0.200.50 2.00 2.00 0.04 0.04 26.030.0 8.011.0 0.50HTN0860515 Chromium,35 Nickel0.350.75 2.00 2.50 0.04 0.04 15.019.0 33.037.0 0.50HUN0800419 Chromium,39 Nickel0.350.75 2.00 2.50 0.04 0.04 17.021.0 3

22、7.041.0 0.50HWN0800112 Chromium,60 Nickel0.350.75 2.00 2.50 0.04 0.04 10.014.0 58.062.0 0.50HXN0600617 Chromium,66 Nickel0.350.75 2.00 2.50 0.04 0.04 15.019.0 64.068.0 0.50HCJ9260528 Chromium 0.50 max 1.00 2.00 0.04 0.04 26.030.0 4.00 0.50HDJ9300528 Chromium,5 Nickel0.50 max 1.50 2.00 0.04 0.04 26.0

23、30.0 4.07.0 0.50HLN0860429 Chromium,20 Nickel0.200.60 2.00 2.00 0.04 0.04 28.032.0 18.022.0 0.50HNJ9421320 Chromium,25 Nickel0.200.50 2.00 2.00 0.04 0.04 19.023.0 23.027.0 0.50HPN0870526 Chromium,35 Nickel0.350.75 2.00 2.50 0.04 0.04 2428 3337 0.50HG10MNNJ9260419 Chromium,12 Nickel,4 Manganese0.070.

24、11 3.05.0 0.70 0.040 0.03 18.520.5 11.513.5 0.250.45 Cu 0.50Nb(Cb)DN0.200.30CT15CN0815120 Chromium,33 Nickel,1 Niobium0.05 0.15 0.15 1.50 0.15 1.50 0.03 0.03 19.021.0 31.034.0 Nb 0.501.50AWhere ellipses () appear in this table there is no requirement, and the element need not be analyzed or reported

25、.BCastings having a specified molybdenum range agreed upon by the manufacturer and the purchaser may also be furnished under these specifications.CNiobium (Nb) and Columbium (Cb) both designate element 41.DGrade HG10MNN shall have a niobium content of not less than 8 times the carbon, but not over 1

26、.00 %.A297/A297M 142SUPPLEMENTARY REQUIREMENTSThe following supplementary requirements shall not apply unless specified in the purchase order. Alist of standardized supplementary requirements for use at the option of the purchaser is included inSpecification A781/A781M or A957/A957M. Those which are

27、 ordinarily considered suitable for usewith this specification are given below. Others enumerated in A781/A781M or A957/A957M may beused with this specification upon agreement between the manufacturer and purchaser.TABLE S14.1 Tensile RequirementsAGradeTypeTensileStrength, minYield Point,minElongati

28、onin 2in.50mm,min,%Bksi (MPa) ksi (MPa)HF 19 Chromium, 9Nickel70 (485) 35 (240) 25HH 25 Chromium, 12Nickel75 (515) 35 (240) 10HI 28 Chromium, 15Nickel70 (485) 35 (240) 10HK 25 Chromium, 20Nickel65 (450) 35 (240) 10HE 29 Chromium, 9Nickel85 (585) 40 (275) 9HT 15 Chromium, 35Nickel65 (450) . . 4HU 19

29、Chromium, 39Nickel65 (450) . . 4HW 12 Chromium, 60Nickel60 (415) . . .HX 17 Chromium, 66Nickel60 (415) . . .HC 28 Chromium 55 (380) . . .HD 28 Chromium, 5Nickel75 (515) 35 (240) 8HL 29 Chromium, 20Nickel65 (450) 35 (240) 10HN 20 Chromium, 25Nickel63 (435) . . 8HP 26 Chromium, 35Nickel62.5 (430) 34 (

30、235) 4.5HG10MNN19 Chromium, 12Nickel,4 Manganese76 (525) 33 (225) 20CT15C 20 Chromium, 33Nickel,1 Niobium63 435 25 170 20.0AWhere ellipses () appear in this table there is no requirement, and the elementneed not be analyzed or reported.BWhen ICI test bars are used in tensile testing as provided for

31、in this specification,the gage length to reduced section diameter ratio shall be 4 to 1.A297/A297M 143S1. Magnetic Particle ExaminationS2. Radiographic ExaminationS3. Liquid Penetrant ExaminationS4. Ultrasonic ExaminationS5. Examination of Weld PreparationS6. CertificationS7. Prior Approval of Major

32、 Weld RepairsS8. MarkingS14. Tension TestS14.1 One tension test shall be made from material repre-senting each heat. The bar from which the test specimen istaken shall be heat treated in production furnaces to the sameprocedure as the castings it represents. The results shallconform to the requireme

33、nts specified in Table S14.1.S14.2 Test bars shall be poured in separately cast keelblocks shown in Specification A781/A781M, unless the pur-chase order is for investment castings, in which case, testmaterial shall be poured in accordance with the requirements ofSpecification A957/A957M.S14.3 Tensio

34、n test specimens may be cut from heat-treatedcastings; or from as-cast castings if no heat treatment isspecified for the castings, instead of from test bars when agreedupon between the manufacturer and the purchaser or at theoption of the producer if suitable separately cast test material isnot avai

35、lable.S14.4 Test specimens shall be the standard round 2-in.50-mm gage length specimen shown in Specification A370,unless the purchase order is for investment castings, in whichcase, the specimen shall be in accordance with SpecificationA957/A957M.S14.5 If the results of the mechanical tests for any

36、 heat donot conform to the requirements specified, the castings may bere-heat treated and re-tested, but may not be solution treated orre-austenitized more than twice.S14.6 If any test specimen shows defective machining ordevelops flaws, it may be discarded and another specimensubstituted from the s

37、ame heat.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A297/A297M 10) that may impact the use of this standard. (Approved May 1, 2014.)(1) Table 1, defined ellipses in note A and re-lettered subse-quent footnotes.(2) Table 1, ad

38、ded UNS numbers.(3) Supplementary requirements, cited A957/A957M.(4) Supplementary requirement S9, renumbered to S14 to be inagreement with A781/A781M and A957/A957M.(5) Table S14.1, defined ellipses in note A and re-letteredsubsequent footnotes.ASTM International takes no position respecting the va

39、lidity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is su

40、bject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headqu

41、arters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This stand

42、ard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A297/A297M 144