ASTM A479 A479M-2013 Standard Specification for Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels《锅炉和其他压力容器用不锈钢棒材和型材标准规格》.pdf

1、Designation: A479/A479M 12A479/A479M 13 Used in USDOE-NE StandardsStandard Specification forStainless Steel Bars and Shapes for Use in Boilers andOther Pressure Vessels1This standard is issued under the fixed designation A479/A479M; the number immediately following the designation indicates the year

2、of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Departmen

3、t of Defense.1. Scope*1.1 This specification2 covers hot- and cold-finished bars of stainless steel, including rounds, squares, and hexagons, andhot-rolled or extruded shapes such as angles, tees, and channels for use in boiler and pressure vessel construction.2NOTE 1There are standards covering hig

4、h nickel, chromium, austenitic corrosion, and heat-resisting alloy materials. These standards are under thejurisdiction of ASTM Subcommittee B02.07 and may be found in Annual Book of ASTM Standards, Vol 02.04.1.2 The values stated in either SI units or inch-pound units are to be regarded separately

5、as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.3 Unless the order specifies the applicable “M” specification designation

6、, the material shall be furnished to the inch-poundunits.2. Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless SteelsA370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA484/A484M Specification for

7、 General Requirements for Stainless Steel Bars, Billets, and ForgingsA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsE112 Test Methods for Determining Average Grain SizeE527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)2.2 SAE Doc

8、ument:4SAE J 1086 Recommended Practice for Numbering Metals and Alloys3. General Requirements3.1 The following requirements for orders for material furnished under this specification shall conform to the applicablerequirements of the current edition of Specification A484/A484M.3.1.1 Definitions,3.1.

9、2 General requirements for delivery,3.1.3 Ordering information,3.1.4 Process,3.1.5 Special tests,3.1.6 Heat treatment,3.1.7 Dimensions and permissible variations,3.1.8 Workmanship, finish, and appearance,1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel an

10、d RelatedAlloysand is the direct responsibility of Subcommittee A01.17on Flat-Rolled and Wrought Stainless Steel.Current edition approved Nov. 1, 2012April 1, 2013. Published November 2012April 2013. Originally approved in 1962. Last previous edition approved in 20112012 asA479/A479M 11.A479/A479M 1

11、2. DOI: 10.1520/A0479_A0479M-12.10.1520/A0479_A0479M-13.2 For ASME Boiler and Pressure Vessel Code applications see related Specification SA-479/SA-479M in Section II of that Code.3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org.

12、 For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.4 Available from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sae.org.This document is not an ASTM standard and is intended only

13、 to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versio

14、nof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.9 Number of tests/test methods,3.1.10

15、 Specimen preparation,3.1.11 Retreatment,3.1.12 Inspection,3.1.13 Rejection and rehearing,3.1.14 Material test report,3.1.15 Certification, and3.1.16 Packaging, marking, and loading.4. Other Requirements4.1 In addition to the requirements of this specification, all requirements of the current editio

16、ns of Specification A484/A484Mshall apply. Failure to comply with the general requirements of Specification A484/A484M constitutes nonconformance with thisspecification.5. Chemical Composition5.1 Chemical composition shall be reported to the purchaser, or his representative, and shall conform to the

17、 requirementsspecified in Table 1.5.2 When a product analysis is performed or requested by the purchaser, the tolerance limits as described in SpecificationA484/A484M apply unless Supplementary Requirement S3 is invoked.5.3 Methods and practices relating to chemical analysis required by this specifi

18、cation shall be in accordance with Test Methods,Practices, and Terminology A751.6. Grain Size for Austenitic Grades6.1 All austenitic grades shall be tested for average grain size by Test Methods E112.6.2 The H grades shall conform to an average grain size as follows:6.2.1 ASTM No. 6 or coarser for

19、Types 304H, 309H, 310H, and 316H,6.2.2 ASTM No. 7 or coarser for Types 321H, 347H, and 348H.6.3 For S32615, the grain size as determined in accordance with Test Methods E112, comparison method, Plate 11, shall be No.3 or finer.6.4 Supplementary Requirement S1 shall be invoked when nonH grade austeni

20、tic stainless steels are ordered for ASME Codeapplications for service above 1000F 540C.7. Mechanical Properties Requirements7.1 The material shall conform to the mechanical property requirements specified in Table 2 for the grade ordered. At least oneroom-temperature test shall be performed by the

21、manufacturer on a sample from at least one bar or shape from each lot of material.7.2 The yield strength shall be determined by the offset (0.2 %) method as prescribed in Test Methods and Definitions A370.7.3 Martensitic material supplied in the annealed condition shall be capable of meeting the har

22、dened and tempered mechanicalproperties when heat treated.7.4 Hardness measurements, when required, shall be made at a location midway between the surface and the center of the crosssection.7.5 Martensitic grades shall be capable of meeting the hardness requirements after heat treating as specified

23、in Table 3.8. Corrosion Testing8.1 Austenitic stainless steels solution annealed by the alternative method shall be tested and pass the intergranular corrosiontest requirements described in S2.9. Testing for Intermetallic Compounds9.1 When specified by the purchaser in the purchase order, the manufa

