ASTM B138 B138M-2006 Standard Specification for Manganese Bronze Rod Bar and Shapes《锰青铜杆材、棒材和型的材标准规范》.pdf

1、Designation: B 138/B 138M 06Standard Specification forManganese Bronze Rod, Bar, and Shapes1This standard is issued under the fixed designation B 138/B 138M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision

2、. A number in parentheses indicates the year of last reapproval.A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification establishes the requirements

3、for man-ganese bronze rod, bar and shapes produced in Copper AlloyUNS Nos. C67000, C67500, or C67600.1.2 The values stated in inch-pound units or SI units are tobe regarded separately in the standard. Within the text, the SIvalues are given in brackets. The values stated in each systemof units are n

4、ot exact equivalents; each system is independentof the other. Combining values from the two systems mayresult in nonconformance with the specification.1.3 The following safety hazard caveat pertains only to thePerformance Requirements section of this specification. Thisstandard does not purport to a

5、ddress all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.1.4 WarningMercury is a definite health hazard in useand

6、 disposal.NOTE 1Product suitable for hot forging applications is availableunder Specification B 124/B 124M.2. Referenced Documents2.1 ASTM Standards:2B 124/B 124M Specification for Copper and Copper AlloyForging Rod, Bar, and ShapesB 154 Test Method for Mercurous Nitrate Test for CopperAlloysB 249/B

7、 249M Specification for General Requirements forWrought Copper and Copper-Alloy Rod, Bar, Shapes andForgingsB 858 Test Method for Ammonia Vapor Test for Determin-ing Susceptibility to Stress Corrosion Cracking in CopperAlloysE8 Test Methods for Tension Testing of Metallic MaterialsE8M Test Methods f

8、or Tension Testing of Metallic Mate-rials MetricE54 Test Methods for Chemical Analysis of SpecialBrasses and Bronzes3E62 Test Methods for Chemical Analysis of Copper andCopper Alloys (Photometric Methods)E 478 Test Methods for Chemical Analysis of CopperAlloys3. General Requirements3.1 The following

9、 sections of Specification B 249/B 249Mconstitute a part of this specification:3.1.1 Terminology,3.1.2 Materials and Manufacture,3.1.3 Workmanship, Finish and Appearance,3.1.4 Sampling,3.1.5 Number of Tests and Retests,3.1.6 Specimen Preparation,3.1.7 Test Methods,3.1.8 Significance of Numerical Lim

10、its,3.1.9 Inspection,3.1.10 Rejection and Rehearing,3.1.11 Certification,3.1.12 Test Report,3.1.13 Packaging and Package Marking, and3.1.14 Supplementary Requirements.3.2 In addition, when a section with a title identical to oneof those referenced in 3.1 appears in this specification, itcontains add

11、itional requirements which supplement those ap-pearing in Specification B 249/B 249M.4. Ordering Information4.1 Include the following when placing orders for productunder this specification, as applicable:4.1.1 ASTM designation and year of issue,4.1.2 Copper Alloy UNS No. designation (for example,C6

12、7000),4.1.3 Temper,4.1.4 Form of product (for example, round, hexagonal),1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.02 on Rod,Bar, Wire, Shapes, and Forgings.Current edition approved Feb. 1, 2006.

13、 Published February 2006. Originallyapproved in 1941. Last previous edition approved in 2001 as B 138/B 138M 01.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the

14、standards Document Summary page onthe ASTM website.3Withdrawn.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.5 Dimensions (for example, diameter, distance between

15、parallel surfaces, width, thickness),4.1.6 Tolerances for shapes,4.1.7 Edge contours,4.1.8 Length,4.1.9 Quantity (total weight, footage or number of pieces),4.1.10 If product is purchased for agencies of the U.S.government (see Supplementary Requirements section ofSpecification B 249/B 249M).4.2 The

16、 following options are available and should bespecified at the time of placing the order when required:4.2.1 Heat identification or traceability details (Specifica-tion B 249/B 249M),4.2.2 Piston finish (Performance Requirements section),4.2.3 Residual stress test (Performance Requirements sec-tion)

17、,4.2.3.1 Ammonia Vapor Test or Mercurous Nitrate Test,4.2.3.2 For Ammonia Vapor Test, pH value other than 10.4.2.4 Certification (Specification B 249/B 249M), and4.2.5 Mill Test Report (Specification B 249/B 249M).5. Material and Manufacture5.1 MaterialThe material of manufacture shall be castbillet

18、s of Copper Alloy UNS No. C67000, C67500, or C67600as specified in the ordering information, and shall be of suchpurity and soundness as to be suitable for hot working.5.2 Manufacture:5.2.1 The product shall be manufactured by hot working(extrusion, forging, or rolling) to produce a uniform wroughts

