1、Designation:A572/A572M07 Designation: A572/A572M 12American Association StateHighway and TransportationOfficals StandardAASHTO No.: M223Standard Specification forHigh-Strength Low-Alloy Columbium-Vanadium StructuralSteel1This standard is issued under the fixed designation A572/A572M; the number imme
2、diately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard ha
3、s been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers five grades of high-strength low-alloy structural steel shapes, plates, sheet piling, and bars. Grades42 290, 50 345, and 55 380 are intended for riveted, bolted, or welded structures. Grades 60 4
4、15 and 65 450 are intendedfor riveted or bolted construction of bridges, or for riveted, bolted, or welded construction in other applications.1.2 For applications, such as welded bridge construction, where notch toughness is important, notch toughness requirements areto be negotiated between the pur
5、chaser and the producer.1.3Specification1.3 Specification A588/A588M shall not be substituted for Specification A572/A572M without agreement between thepurchaser and the supplier.1.4 The use of columbium, vanadium, titanium, nitrogen, or combinations thereof, within the limitations noted in Section
6、5, isrequired; the selection of type (1, 2, 3, or 5) is at the option of the producer, unless otherwise specified by the purchaser. (SeeSupplementary Requirement S90.)1.5 The maximum thicknesses available in the grades and products covered by this specification are shown in Table 1.1.6 When the stee
7、l is to be welded, a welding procedure suitable for the grade of steel and intended use or service is to beutilized. See Appendix X3 of Specification A6/A6M for information on weldability.1.7 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within t
8、he text, the SI unitsare shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be usedindependently of the other, without combining values in any way.1.8 The text of this specification contains notes or footnotes, or both, that provide explanator
9、y material. Such notes andfootnotes, excluding those in tables and figures, do not contain any mandatory requirements.1.9 For structural products produced from coil and furnished without heat treatment or with stress relieving only, the additionalrequirements, including additional testing requiremen
10、ts and the reporting of additional tests, of A6/A6M apply.2. Referenced Documents2.1 ASTM Standards:2A6/A6M Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet PilingA36/A36M Specification for Carbon Structural SteelA514/A514M Specification for High-Yie
11、ld-Strength, Quenched and Tempered Alloy Steel Plate, Suitable for WeldingA588/A588M Specification for High-Strength Low-Alloy Structural Steel, up to 50 ksi 345 MPa Minimum Yield Point, withAtmospheric Corrosion Resistance3. General Requirements for Delivery3.1 Structural products furnished under t
12、his specification shall conform to the requirements of the current edition ofSpecification A6/A6M, for the specific structural product ordered, unless a conflict exists in which case this specification shallprevail.3.2 Coils are excluded from qualification to this specification until they are proces
13、sed into a finished structural product.1This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.02on Structural Steel for Bridges, Buildings, Rolling Stock and Ships.Current edition approved
14、MarchMay 1, 2007.2012. Published March 2007.May 2012. Originally approved in 1966. Last previous edition approved in 20062007 asA572/A572M 067. DOI: 10.1520/A0572_A0572M-0712.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. Fo
15、r Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may
16、not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the
17、end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Structural products produced from coil means structural products that have been cut to individual lengths from a coil. Theprocessor directly controls, or is responsi
18、ble for, the operations involved in the processing of a coil into a finished structuralproduct. Such operations include decoiling, leveling or straightening, hot-forming or cold-forming (if applicable), cutting to length,testing, inspection, conditioning, heat treatment (if applicable), packaging, m
19、arking, loading for shipment, and certification.NOTE 1For structural products produced from coil and furnished without heat treatment or with stress relieving only, two test results are to bereported for each qualifying coil. Additional requirements regarding structural products produced from coil a
20、re described in A6/A6M.4. Materials and Manufacture4.1 The steel shall be semi-killed or killed5. Chemical Composition5.1 The heat analysis shall conform to the requirements prescribed in Table 2 and Table 3.5.2 The steel shall conform on product analysis to the requirements prescribed in Table 2 an
21、d Table 3, subject to the productanalysis tolerances in Specification A6/A6M.TABLE 1 Maximum Product Thickness or SizeGradeYield Point, min Maximum Thickness or SizeZees and RolledTeesksi MPaPlates and BarsStructural ShapeFlange or LegThicknessSheet Pilingin. mm in. mm42 290A42 290 6 150 all all all
22、 all50 345A50 345 4B100Ball all all all55 380 55 380 2 50 all all all all60 415A60 415 114C32C2 50 all all65 450 65 450 114 32 2 50 not available allAIn the above tabulation, Grades 42, 50, and 60 290, 345, and 415, are the yield point levels most closely approximating a geometric progression patter
23、n between36 ksi 250 MPa, min, yield point steels covered by Specification A36/A36M and 100 ksi 690 MPa, min, yield strength steels covered by Specification A514/A514M.BRound bars up to and including 11 in. 275 mm in diameter are permitted.CRound bars up to and including 312 in. 90 mm in diameter are
24、 permitted.TABLE 2 Chemical RequirementsA(Heat Analysis)Diameter, Thickness,or DistanceBetween ParallelFaces, in. mmPlates and BarsStructuralShapeFlange orLegThickness,in. mmGradeCarbon,max, %Manganese,Bmax, %Phosphorus,max, %Sulfur,max,%SiliconPlates to 112 in. 40mm Thick,Shapes withFlange or LegTh
25、ickness to 3 in.75 mm inclusive,Sheet Piling,Bars, Zees, andRolled TeesCPlates Over 112 in.40 mm Thick andShapes with FlangeThicknessOver 3 in.75 mmmax, % range, %6 150 all 42 290 0.21 1.35D0.04 0.05 0.40 0.150.404 100Eall 50 345 0.23 1.35D0.04 0.05 0.40 0.150.402 50Fall 55 380 0.25 1.35D0.04 0.05 0
26、.40 0.15-0.40114 32F#2 50 60 415 0.26 1.35D0.04 0.05 0.40G12 114 1332 1-2 25-50 65 450 0.23 1.65 0.04 0.05 0.40G#12 13H# 1H65 450 0.26 1.35 0.04 0.05 0.40GACopper when specified shall have a minimum content of 0.20 % by heat analysis (0.18 % by product analysis).BManganese, minimum, by heat analysis
27、 of 0.80 % (0.75 % by product analysis) shall be required for all plates over38 in. 10 mm in thickness; a minimum of 0.50 %(0.45 % by product analysis) shall be required for plates38 in. 10 mm and less in thickness, and for all other products. The manganese to carbon ratio shall not be lessthan2to1.
