ASTM A817-2003 Standard Specification for Metallic-Coated Steel Wire for Chain-Link Fence Fabric and Marcelled Tension Wire《链接围栏网和制成波状抗拉金属线用金属涂覆钢丝标准规范》.pdf

1、Designation: A 817 03Standard Specification forMetallic-Coated Steel Wire for Chain-Link Fence Fabric andMarcelled Tension Wire1This standard is issued under the fixed designation A 817; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revisi

2、on, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers metallic-coated carbon steelwire used in the manufacture of chain-link fen

3、ce fabric andmarcelled tension wire. Three types of coatings are covered:1.1.1 Type IAluminum-coated (aluminized),1.1.2 Type IIZinc-coated (galvanized), and1.1.3 Type IIIZinc-5 % Aluminum-Mischmetal (Zn-5Al-MM) alloy-coated.1.2 The chain-link fabric woven from wire in this specifi-cation is covered

4、separately by SpecificationsA 491 for Type I,A 392 for Type II, and F 1345 for Type III.1.3 The marcelled tension wire manufactured from wire inthis specification is covered separately in Specifications A 824and F 1664.1.4 This specification does not cover the wire used forSpecificationA 392 when th

5、e chain-link fence producer appliesthe coating after the weaving process.1.5 The values stated in inch-pound units are to be regardedas the standard. The values given in brackets are provided forinformation only.2. Referenced Documents2.1 ASTM Standards:A 90/A 90M Test Method for Weight Mass of Coat

6、ing onIron or Steel Articles with Zinc and Zinc-Alloy Coatings2A 370 Test Methods and Definitions for Mechanical Testingof Steel Products3A 392 Specification for Zinc-Coated Steel Chain-LinkFence Fabric2A 428/A 428M Test Method for Weight of Coating onAluminum-Coated Iron or Steel Articles2A 491 Spe

7、cification for Aluminum-Coated Steel Chain-Link Fence Fabric2A 700 Practices for Packaging, Marking, and LoadingMethods for Steel Products for Domestic Shipment4A 824 Specification for Metallic-Coated Steel MarcelledTension Wire for Use With Chain Link Fence2A 902 Terminology Relating to Metallic Co

8、ated Steel Prod-ucts2B6 Specification for Zinc5B 750 Specification for Zinc-5 % Aluminum-MischmetalAlloy (UNS Z38510) in Ingot Form for Hot-Dip Coatings5E29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications6E47 Test Methods for Chemical Analysis of Zinc D

9、ie-Casting Alloys7E 536 Test Method for Chemical Analysis of Zinc and ZincAlloys8F 1345 Specification for Zinc-5 % Aluminum-MischmetalAlloy-Coated Steel Chain-Link Fence Fabric2F 1664 Specification for Poly (Vinyl Chloride) (PVC)-Coated Steel Tension Wire Used With Chain-Link Fence22.2 International

10、 Lead Zinc Research Organization:GF-1 Standard Practice for Determination of Cerium andLanthanum Compositions in GalfanAlloy (5 %Al-0.04 %La-0.04 % Ce Bal SHG Zn)93. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, see Terminology A 902.4. Ordering Information4.1 Order

11、s for metallic-coated steel wire for chain link fencefabric or marcelled tension wire shall include the followinginformation:4.1.1 Quantity.4.1.2 Name of product.4.1.3 Coated wire diameter.4.1.4 Type of coating (see 5.3).1This specification is under the jurisdiction of ASTM Committee A05 onMetallic-

12、Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.12 on Wire Specifications.Current edition approved April 10, 2003. Published May 2003. Originallyapproved in 1983. Last previous edition approved in 2000 as A 817 00.2Annual Book of ASTM Standards, Vol 01.06.3Annual B

13、ook of ASTM Standards, Vol 01.03.4Annual Book of ASTM Standards, Vol 01.05.5Annual Book of ASTM Standards, Vol 02.04.6Annual Book of ASTM Standards, Vol 14.02.7Discontinued; see 1996 Annual Book of ASTM Standards , Vol 03.05.8Annual Book of ASTM Standards, Vol 03.06.9Available from International Lea

14、d Zinc Research Organization, P.O. Box12036, Research Triangle Park, NC 27709.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.5 Class of coating, if applicable (se

