ASTM A507-2010 Standard Specification for Drawing Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧拉制合金钢薄板材与带材标准规范》.pdf

1、Designation: A507 10Standard Specification forDrawing Alloy Steel, Sheet and Strip, Hot-Rolled and Cold-Rolled1This standard is issued under the fixed designation A507; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of la

2、st revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers hot-rolled a

3、nd cold-rolleddrawing alloy-steel sheet and strip. Material of this quality isproduced principally for applications involving severe coldplastic deformation such as deep drawn or severely formedparts. This steel is produced by a closely controlled steel-making practice designed to assure internal so

4、undness, relativeuniformity of chemical composition, and freedom from injuri-ous imperfections.1.2 The material covered by this specification may befurnished in several conditions, heat treatments, surface fin-ishes, and edges, as specified herein, in coils or cut lengths.2. Referenced Documents2.1

5、ASTM Standards:2A505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA941 Terminology Relating to Steel, Stainless Steel, Re-lated Alloys, and Ferroalloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 capable ofas used in t

6、his specification, means thattests need not be performed. However, if application by thepurchaser establishes that the material does not meet therequirements, the material shall be subject to rejection.3.1.2 drawing alloy steelalloy-steel sheet and strip in-tended for applications involving severe c

7、old plastic deforma-tion such as deep drawn or severely formed parts.3.1.3 standard steelssteel chemical compositions definedas “standard” by the Society of Automotive Engineers (SAE).See Table 1.3.1.4 steels other than standardsteel chemical composi-tions other than those defined as “standard,” and

8、 furnished tothe composition limits shown in Table 2.4. General Requirements and Ordering Information4.1 Material supplied to this specification shall conform toSpecification A505, which includes the general requirementsand establishes the rules for the ordering information thatshould be complied wi

9、th when purchasing material to thisspecification.4.2 In addition to the Ordering Information required bySpecification A505, the following shall also be included:4.2.1 Mechanical properties, if required (show propertiesdesired, which must be consistent with the grade and heattreatment),4.2.2 Surface

10、finish, if other than that normally furnished(see Section 10), and4.2.3 Application, or end use (identification of the part to bemade).5. Manufacture5.1 RollingThe material shall be furnished either hot-rolled or cold-rolled, as specified on the order.5.2 Heat TreatmentUnless otherwise specified on

11、theorder, the material shall be furnished spheroidize-annealed.(See Terminology A941 for heat treatment terms.)5.2.1 If the material is to be heat treated by other than theproducer, the order shall so state. The material may be orderedin the as-rolled condition, in such cases.6. Chemical Requirement

12、s Chemical Requirements6.1 The heat (cast) analysis shall conform to the require-ments for the grade specified on the order.6.1.1 Standard steels listed in Table 1 are those commonlyproduced for drawing alloy-steel sheet and strip.6.1.2 Nonstandard steel grades may be specified, using theranges and

13、limits shown in Table 2.7. Metallurgical Structure7.1 Microstructure:1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved April 1, 2010.

14、 Published April 2010. Originallyapproved in 1964. Last previous edition approved in 2006 as A507 06. DOI:10.1520/A0507-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, re

15、fer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7.1.1 RequirementsAt least 75 % of the carbide micro-stru

16、cture shall be of the globular type.7.1.2 Number of TestsThe number of tests shall be inaccordance with the producers standard quality control pro-cedures. A specific number of tests is not required, but thematerial shall be produced by manufacturing practices estab-lished to assure compliance with

17、the specified requirements.The material shall be subjected to mill tests and inspectionprocedures to assure such compliance. For government pro-curement, mill tests and inspection procedures utilized to showconformance to the microstructure requirements shall be madeavailable on request.8. Mechanica

18、l Requirements8.1 Tension and Hardness Tests:8.1.1 RequirementsWhen tension tests or hardness tests,or both are specified on the order, the test results shall conformto the requirements specified on the order. Yield strength,tensile strength, and elongation requirements may be specified.The tensile