24、cturer shall test the austenitic or austenitic-ferritic(duplex) stainless steel material in its final condition in accordance with supplementary test requirements S6.NOTE 2Many, if not all, duplex stainless steels and some austenitic stainless steels will form intermetallic phases or compounds such

25、as sigma, chi,and laves phases when exposed to temperatures below the specified annealing temperature or cooled slowly from a higher temperature during casting,welding, or annealing. These phases can have a negative effect on mechanical properties and corrosion resistance. These phases can typically

26、 be removedby correct annealing and cooling practices. The presence of these phases can be demonstrated by tests, typically involving metallography, impacttoughness, or corrosion resistance, although the testing requirements may be different for different alloy grades. Such testing may or may not be

27、 routinelyperformed by the manufacturer.A479/A479M 132TABLE 1 Chemical RequirementsUNSDesigna-tionATypeComposition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Nitrogen Molyb-denum Other ElementsCAustenitic GradesN08020 Alloy 20 0.07 2.00 0.045 0.035 1.00 19.021.0 32.038.0 . . . 2

28、.003.00 Cu 3.04.0Cb 8XC1.00N08020 Alloy 20 0.07 2.00 0.045 0.035 1.00 19.021.0 32.038.0 . . . 2.003.00 Cu 3.04.0;Cb 8xC1.00N08367 . . . 0.030 2.00 0.040 0.030 1.00 20.022.0 23.525.5 0.180.25 6.07.0 Cu 0.75N08700 . . . 0.040 2.00 0.040 0.030 1.00 19.023.0 24.026.0 . . . 4.35.0 Cu 0.50;Cb 8xC0.40N0890

29、4 904L 0.020 2.00 0.045 0.035 1.00 19.023.0 23.028.0 0.10 4.05.0 Cu 1.02.0S20161 . . . 0.15 4.06.0 0.045 0.030 3.04.0 15.018.0 4.06.0 0.080.20 . . . . . .S20910 XM-19 0.06 4.06.0 0.045 0.030 1.00 20.523.5 11.513.5 0.200.40 1.503.00 Cb 0.100.30;V 0.100.30S21600 XM-17 0.08 7.59.0 0.045 0.030 1.00 17.5

30、20.5 5.07.0 0.250.50 2.003.00 . . .S21603 XM-18 0.03 7.59.0 0.045 0.030 1.00 17.520.5 5.07.0 0.250.50 2.003.00 . . .S21800S21904. . .XM-110.100.047.09.08.010.00.0600.0450.0300.0303.54.51.0016.018.019.021.58.09.05.57.50.080.180.150.40. . . . . .S24000 XM-29 0.08 11.514.5 0.060 0.030 1.00 17.019.0 2.3

31、3.7 0.200.40 . . . . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.019.0 8.010.0 0.10 . . . . . .S30400 304 0.08D 2.00 0.045 0.030 1.00 18.020.0 8.010.5 . . . . . . . . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.020.0 8.012.0 . . . . . . . . .S30409 304H 0.040.10 2.00 0.045 0.030 1.00 18.020.0 8.010.

32、5 . . . . . . . . .S30451 304N 0.08 2.00 0.045 0.030 1.00 18.020.0 8.012.0 0.100.16 . . . . . .S30453 304LN 0.030 2.00 0.045 0.030 1.00 18.020.0 8.011.0 0.100.16 . . . . . .S30600 . . . 0.018 2.00 0.020 0.020 3.74.3 17.018.5 14.015.5 . . . 0.20 Cu 0.50S30815 . . . 0.050.10 0.80 0.040 0.030 1.402.00

33、20.022.0 10.012.0 0.140.20 . . . Ce 0.030.08S30908 309S 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30909 309H 0.040.10 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.024.0 12.016.0 . . . . . . Cb 10C- 1.10S30880 ER308E 0.08 1.0

34、02.50 0.030 0.030 0.250.60 19.522.0 9.011.0 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . . . .S31009 310H 0.040.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . . . .S31040 310Cb 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . . . Cb 10C-1.10S31050

35、 . . . 0.025 2.00 0.020 0.015 0.4 24.026.0 20.523.5 0.090.15 1.602.60 . . .S31254 . . . 0.020 1.00 0.030 0.010 0.80 19.520.5 17.518.5 0.180.22 6.06.5 Cu 0.501.00S31600 316 0.08C 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31603 316L 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . .

36、. 2.003.00 . . .S31609 316H 0.040.10 2.00 0.045 0.030 1.00 16.018.0 10.014.0 . . . 2.003.00 . . .S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Ti 5(C+N)- 0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.10 2.003.00 Cb 10C- 1.10S31651 316N 0.08 2.00 0.045 0.03

37、0 1.00 16.018.0 10.014.0 0.100.16 2.003.00 . . .S31653 316LN 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 0.100.16 2.003.00 . . .S31700 317 0.08 2.00 0.045 0.030 1.00 18.020.0 11.015.0 . . . 3.04.0 . . .S31725 . . . 0.030 2.00 0.045 0.030 1.00 18.020.0 13.517.5 0.20 4.05.0 . . .S31726 . . . 0.030 2

38、.00 0.045 0.030 1.00 17.020.0 14.517.5 0.100.20 4.05.0 . . .S31727 . . . 0.030 1.00 0.030 0.030 1.00 17.519.0 14.516.5 0.150.21 3.84.5 Cu 2.84.0S32050 . . . 0.030 1.50 0.035 0.020 1.00 22.024.0 20.023.0 0.210.32 6.06.8 Cu 0.40S32053 . . . 0.030 1.00 0.030 0.010 1.00 22.024.0 24.026.0 0.170.22 5.06.0

39、 . . .S32100 321 0.08D 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Ti 5(C+N)- 0.70FS32109 321H 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Ti 4(C+N)- 0.70FS32615 . . . 0.07 2.00 0.045 0.030 4.86.0 16.519.5 19.022.0 . . . 0.301.50 Cu 1.502.50S32654 . . . 0.020 2.04.0 0.030 0.00

40、5 0.50 24.025.0 21.023.0 0.450.55 7.08.0 Cu 0.300.60S33228 . . . 0.040.08 1.00 0.020 0.015 0.30 26.028.0 31.033.0 . . . . . . Cb 0.601.00;Ce 0.050.10;Al 0.025S34565 . . . 0.030 5.07.0 0.030 0.010 1.00 23.025.0 16.018.0 0.400.60 4.05.0 Cb 0.10S34700 347 0.08D 2.00 0.045 0.030 1.00 17.019.0 9.012.0 .

41、. . . . . Cb 10C1.10S34709 347H 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Cb 8C1.10S34800 348 0.08D 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . (Cb+Ta) 10C1.10;Ta 0.10;Co 0.20S34809 348H 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . (Cb + Ta) 8C1.10;Co 0.20;Ta

42、0.10S35315 . . . 0.040.08 2.00 0.040 0.030 1.202.00 24.026.0 34.036.0 0.120.18 . . . Ce 0.030.08S38815 . . . 0.030 2.00 0.040 0.020 5.506.50 13.015.0 15.017.0 . . . 0.751.50 Al 0.30;Cu 0.751.50Austenitic-Ferritic GradesS31803 . . . 0.030 2.00 0.030 0.020 1.00 21.023.0 4.56.5 0.080.20 2.53.5 . . .S32

43、101 . . . 0.040 4.06.0 0.040 0.030 1.00 21.022.0 1.351.70 0.200.25 0.100.80 Cu 0.100.80A479/A479M 13310. Certification10.1 The material manufacturers certificate of compliance certifying that the material was manufactured and tested inaccordance with this specification, together with a report of the

44、 results required by this specification and the purchase order, shallbe furnished at the time of shipment. The certification shall be positively relatable to the lot of material represented.11. Product Marking11.1 In addition to the marking requirements of Specification A484/A484M, materials that ha

45、ve been heat treated or have beenstrain hardened shall be identified by placement of the following symbols after the grade designation:11.1.1 Austenitic Grades:11.1.1.1 All grades in the annealed conditionA,11.1.1.2 Strain hardened Type 316, Level 1S1,11.1.1.3 Strain hardened Type 316, Level 2S2,11.

46、1.1.4 Hot-rolled Type XM-19H,11.1.1.5 Strain hardened Type XM-19S,11.1.1.6 Material meeting Supplementary Requirement S1ELT (unnecessary for H grades).TABLE 1 ContinuedUNSDesigna-tionATypeComposition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Nitrogen Molyb-denum Other ElementsC

47、S32202 . . . 0.030 2.00 0.040 0.010 1.00 21.524.0 1.002.80 0.180.26 0.45 . . .S32205 . . . 0.030 2.00 0.030 0.020 1.00 22.023.0 4.56.5 0.140.20 3.03.5 . . .S32506 . . . 0.030 1.00 0.040 0.015 0.90 24.026.0 5.57.2 0.080.20 3.03.5 W 0.050.30S32550 . . . 0.04 1.50 0.040 0.030 1.00 24.027.0 4.56.5 0.100

48、.25 2.93.9 Cu 1.502.50S32750 . . . 0.030 1.20 0.035 0.020 0.80 24.026.0 6.08.0 0.240.32 3.05.0 Cu 0.50S32760G . . . 0.030 1.00 0.030 0.010 1.00 24.026.0 6.08.0 0.200.30 3.04.0 Cu 0.501.00;W 0.501.00S32906 . . . 0.030 0.801.50 0.030 0.030 0.50 28.030.0 5.87.5 0.300.40 1.502.60 Cu 0.80S32950 . . . 0.03 2.00 0.035 0.010 0.60 26.029.0 3.55.2 0.150.35 1.002.50 . . .S39277 . . . 0.025 0.80 0.025 0.002 0.80 24.026.0 6.58.0 0.230.33 3.04.0 Cu 1.202.00W 0.801.20S82441 . . . 0.030 2.54.0 0.035 0.005 0.70 23.025.0 3.04.5 0.200.30 1.002.00 Cu 0.100.80Ferritic GradesS40500 405 0.08 1.00 0.040 0.030 1