15、e Table 1 or Table 2).4.1.6 Packaging requirements (see Section 14).4.1.7 Certification or test report, or both, if specified (seeSection 13).4.1.8 ASTM designation and year of issue.NOTE 1A typical ordering description is as follows: 80 000-lbsteelwire for chain-link fence fabric, 0.148-in. diamete

16、r, Type II, Class 2,in 500 to 600-lb catchweight coils on tubular carriers to ASTMA 817 _.5. Materials and Manufacture5.1 The steel rod from which the wire is drawn shall bemanufactured by the open-hearth, electric-furnace, or basic-oxygen process.5.2 The wire shall be cold-drawn, then metallic-coat

17、ed atfinished size to produce the specified mechanical properties.5.3 The wire shall be furnished with one of three types ofcoating, as specified:5.3.1 Type IAluminum-Coated (Aluminized), in one classof coating weight as specified in Table 1.5.3.2 Type IIZinc-Coated (Galvanized), with coatingweights

18、 as specified in Table 1.5.3.3 Type IIIZn-5Al-MM Alloy Coated, with coatingweights as specified in Table 1.5.4 Type I coating shall be produced by a hot-dip process.Type II coating shall be produced by either a hot-dip or anelectrolytic process at the option of the producer. Type IIIcoating shall be

19、 produced by a hot-dip process.5.5 The ingot or pig aluminum used for Type I coating shallconform to the following impurity limits: copper, 0.10 % max,iron, 0.50 % max.5.6 Slab zinc if used for Type II coating shall be one of theappropriate grades that are described in Specification B6.5.7 The ingot

20、 used for Type III coating shall conform toSpecification B 750.5.7.1 Method of AnalysisThe determination of chemicalcomposition shall be made in accordance with suitable chemi-cal methods (Test Methods E47orE536), or other methods.In case of dispute, the results secured by Test Methods E47shall be t

21、he basis of acceptance.5.7.2 A standard practice for X-ray fluorescence spectrom-etry for determination of cerium and lanthanum in a Zn-5Al-MM alloy has been established by the International LeadZinc Research Organization (as Standard Practice GF-1).96. Mechanical Properties6.1 The metallic-coated w

22、ire for chain-link fence fabricshall meet the minimum breaking strength shown in Table 2when tested in accordance with Test Methods and DefinitionsA 370.6.2 The metallic coated wire for marcelled tension wireshall have a breaking strength of 1 950 lbf 8 670 N minimumand 3 200 lbf 14 230 N maximum wh

23、en tested in accordancewith Test Methods and Definitions A 370.7. Size and Tolerance7.1 The diameter of the coated wire shall be determined asthe average of two readings taken at right angles to each other,and in accordance with Practice E29.7.2 The permissible variation from the specified diameter

24、ofthe coated wire shall be 60.005 in. 0.13 mm.NOTE 2It is recognized that the surfaces of heavy metallic coatings,particularly those produced by the hot-dip process, are not perfectlysmooth. If the tolerance specified is rigidly applied to such irregularitiesthat are inherent to the product, unjusti

25、fied rejections of wire that wouldactually be satisfactory for use would occur. Therefore, it is intended thatthis tolerance be used in gaging the uniform areas of the coated wire.8. Weight of Coating8.1 Coating weights for Types I, II, or III shall conform tothe requirements of Table 1.8.2 Coating

26、Weight Determination:8.2.1 The coating weight for Type I shall be determined inaccordance with Test Method A 428/A 428M.8.2.2 The coating weight for Types II or III shall bedetermined in accordance with Test Method A 90/A 90M.9. Adherence of Coating9.1 The undeformed length of coated wire as represe

27、nted bythe test specimens shall be capable of being wrapped in a closehelix at a rate not exceeding 15 turns/min around a cylindricalsteel mandrel having a diameter equal to three times the testspecimen without cracking or flaking the coating to such anTABLE 1 Minimum Weight of Metallic CoatingSpeci

28、fied Diameter ofCoated Wire, in. mmMinimum Weight of Coating, oz/ft2g/m2 of Uncoated Wire SurfaceType I Type II, Class 3 Type II, Class 4 Type II, Class 5 Type III, Class 60 Type III, Class 1000.192 4.88 0.40 122 1.00 305 1.20 366 2.00 610 0.60 183 1.00 3050.177 4.50A0.40 122 0.90 275 1.20 366 2.00

