1、Designation: A962/A962M 15A962/A962M 16Standard Specification forCommon Requirements for Bolting Intended for Use at AnyTemperature from Cryogenic to the Creep Range1This standard is issued under the fixed designation A962/A962M; the number immediately following the designation indicates the yearof
2、original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers a group of common requirements t
3、hat shall apply to carbon, alloy, stainless steel, and nickel alloybolting under any of the following ASTM Specifications (or under any other ASTM Specifications that invoke this specificationor portions thereof):Title of Specifications ASTM DesignationAlloy-Steel and Stainless Steel Bolting Materia
4、lsfor High-Temperature ServiceA193/A193MCarbon and Alloy Steel Nuts for Bolts for HighPressure and High-Temperature ServiceA194/A194MAlloy Steel Bolting Materials for Low-TemperatureServiceA320/A320MAlloy-Steel Turbine-Type Bolting MaterialSpecially Heat Treated for High-TemperatureServiceA437/A437M
5、High-Temperature Bolting Materials With ExpansionCoefficients Comparable to Austenitic StainlessSteelsA453/A453MAlloy-Steel Bolting Materials for Special Applications A540/A540MPrecipitation-Hardening Bolting Material (UNSN07718) for High Temperature ServiceA1014/A1014M1.2 In case of conflict, the r
6、equirements of the individual product specification shall prevail over those of this specification.1.3 Fasteners are a wide-ranging classification that includes screws, bolts, nuts, washers, stud bolts, rivets, powder-actuatedstuds, staples, tacks, and pins. Bolting, which is composed of bolting mat
7、erials, such as rods, bars, flats, and forgings, which aresubsequently manufactured into bolting components, are a special sub-group of fasteners. Bolting materials and components havedesignated compositions and specific properties intended for applications in aggressive service where commercial gen
8、eric fastenersmay not be suitable or have insufficient fitness for purpose under certain conditions. These conditions include cryogenic or hightemperature service, or excessive vibration, impact, or shock. To further address any other special service conditions where boltingis intended for use, addi
9、tional requirements may be specified by mutual agreement between the purchaser and supplier.1.4 Supplementary requirements are provided for use at the option of the purchaser. The supplementary requirements only applywhen specified individually by the purchaser in the purchase order or contract.1.5
10、This specification is expressed in both inch-pound units and in SI units. Unless the purchase order or contract specifies theapplicable “M” specification designation (SI units) the inch-pound units shall apply. The values stated in either SI units orinch-pound units are to be regarded separately as
11、standard. Within the text, the SI units are shown in brackets. The values statedin each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining valuesfrom the two systems may result in nonconformance with the specification.1 This specification
12、is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.22on Steel Forgings and Wrought Fittings for Piping Applications and Bolting Materials for Piping and Special Purpose Applications.Current edition approved
13、Dec. 1, 2015March 1, 2016. Published December 2015March 2016. Originally approved in 1997. Last previous edition approved in 20142015as A962/A962MA962/A962M 15.14a. DOI: 10.1520/A0962_A0962M-15.10.1520/A0962_A0962M-16.This document is not an ASTM standard and is intended only to provide the user of
14、an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as publ
15、ished by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States12. Referenced DocumentsThe following documents shall form a part