19、properties will vary depending on the chemicalcomposition, condition, and heat treatment. Producers arefrequently consulted as to grade, resultant mechanical proper-ties, recommended heat treatment, and other informationneeded to establish the property parameters to meet end useTABLE 1 Standard Stee

20、ls Commonly Produced for Drawing Alloy-Steel Sheet and StripUNSDesignationSAE No.Chemical Composition Ranges and Limits, % (Heat Analysis)ACMnPSSiBNi Cr Mo V. . . E3310 0.080.13 0.450.60 0.025 0.025 0.150.30 3.253.75 1.401.75 . . . . . .G40120 4012 0.090.14 0.751.00 0.025 0.025 0.150.30 . . . . . .

21、0.150.25 . . .G41180 4118 0.180.23 0.700.90 0.025 0.025 0.150.30 . . . 0.400.60 0.080.15 . . .G41300 4130 0.280.33 0.400.60 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41350 4135 0.330.38 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41370 4137 0.350.40 0.700.90 0.025 0.025 0.15

22、0.30 . . . 0.801.10 0.150.25 . . .G41400 4140 0.380.43 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41420 4142 0.400.45 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41450 4145 0.430.48 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41470 4147 0.450.50 0.751

23、00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41500 4150 0.480.53 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G43200 4320 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 0.400.60 0.200.30 . . .G43400 4340 0.380.43 0.600.80 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .

24、G43406 E4340 0.380.43 0.650.85 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .G45200 4520 0.180.23 0.450.65 0.025 0.025 0.150.30 . . . . . . 0.450.60 . . .G46150 4615 0.130.18 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .G46200 4620 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00

25、 . . . 0.200.30 . . .G47180 4718 0.160.21 0.700.90 0.025 0.025 0.150.30 0.901.20 0.350.55 0.300.40 . . .G48150 4815 0.130.18 0.400.60 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .G48200 4820 0.180.23 0.500.70 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .G50150 5015 0.120.17 0.300.50 0.025

26、0.025 0.150.30 . . . 0.300.50 . . . . . .G50460 5046 0.430.50 0.751.00 0.025 0.025 0.150.30 . . . 0.200.35 . . . . . .G51150 5115 0.130.18 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51200 5120 0.170.22 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51300 5130 0.280.33 0.700.9

27、0 0.025 0.025 0.150.30 . . . 0.801.10 . . . . . .G5132 5132 0.300.35 0.600.90 0.025 0.025 0.150.30 . . . 0.751.00 . . . . . .G51400 5140 0.380.43 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51500 5150 0.480.53 0.790.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51600 5160 0.550.65

28、0.751.00 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G15116 E51100 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 0.901.15 . . . . . .G15216 E52100 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 1.301.60 . . . . . .G61500 6150 0.480.53 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . 0.15 minG61580

29、 6158 0.550.62 0.701.10 0.025 0.015 0.150.30 . . . 0.901.20 . . . 0.100.20G86150 8615 0.130.18 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86170 8617 0.150.20 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86200 8620 0.180.23 0.700.90 0.035 0.035 0.150.30 0.400.70

30、0.400.60 0.150.25 . . .G86300 8630 0.280.33 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86400 8640 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86420 8642 0.400.45 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86450 8645 0.430.48 0.751.0

31、0 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86500 8650 0.480.53 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86550 8655 0.500.60 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86600 8660 0.550.65 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 .

