ASTM A625 A625M-2013 Standard Specification for Tin Mill Products Black Plate Single-Reduced《单压延的镀锡轧制黑钢板的标准规格》.pdf

1、Designation: A625/A625M 08A625/A625M 13Standard Specification forTin Mill Products, Black Plate, Single-Reduced1This standard is issued under the fixed designation A625/A625M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the yea

2、r of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers single

3、-reduced black plate produced from low carbon, cold-reduced steel, furnished in coils andcut sizes, for use in the manufacture of containers, closures, signs, toys and other products, as well as for plating applications.1.2 It may be supplied dry or oiled and with or without surface treatment. This

4、product is normally supplied with a trimmededge.1.3 This specification is applicable to orders in either inch-pound units (as A625), which is supplied in thicknesses from 135-lbbase weight (0.0149 in.) and lighter, or SI units (as A625M), which is supplied in thicknesses from 0.378 mm and lighter.1.

5、4 The values stated in either inch-pound or SI units are to be regarded as standard. Within the text, the SI units are shownin brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of theother. Combining values from the two systems ma

6、y result in nonconformance with this specification.2. Referenced Documents2.1 ASTM Standards:2A623 Specification for Tin Mill Products, General RequirementsA623M Specification for Tin Mill Products, General Requirements Metric3. Ordering Information3.1 Orders for product under this specification sha

7、ll include the following information, as required and applicable, to adequatelydescribe the desired materials.3.1.1 Name of product (single-reduced black plate).3.1.2 Surface appearance and finish (Section 4).3.1.2.1 Dry.3.1.2.2 Oiled (type of oil; mineral or suitable for lithographing) (Section 5).

8、3.1.2.3 Chemically treated and oiled (see Specification A623 or Specification A623M).3.1.3 Thickness (see Specification A623 or Specification A623M).3.1.4 Width.3.1.5 Length, for cut sizes only.3.1.6 Rolling direction must be specified by underlining the steel (rolling width) for cut sizes.3.1.7 Ste

9、el type (see Specification A623 or Specification A623M).3.1.8 Mechanical designation requirements (see Specification A623 or Specification A623M).3.1.9 Intended application.3.1.10 Quantity, in base boxes SITAs (see Note 5).3.1.11 On coils, specify minimum of range or acceptable inside diameters. The

10、 standard inside diameter is approximately 16in. if ordered to Specification A625 410 mm if ordered to Specification A625M. Coils should be specified to a maximum coilweight if ordered to Specification A625 mass if ordered to Specification A625M or maximum outside diameter, or both.3.1.12 Packaging.

11、1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloysand is the direct responsibility of Subcommittee A01.20on Tin Mill Products.Current edition approved Oct. 1, 2008Oct. 1, 2013. Published October 2008October 2013. Originally approved in 196

12、8. Last previous edition approved in 20032008 asA625/A625M 03.A625/A625M 08. DOI: 10.1520/A0625_A0625M-08.10.1520/A0625_A0625M-13.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume informati

13、on, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict

14、 all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428

15、-2959. United States13.1.13 ASTM specification designation and year of issue.3.1.14 Special requirements, where applicable.NOTE 1A typical ordering description is as follows: 1000 Base Boxes, Single-Reduced Black Plate, oiled, 80 lb base weight, 30 in. by coil, MR,T5CA for lithographed can bodies to

16、 ASTM A625/A625M - XX. 600 SITAs, Single-Reduced Black Plate, oiled, 0.25 mm, 810 mm by coil, MR, T5CAfor lithographed can bodies to Specification A625/A625M.NOTE 2A typical ordering description for cut sizes is as follows: 500 Base Boxes, Single Reduced Black Plate, oiled, 80 lb base weight MR, T-2

17、BA, 7C, 3034 in. by 30716 in., for lithographed can bodies in accordance with Specification A625/A625M - XX. 100 SITAS,SITAs, Single Reduced BlackPlate, oiled, MR, T-2 BA, 7C, 0.28 mm thickness, 781 by 773 mm, for lithographed can bodies in accordance with Specification A625M/A 625M - XX.NOTE 3The p

18、roduction of coils does not afford the same opportunity for inspection, grading, and sorting as does the production of cut sizes.Accordingly, appropriate processing and quality control procedures are required by the purchaser to obtain optimum utilization of the material. Cut sizesare line-inspected

19、 visually and mechanically during production. Sheets having surface imperfections that will not interfere with their utilizations areincluded.NOTE 4Single-reduced black plate is highly susceptible to rusting and must be properly handled during transit and storage.NOTE 5In inch-pound units single-red

20、uced black plate is supplied on an area basis expressed in base boxes. In coils, the number of base boxes iscomputed from the measured length and the specified width. In cut lengths, the number of base boxes is computed from the specified length and widthdimensions and sheet count. For calculating m

21、ass, the density of steel for tin mill products is 0.2836 lbf/in.3. In SI units single-reduced black plate issupplied on an area basis computed in SITAs. In coils, the number of SITAs is computed from the specified length and the specified width. In cut lengths,the number of SITAs is computed from t

22、he specified length and width dimensions and sheet count. For calculating mass, the density of steel for tin milltests is 7850 kg/m2.4. Surface Appearance and Finish4.1 Surface AppearanceSingle-reduced black plate is customarily produced with ground roll and shot-blasted roll finishes asfollows:4.1.

23、1 Ground-Roll Finishes:4.1.1.1 7AA lustrous smooth finish intended for electroplating by the purchaser.4.1.1.2 7BA smooth finish that may contain fine grit lines. This finish is specified for special applications.4.1.1.3 7CA smooth finish with grit lines. The surface roughness will range from 10 to

24、25 in. Ra 0.254 to 0.635 m Ra.This is the standard finish for tin mill products.4.1.2 Blasted and/or Otherwise Textured Roll Finishes:4.1.2.1 5AA shot-blasted finish (SBF) intended for lithographing.4.1.2.2 5CAshot-blasted finish (SBF) for general applications. The surface roughness will range from

25、30 to 60 in. Ra 0.760to 1.52 m Ra.5. Oiling5.1 Black plate is furnished oiled or dry. Unless indicated by the purchaser, single-reduced black plate will be supplied dry.Anyrequired oiling treatment will be negotiated between the purchaser and the supplier.6. General Requirements for Delivery6.1 Prod

26、uct furnished under this specification shall conform to the applicable requirements of the current edition of SpecificationA623 or Specification A623M unless otherwise provided herein.7. Keywords7.1 black plate; single reduced; steel; tin mill productsASTM International takes no position respecting

27、the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard

28、 is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International H

29、eadquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This

30、standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A625/A625M 132