ASTM A625 A625M-2003 Standard Specification for Tin Mill Products Black Plate Single Reduced.pdf

1、Designation: A 625/A 625M 03Standard Specification forTin Mill Products, Black Plate, Single-Reduced1This standard is issued under the fixed designation A 625/A 625M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last

2、 revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers single-reduced

3、 black plateproduced from low carbon, cold-reduced steel, furnished incoils and cut sizes, for use in the manufacture of containers,closures, signs, toys and other products, as well as for platingapplications.1.2 It may be supplied dry or oiled and with or withoutsurface treatment. This product is n

4、ormally supplied with atrimmed edge.1.3 This specification is applicable to orders in eitherinch-pound units (as A 625), which is supplied in thicknessesfrom 128-lb base weight (0.0141 in.) and lighter, or SI units (asA 625M), which is supplied in thicknesses from 0.358 mm andlighter.1.4 The values

5、stated in either inch-pound or SI units are tobe regarded as standard. Within the text, the SI units are shownin brackets. The values stated in each system are not exactequivalents; therefore, each system must be used indepen-dently of the other. Combining values from the two systemsmay result in no

6、nconformance with this specification.2. Referenced Documents2.1 ASTM Standards:A 623 Specification for Tin Mill Products, General Require-ments2A 623M Specification for Tin Mill Products, General Re-quirements Metric23. Ordering Information3.1 Orders for product under this specification shall includ

7、ethe following information, as required and applicable, toadequately describe the desired materials.3.1.1 Name of product (single-reduced black plate).3.1.2 Surface appearance and finish (Section 4).3.1.2.1 Dry.3.1.2.2 Oiled (type of oil; mineral or suitable for lithograph-ing) (Section 5).3.1.2.3 C

8、hemically treated and oiled (see SpecificationA 623 or Specification A 623M).3.1.3 Thickness (see Specification A 623 or SpecificationA 623M).3.1.4 Width.3.1.5 Length, for cut sizes only.3.1.6 Rolling direction must be specified by underlining thesteel (rolling width) for cut sizes.3.1.7 Steel type

9、(see Specification A 623 or SpecificationA 623M).3.1.8 Mechanical designation requirements (see Specifica-tion A 623 or Specification A 623M).3.1.9 Intended application.3.1.10 Quantity, in base boxes SITAs (see Note 5).3.1.11 On coils, specify minimum of range or acceptableinside diameters. The stan

10、dard inside diameter is approxi-mately 16 in. if ordered to Specification A 625 410 mm ifordered to Specification A 625M. Coils should be specified toa maximum coil weight if ordered to SpecificationA 625 massif ordered to Specification A 625M or maximum outsidediameter, or both.3.1.12 Packaging.3.1

11、.13 ASTM specification designation and year of issue.3.1.14 Special requirements, where applicable.NOTE 1Atypical ordering description is as follows: 1000 Base Boxes,Single-Reduced Black Plate, oiled, 80 lb base weight, 30 in. by coil, MR,T5CA for lithographed can bodies to ASTM A 625/A 625M - XX. 6

12、00SITAs, Single-Reduced Black Plate, oiled, 0.25 mm, 810 mm by coil, MR,T5CA for lithographed can bodies to Specification A 625/A 625M.NOTE 2A typical ordering description for cut sizes is as follows: 500Base Boxes, Single Reduced Black Plate, oiled, 80 lb base weight MR, T-2BA, 7C, 3034 in. by 3071

13、6 in., for lithographed can bodies in accordancewith Specification A 625/A 625M - XX. 100 SITAS, Single ReducedBlack Plate, oiled, MR, T-2 BA, 7C, 0.28 mm thickness, 781 by 773 mm,for lithographed can bodies in accordance with Specification A 625M/A 625M - XX.NOTE 3The production of coils does not a

14、fford the same opportunityfor inspection, grading, and sorting as does the production of cut sizes.Accordingly, appropriate processing and quality control procedures are1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct r

15、esponsibility of SubcommitteeA01.20 on Tin Mill Products.Current edition approved Sept. 10, 2003. Published November 2003. Originallyapproved in 1968. Last previous edition approved in 1998 as A 625/A 625M 98.2Annual Book of ASTM Standards, Vol 01.06.1Copyright ASTM International, 100 Barr Harbor Dr

16、ive, PO Box C700, West Conshohocken, PA 19428-2959, United States.required by the purchaser to obtain optimum utilization of the material.Cut sizes are line-inspected visually and mechanically during production.Sheets having surface imperfections that will not interfere with theirutilizations are in

17、cluded.NOTE 4Single-reduced black plate is highly susceptible to rusting andmust be properly handled during transit and storage.NOTE 5In inch-pound units single-reduced black plate is supplied onan area basis expressed in base boxes. In coils, the number of base boxesis computed from the measured le

18、ngth and the specified width. In cutlengths, the number of base boxes is computed from the specified lengthand width dimensions and sheet count. For calculating mass, the densityof steel for tin mill products is 0.2836 lbf/in.3. In SI units single-reducedblack plate is supplied on an area basis comp

19、uted in SITAs. In coils, thenumber of SITAs is computed from the specified length and the specifiedwidth. In cut lengths, the number of SITAs is computed from the specifiedlength and width dimensions and sheet count. For calculating mass, thedensity of steel for tin mill tests is 7850 kg/m2.4. Surfa

20、ce Appearance and Finish4.1 Surface AppearanceSingle-reduced black plate is cus-tomarily produced with ground roll and shot-blasted rollfinishes as follows:4.1.1 Ground-Roll Finishes:4.1.1.1 7AA lustrous smooth finish intended for electro-plating by the purchaser.4.1.1.2 7BAsmooth finish that may co

21、ntain fine grit lines.This finish is specified for special applications.4.1.1.3 7CA smooth finish with grit lines. The surfaceroughness will range from 10 to 25 in. Ra 0.254 to 0.635 mRa. This is the standard finish for tin mill products.4.1.2 Blasted and/or Otherwise Textured Roll Finishes:4.1.2.1

22、5AA shot-blasted finish (SBF) intended for litho-graphing.4.1.2.2 5CA shot-blasted finish (SBF) for general appli-cations. The surface roughness will range from 30 to 60 in. Ra0.760 to 1.52 m Ra.5. Oiling5.1 Black plate is furnished oiled or dry. Unless indicated bythe purchaser, single-reduced blac

23、k plate will be supplied dry.Any required oiling treatment will be negotiated between thepurchaser and the supplier.6. General Requirements for Delivery6.1 Product furnished under this specification shall conformto the applicable requirements of the current edition of Speci-fication A 623 or Specifi

24、cation A 623M unless otherwise pro-vided herein.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights,

25、 and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for rev

26、ision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you

27、 shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A 625/A 625M 032