ASTM B333-2003(2013) Standard Specification for Nickel-Molybdenum Alloy Plate Sheet and Strip《镍钼合金板材、薄板材和带材标准规格》.pdf

1、Designation: B333 03 (Reapproved 2013)Standard Specification forNickel-Molybdenum Alloy Plate, Sheet, and Strip1This standard is issued under the fixed designation B333; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of l

2、ast revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification2covers plate, sheet

3、, and strip ofnickel-molybdenum alloys (UNS N10001, N10665, N10675,N10629, and N10624)* as shown in Table 1, for use in generalcorrosive service.1.2 The following products are covered under this specifi-cation:1.2.1 Sheet and StripHot or cold rolled, solution annealed,and descaled unless solution an

4、neal is performed in an atmo-sphere yielding a bright finish.1.2.2 PlateHot or cold rolled, solution annealed, anddescaled.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for informatio

5、n onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sh

6、eet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B906 Specification for General Requirements for Flat-Rolled Nicke

7、l and Nickel Alloys Plate, Sheet, and StripE112 Test Methods for Determining Average Grain SizeE140 Hardness Conversion Tables for Metals RelationshipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, andScleroscope Hardness3. Terminology3.1 Definitions

8、 of Terms Specific to This Standard:3.1.1 cold-rolled plate, nmaterial316 to38 in. (4.76 to9.52 mm), inclusive, in thickness.3.1.2 hot-rolled plate, nmaterial316 in. (4.76 mm) andover in thickness.3.1.3 plate, nmaterial316 in. (4.76 mm) and over inthickness.3.1.4 sheet and strip, nmaterial under316

9、in. (4.76 mm) inthickness.4. General Requirements4.1 Material furnished under this specification shall con-form to the applicable requirements of Specification B906unless otherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that ar

10、e necessary for material ordered under thisspecification. Examples of such requirements include, but arenot limited to the following:5.1.1 AlloyTable 1,5.1.2 DimensionsThickness (in decimals of an inch),width, and length (inch or fractions of an inch),5.1.3 Optional RequirementPlate; how the plate i

11、s to becut (Specification B906, Table A2.3)5.1.4 CertificationState if certification or a report of testresults is required (Specification B906, Section 21),5.1.5 Purchase InspectionState which tests or inspectionsare to be witnessed (Specification B906, Section 18), and5.1.6 Samples for Product (Ch

12、eck) AnalysisState whethersamples should be furnished (Specification B906, Section7.2.2).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edi

13、tion approved Feb. 1, 2013. Published February 2013. Originallyapproved in 1958. Last previous edition approved in 2008 as B333 03 (2008).DOI: 10.1520/B0333-03R13.* New designation established in accordance with ASTM E527 and SAE J 1086,Practice for Numbering Metals and Alloys (UNS).2For ASME Boiler

14、 and Pressure Vessel Code applications, see related Specifi-cation SB-333 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards D

15、ocument Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Chemical Composition6.1 The material shall conform to the composition limitsspecified in Table 1.6.2 If a product (check) analysis is made by t

16、he purchaser,the material shall conform to the requirements specified inTable 1 and Specification B906.7. Mechanical Properties and Other Requirements7.1 Tensile PropertiesThe material shall conform to theroom temperature tensile properties prescribed in Table 2.7.2 HardnessThe hardness values given

17、 in Table 2 areinformative only.7.3 Grain Size for Sheet and StripSheet and strip shallconform to the grain sizes as illustrated in Plate 1 of TestMethods E112. The requirements shall be as indicated in Table3.8. Dimensions, Mass, and Permissible Variations8.1 WeightFor calculations of mass or weigh

18、t, the follow-ing densities shall be used:DensityAlloy lb/in.3(g/cm3)N10001 0.334 (9.24)N10665 0.333 (9.22)N10675 0.333 (9.22)N10629 0.333 (9.22)N10624 0.322 (8.9)8.2 Thickness:8.2.1 Sheet and StripThe thickness shall be measuredwith the micrometer spindle38 in. (9.525 mm) or more fromany edge for m

19、aterial 1 in. (25.4 mm) or over in width and atany place on material under 1 in. (25.4 mm) in width.8.3 Length:8.3.1 Sheet and StripSheet and strip may be ordered to cutlengths, in which case a variation of18 in. (3.175 mm) over thespecified length shall be permitted, with a 0 minus tolerance.8.4 St

20、raightness:8.4.1 The edgewise curvature (depth of chord) of flat sheet,strip, and plate shall not exceed 0.05 in. (1.27 mm) multipliedby the length in feet or 0.04 mm multiplied by the length incentimetres.8.4.2 Straightness for coiled strip is subject to agreementbetween the manufacturer and the pu