16、of this specification to the extent specified. The latest issue shall apply unless oth-erwise specified.2.1 ASTM Standards:2A29/A29M Specification for General Requirements for Steel Bars, Carbon and Alloy, Hot-WroughtA193/A193M Specification forAlloy-Steel and Stainless Steel Bolting for HighTempera
17、ture or High Pressure Service and OtherSpecial Purpose ApplicationsA194/A194M Specification for Carbon Steel, Alloy Steel, and Stainless Steel Nuts for Bolts for High Pressure or HighTemperature Service, or BothA320/A320M Specification for Alloy-Steel and Stainless Steel Bolting for Low-Temperature
18、ServiceA370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA380 Practice for Cleaning, Descaling, and Passivation of Stainless Steel Parts, Equipment, and SystemsA437/A437M Specification for Stainless and Alloy-Steel Turbine-Type Bolting Specially Heat Treated for High-Temperat
19、ureServiceA453/A453M Specification for High-Temperature Bolting, with Expansion Coefficients Comparable to Austenitic StainlessSteelsA484/A484M Specification for General Requirements for Stainless Steel Bars, Billets, and ForgingsA540/A540M Specification for Alloy-Steel Bolting for Special Applicati
20、onsA700 Guide for Packaging, Marking, and Loading Methods for Steel Products for ShipmentA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsA788/A788M Specification for Steel Forgings, General RequirementsA941 Terminology Relating to Steel, Stainless Steel, Related
21、Alloys, and FerroalloysA967 Specification for Chemical Passivation Treatments for Stainless Steel PartsA1014/A1014M Specification for Precipitation-Hardening Bolting (UNS N07718) for High Temperature ServiceE3 Guide for Preparation of Metallographic SpecimensE381 Method of Macroetch Testing Steel Ba
22、rs, Billets, Blooms, and ForgingsE384 Test Method for Knoop and Vickers Hardness of MaterialsE566 Practice for Electromagnetic (Eddy Current) Sorting of Ferrous MetalsE1417 Practice for Liquid Penetrant TestingE1444 Practice for Magnetic Particle TestingE1916 Guide for Identification of Mixed Lots o
23、f MetalsF788/F788M Specification for Surface Discontinuities of Bolts, Screws, and Studs, Inch and Metric SeriesF812 Specification for Surface Discontinuities of Nuts, Inch and Metric SeriesF1470 Practice for Fastener Sampling for Specified Mechanical Properties and Performance InspectionF2328 Test
24、Method for Determining Decarburization and Carburization in Hardened and Tempered Threaded Steel Bolts,Screws, Studs, and NutsF2328M Test Method for Determining Decarburization and Carburization in Hardened and Tempered Threaded Steel Bolts,Screws, Studs, and Nuts (Metric)2.2 AIAG Standard:3AIAG B-5
25、 02.00 Primary Metals Identification Tag Application Standard2.3 ASME Standards:4B1.1 Screw ThreadsB1.13M Metric Screw Threads M ProfileB1.2 Gages and Gaging for Unified Screw ThreadsB1.3M Screw Thread Gaging Systems for Dimensional Acceptability of Metric Screw ThreadsB18.2.1 Square and Hex Bolts a
26、nd ScrewsB18.2.3.6M Metric Heavy BoltsB18.3 Hexagon Socket and Spline Socket ScrewsB18.18 Quality Assurance for FastenersB18.31.2 Continuous Thread Stud, Double-End Stud, and Flange Bolting Stud (Stud Bolt) (Inch Series)2.4 Other Documents:ASNT Recommended Practice No. SNT-TC-1A52 For referencedASTM
27、 standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3 Available from Automotive Industry Action Group (AIAG), 26200 Lahser Rd., Suite
28、 200, Southfield, MI 48033, http:/www.aiag.org.4 Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Two Park Ave., New York, NY 10016-5990, http:/www.asme.org.5 Available from American Society for Nondestructive Testing (ASNT), P.O. Box 28518, 1711 Arlin
29、gate Ln., Columbus, OH 43228-0518, http:/www.asnt.org.A962/A962M 1623. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 bara solid rolled or forged section that is long in relationship to its cross-sectional dimensions with a relatively constantcross section throughout its length.
