ASTM A573 A573M-2005 Standard Specification for Structural Carbon Steel Plates of Improved Toughness.pdf

1、Designation: A 573/A 573M 05Standard Specification forStructural Carbon Steel Plates of Improved Toughness1This standard is issued under the fixed designation A 573/A 573M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers structural quality carbon-manganese-silicon steel plates in three tensile strength range

3、sintended primarily for service at atmospheric temperatureswhere improved notch toughness is important.1.2 Plates covered by this specification are limited to amaximum thickness of 1.5 in. 40 mm.1.3 If the steel is to be welded, it is presupposed that awelding procedure suitable for the grade of ste

4、el and intendeduse or service will be utilized. See Appendix X 3 of Specifi-cation A 6/A 6M for information on weldability.1.4 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in e

5、achsystem are not exact equivalents; therefore, each system is tobe used independently of the other without combining values inany way.2. Referenced Documents2.1 ASTM Standards:2A 6/A 6M Specification for General Requirements forRolled Structural Steel Bars, Plates, Shapes, and SheetPiling3. General

6、 Requirements for Delivery3.1 Plates furnished under this specification shall conformto the requirements of the current edition of SpecificationA 6/A 6M, unless a conflict exists in which case this specifi-cation shall prevail.4. Materials and Manufacture4.1 The steel shall be made to fine grain pra

7、ctice.5. Chemical Composition5.1 The heat analysis shall conform to the requirementsgiven in Table 1.5.2 The product analysis shall conform to the requirementsgiven in Table 1 subject to the product analysis tolerances inSpecification A 6/A 6M.6. Tension Test6.1 The plates, as represented by the ten

8、sion test specimens,shall conform to the tensile requirements given in Table 2.7. Keywords7.1 carbon steel; plates; structural steel; toughness; weldedconstruction1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel, and Related Alloys and is the direct respon

9、sibility of SubcommitteeA01.02 on Structural Steel for Bridges, Buildings, Rolling Stock, and Ships.Current edition approved Sept. 1, 2005. Published September 2005. Originallyapproved in 1966. Last previous edition approved in 2000 as A 573/A 573M 00a.2For referenced ASTM standards, visit the ASTM

10、website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.TABLE 1 Chemical Requirements (Heat Analysis)Composition, %Grade 58400Grade 65450Grade 70485Carbon, max:12 i

11、n. 13 mm and under 0.23 0.24 0.27Over12 in. 13 mm to 112in.,40 mm, incl0.23 0.26 0.28ManganeseA0.600.90 0.851.20 0.851.20Phosphorus, max 0.035 0.035 0.035Sulfur, max 0.04 0.04 0.04Silicon 0.100.35 0.150.40 0.150.40AFor each reduction of 0.01 percentage point below the specified maximum forcarbon, an

12、 increase of 0.06 percentage points above the specified maximum formanganese is permitted, up to a maximum of 1.50 % for Grades 58 and 65; andup to a maximum of 1.60 % for Grade 70.TABLE 2 Tensile RequirementsAGrade 58400Grade 65450Grade 70485Tensile strength, ksiMPa587140049065774505307090485620Yie

13、ld point, min, ksiMPa322203524042290Elongation in 8 in. 200mm minB,C,%21 20 18Elongation in 2 in. 50mm, minB,C,%24 23 21ASee the Orientation subsection in the Tension Tests section of SpecificationA 6/A 6M.BElongation need not be determined for floor plate.CFor plates wider than 24 in. 600 mm, the e

14、longation requirement is reducedtwo percentage points. See the Elongation Requirement Adjustments subsectionin the Tension Tests section of Specification A 6/A 6M.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West

15、 Conshohocken, PA 19428-2959, United States.SUPPLEMENTARY REQUIREMENTSStandardized supplementary requirements for use at the option of the purchaser are listed inSpecification A 6/A 6M. Supplementary requirements shall not apply unless specified in the purchaseorder or contract.SUMMARY OF CHANGESCom

16、mittee A01 has identified the location of selected changes to this standard since the last issue(A 573/A 573M 00a) that may impact the use of this standard.(1) Table 1 was revised.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item m

17、entionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committ

18、ee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meet

19、ing of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, P

20、O Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A 573/A 573M 052