ASTM A572 A572M-2013 Standard Specification for High-Strength Low-Alloy Columbium-Vanadium Structural Steel《高强度低合金铌钒结构钢的标准规格》.pdf

1、Designation: A572/A572M 12aA572/A572M 13 American Association StateHighway and TransportationOfficals StandardAASHTO No.: M223Standard Specification forHigh-Strength Low-Alloy Columbium-Vanadium StructuralSteel1This standard is issued under the fixed designation A572/A572M; the number immediately fo

2、llowing the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been app

3、roved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers five grades of high-strength low-alloy structural steel shapes, plates, sheet piling, and bars. Grades42 290, 50 345, and 55 380 are intended for riveted, bolted, or welded structures. Grades 60 415 and 65

4、450 are intendedfor riveted or bolted construction of bridges, or for riveted, bolted, or welded construction in other applications.1.2 For applications, such as welded bridge construction, where notch toughness is important, notch toughness requirements areto be negotiated between the purchaser and

5、 the producer.1.3 Specification A588/A588M shall not be substituted for Specification A572/A572M without agreement between thepurchaser and the supplier.1.4 The use of columbium, vanadium, titanium, nitrogen, or combinations thereof, within the limitations noted in Section 5, isrequired; the selecti

6、on of type (1, 2, 3, or 5) is at the option of the producer, unless otherwise specified by the purchaser. (SeeSupplementary Requirement S90.)1.5 The maximum thicknesses available in the grades and products covered by this specification are shown in Table 1.1.6 When the steel is to be welded, a weldi

7、ng procedure suitable for the grade of steel and intended use or service is to beutilized. See Appendix X3 of Specification A6/A6M for information on weldability.1.7 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI unitsare s

8、hown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be usedindependently of the other, without combining values in any way.1.8 The text of this specification contains notes or footnotes, or both, that provide explanatory material. Such notes and

9、footnotes, excluding those in tables and figures, do not contain any mandatory requirements.1.9 For structural products produced from coil and furnished without heat treatment or with stress relieving only, the additionalrequirements, including additional testing requirements and the reporting of ad

10、ditional tests, of A6/A6M apply.2. Referenced Documents2.1 ASTM Standards:2A6/A6M Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet PilingA36/A36M Specification for Carbon Structural SteelA514/A514M Specification for High-Yield-Strength, Quenched and

11、Tempered Alloy Steel Plate, Suitable for WeldingA588/A588M Specification for High-Strength Low-Alloy Structural Steel, up to 50 ksi 345 MPa Minimum Yield Point, withAtmospheric Corrosion Resistance1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and Relat

12、edAlloys and is the direct responsibility of Subcommittee A01.02on Structural Steel for Bridges, Buildings, Rolling Stock and Ships.Current edition approved Nov. 1, 2012Oct. 1, 2013. Published March 2013October 2013. Originally approved in 1966. Last previous edition approved in 2012 asA572/A572M 12

13、.A572/A572M 12a. DOI: 10.1520/A0572_A0572M-12A.10.1520/A0572_A0572M-13.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the AST

14、M website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult

15、 prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA

16、 19428-2959. United States1TABLE 1 Maximum Product Thickness or SizeGradeYield Point, min Maximum Thickness or SizeZees and RolledTeesksi MPa Plates and BarsStructural ShapeFlange or LegThickness Sheet Pilingin. mm in. mm42 290A 42 290 6 150 all all all all50 345A 50 345 4B 100B all all all all55 38

17、0 55 380 2 50 all all all all60 415A 60 415 114C 32C 2 50 all all65 450 65 450 114 32 2 50 not available allA In the above tabulation, Grades 42, 50, and 60 290, 345, and 415, are the yield point levels most closely approximating a geometric progression pattern between 36ksi 250 MPa, min, yield poin

18、t steels covered by Specification A36/A36M and 100 ksi 690 MPa, min, yield strength steels covered by Specification A514/A514M.B Round bars up to and including 11 in. 275 mm in diameter are permitted.C Round bars up to and including 312 in. 90 mm in diameter are permitted.TABLE 2 Chemical Requiremen

19、tsA(Heat Analysis)Diameter, Thickness,or DistanceBetween ParallelFaces, in. mmPlates and BarsStructuralShapeFlange orLegThickness,in. mmGrade Carbon,max, % Manganese,Bmax, % Phosphorus,max, %Sulfur,max,%SiliconPlates to 112 in. 40mm Thick,Shapes withFlange or LegThickness to 3 in.75 mm inclusive,She

20、et Piling,Bars, Zees, andRolled TeesCPlates Over 112 in.40 mm Thick andShapes with FlangeThicknessOver 3 in.75 mmmax, % range, %6 150 all 42 290 0.21 1.35D 0.04 0.05 0.40 0.150.404 100E all 50 345 0.23 1.35D 0.04 0.05 0.40 0.150.402 50F all 55 380 0.25 1.35D 0.04 0.05 0.40 0.15-0.40114 32F #2 50 60

21、415 0.26 1.35D 0.04 0.05 0.40 G12 114 1332 1-2 25-50 65 450 0.23 1.65 0.04 0.05 0.40 G#12 13H # 1H 65 450 0.26 1.35 0.04 0.05 0.40 GA Copper when specified shall have a minimum content of 0.20 % by heat analysis (0.18 % by product analysis).B Manganese, minimum, by heat analysis of 0.80 % (0.75 % by

22、 product analysis) shall be required for all plates over 38 in. 10 mm in thickness; a minimum of 0.50 %(0.45 % by product analysis) shall be required for plates 38 in. 10 mm and less in thickness, and for all other products. The manganese to carbon ratio shall not be lessthan 2 to 1.C Bars over 112

23、in. 40 mm in diameter, thickness, or distance between parallel faces shall be made by a killed steel practice.D For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum ispermitted, up to a maximum of 1

24、.60 %.E Round bars up to and including 11 in. 275 mm in diameter are permitted.F Round bars up to and including 312 in. 90 mm in diameter are permitted.G The size and grade is not described in this specification.H An alternative chemical requirement with a maximum carbon of 0.21 % and a maximum mang

25、anese of 1.65 % is permitted, with the balance of the elements as shownin Table 2.TABLE 3 Alloy ContentTypeA Elements HeatAnalysis, %1 Columbium 0.0050.05B2 Vanadium 0.010.15C3 ColumbiumVanadiumColumbium plus vanadium0.005-0.05B0.010.150.020.15C3 ColumbiumVanadiumColumbium plus vanadium0.005-0.05B0.