28、CBars over 112 in. 40 mm in diameter, thickness, or distance between parallel faces shall be made by a killed steel practice.DFor each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximumis permitted, up to
29、a maximum of 1.60 %.ERound bars up to and including 11 in. 275 mm in diameter are permitted.FRound bars up to and including 312 in. 90 mm in diameter are permitted.GThe size and grade is not described in this specification.HAn alternative chemical requirement with a maximum carbon of 0.21 % and a ma
30、ximum manganese of 1.65 % is permitted, with the balance of the elements as shownin Table 2.A572/A572M 1226. Mechanical Properties6.1 Tensile Properties:6.1.1 The material as represented by the test specimens shall conform to the tensile properties given in Table 4.7. Test Reports7.1 In addition to
31、the Test Reports requirements in Specification A6/A6M, when Specification A588/A588M is substituted forSpecification A572/A572M, the test report shall include the statement “Specification A588/A588M substituted” and the heatanalysis of all elements required in Specification A588/A588M. substituted.”
32、8. Keywords8.1 bars; bolted construction; bridges; buildings; columbium-vanadium; high-strength; low-alloy; plates; riveted construction;shapes; sheet piling; steel; structural steel; welded constructionSUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the orde
33、r or contract. StandardizedTABLE 3 Alloy ContentTypeAElementsHeatAnalysis, %1 ColumbiumB0.0050.05C2 Vanadium 0.010.153 ColumbiumBVanadiumColumbium plus vanadium0.005-0.05C0.010.150.020.15D5 TitaniumNitrogenVanadium0.006-0.040.0030.0150.06 maxAAlloy content shall be in accordance with Type 1, 2, 3, o
34、r 5 and the contentsof the applicable elements shall be reported on the test report.BColumbium shall be restricted to the following thicknesses and sizes unlesskilled steel is furnished. Killed steel shall be confirmed by a statement of killed steelon the test report, or by a report on the presence
35、of a sufficient quantity of a strongdeoxidizing element, such as silicon at 0.10 % or higher, or aluminum at 0.015 %or higher. See table below.CProduct analysis limits = 0.004 to 0.06 %.DProduct analysis limits = 0.01 to 0.16 %.GradesMaximum Plate, Bar,SheetPiling, Zees, and RolledTee Thicknesses, i
36、n. mmMaximum StructuralShape Flange or LegThickness,in. mm42, 50, and 5534 1.5290, 345, and38020 4060 and 6512 1415 and 450 13 25TABLE 4 Tensile RequirementsAGradeYield Point, min Tensile Strength, minMinimum Elonga-tion, %B,C,Dksi MPa ksi MPain8in.200 mmin2in.50 mm42 290 42 290 60 415 20 2450 345 5
37、0 345 65 450 18 2155 380 55 380 70 485 17 2060 415 60 415 75 520 16 1865 450 65 450 80 550 15 17ASee specimen Orientation under the Tension Tests section of SpecificationA6/A6M.BElongation not required to be determined for floor plate.CFor wide flange shapes over 426 lb/ft 634 kg/m, elongation in 2
38、in. 50 mmof 19 % minimum applies.DFor plates wider than 24 in. 600 mm, the elongation requirement is reducedtwo percentage points for Grades 42, 50, and 55 290, 345, and 380, and threepercentage points for Grades 60 and 65 415 and 450. See elongation require-ment adjustments in the Tension Tests sec
39、tion of Specification A6/A6M.A572/A572M 123supplementary requirements for use at the option of the purchaser are listed in Specification A6/A6M.Those that are considered suitable for use with this specification are listed by title:S5. Charpy V-Notch Impact Test.S18. Maximum Tensile StrengthS30. Char
40、py V-Notch Impact Test for Structural Shapes: Alternate Core LocationS32. Single Heat Bundles.In addition, the following supplementary requirements are suitable for use:S81. Tensile StrengthS81.1 For Grade 50 345 steel of thicknesses34 in. 20 mm and less, the tensile strength shall be a minimum of 7
41、0 ksi 485MPa.S90. TypeS90.1 The specific type of steel shall be as specified by the purchaser in the order or contract.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A572/A572M 067) that may impact the use of this standard. (Appr
42、oved MarchMay 1, 2007.)(1) Added 1.3 and new2012.)(1) Revised Section 7 .Committee A01 has identified the location of selected changes to this standard since the last issue (A572/A572M 04) thatmay impact the use of this standard. (Approved March 1, 2006.)(1) The maximum permitted manganese was chang
43、ed from 1.50 % to 1.60 % for grades 42, 50, 55, and 60 in Table 2.to eliminate redundant language.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determ
44、ination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or w
45、ithdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that
46、your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (s
47、ingle or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A572/A572M 124