19、tructure in the finished product.5.2.2 The product shall be finished by such cold working,annealing, and straightening as may be necessary to achievethe required properties.6. Chemical Composition6.1 The material shall conform to the chemical compositionrequirements in Table 1 for the Copper Alloy U

20、NS No.specified in the ordering information.6.1.1 These compositional limits do not preclude the pres-ence of other elements. By agreement between the manufac-turer and the purchaser, limits may be established and analysisrequired for unnamed elements.6.2 For copper alloys in which zinc is specified

21、 as the“remainder,” either copper or zinc may to be taken as thedifference between the sum of results for all elements deter-mined and 100 %. When copper is so determined, that differ-ence value shall conform to the requirements given in Table 1.6.2.1 When all elements in Table 1 are determined, the

22、 sumof results shall be 99.5 % min.7. Temper7.1 The standard tempers for products described in thisspecification are given in Tables 2 and 3.7.1.1 Soft Anneal Temper (O60),7.1.2 As Hot Rolled Temper (M20),7.1.3 As Hot Extruded Temper (M30),7.1.4 Half-Hard Temper (H02), and7.1.5 Hard Temper (H04).8.

23、Mechanical Property Requirements8.1 Tensile Requirements:8.1.1 The product furnished under this specification shallconform to the tensile requirements prescribed in Table 2 orTable 3 when tested in accordance with Test Methods E8orE8M.9. Performance Requirements9.1 Residual Stress Test:9.1.1 When sp

24、ecified in the contract or purchase order, theproduct shall be tested for residual stress according to therequirements of Test Method B 154 or Test Method B 858 andshow no signs of cracking. (WarningMercury is a definitehealth hazard. With the mercurous nitrate test, equipment forthe detection and r

25、emoval of mercury vapor produced involatilization is recommended. The use of protective gloves forthis test is recommended.)9.1.2 When the ammonia vapor test is used, the test pHvalue appropriate for the intended application shall be 10unless otherwise specified by the purchaser.NOTE 2Aresidual stre

26、ss test provides information about the adequacyof the stress relief of the material. Bar straightening is a method ofmechanical stress relief. Stress relief annealing is a method of thermalstress relief.9.2 Piston FinishWhen specified in the contract or pur-chase order, round rod over 0.500 in. 13 m

27、m in diameter shallbe furnished piston finish.10. Purchases for U.S. Government10.1 Product purchased for agencies of the U.S. governmentshall conform to the additional requirements prescribed in theSupplementary Requirements section of Specification B 249/B 249M.11. Dimensions and Permissible Varia

28、tions11.1 The dimensions and tolerances for product describedby this specification shall be as specified in SpecificationB 249/B 249M with particular reference to the following tablesand related paragraphs:11.2 Diameter or Distance Between Parallel Surfaces:11.2.1 Rod: Round, Hexagonal, Octagonal, d

29、rawnReferto Table 2.11.2.2 Rod, M30 Temper,Refer to Table 5 for UNS AlloyNo. C67000 and Table 4 for UNS Alloy Nos. C67500 andC67600.11.2.3 Rod, Round, M20 TemperRefer to Table 6.TABLE 1 Chemical RequirementsElement, % Copper Alloy UNS No.C67000 C67500 C67600CopperA63.068.0 57.060.0 57.060.0Tin 0.50

30、max 0.501.5 0.501.5Lead 0.20 max 0.20 max 0.501.0Zinc remainder remainder remainderIron 2.04.0 0.82.0 0.401.3Aluminum 3.06.0 0.25 max . . .Manganese 2.55.0 0.050.50 0.050.50AIncludes silver.B 138/B 138M 062TABLE 2 Tensile Requirements, in./lbFormTemper DesignationDiameter or DistanceBetween Parallel

31、Surface,Ain.TensileStrength,min, ksiYield Strength at 0.5 %Extension Under Load,min, ksiElongationmin, %BCode NameCopper Alloy UNS No. C67000Rod and bar O60H02H04soft-annealhalf-hardhardall sizesall sizesall sizes851051154560681075M10M20M30as hot forgedas hot rolledas hot extrudedall sizesCC CCopper

32、 Alloy UNS Nos. C67500 and C67600Rod O60 soft anneal all sizes 55 22 20H02 half-hard 1 and under 72 36 13over 1 to 212 incl 70 35 15over 212 65 32 17H04 hard 1 and under 80 56 8over 1 to 112 incl 76 52 10over 112 to 212 incl 73 48 12over 212 68 45 16Bar O60 soft anneal all sizes 55 22 20H02 half-har

33、d 1 and under 72 36 13over 1 to 212 incl 70 35 15over 212 65 32 17H04 hard 1 and under 76 52 8over 1 to 212 incl 72 47 12over 212 68 45 16ShapesDO60 soft anneal all sizes 55 22 20AFor rectangular bar, the Distance Between Parallel Surfaces refers to thickness.BElongation in 43 diameter or thickness

