ASTM A507-2016 Standard Specification for Drawing Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧拉拔合金钢薄板和带材的标准规格》.pdf

1、Designation: A507 12A507 16Standard Specification forDrawing Alloy Steel, Sheet and Strip, Hot-Rolled and Cold-Rolled1This standard is issued under the fixed designation A507; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the yea

2、r of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers

3、hot-rolled and cold-rolled drawing alloy-steel sheet and strip. Material of this quality is producedprincipally for applications involving severe cold plastic deformation such as deep drawn or severely formed parts. This steel isproduced by a closely controlled steel-making practice designed to assu

4、re internal soundness, relative uniformity of chemicalcomposition, and freedom from injurious imperfections.1.2 The material covered by this specification may be furnished in several conditions, heat treatments, surface finishes, andedges, as specified herein, in coils or cut lengths.2. Referenced D

5、ocuments2.1 ASTM Standards:2A505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 capable ofa

6、s used in this specification, means that tests need not be performed. However, if application by the purchaserestablishes that the material does not meet the requirements, the material shall be subject to rejection.3.1.2 drawing alloy steelalloy-steel sheet and strip intended for applications involv

7、ing severe cold plastic deformation suchas deep drawn or severely formed parts.3.1.3 standard steelssteel chemical compositions defined as “standard” by the Society of Automotive Engineers (SAE). SeeTable 1.3.1.4 steels other than standardsteel chemical compositions other than those defined as “stan

8、dard,” and furnished to thecomposition limits shown in Table 2.4. General Requirements and Ordering Information4.1 Material supplied to this specification shall conform to Specification A505, which includes the general requirements andestablishes the rules for the ordering information that should be

9、 complied with when purchasing material to this specification.4.2 In addition to the Ordering Information required by Specification A505, the following shall also be included:4.2.1 Mechanical properties, if required (show properties desired, which must be consistent with the grade and heat treatment

10、),4.2.2 Surface finish, if other than that normally furnished (see Section 10), and4.2.3 Application, or end use (identification of the part to be made).5. Manufacture5.1 RollingThe material shall be furnished either hot-rolled or cold-rolled, as specified on the order.1 This specification is under

11、the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.19on Steel Sheet and Strip.Current edition approved May 1, 2012May 1, 2016. Published May 2012May 2016. Originally approved in 1964. Last previous edition approved i

12、n 20102012 asA507 10.A507 12. DOI: 10.1520/A0507-12.10.1520/A0507-16.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM

13、website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult p

14、rior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 1

15、9428-2959. United States1TABLE 1 Standard Steels Commonly Produced for Drawing Alloy-Steel Sheet and StripSteelDesignationNo.Chemical Composition Ranges and Limits, % (Heat Analysis)AC Mn P S SiB Ni Cr Mo VE3310C 0.080.13 0.450.60 0.025 0.025 0.150.30 3.253.75 1.401.75 . . . . . .E3310C 0.080.13 0.4

16、50.60 0.025 0.025 0.150.35 3.253.75 1.401.75 . . . . . .4012C 0.090.14 0.751.00 0.025 0.025 0.150.30 . . . . . . 0.150.25 . . .4012C 0.090.14 0.751.00 0.025 0.025 0.150.35 . . . . . . 0.150.25 . . .4118 0.180.23 0.700.90 0.025 0.025 0.150.30 . . . 0.400.60 0.080.15 . . .4118 0.180.23 0.700.90 0.025

17、0.025 0.150.35 . . . 0.400.60 0.080.15 . . .4130 0.280.33 0.400.60 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4130 0.280.33 0.400.60 0.025 0.025 0.150.35 . . . 0.801.10 0.150.25 . . .4135 0.330.38 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4135 0.330.38 0.700.90 0.025 0.025 0.

18、150.35 . . . 0.801.10 0.150.25 . . .4137 0.350.40 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4137 0.350.40 0.700.90 0.025 0.025 0.150.35 . . . 0.801.10 0.150.25 . . .4140 0.380.43 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4140 0.380.43 0.751.00 0.025 0.025 0.150.35 .