30、 See Specification A29/A29M for definitions relating to the production of hot wrought and coldfinished bars.3.1.2 boltinga general term which includes bolting materials (rolled or forged bars or blanks, wire, rod, threaded bar, rotarypierced or extruded seamless tubes, bored bars, or forged hollows
31、from forged or rolled bar segments), which are manufacturedinto bolting components, including but not limited to, connectors, pins, restraining device components, shafts, bolts, nuts, screws,studs, and washers.3.1.3 bolting componentscomponents, such as bolts, nuts, screws, studs, washers, connector
32、s, and pins, are finished productswhich join, fasten, restrain, or position objects.3.1.4 bolting materialsstarting materials used for the manufacture of bolting components, such as rolled or forged or threadedsolid bars, blanks, wires, rods, or tubes or other hollow sections, that may be further pr
33、ocessed by heat treatment, cold working,forging, threading, or machining.3.1.5 certifying organizationthe company or association responsible for the conformance and marking of the product to thespecification requirements.3.1.6 classa term used to differentiate between different heat treatment condit
34、ions or strength levels, or both, often within thesame grade but sometimes within the same family of materials. May also apply to work hardened condition or strength level, orboth.3.1.7 gradean alloy described individually and identified by its own designation in a table of chemical requirements wit
35、hinany specification.3.1.8 length, components subject to full size testingthat portion of the bolting component whose body diameter isapproximately the same as the nominal thread size.3.1.9 lotunless otherwise specified, a lot shall consist of:3.1.9.1 bolting, heat treated in batch type furnacesall
36、bolting material of the same heat or cast of material, condition, finish,and size subjected to the same heat treatment in one tempering charge and submitted for inspection at the same time.3.1.9.2 bolting, heat treated in continuous type furnacesall bolting material of the same heat or cast of mater
37、ial, condition,finish, and size heat treated without interruption in a continuous type furnace.3.1.9.3 bolting, non heat treated (strain hardened)all bolting material of the same heat or cast of material, condition, reduction(cold work), finish, and size.3.1.9.4 components, machined from bolting mat
38、erialall bolting components machined from the same lot of bolting materialdefined as outlined in either 3.1.9.1 or 3.1.9.2, above without any subsequent heat treatment or hot or cold forming.3.1.9.5 components, heat treated in batch type furnacesall bolting component items produced by any manufactur
39、ing process(such as rolling, forging, or machining) from the same heat or cast of material, of the same prior condition, the same size, andsubjected to the same heat treatment in one tempering charge.3.1.9.6 components, heat treated in continuous type furnacesall bolting component items produced by
40、any manufacturingprocess (such as rolling, forging, or machining) from the same heat or cast of material, of the same prior condition, of the samesize, and then subjected to the same heat treatment in a four hour period and in one tempering charge.3.1.9.7 components, non heat treated (strain hardene
41、d)all bolting components of the same heat or cast of material, condition,reduction (cold work), finish, and size.3.1.9.8 strain hardened materialaustenitic stainless steel material which has been subjected to cold working sufficient to causea significant increase in strength.3.2 DefinitionsFor defin
42、itions of other terms used in this specification, refer to Terminology A941.4. Ordering Information4.1 It is the purchasers responsibility to specify in the purchase order all information necessary to purchase the needed material.Examples of such information include, but are not limited, to the foll
43、owing:4.1.1 Quantity and size,4.1.2 Product specification number with grade, class, type, as applicable, and including the product specification year date,4.1.3 Any additional information required by the individual product specification,4.1.4 Supplementary requirements,4.1.5 Additional requirements
44、(see 5.3, 5.5, 5.6, 6.1, 7.4, 13.1, 13.3.1, 13.3.3, 13.5.2, 13.6, 15.8, and 19.1).4.1.6 Additional ordering options provided in the individual product specification, and4.1.7 Dimensions (diameter, length of point, overall length, finish, shape, threads, etc.).A962/A962M 1635. Melting Process5.1 The
45、steel shall be produced by any of the following processes: basic-oxygen, electric-furnace, or vacuum-induction melting(VIM). The molten steel may be vacuum-treated prior to or during pouring of the ingot or strand casting.5.2 Unless otherwise specified in the individual product specification, the st
46、eel shall be fully killed. Use of the basic oxygenprocess shall be limited to grades containing less than 6 % chromium.5.3 If a specific type of melting is required by the purchaser, it shall be stated on the purchase order.5.4 The primary melting may incorporate separate degassing or refining and m
47、ay be followed by secondary melting such aselectroslag remelting or vacuum remelting. If secondary melting is employed, the heat shall be defined as all of the ingot remeltedfrom a single primary heat.5.5 Steel may be cast in ingots or may be continuously cast. When steel of different grades is cont
48、inuously cast identificationof the resultant transition material is required. The steel producer shall remove the transition material by an established procedurethat positively separates the grades. Should the purchaser deem it necessary to have the transition zone of two heats of the samegrade whic
49、h are continuously cast discarded, the purchaser shall invoke Supplementary Requirement S53.5.6 QualityThe steel producer quality control procedures shall provide sufficient testing of carbon and alloy steels inaccordance with Method E381 or other suitable method as agreed upon between the purchaser and the producer to assure theinternal quality of the product.5.6.1 Ingot Cast ProductVisual examination of transverse sections shall show no imperfections worse than the macrographsof Method E381 S2-R2-C3 or equivalent as agreed upon.5.6.2 Strand Cast Prod