32、 . .G87200 8720 0.180.23 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G87350 8735 0.330.38 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G87400 8740 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G92600 9260 0.550.65 0.701.00 0.025 0.025 1.802

33、20 . . . . . . . . . . . .G92620 9262 0.550.65 0.751.00 0.025 0.025 1.802.20 . . . 0.250.40 . . . . . . . . E9310 0.080.13 0.450.65 0.025 0.025 0.200.35 3.003.50 1.001.40 0.080.15 . . .AThe chemical ranges and limits shown are subject to product analysis tolerances. See Specification A505.BOther si

34、licon limits can be substituted on agreement between the purchaser and producer.A507 102requirements. Rockwell hardness requirements may be speci-fied, providing the requirements are compatible with thetension test requirements.8.1.2 Number of TestsTwo tension tests and two hardnesstests, when speci

35、fied, shall be taken at random from each heat(cast) and heat treatment lot.9. Other Tests and Requirements9.1 End Use Suitability:9.1.1 When steel is to be furnished in the spheroidize-annealed condition, the user and producer shall review anypart(s) to be produced to reach adequate agreement on cap

36、a-bility to produce said parts.9.1.2 Material in the spheroidize-annealed condition gener-ally work hardens and may require stress-relief-annealingbetween drawing operations.10. Workmanship, Finish, and Appearance10.1 Surface Finish:10.1.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial sha

37、ll be furnished descaled and oiled. When required,the material may be specified to be furnished not oiled.10.1.2 Cold-RolledUnless otherwise specified, cold-rolled material shall be furnished with a commercial dull mattefinish and shall be oiled. When required, the material may bespecified to be fur

38、nished not oiled.10.2 Edges:10.2.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial shall be furnished with Mill Edge. The material maybe specified to have other types of edges, in accordance withSpecification A505.10.2.2 Cold-RolledUnless otherwise specified, cold-rolled sheet shall be furn

39、ished with Cut Edge and cold-rolledstrip shall be furnished with No. 3 Edge. The material may bespecified to have other types of edges, in accordance withSpecification A505.11. Keywords11.1 alloy steel with improved formability; cold-rolled alloysteel; deep drawn alloy steel; drawing alloy steel she

40、et;drawing alloy steel strip; forming alloy steel; hot-rolled alloysteel; special soundness alloy steelTABLE 2 Heat (Cast) Analysis Ranges for Other Than StandardSteel Alloy Sheet and StripElementWhen Maximum ofSpecified Element Is, %Range orLimit, %Carbon To 0.55 incl 0.05Over 0.55 to 0.70 incl 0.0

41、8Over 0.70 to 0.80 incl 0.10Over 0.80 to 0.95 incl 0.12Over 0.95 to 1.35 incl 0.13Manganese To 0.60 incl 0.20Over 0.60 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.90 incl 0.30Over 1.90 to 2.10 incl 0.40Phosphorus . . . 0.025 maxSulfur . . . 0.025 maxSilicon To 0.15 incl 0.08Over 0.15

42、to 0.20 incl 0.10Over 0.20 to 0.40 incl 0.15Over 0.40 to 0.60 incl 0.20Over 0.60 to 1.00 incl 0.30Over 1.00 to 2.20 incl 0.40Copper To 0.60 inclOver 0.60 to 1.50 inclOver 1.50 to 2.00 incl0.200.300.35Nickel To 0.50 incl 0.20Over 0.50 to 1.50 incl 0.30Over 1.50 to 2.00 incl 0.35Over 2.00 to 3.00 incl

43、 0.40Over 3.00 to 5.30 incl 0.50Over 5.30 to 10.00 incl 1.00Chromium To 0.40 incl 0.15Over 0.40 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.60 incl 0.30Over 1.60 to 1.75 incl 0.35Over 1.75 to 2.10 incl 0.40Over 2.10 to 3.99 incl 0.50Molybdenum To 0.10 incl 0.05Over 0.10 to 0.20 incl 0

44、07Over 0.20 to 0.50 incl 0.10Over 0.50 to 0.80 incl 0.15Over 0.80 to 1.15 incl 0.20Vanadium To 0.25 inclOver 0.25 to 0.50 incl0.050.10A507 103SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue (A507 06)that may impact the use of thi

45、s standard. (Approved April 1, 2010.)(1) Footnote B added to Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of an

46、y such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are i

47、nvited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not receiv

48、ed a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of

49、this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A507 104