21、rchaser.8.5 Squareness (Sheet)For sheets of all thicknesses andwidths of 6 in. (152.4 mm) or more, the angle between adjacentsides shall be 90 6 0.15 degrees (116 in. in 24 in. or 2.6mm/m).8.6 FlatnessPlate, sheet, and strip shall be commerciallyflat.8.7 Edges:8.7.1 Plates shall have sheared, abrasi

22、ve cut, or plasma-torch-cut edges as specified.8.7.2 Sheet and strip shall have sheared or slit edges.9. Product Marking9.1 Each plate, sheet, or strip shall be marked on one facewith the specification number, alloy, heat number, manufactur-ers identification, and size. The markings shall have nodel

23、eterious effect on the material or its performance and shallbe sufficiently stable to withstand normal handling.9.2 Each bundle or shipping container shall be marked withthe name of the material; this specification number; alloy; thesize; gross, tare, and net weight; consignor and consigneeaddress;

24、contract or order number; and such other informationas may be defined in the contract or order.10. Keywords10.1 plate; sheet; strip; UNS N10001; UNS N10629; UNSN10665; UNS N10675; UNS N10624TABLE 1 Chemical RequirementsElementComposition Limits, %AlloyN10001AlloyN10665AlloyN10675AlloyN10629AlloyN106

25、24Nickel remainderAremainderA65.0 min remainderABalMolybdenum 26.030.0 26.030.0 27.032.0 26.030.0 21.0-25.0Iron 4.06.0 2.0 max 1.03.0 1.06.0 5.0-8.0Chromium 1.0 max 1.0 max 1.03.0 0.51.5 6.0-10.0Carbon, max 0.05 0.02 0.01 0.01 0.01Silicon, max 1.0 0.10 0.10 0.05 0.10Cobalt, max 2.5 1.00 3.0 2.5 1.0M

26、anganese,max1.0 1.0 3.0 1.5 1.0Phosphorus,max0.04 0.04 0.030 0.04 0.025Sulfur, max 0.03 0.03 0.010 0.01 0.01Vanadium 0.20.4 . 0.20 max . .Nickel plusMolybdenum. . 94.098.0 .Aluminum . . 0.50 max 0.10.5 0.5Columbium(Nb), max. . 0.20 .Copper, max . . 0.20 0.5 0.5Tantalum,max. . 0.20 .Titanium,max. . 0

27、.20 .Tungsten,max. . 3.0 .Zirconium,max. . 0.10 .Magnesium,max. . . . .ASee Specification B906.B333 03 (2013)2APPENDIX(Nonmandatory Information)X1. HEAT TREATMENTX1.1 Proper heat treatment during or subsequent to fabrica-tion is necessary for optimum performance, and the manufac-turer shall be consu

28、lted for details.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of

29、 such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for a

30、dditional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to

31、 the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at

32、the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE 2 Mechanical Property RequirementsAlloyThickn

33、ess,in. (mm)Tensile Strength,min, psi (MPa)Yield Strength(0.2 % Offset),min, psi (MPa)Elongationin2in.(50.8 mm)or 4DAmin, %RockwellHardness,BmaxSheet and StripN10001 Under316 (4.76) 115 000 (795) 50 000 (345) 45 100 HRBN10665 Under316 (4.76) 110 000 (760) 51 000 (350) 40 100 HRBN10675 Under316 (4.76

34、) 110 000 (760) 51 000 (350) 40 100 HRBN10629 Under316 (4.76) 110 000 (760) 51 000 (350) 40 100 HRBN10624 Under316 (4.76) 104 000 (720) 46 000 (320) 40 100 HRBPlateN10001316 to 212 in. (4.76 to 63.5 mm), incl 100 000 (690) 45 000 (310) 40 100 HRBN10665316 to 212 in. (4.76 to 63.5 mm), incl 110 000 (

35、760) 51 000 (350) 40 100 HRBN10675316 to 212 in. (4.76 to 63.5 mm), incl 110 000 (760) 51 000 (350) 40 100 HRBN10629316 to 212 in. (4.76 to 63.5 mm), incl 110 000 (760) 51 000 (350) 40 100 HRBN10624316 to 212 in. (4.76 to 63.5 mm), incl 104 000 (720) 46 000 (320) 40 100 HRBAD refers to the diameter

36、of the tension specimen.BHardness values are shown for information purposes only and are not to be used as a basis for rejection or acceptance. For approximate hardness conversions, seeHardness Conversion Tables E140.TABLE 3 Grain Size for Annealed SheetThickness,in. (mm)ASTM MicrograinSize Number,maxAverage GrainDiameter, max,mm (in.)0.125 (3.175) and under 3.0 0.127 (0.0050)Over 0.125 (3.175) 1.5 0.214 (0.0084)B333 03 (2013)3