19、 . . 0.801.10 0.150.25 . . .4142 0.400.45 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4142 0.400.45 0.751.00 0.025 0.025 0.150.35 . . . 0.801.10 0.150.25 . . .4145 0.430.48 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4145 0.430.48 0.751.00 0.025 0.025 0.150.35 . . . 0.8

20、01.10 0.150.25 . . .4147C 0.450.50 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4147C 0.450.50 0.751.00 0.025 0.025 0.150.35 . . . 0.801.10 0.150.25 . . .4150 0.480.53 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .4150 0.480.53 0.751.00 0.025 0.025 0.150.35 . . . 0.801.10

21、0.150.25 . . .4320 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 0.400.60 0.200.30 . . .4320 0.170.22 0.450.65 0.025 0.025 0.150.35 1.652.00 0.400.60 0.200.30 . . .4340 0.380.43 0.600.80 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .4340 0.380.43 0.600.80 0.025 0.025 0.150.35 1.652.00 0.700

22、.90 0.200.30 . . .E4340 0.380.43 0.650.85 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .E4340 0.380.43 0.650.85 0.025 0.025 0.150.35 1.652.00 0.700.90 0.200.30 . . .4520C 0.180.23 0.450.65 0.025 0.025 0.150.30 . . . . . . 0.450.60 . . .4520C 0.180.23 0.450.65 0.025 0.025 0.150.35 . . . . . .

23、0.450.60 . . .4615 0.130.18 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .4615 0.130.18 0.450.65 0.025 0.025 0.150.35 1.652.00 . . . 0.200.30 . . .4620 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .4620 0.170.22 0.450.65 0.025 0.025 0.150.35 1.652.00 . . . 0.200.30

24、 . . .4718 0.160.21 0.700.90 0.025 0.025 0.150.30 0.901.20 0.350.55 0.300.40 . . .4718 0.160.21 0.700.90 0.025 0.025 0.150.35 0.901.20 0.350.55 0.300.40 . . .4815 0.130.18 0.400.60 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .4815 0.130.18 0.400.60 0.025 0.025 0.150.35 3.253.75 . . . 0.200.30 .

25、 . .4820 0.180.23 0.500.70 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .4820 0.180.23 0.500.70 0.025 0.025 0.150.35 3.253.75 . . . 0.200.30 . . .5015 0.120.17 0.300.50 0.025 0.025 0.150.30 . . . 0.300.50 . . . . . .5015 0.120.17 0.300.50 0.025 0.025 0.150.35 . . . 0.300.50 . . . . . .5046 0.430

26、.50 0.751.00 0.025 0.025 0.150.30 . . . 0.200.35 . . . . . .5046 0.430.50 0.751.00 0.025 0.025 0.150.35 . . . 0.200.35 . . . . . .5115 0.130.18 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .5115 0.130.18 0.700.90 0.025 0.025 0.150.35 . . . 0.700.90 . . . . . .5120 0.170.22 0.700.90 0.025 0

27、.025 0.150.30 . . . 0.700.90 . . . . . .5120 0.170.22 0.700.90 0.025 0.025 0.150.35 . . . 0.700.90 . . . . . .5130 0.280.33 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . . . .5130 0.280.33 0.700.90 0.025 0.025 0.150.35 . . . 0.801.10 . . . . . .5132 0.300.35 0.600.80 0.025 0.025 0.150.30 . . .

28、0.751.00 . . . . . .5132 0.300.35 0.600.80 0.025 0.025 0.150.35 . . . 0.751.00 . . . . . .5140 0.380.43 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .5140 0.380.43 0.700.90 0.025 0.025 0.150.35 . . . 0.700.90 . . . . . .5150 0.480.53 0.790.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .

29、5150 0.480.53 0.790.90 0.025 0.025 0.150.35 . . . 0.700.90 . . . . . .5160 0.560.64 0.751.00 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .5160 0.560.64 0.751.00 0.025 0.025 0.150.35 . . . 0.700.90 . . . . . .E51100C 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 0.901.15 . . . . . .E51100C 0.951.10

30、0.250.45 0.025 0.025 0.150.35 . . . 0.901.15 . . . . . .E52100 0.981.10 0.250.45 0.025 0.025 0.150.30 . . . 1.301.60 . . . . . .E52100 0.981.10 0.250.45 0.025 0.025 0.150.35 . . . 1.301.60 . . . . . .6150 0.480.53 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . 0.15 min6150 0.480.53 0.700.90 0.02

31、5 0.025 0.150.35 . . . 0.801.10 . . . 0.15 min6158C 0.550.62 0.701.10 0.025 0.015 0.150.30 . . . 0.901.20 . . . 0.100.206158C 0.550.62 0.701.10 0.025 0.015 0.150.35 . . . 0.901.20 . . . 0.100.208615 0.130.18 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .8615 0.130.18 0.700.90 0.025 0

32、.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8617 0.150.20 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .8617 0.150.20 0.700.90 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8620 0.180.23 0.700.90 0.035 0.035 0.150.30 0.400.70 0.400.60 0.150.25 . . .8620 0.180.23 0.700.90 0.0