29、610 0.60 183 1.00 3050.148 3.76 0.40 122 0.90 275 1.20 366 2.00 610 0.60 183 1.00 3050.135 3.43 0.40 1220.120 3.05 0.35 107 0.85 259 1.20 366 2.00 610 0.60 183 1.00 3050.113 2.87 0.30 92 0.80 244 1.20 366 2.00 610 0.60 183 1.00 305ASize 177 in. is only used for tension wire, not chain-link fabric.TA

30、BLE 2 Breaking StrengthSpecified Diameter of CoatedWire, in. mmBreaking Strength, min,lbf N0.192 4.88 2170 96500.148 3.76 1290 57400.135 3.43 1290 57400.120 3.05 850 37800.113 2.87 750 3340A817032extent that any coating metal can be removed by rubbing withthe bare fingers. Loosening or detachment du

31、ring the adhesiontest of superficial, small particles of coating metal formed bymechanical polishing of the surface of the coated wire shall notbe considered cause for rejection.10. Number of Tests and Retests10.1 Alot shall consist of all of the coils of wire of the samesize, type, and class, and s

32、hall be offered for inspection at onetime.Awire sample of sufficient length, approximately 4 ft 1.2m, shall be cut from either end of each coil selected for testsdescribed in Sections 6, 8, and 9.10.2 The number of test specimens taken from the ends ofcoils during production to ensure compliance wit

33、h Sections 6and 7 varies with the quality-control procedures and themanufacturing facilities of each manufacturer, but is generallynot less than 10 % of the coils produced. For the purpose offinal product testing, one specimen from every ten coils orfraction thereof in a lot shall be selected at ran

34、dom, or a totalof seven specimens, whichever is less.10.3 If one or more of the wire specimens fail any require-ment, the lot shall be retested. For retest purposes the originallot shall be regrouped into 50 coil lots or fraction thereof. Eachlot shall be tested for the property in which the origina

35、l samplefailed to comply at a frequency of 10 % or more so that thetotal number of tests is at least double the original. Any lot thatexhibits a failure shall be rejected. If during retesting anadditional quality parameter is observed to be defective, the lotof 50 is subject to rejection for that ca

36、use. The manufacturer ispermitted to test each coil in the failed lot for the property inwhich failure occurred and reject only the nonconformingcoils.11. Inspection11.1 Unless otherwise specified in the contract or purchaseorder, the producer is responsible for the performance of allinspection and

37、test requirements of this specification. Except asotherwise specified in the contract or purchase order, theproducer shall use his own or any other suitable facilities forthe performance of the inspection and test requirements unlessdisapproved by the purchaser at the time the order is placed.The pu

38、rchaser shall have the right to perform any of theinspections and tests set forth in this specification when suchinspections and tests are deemed necessary to ensure that thematerial conforms to prescribed requirements.12. Rejection and Rehearing12.1 Material that fails to conform to the requirement

39、s ofthis specification shall be rejected. Rejections shall be reportedto the producer or supplier promptly and in writing. In case ofdissatisfaction with the results of the test, the producer orsupplier may make claim for a rehearing.12.2 The material must be adequately protected and cor-rectly iden

40、tified in order that the producer may make a properinvestigation.13. Certification13.1 When specified in the purchase order or contract, aproducers or suppliers certification shall be furnished to thepurchaser that the material was manufactured, sampled, tested,and inspected in accordance with this

41、specification and hasbeen found to meet the requirements. When specified in thecontract or purchase order, a report of the test results shall befurnished.14. Packaging, Marking, and Loading14.1 Marking shall be by a tag securely attached to each coilof wire and shall show the identity of the produce

42、r, size of wire,type of coating, class of coating (if applicable), and ASTMdesignation.14.2 Packaging of the coils of wire shall be by agreementbetween the producer and the purchaser. This agreement mayinclude coil dimensions and weight.14.3 Unless otherwise specified, the packaging, marking,and loa

43、ding shall be in accordance with Practices A 700.15. Keywords15.1 chain-link fencing materials; fence fabric; fencingmaterial; metallic-coated steel wire; steel wire; tension wire;wireSUMMARY OF CHANGESThis section identifies the location of selected changes to this specification. For the convenienc

44、e of the user,Committee A05 has highlighted those changes that may impact the use of this specification. This section mayalso include descriptions of the changes or reasons for the changes, or both.A 817/A 817M - 03:(1) Added .135” wire to Table 1.(2) Added .135” wire to Table 2.A817033ASTM Internat

45、ional takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely the

46、ir own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should

47、be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standar

48、ds, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A817034