ASTM A314-2013 Standard Specification for Stainless Steel Billets and Bars for Forging《锻造用不锈钢及耐热钢坯及钢棒的标准规格》.pdf

1、Designation: A314 08A314 13Standard Specification forStainless Steel Billets and Bars for Forging1This standard is issued under the fixed designation A314; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.

2、A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers stainless steel billets a

3、nd bars intended only for forging.2. Referenced Documents2.1 ASTM Standards:2A484/A484M Specification for General Requirements for Stainless Steel Bars, Billets, and ForgingsA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsE527 Practice for Numbering Metals and Al

4、loys in the Unified Numbering System (UNS)2.2 Other Document:SAE J1086 Recommended Practice for Numbering Metals and Alloys33. Ordering Information3.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Such requireme

5、nts may include but are not limited to the following:3.1.1 Quantity (weight or number of pieces),3.1.2 Name of material: type or UNS designation (Table 1),3.1.3 Condition,3.1.4 Cross section (round, round-cornered square, etc.),3.1.5 Form: bar or forging billet,3.1.6 Applicable dimensions, including

6、 size, thickness, width, and length,3.1.7 ASTM designation and date of issue,3.1.8 Preparation for delivery (see Specification A484/A484M),3.1.9 Marking (see Specification A484/A484M), and3.1.10 Exceptions to the specification or special requirements.3.2 If possible, the intended use of the item sho

7、uld be given on the purchase order especially when the item is ordered for aspecific end use or uses.NOTE 1A typical ordering description is as follows: 10 000 lb, Type 420, annealed, round-cornered square billets, ASTM A314 dated forvalve parts.4. Manufacture4.1 AnnealingBlooms and billets of the 4

8、00 series of stainless steel types which are highly hardenable, such as Types 414,420, 431, 440A, 440B, and 440C, are commonly annealed prior to shipment and so specified in order to avoid the possibility ofthermal cracking. Those grades are not normally furnished in the as-rolled or as-forged condi

9、tion. Other hardenable grades, suchas Types 403, 410, 416, and 416 Se, which may also require annealing, depending on their composition and size, are furnishedsuitable for cold cutting when so specified on the purchase order.1 This specification is under the jurisdiction ofASTM Committee A01 on Stee

10、l, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.17on Flat-Rolled and Wrought Stainless Steel.Current edition approved Oct. 1, 2008May 1, 2013. Published October 2008June 2013. Originally approved in 1947. Last previous edition approved in 20022008 asA314 97

11、2002).A314 08. DOI: 10.1520/A0314-08.10.1520/A0314-13.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3 Avai

12、lable from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sae.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may

13、not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the

14、end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1TABLE 1 Chemical RequirementsUNSDesig-nationATypeNumberChemical Composition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Molyb-denum Nitrogen Other

15、ElementsAustenitic GradesS20161 . . . 0.15 4.006.00 0.040 0.040 3.004.00 15.0018.00 4.006.00 . . . 0.080.20 . . .S20200 202 0.15 7.5010.00 0.060 0.030 1.00 17.0019.00 4.006.00 . . . 0.25 . . .S20910 XM-19 0.06 4.006.00 0.040 0.030 1.00 20.5023.50 11.5013.50 1.503.00 0.200.40 Cb 0.100.30V 0.100.30S21

16、800 . . . 0.10 7.009.00 0.060 0.030 3.504.50 16.0018.00 8.009.00 . . . 0.080.18 . . .S21900 XM-10 0.08 8.0010.00 0.060 0.030 1.00 19.0021.50 5.507.50 . . . 0.150.40 . . .S21904 XM-11 0.04 8.0010.00 0.060 0.030 1.00 19.0021.50 5.507.50 . . . 0.150.40 . . .S24000 XM-29 0.08 11.5014.50 0.060 0.030 1.00

17、 17.0019.00 2.253.75 . . . 0.200.40 . . .S24100 XM-28 0.15 11.0014.00 0.060 0.030 1.00 16.5019.00 0.502.25 . . . 0.200.45 . . .S28200 . . . 0.15 17.0019.00 0.045 0.030 1.00 17.0019.00 . . . 0.751.25 0.400.60 . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.0019.00 8.0010.00 . . . 0.10 . . .S30215 302B

18、0.15 2.00 0.045 0.030 2.003.00 17.0019.00 8.0010.00 . . . . . . . . .S30300 303 0.15 2.00 0.20 0.15 min 1.00 17.0019.00 8.0010.00 . . . . . . . . .S30323 303Se 0.15 2.00 0.20 0.06 1.00 17.0019.00 8.0010.00 . . . . . . Se 0.15 minS30400 304 0.08 2.00 0.045 0.030 1.00 18.0020.00 8.0010.50 . . . 0.10 .

19、 . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.0020.00 8.0012.00 . . . 0.10 . . .S30500 305 0.12 2.00 0.045 0.030 1.00 17.0019.00 10.5013.00 . . . . . . . . .S30800 308 0.08 2.00 0.045 0.030 1.00 19.0021.00 10.0012.00 . . . . . . . . .S30900 309 0.20 2.00 0.045 0.030 1.00 22.0024.00 12.0015.00 . . .

20、 . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.0024.00 12.0015. . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.0024.00 12.0016.00 . . . . . . Cb + Ta 10 CS31000 310 0.25 2.00 0.045 0.030 1.50 24.0026.00 19.0022.00 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.50 24.0026.00 1

21、9.0022.00 . . . . . . . . .S31400 314 0.25 2.00 0.045 0.030 1.503.00 23.0026.00 19.0022.00 . . . . . . . . .S31600 316 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . . .S31603 316L 0.030 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . . .S31635 316Ti 0.08 2.00 0.045 0.0

22、30 1.00 16.0018.00 10.0014.00 2.003.00 . . . Ti 5 (C+N)min; 0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 . . . Cb + Ta 10 C min; 1.10S31700 317 0.08 2.00 0.045 0.030 1.00 18.0020.00 11.0015.00 3.004.00 0.10S32100 321 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0012.00 . . .