26、010.15C0.020.15D5 TitaniumNitrogenVanadium0.006-0.040.0030.0150.06 maxA Alloy content shall be in accordance with Type 1, 2, 3, or 5 and the contents ofthe applicable elements shall be reported on the test report.B Product analysis limits = 0.004 to 0.06 %.C Product analysis limits = 0.010.005 to 0.

27、16 %.0.17%D Product analysis limits = 0.01 to 0.16 %.A572/A572M 1323. General Requirements for Delivery3.1 Structural products furnished under this specification shall conform to the requirements of the current edition ofSpecification A6/A6M, for the specific structural product ordered, unless a con

28、flict exists in which case this specification shallprevail.3.2 Coils are excluded from qualification to this specification until they are processed into a finished structural product.Structural products produced from coil means structural products that have been cut to individual lengths from a coil

29、. Theprocessor directly controls, or is responsible for, the operations involved in the processing of a coil into a finished structuralproduct. Such operations include decoiling, leveling or straightening, hot-forming or cold-forming (if applicable), cutting to length,testing, inspection, conditioni

30、ng, heat treatment (if applicable), packaging, marking, loading for shipment, and certification.NOTE 1For structural products produced from coil and furnished without heat treatment or with stress relieving only, two test results are to be reportedfor each qualifying coil. Additional requirements re

31、garding structural products produced from coil are described in A6/A6M.4. Materials and Manufacture4.1 The steel shall be killed5. Chemical Composition5.1 The heat analysis shall conform to the requirements prescribed in Table 2 and Table 3.5.2 The steel shall conform on product analysis to the requ

32、irements prescribed in Table 2 and Table 3, subject to the productanalysis tolerances in Specification A6/A6M.6. Mechanical Properties6.1 Tensile Properties:6.1.1 The material as represented by the test specimens shall conform to the tensile properties given in Table 4.7. Test Reports7.1 In addition

33、 to the Test Reports requirements in Specification A6/A6M, when Specification A588/A588M is substituted forSpecification A572/A572M, the test report shall include the statement “Specification A588/A588M substituted.”8. Keywords8.1 bars; bolted construction; bridges; buildings; columbium-vanadium; hi

34、gh-strength; low-alloy; plates; riveted construction;shapes; sheet piling; steel; structural steel; welded constructionTABLE 4 Tensile RequirementsAGradeYield Point, min Tensile Strength, min Minimum Elonga-tion, % B,C,Dksi MPa ksi MPa in 8 in.200 mm in 2 in.50 mm42 290 42 290 60 415 20 2450 345 50

35、345 65 450 18 2155 380 55 380 70 485 17 2060 415 60 415 75 520 16 1865 450 65 450 80 550 15 17A See specimen Orientation under the Tension Tests section of SpecificationA6/A6M.B Elongation not required to be determined for floor plate.C For wide flange shapes over 426 lb/ft 634 kg/m, elongation in 2

36、 in. 50 mm of19 % minimum applies.D For plates wider than 24 in. 600 mm, the elongation requirement is reduced twopercentage points for Grades 42, 50, and 55 290, 345, and 380, and threepercentage points for Grades 60 and 65 415 and 450. See elongation require-ment adjustments in the Tension Tests s

37、ection of Specification A6/A6M.A572/A572M 133SUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the order or contract. Standardizedsupplementary requirements for use at the option of the purchaser are listed in Specification A6/A6M.Those that are considered suit

38、able for use with this specification are listed by title:S5. Charpy V-Notch Impact Test.S18. Maximum Tensile StrengthS30. Charpy V-Notch Impact Test for Structural Shapes: Alternate Core LocationS32. Single Heat Bundles.In addition, the following supplementary requirements are suitable for use:S81.

39、Tensile StrengthS81.1 For Grade 50 345 steel of thicknesses 34 in. 20 mm and less, the tensile strength shall be a minimum of 70 ksi 485MPa.S90. TypeS90.1 The specific type of steel shall be as specified by the purchaser in the order or contract.S99. Interlock StrengthS99.1 The minimum strength of t

40、he interlocked joint required for certain services may be specified for certain sheet pilingsections subject to specific agreement between the material purchaser and the manufacturer.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue

41、(A572/A572M 12a) that may impact the use of this standard. (Approved Oct. 1, 2013.)(1) Added Supplementary Requirement S99.(2) Revised Table 3.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A572/A572M 12) that may impact the use

42、of this standard. (Approved Nov. 1, 2012.)(1) Revised 4.1 to allow killed steel only.(2) Revised Table 3 to remove a footnote on Columbium restrictions and to remove information on non-killed steels.A572/A572M 134Committee A01 has identified the location of selected changes to this standard since th

43、e last issue(A572/A572M 07) that may impact the use of this standard. (Approved May 1, 2012.)(1) Revised Section 7 to eliminate redundant language.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users o

44、f this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every fiv

45、e years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical co

46、mmittee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA

47、19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A572/A572M 135