33、35 0.035 0.150.35 0.400.70 0.400.60 0.150.25 . . .A507 1625.2 Heat TreatmentUnless otherwise specified on the order, the material shall be furnished spheroidize-annealed. (SeeTerminology A941 for heat treatment terms.)5.2.1 If the material is to be heat treated by other than the producer, the order

34、shall so state. The material may be ordered inthe as-rolled condition, in such cases.6. Chemical Requirements6.1 The heat (cast) analysis shall conform to the requirements for the grade specified on the order.6.1.1 Standard steels listed in Table 1 are those commonly produced for drawing alloy-steel

35、 sheet and strip.6.1.2 Nonstandard steel grades may be specified, using the ranges and limits shown in Table 2.7. Metallurgical Structure7.1 Microstructure:7.1.1 RequirementsAt least 75 % of the carbide microstructure shall be of the globular type.7.1.2 Number of TestsThe number of tests shall be in

36、 accordance with the producers standard quality control procedures. Aspecific number of tests is not required, but the material shall be produced by manufacturing practices established to assurecompliance with the specified requirements. The material shall be subjected to mill tests and inspection p

37、rocedures to assure suchcompliance. For government procurement, mill tests and inspection procedures utilized to show conformance to the microstructurerequirements shall be made available on request.8. Mechanical Requirements8.1 Tension and Hardness Tests:8.1.1 RequirementsWhen tension tests or hard

38、ness tests, or both are specified on the order, the test results shall conform tothe requirements specified on the order. Yield strength, tensile strength, and elongation requirements may be specified. The tensileproperties will vary depending on the chemical composition, condition, and heat treatme

39、nt. Producers are frequently consulted asto grade, resultant mechanical properties, recommended heat treatment, and other information needed to establish the propertyparameters to meet end use requirements. Rockwell hardness requirements may be specified, providing the requirements arecompatible wit

40、h the tension test requirements.8.1.2 Number of TestsTwo tension tests and two hardness tests, when specified, shall be taken at random from each heat (cast)and heat treatment lot.9. Other Tests and Requirements9.1 End Use Suitability:9.1.1 When steel is to be furnished in the spheroidize-annealed c

41、ondition, the user and producer shall review any part(s) to beproduced to reach adequate agreement on capability to produce said parts.SteelDesignationNo.Chemical Composition Ranges and Limits, % (Heat Analysis)AC Mn P S SiB Ni Cr Mo V8630 0.280.33 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.1

42、50.25 . . .8630 0.280.33 0.700.90 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8640 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .8640 0.380.43 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8642C 0.400.45 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.6

43、0 0.150.25 . . .8642C 0.400.45 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8645 0.430.48 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .8645 0.430.48 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8650C 0.480.53 0.751.00 0.025 0.025 0.150.30 0.400.70 0

44、.400.60 0.150.25 . . .8650C 0.480.53 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8655 0.510.59 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .8655 0.510.59 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8660 0.550.65 0.751.00 0.025 0.025 0.150.30 0.400

45、.70 0.400.60 0.150.25 . . .8660 0.550.65 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.150.25 . . .8720 0.180.23 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .8720 0.180.23 0.700.90 0.025 0.025 0.150.35 0.400.70 0.400.60 0.200.30 . . .8735C 0.330.38 0.751.00 0.025 0.025 0.150.30

46、0.400.70 0.400.60 0.200.30 . . .8735C 0.330.38 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.200.30 . . .8740C 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .8740C 0.380.43 0.751.00 0.025 0.025 0.150.35 0.400.70 0.400.60 0.200.30 . . .9260 0.560.64 0.751.00 0.025 0.025 1.

47、802.20 . . . . . . . . . . . .9262C 0.550.65 0.751.00 0.025 0.025 1.802.20 . . . 0.250.40 . . . . . .E9310C 0.080.13 0.450.65 0.025 0.025 0.200.35 3.003.50 1.001.40 0.080.15 . . .A The chemical ranges and limits shown are subject to product analysis tolerances. See Specification A505.B Other silicon

48、 limits can be substituted on agreement between the purchaser and producer.C Not an S.A.E. Steel Designation.A507 1639.1.2 Material in the spheroidize-annealed condition generally work hardens and may require stress-relief-annealing betweendrawing operations.10. Workmanship, Finish, and Appearance10.1 Surface Finish:10.1.1 Hot-RolledUnless otherwise specified, hot-rolled material shall be