34、of specimen. In any case, a minimum gage length of 1 in. shall be used.CSee Note 3. The tensile properties of as-hot-forged (M10), as-hot-rolled (M20), and as-hot-extruded (M30) are essentially the same as those shown for rod and bar,but have not been finalized for publication.DTensile requirements

35、for drawn shapes shall be as agreed upon between the manufacturer and the purchaser at the time of the order.TABLE 3 Tensile Requirements, SIFormTemper DesignationDiameter or DistanceBetween ParallelSurface,AmmTensile Strength,min, MPaYield Strength at 0.5 %Extension Under Load,min, MPaElongationmin

36、, %BCode NameCopper Alloy UNS No. C67000Rod and bar O60H02H04soft-annealhalf-hardhardall sizesall sizesall sizes5857207903104154701075M10M20M30as hot forgedas hot rolledas hot extrudedall sizesCCCCopper Alloy UNS Nos. C67500 and C67600Rod O60 soft anneal all sizes 380 150 20H02 half-hard 25 and unde

37、r 500 250 13over 25 to 65 incl 450 240 15over 65 450 220 17H04 hard 25 and under 550 385 8over 25 to 38 incl 525 360 10over 38 to 65 incl 510 330 12over 65 470 310 16Bar O60 soft anneal all sizes 380 150 20H02 half-hard 25 and under 500 250 13over 25 to 65 incl 450 240 15over 65 450 220 17H04 hard 2

38、5 and under 525 360 8over 25 to 65 incl 500 325 12over 65 470 310 16ShapesDO60 soft anneal all sizes 380 150 20AFor rectangular bar, the Distance Between Parallel Surfaces refers to thickness.BElongation in 43 diameter or thickness of specimen. In any case, a minimum gage length of 25 mm shall be us

39、ed.CSee Note 3. The tensile properties of as-hot-forged (M10), as-hot-rolled (M20), and as-hot-extruded (M30) are essentially the same as those shown for rod and bar,but have not been finalized for publication.DTensile requirements for drawn shapes shall be as agreed upon between the manufacturer an

40、d the purchaser at the time of the order.B 138/B 138M 06311.2.4 Rod, Piston FinishRefer to Table 3.11.2.5 Rod, M10 TemperRefer to Table 12.11.3 Width and Thickness:11.3.1 Bar, Rectangular and Square, drawnRefer toTables 9 and 11.11.3.2 Bar in M10 TemperRefer to Table 12.NOTE 3M10 as-hot-forged rod a

41、nd bar are generally produced in sizesover 312 in. 88 mm in diameter and should not be confused with M30as-hot-extruded or M20 as-hot-rolled rod and bar.11.3.3 Bar, Rectangular and Square in M30 TemperReferto Table 4 for thickness and width for UNS Alloy Nos. C67500and C67600, and to Table 5 for UNS

42、 Alloy No. C67000.11.4 ShapesThe dimensional tolerances for shapes shallbe agreed upon between the manufacturer and the purchaser.11.5 Lengths:11.5.1 Rod, Bar, and ShapesRefer to Table 13 for toler-ances.11.5.2 Schedule of LengthsRefer to Table 14 for specificand stock with ends for UNS Alloy Nos. C

43、67500 and C67600and to Table 15 for UNS Alloy No. C67000.11.6 Straightness:11.6.1 Rod, Bar, and Shapes, drawnRefer to Table 16.11.6.2 Shafting RodRefer to Table 17.11.6.3 Rod, Bar and Shapes in M20, M30 or M10Tempers shall have straightness requirements as agreed uponbetween the manufacturer and the

44、 purchaser.11.7 Edge Contours:11.7.1 For a description of edge contours, refer to thesection entitled, “Edge Contours” and Figs. 1, 2, and 3 inSpecification B 249/B 249M.12. Test Methods12.1 Chemical Analysis:12.1.1 In cases of disagreement, determine the compositionusing the following methods:Eleme

45、nt Test MethodsAluminum E54Copper E 478Iron E54Lead E 478 (atomic absorption)Manganese E62Tin E 478 (titrimetric)Zinc E 478 (titrimetric)12.1.2 Test method(s) to be followed for the determinationof element(s) resulting from contractual or purchase orderagreement shall be as agreed upon between the m

46、anufacturer orsupplier and the purchaser.13. Keywords13.1 manganese bronze bar; manganese bronze rod; man-ganese bronze shape; UNS No. C67000; UNS No. C67500;UNS No. C67600SUMMARY OF CHANGESCommittee B05 has identified the location of selected changes to this standard since the last issue(B 138/B 13

47、8M 01) that may impact the use of this standard. (Approved Feb. 1, 2006.)(1) Section 11 was revised to clarify and coordinate withSpecification B 249/B 249M.(2) Various sections were editorially revised to conform withthe latest changes to B05 Outline of Form.ASTM International takes no position res

48、pecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This

49、standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your view