23、 . . . Ti 5 C minS33228 . . . 0.040.08 1.00 0.020 0.015 0.030 26.0028.00 31.0033.00 . . . . . . Cb 0.61.0Ce 0.050.10Al 0.025S34700 347 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . . . . . . Cb + Ta 10 CminS34800 348 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . . . . . . Cb + Ta 10 Cmin; Ta

24、 0.10S38031 . . . 0.015 2.0 0.020 0.010 0.3 26.028.0 30.032.0 6.07.0 0.150.25 Cu 1.01.5S38926 . . . 0.020 2.00 0.03 0.01 0.5 19.0021.00 24.0026.00 6.07.0 0.150.25 Cu 0.51.5Austenitic-Ferritic GradesS32202 . . 0.030 2.00 0.030 0.010 1.00 21.5024.00 1.002.80 0.45 0.180.26 . . .S32760C . . . 0.030 1.00

25、 0.030 0.010 1.00 24.0026.00 6.008.00 3.004.00 0.200.30 Cu 0.501.00W 0.501.00S32950 . . . 0.03 2.00 0.035 0.010 0.60 26.0029.00 3.505.20 1.002.50 0.150.35 . . .S32950 . . . 0.03 2.00 0.035 0.010 0.60 26.0029.00 3.505.20 1.002.50 0.150.35 . . .S82441 . . . 0.030 2.504.00 0.035 0.005 0.70 23.025.0 3.0

26、4.5 1.002.00 0.200.30 Cu 0.100.80Ferritic GradesS42900 429 0.12 1.00 0.040 0.030 1.00 14.0016.00 . . . . . . . . . . . .S43000 430 0.12 1.00 0.040 0.030 1.00 16.0018.00 . . . . . . . . . . . .S43020 430F 0.12 1.25 0.06 0.15 min 1.00 16.0018.00 . . . 0.60D . . . . . .S43023 430F Se 0.12 1.25 0.06 0.0

27、6 1.00 16.0018.00 . . . . . . . . . Se 0.15 minS44600 446 0.20 1.50 0.040 0.030 1.00 23.0027.00 . . . . . . 0.25 . . .S44625 XM-27E 0.010 0.40 0.020 0.020 0.40 25.0027.50 0.50 0.751.50 0.015 . . .Martensitic GradesS40300 403 0.15 1.00 0.040 0.030 0.50 11.5013.00 . . . . . . . . . . . .S41000 410 0.1

28、5 1.00 0.040 0.030 1.00 11.5013.50 . . . . . . . . . . . .S41400 414 0.15 1.00 0.040 0.030 1.00 11.5013.50 1.252.50 . . . . . . . . .S41425 . . . 0.05 0.501.00 0.020 0.005 0.50 12.015.0 4.07.0 1.502.00 0.060.12 Cu 0.30S41600 416 0.15 1.25 0.06 0.15 min 1.00 12.0014.00 . . . 0.60D . . . . . .S41623 4

29、16Se 0.15 1.25 0.06 0.06 1.00 12.0014.00 . . . . . . . . . Se 0.15 minS42000 420 0.15 min 1.00 0.040 0.030 1.00 12.0014.00 . . . . . . . . . . . .S42010 . . . 0.150.30 1.00 0.04 0.03 1.00 13.5015.00 0.350.85 0.400.85 . . . . . .S43100 431 0.20 1.00 0.040 0.030 1.00 15.0017.00 1.252.50 . . . . . . .

30、 .S44002 440A 0.600.75 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S44003 440B 0.750.95 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S44004 440C 0.951.20 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S50100 501 0.10 min 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . .

31、 . . . .S50200 502 0.10 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . . . . . .A New designation established in accordance with Practice E527 and SAE J1086.B Maximum unless otherwise indicated.A314 1324.2 ConditioningMaterial may be conditioned by chipping or grinding to remove injurious surface d

32、efects provided the depthof conditioning does not exceed that which will affect the surface condition or dimensions of the article to be forged from the baror billet.5. Chemical Composition5.1 The steel shall conform to the chemical composition prescribed in Table 1 for the respective grades.5.2 Met

33、hods and practices relating to chemical analysis required by this specification shall be in accordance with Test Methods,Practices, and Terminology A751.6. Dimensions6.1 Billets and bars shall conform to the shape and dimensions specified by the purchaser within a permissible variation of65 %.7. Gen

34、eral Requirements7.1 In addition to the requirements of this specification, all requirements of the current edition of Specification A484/A484Mshall apply. Failure to comply with the general requirements of Specification A484/A484M constitutes nonconformance with thisspecification.8. Keywords8.1 aus

35、tenitic stainless steel; austenitic-ferritic duplex stainless steel; ferritic stainless steel; martensitic stainless steel; stainlesssteel bars; stainless steel billetsSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A31497 (2002)

36、08) that may impact the use of this standard. (Approved Oct. 1, 2008May 1, 2013.)(1) New grade S32202 added Added UNS S82441 to Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this stan

37、dard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and

38、if not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, wh

39、ich you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,

40、United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C % Cr + 3.3 % Mo + 16 % N $ 40.D At the option of the manufacturer.E Nickel plus copper combined; 0.50 max. Product analysis tolerance over the maximum limit for carbon and nitrogen to be 0.002 %.A314 133