ASTM A314-2008 Standard Specification for Stainless Steel Billets and Bars for Forging《锻造用不锈及耐热钢坯及钢棒规格》.pdf

1、Designation: A 314 08Standard Specification forStainless Steel Billets and Bars for Forging1This standard is issued under the fixed designation A 314; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A num

2、ber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers stainless steel billets and ba

3、rsintended only for forging.2. Referenced Documents2.1 ASTM Standards:2A 484/A 484M Specification for General Requirements forStainless Steel Bars, Billets, and ForgingsA 751 Test Methods, Practices, and Terminology forChemical Analysis of Steel ProductsE 527 Practice for Numbering Metals and Alloys

4、 in theUnified Numbering System (UNS)2.2 Other Document:SAE J1086 Recommended Practice for Numbering Metalsand Alloys33. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Such requirements may

5、 include but are notlimited to the following:3.1.1 Quantity (weight or number of pieces),3.1.2 Name of material: type or UNS designation (Table 1),3.1.3 Condition,3.1.4 Cross section (round, round-cornered square, etc.),3.1.5 Form: bar or forging billet,3.1.6 Applicable dimensions, including size, t

6、hickness,width, and length,3.1.7 ASTM designation and date of issue,3.1.8 Preparation for delivery (see Specification A 484/A 484M),3.1.9 Marking (see Specification A 484/A 484M), and3.1.10 Exceptions to the specification or special require-ments.3.2 If possible, the intended use of the item should

7、be givenon the purchase order especially when the item is ordered fora specific end use or uses.NOTE 1A typical ordering description is as follows: 10 000 lb, Type420, annealed, round-cornered square billets, ASTM A 314 datedfor valve parts.4. Manufacture4.1 AnnealingBlooms and billets of the 400 se

8、ries ofstainless steel types which are highly hardenable, such as Types414, 420, 431, 440A, 440B, and 440C, are commonly annealedprior to shipment and so specified in order to avoid thepossibility of thermal cracking. Those grades are not normallyfurnished in the as-rolled or as-forged condition. Ot

9、her hard-enable grades, such as Types 403, 410, 416, and 416 Se, whichmay also require annealing, depending on their compositionand size, are furnished suitable for cold cutting when sospecified on the purchase order.4.2 Conditioning Material may be conditioned by chip-ping or grinding to remove inj

10、urious surface defects providedthe depth of conditioning does not exceed that which will affectthe surface condition or dimensions of the article to be forgedfrom the bar or billet.5. Chemical Composition5.1 The steel shall conform to the chemical compositionprescribed in Table 1 for the respective

11、grades.5.2 Methods and practices relating to chemical analysisrequired by this specification shall be in accordance with TestMethods, Practices, and Terminology A 751.6. Dimensions6.1 Billets and bars shall conform to the shape and dimen-sions specified by the purchaser within a permissible variatio

12、nof 65%.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved Oct. 1, 2008. Published October 2008. Originallyapproved

13、in 1947. Last previous edition approved in 2002 as A 314 97 (2002).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM we

14、bsite.3Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United

15、 States.TABLE 1 Chemical RequirementsUNSDesig-nationATypeNumberChemical Composition, %BCarbonMan-ganesePhos-phorusSulfur Silicon Chromium NickelMolyb-denumNitrogenOtherElementsAustenitic GradesS20161 . . . 0.15 4.006.00 0.040 0.040 3.004.00 15.0018.00 4.006.00 . . . 0.080.20 . . .S20200 202 0.15 7.5

16、010.00 0.060 0.030 1.00 17.0019.00 4.006.00 . . . 0.25 . . .S20910 XM-19 0.06 4.006.00 0.040 0.030 1.00 20.5023.50 11.5013.50 1.503.00 0.200.40 Cb 0.100.30V 0.100.30S21800 . . . 0.10 7.009.00 0.060 0.030 3.504.50 16.0018.00 8.009.00 . . . 0.080.18 . . .S21900 XM-10 0.08 8.0010.00 0.060 0.030 1.00 19

17、.0021.50 5.507.50 . . . 0.150.40 . . .S21904 XM-11 0.04 8.0010.00 0.060 0.030 1.00 19.0021.50 5.507.50 . . . 0.150.40 . . .S24000 XM-29 0.08 11.5014.50 0.060 0.030 1.00 17.0019.00 2.253.75 . . . 0.200.40 . . .S24100 XM-28 0.15 11.0014.00 0.060 0.030 1.00 16.5019.00 0.502.25 . . . 0.200.45 . . .S2820

18、0 . . . 0.15 17.0019.00 0.045 0.030 1.00 17.0019.00 . . . 0.751.25 0.400.60 . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.0019.00 8.0010.00 . . . 0.10 . . .S30215 302B 0.15 2.00 0.045 0.030 2.003.00 17.0019.00 8.0010.00 . . . . . . . . .S30300 303 0.15 2.00 0.20 0.15 min 1.00 17.0019.00 8.0010.00 .

