ASTM A328 A328M-2007(2012) Standard Specification for Steel Sheet Piling 《钢板桩的标准规格》.pdf

1、Designation: A328/A328M 07 (Reapproved 2012)American Association StateHighway and Transportation Officials StandardAASHTO No.: M 202Standard Specification forSteel Sheet Piling1This standard is issued under the fixed designation A328/A328M; the number immediately following the designation indicates

2、the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the D

3、epartment of Defense.1. Scope1.1 This specification covers carbon steel sheet piling ofstructural quality for use in the construction of dock walls, seawalls, cofferdams, excavations, and like applications (seeSpecification A572/A572M).1.2 When the steel is to be welded, it is presupposed that aweld

4、ing procedure suitable for the grade of steel and intendeduse or service will be utilized. See Appendix X3 of Specifica-tion A6/A6M for information on weldability.1.3 The values stated in either inch-pound units or SI unitsare to be regarded as standard. Within the text, the SI units areshown in bra

5、ckets. The values stated in each system are notexact equivalents; therefore, each system must be used inde-pendently of the other. Combining values from the two systemsmay result in nonconformance with this specification.1.4 For sheet piling produced from coil and furnishedwithout heat treatment or

6、with stress relieving only, theadditional requirements, including additional testing require-ments and the reporting of additional test results, of Specifi-cation A6/A6M apply.2. Referenced Documents2.1 ASTM Standards:2A6/A6M Specification for General Requirements for RolledStructural Steel Bars, Pl

7、ates, Shapes, and Sheet PilingA572/A572M Specification for High-Strength Low-AlloyColumbium-Vanadium Structural Steel3. General Requirements for Delivery3.1 Sheet piling furnished under this specification shallconform to the requirements of the current edition of Specifi-cation A6/A6M, for the speci

8、fic sheet piling ordered, unless aconflict exists, in which case this specification shall prevail.3.2 Coils are excluded from qualification to this specifica-tion until they are processed into finished sheet piling. Sheetpiling produced from coil means sheet piling that has been cutto individual len

9、gths from a coil. The processor directlycontrols, or is responsible for, the operations involved in theprocessing of a coil into finished sheet piling. Such operationsinclude decoiling, leveling, hot-forming or cold-forming (ifapplicable), cutting to length, testing, inspection, conditioning,heat tr

10、eatment (if applicable), packaging, marking, loading forshipment, and certification.NOTE 1For sheet piling produced from coil and furnished withoutheat treatment or with stress relieving only, two test results are to bereported for each qualifying coil. Additional requirements regarding sheetpiling

11、produced from coil are described in Specification A6/A6M.4. Process4.1 The steel may be made by any process that producesmaterial meeting the requirements set forth in this specifica-tion.5. Chemical Requirements5.1 The heat analysis shall conform to the requirementsprescribed in Table 1.5.2 The ste

12、el shall conform on product analysis to therequirements prescribed in Table 1, subject to the productanalysis tolerances in Specification A6/A6M.6. Mechanical Requirements6.1 The material, as represented by the test specimens,shall conform to the requirements as to tensile propertiesprescribed in Ta

13、ble 2.6.2 A minimum tensile strength of 60 ksi 415 MPa and aminimum yield point of 36 ksi 250 MPa shall be permittedfor piling sections used in the fabrication of cold-formedconnections.7. Keywords7.1 carbon; cofferdams; dock walls; excavations; sea walls;sheet piling; steel; structural steel1This s

14、pecification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.02 on Structural Steel for Bridges, Buildings, Rolling Stock and Ships.Current edition approved March 1, 2012. Published March 2012. Originally

15、published in 1950. Last previous edition approved in 2007 as A328/A328M 07.DOI: 10.1520/A0328_A0328M-07R12.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the stand

16、ards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.SUPPLEMENTARY REQUIREMENTSThe following supplementary requirement shall apply only when specified in the purchase order:S99. Interlock Stre

17、ngthS99.1. The minimum strength of the interlocked joint re-quired for certain services may be specified for certain sheetpiling sections subject to specific agreement between thematerial purchaser and the manufacturer.ASTM International takes no position respecting the validity of any patent rights

18、 asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any ti

19、me by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will

20、receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM

21、International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or t

22、hrough the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE 1 Chemical RequirementsElementComposition, %Heat analysisPhosphorus, max 0.035Sulfur, max 0.04Copper (when specified), min 0.20TABLE 2 Tensile

23、RequirementsTensile strength, min, ksi MPaA65 450Yield point, min, ksi MPa 39 270Elongation in 8 in. 200 mm, min, %B17Elongation in 2 in. 50 mm, min, % 20APrior toA328/A328M 05, the minimum tensile strength was 70 ksi 485 MPa.BSee Elongation Requirement Adjustments in the Tension Tests section ofSpecification A6/A6M. See Specimen Orientation in the Tension Tests section ofSpecification A6/A6M.A328/A328M 07 (2012)2