ASTM A650 A650M-2013 Standard Specification for Tin Mill Products Black Plate Double Reduced《双压延的薄片黑钢板标准规格》.pdf

1、Designation: A650/A650M 03 (Reapproved 2008)A650/A650M 13Standard Specification forTin Mill Products, Black Plate, Double Reduced1This standard is issued under the fixed designation A650/A650M; the number immediately following the designation indicates the yearof original adoption or, in the case of

2、 revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers double-reduced black plate, produced from low-carbon cold-reduced st

3、eel, furnished in coils andcut sizes, for use predominantly in the manufacture of containers. The product may be specified “as rolled,” without the removalof the rolling solution, and with no additional surface or oiling treatment. It may also be specified “cleaned” with the rollingsolution removed,

4、 with or without surface treatment and oiling. This product is normally supplied with trimmed edges.1.2 This specification is applicable to orders in either inch-pound units (as A650) which is supplied in thicknesses 0.0050 in.to 0.0113 in. or SI units as A650M which is supplied in thicknesses from

5、0.127 to 0.287 mm.1.3 The values stated in either inch-pound or SI units are to be regarded as standard. Within the text, the SI units are shownin brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of theother. Combining values fro

6、m the two systems may result in nonconformance with this specification.2. Referenced Documents2.1 ASTM Standards:2A623 Specification for Tin Mill Products, General RequirementsA623M Specification for Tin Mill Products, General Requirements Metric3. Ordering Information3.1 Orders for material under t

7、his specification shall include the following information, as required and applicable, to adequatelydescribe the desired materials.3.1.1 Name of material (double-reduced black plate),3.1.1.1 As rolled, with the rolling solution not removed,3.1.1.2 Cleaned, with the rolling solution removed, not reoi

8、led,3.1.1.3 Cleaned and oiled, with the rolling solution removed and reoiled,3.1.1.4 Cleaned, chemically treated and oiled, with the rolling solution removed, chemically treated and reoiled.3.1.2 Thickness (see Specification A623 Specification A623M),3.1.3 Width,3.1.4 Length, for cut sizes only,3.1.

9、5 Rolling direction must be specified by underlining the slit (rolling width) for cut sizes (see 4.1),3.1.6 Steel type (see Specification A623 Specification A623M),3.1.7 Mechanical designation requirements (see Specification A623 Specification A623M),3.1.8 Intended application,3.1.9 Quantity, in bas

10、e boxes SITASSITAs (see Note 5),3.1.10 On coils, specify minimum or range of acceptable inside diameters. The standard inside diameter is approximately 16in. if ordered to Specification A650 410 mm if ordered to Specification A650M. Coils should be specified to a maximum coilweight if ordered to Spe

11、cification A650 mass if ordered to Specification A650M or maximum outside diameter,3.1.11 Packaging,3.1.12 Special requirements where applicable, and1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloysand is the direct responsibility of Subc

12、ommittee A01.20on Tin Mill Products.Current edition approved Oct. 1, 2008Oct. 1, 2013. Published October 2008 October 2013. Originally approved in 1971. Last previous edition approved in 20032008 asA650/A650M 03.A650/A650M 03(2008). DOI: 10.1520/A0650_A0650M-03R08.10.1520/A0650_A0650M-13.2 For refer

13、encedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide th

14、e user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standa

15、rd as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.13 ASTM specification number and year of issue (A65

16、0/A650M 88).NOTE 1A typical ordering description is as follows: 1200 base boxes double-reduced black plate, cleaned and oiled, 60-lb base weight, 33 116 in.by coil, MR, DR8 CA, for 401 by 411 can bodies to ASTM Specification A650/A650M - XX. 250 SITAS,SITAs, double-reduced black plate, cleanedand oi

17、led, 0.17 mm thickness, 840 mm by coil, MR, DR8 CA, for 99 mm can bodies to ASTM Specification A650/A650M.NOTE 2A typical ordering description for cut sizes is as follows: 500 base boxes, double-reduced black plate, cleaned and oiled, 60-lb base weightMR, DR8 CA, 7C, 28 by 33 116 in., for 401 by 411

18、 can bodies in accordance with Specification A650/A650M - XX. 100 SITAS,SITAs, double-reducedblack plate, cleaned and oiled, MR, DR8 CA, 7C, 0.28 mm thickness, 781 by 773 mm, for 401 by 411 can bodies in accordance with SpecificationA650M/A 650M - XX.NOTE 3The production of coils does not afford the

19、 same opportunity for inspection, grading, and sorting as does the production of cut sizes.Accordingly, appropriate processing and quality control procedures are required by the purchaser to obtain optimum utilization of the material. Cut sizesare line-inspected visually and mechanically during prod

20、uction. Sheets having surface imperfections that will not interfere with their utilization areincluded.NOTE 4Double-reduced black plate is highly susceptible to rusting and must be properly handled during transit and storage.NOTE 5In inch-pound units, double-reduced black plate is supplied on an are

21、a basis expressed in base boxes. In coils, the number of base boxes iscomputed from the measured length and the specified width. The theoretical weight of a coil is computed by multiplying the number of base boxes ina coil by the specified base weight. In cut lengths, the number of base boxes is com

22、puted from the specified length and width dimensions and sheet count.The theoretical weight of a bundle is computed by multiplying the number of base boxes in the bundle by the specified base weight.In SI units, double-reduced black plate is supplied on an area basis expressed in SITAS.SITAs. In coi

23、ls, the number of SITASSITAs is computed fromthe measured length and the specified width. In cut sizes, the number of SITASSITAs is computed from the specified length and width dimensions andsheet count. For calculating mass, the density of steel for tin mill products is 7850 kg/m3 (see Specificatio

24、n A623M).4. Rolling Direction4.1 Double-reduced black plate is relatively brittle and has very distinct directional properties. The rolling direction must bespecified on cut lengths and will be indicated by underlining the slit (rolling width) dimension. To minimize the flange-crackinghazard when th

25、e product is used for can bodies, the rolling direction must be around the circumference of the can.5. Surface Finish5.1 Base Metal FinishDouble-reduced black plate is produced with a ground roll finish.5.1.1 7CA smooth finish with grit lines. The surface roughness will range from 6 to 25 in. Ra 0.1

26、52 to 0.635 m Ra. Thisis the standard finish for tin mill products.6. General Requirements for Delivery6.1 Material furnished under this specification shall conform to the applicable requirements of the current edition ofSpecification A623 Specification A623M unless otherwise provided herein.7. Keyw

27、ords7.1 black plate; double reduced; steel; tin mill productsSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A650/A650M - 03)(2008) that may impact the use of this standard. (October 1, 2008)2013)(1) Reapproved without changes.“SI

28、TAS” changed to “SITAs” in Section 3.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the ri

29、skof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of thi

30、s standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake

31、your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A650/A650M 132