19、. . . . . . . .S30323 303Se 0.15 2.00 0.20 0.06 1.00 17.0019.00 8.0010.00 . . . . . . Se 0.15 minS30400 304 0.08 2.00 0.045 0.030 1.00 18.0020.00 8.0010.50 . . . 0.10 . . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.0020.00 8.0012.00 . . . 0.10 . . .S30500 305 0.12 2.00 0.045 0.030 1.00 17.0019.00 10

20、.5013.00 . . . . . . . . .S30800 308 0.08 2.00 0.045 0.030 1.00 19.0021.00 10.0012.00 . . . . . . . . .S30900 309 0.20 2.00 0.045 0.030 1.00 22.0024.00 12.0015.00 . . . . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.0024.00 12.0015. . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.002

21、4.00 12.0016.00 . . . . . . Cb + Ta 10 3 CS31000 310 0.25 2.00 0.045 0.030 1.50 24.0026.00 19.0022.00 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.50 24.0026.00 19.0022.00 . . . . . . . . .S31400 314 0.25 2.00 0.045 0.030 1.503.00 23.0026.00 19.0022.00 . . . . . . . . .S31600 316 0.08 2.00 0

22、.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . . .S31603 316L 0.030 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . . .S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 . . . Ti 5 3 (C+N)min; 0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.

23、003.00 . . . Cb + Ta 10 3C min; 1.10S31700 317 0.08 2.00 0.045 0.030 1.00 18.0020.00 11.0015.00 3.004.00 0.10S32100 321 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0012.00 . . . . . . Ti 5 3 CminS33228 . . . 0.040.08 1.00 0.020 0.015 0.030 26.0028.00 31.0033.00 . . . . . . Cb 0.61.0Ce 0.050.10Al 0.025S3

24、4700 347 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . . . . . . Cb + Ta 10 3 CminS34800 348 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . . . . . . Cb + Ta 10 3 Cmin; Ta 0.10S38031 . . . 0.015 2.0 0.020 0.010 0.3 26.028.0 30.032.0 6.07.0 0.150.25 Cu 1.01.5S38926 . . . 0.020 2.00 0.03 0.01 0

25、.5 19.0021.00 24.0026.00 6.07.0 0.150.25 Cu 0.51.5Austenitic-Ferritic GradesS32202 . . 0.030 2.00 0.030 0.010 1.00 21.5024.00 1.002.80 0.45 0.180.26 . . .S32760C. . . 0.030 1.00 0.030 0.010 1.00 24.0026.00 6.008.00 3.004.00 0.200.30 Cu 0.501.00W 0.501.00S32950 . . . 0.03 2.00 0.035 0.010 0.60 26.002

26、9.00 3.505.20 1.002.50 0.150.35 . . .Ferritic GradesS42900 429 0.12 1.00 0.040 0.030 1.00 14.0016.00 . . . . . . . . . . . .S43000 430 0.12 1.00 0.040 0.030 1.00 16.0018.00 . . . . . . . . . . . .S43020 430F 0.12 1.25 0.06 0.15 min 1.00 16.0018.00 . . . 0.60D. .S43023 430F Se 0.12 1.25 0.06 0.06 1.0

27、0 16.0018.00 . . . . . . . . . Se 0.15 minS44600 446 0.20 1.50 0.040 0.030 1.00 23.0027.00 . . . . . . 0.25 . . .S44625 XM-27E0.010 0.40 0.020 0.020 0.40 25.0027.50 0.50 0.751.50 0.015 . . .Martensitic GradesS40300 403 0.15 1.00 0.040 0.030 0.50 11.5013.00 . . . . . . . . . . . .S41000 410 0.15 1.00

28、 0.040 0.030 1.00 11.5013.50 . . . . . . . . . . . .S41400 414 0.15 1.00 0.040 0.030 1.00 11.5013.50 1.252.50 . . . . . . . . .S41425 . . . 0.05 0.501.00 0.020 0.005 0.50 12.015.0 4.07.0 1.502.00 0.060.12 Cu 0.30S41600 416 0.15 1.25 0.06 0.15 min 1.00 12.0014.00 . . . 0.60D. .S41623 416Se 0.15 1.25

29、0.06 0.06 1.00 12.0014.00 . . . . . . . . . Se 0.15 minS42000 420 0.15 min 1.00 0.040 0.030 1.00 12.0014.00 . . . . . . . . . . . .S42010 . . . 0.150.30 1.00 0.04 0.03 1.00 13.5015.00 0.350.85 0.400.85 . . . . . .S43100 431 0.20 1.00 0.040 0.030 1.00 15.0017.00 1.252.50 . . . . . . . . .S44002 440A

30、0.600.75 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S44003 440B 0.750.95 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S44004 440C 0.951.20 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S50100 501 0.10 min 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . . . . . .A314082

31、7. General Requirements7.1 In addition to the requirements of this specification, allrequirements of the current edition of Specification A 484/A 484M shall apply. Failure to comply with the generalrequirements of Specification A 484/A 484M constitutes non-conformance with this specification.8. Keyw

32、ords8.1 austenitic stainless steel; austenitic-ferritic duplex stain-less steel; ferritic stainless steel; martensitic stainless steel;stainless steel bars; stainless steel billetsSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A

33、31497 (2002) that may impact the use of this standard. (Approved Oct. 1, 2008.)(1) New grade S32202 added to Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly

34、advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, eit

35、her reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend

36、. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Ind

37、ividual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 1 ContinuedUNSDesig-nationATypeNumberChemical Composition,

38、 %BCarbonMan-ganesePhos-phorusSulfur Silicon Chromium NickelMolyb-denumNitrogenOtherElementsS50200 502 0.10 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . . . . . .ANew designation established in accordance with Practice E 527 and SAE J1086.BMaximum unless otherwise indicated.C%Cr+3.33 %Mo+163 %N$ 40.DAt the option of the manufacturer.ENickel plus copper combined; 0.50 max. Product analysis tolerance over the maximum limit for carbon and nitrogen to be 0.002 %.A314083