ASTM B409-2006(2016) Standard Specification for Nickel-Iron-Chromium Alloy Plate Sheet and Strip《镍铁铬合金板材 薄板材和带材的标准规格》.pdf

1、Designation: B409 06 (Reapproved 2016)Standard Specification forNickel-Iron-Chromium Alloy Plate, Sheet, and Strip1This standard is issued under the fixed designation B409; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers UNS N08120, UNS N08890,UNS N08800, UNS N08810, and UNS N088113in the form ofrolled plate,

3、sheet, and strip. Alloy UNS N08800 is normallyemployed in service temperatures up to and including 1100F(593C). Alloys UNS N08120, UNS N08810, UNS N08811,and UNS N08890 are normally employed in service tempera-tures above 1100F (593C) where resistance to creep andrupture is required, and they are an

4、nealed to develop controlledgrain size for optimum properties in this temperature range.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standa

5、rd.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateSafety Data Sheet (SDS) for this product/material as provi

6、dedby the manufacturer, to establish appropriate safety and healthpractices, and determine the applicability of regulatory limi-tations prior to use.2. Referenced Documents2.1 ASTM Standards:4B408 Specification for Nickel-Iron-Chromium Alloy Rodand BarB906 Specification for General Requirements for

7、Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE140 Hardness Conversion Tables for Metals RelationshipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, Sclero-scope Hardness, and Leeb HardnessF155 Method of Test for Temper of Strip and She

8、et Metalsfor Electronic Devices (Spring-Back Method) (Withdrawn1982)53. Terminology3.1 Definitions of Terms Specific to This StandardTheterms given in Table 1 shall apply.4. General Requirements4.1 Material furnished under this specification shall con-form to the applicable requirements of Specifica

9、tion B906unless otherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include but are not limited

10、 tothe following:5.1.1 Alloy (Table 2),5.1.2 Condition (Temper)Table 3 and Table 4, AppendixX1, and Specification B906.5.1.3 FinishAppendix X1 and Specification B906.5.1.4 DimensionsThickness, width, and length.5.1.5 Optional Requirements:5.1.5.1 Sheet and StripWhether to be furnished in coil, incut

11、 straight lengths, or in random straight lengths.5.1.5.2 StripWhether to be furnished with commercial slitedge, square edge, or round edge.5.1.5.3 PlateWhether to be furnished specially flattened(see 9.7.2); also how plate is to be cut (Specification B906,Table A3.4 and Table A3.7.5.1.6 Fabrication

12、DetailsNot mandatory but helpful tothe manufacturer:5.1.6.1 Welding or BrazingProcess to be employed.5.1.6.2 PlateWhether material is to be hot-formed.5.1.7 CertificationState if certification or a report of testresults is required (Specification B906).1This specification is under the jurisdiction o

13、f ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved June 1, 2016. Published June 2016. Originallyapproved in 1957. Last previous edition approved in 2011 as B409 06 (2011).DO

14、I: 10.1520/B0409-06R16.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SB 409 in Section II of that Code.3New designations established in accordance with Practice E527 and SAEJ1086, Practice for Numbering Metals and Alloys (UNS).4For referenced ASTM standards, visit

15、 the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.5The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM

16、 International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15.1.8 Samples for Product (Check) AnalysisWhethersamples for product (check) analysis should be furnished (see7.2).5.1.9 Purchaser InspectionIf purchaser wishes to witnesstests or inspection of materi

17、al at place of manufacture, thepurchase order must so state indicating which tests or inspec-tions are to be witnessed (Specification B906).6. Materials and Manufacture6.1 Heat TreatmentThe final heat treatment of UNSN08120 shall be 2150F (1177C) minimum, UNS N08810,2050F (1121C) minimum, UNS N08811

18、 and UNS N08890,2100F (1149C) minimum.7. Chemical Composition7.1 The material shall conform to the composition limitsspecified in Table 2.7.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations in Specification B906.8. Mech

19、anical and Other Requirements8.1 Mechanical PropertiesThe material shall conform tothe mechanical properties specified in Table 3.8.2 Grain SizeAnnealed Alloys UNS N08120, UNSN08810, UNS N08811, and UNS N08890 shall conform to anaverage grain size of ASTM No. 5 or coarser.8.3 Deep-Drawing and Spinni

20、ng Quality Sheet and Strip(Alloy UNS N08800) Shall conform to the grain size andhardness requirements as provided in Table 4.8.3.1 The mechanical properties of Table 3 do not apply todeep drawing and spinning quality sheet and strip.8.4 Annealing TemperatureAlloy UNS N08120 shall beannealed at 2150F

21、 (1177C) minimum, and UNS N08810,2050F (1121C) minimum.9. Dimensions and Permissible Variations9.1 Thickness and Weight:9.1.1 PlateFor plate up to 2 in. (50.8 mm), incl, inthickness, the permissible variation under the specified thick-ness and permissible excess in overweight shall not exceed theamo

22、unts prescribed in Table A3.1 in Specification B906.9.1.1.1 For use with Table A3.1 in Specification B906, plateshall be assumed to weigh 0.287 lb/in.3(7.944 g/cm3).9.1.2 PlateFor plate over 2 in. (50.8 mm) in thickness, thepermissible variations over the specified thickness shall notexceed the amou

23、nts prescribed in Table A3.2 in SpecificationB906.9.1.3 Sheet and StripThe permissible variations in thick-ness of sheet and strip shall be as prescribed in Table A3.3 inSpecification B906. The thickness of sheet and strip shall bemeasured with the micrometer spindle38 in. (9.5 mm) or morefrom eithe

24、r edge for material 1 in. (25.4 mm) or over in widthand at any place on strip under 1 in. in width.9.2 Width or Diameter:9.2.1 PlateThe permissible variations in width of rectan-gular plates and diameter of circular plates shall be asprescribed in Table A3.4 and Table A3.5 in Specification B906.TABL

25、E 1 Product DescriptionProduct Thickness, in. (mm) Width, in. (mm)Hot-rolled plateA 316 and over (B906, Table A3.1 and Table A3.2) (B906, Table A3.4)BHot-rolled sheetA0.018 to 0.250 (0.46 to 6.4), incl (B906, Table A3.3) (B906, Table A3.6)Cold-rolled sheetC0.018 to 0.250 (0.46 to 6.4), incl (B906, T

26、able A3.3) (B906, Table A3.6)Cold-rolled stripC0.005 to 0.250 (0.13 to 6.4), incl (B906, Table A3.3) (B906, Table A3.6)AMaterial316 to14 in. (4.8 to 6.4 mm), incl, in thickness may be furnished as sheet or plate provided the material meets the specification requirements for the conditionordered.BHot

27、-rolled plate, in widths 10 in. (254 mm) and under, may be furnished as hot-finished rectangles with sheared or cut edges in accordance with Specification B408,provided the mechanical property requirements of this specification are met.CMaterial under 48 in. (1219 mm) in width may be furnished as sh

28、eet or strip provided the material meets the specification requirements for the condition ordered.TABLE 2 Chemical RequirementsElementComposition Limits, %AlloyN08120AlloyN08890AlloysN08800,N08810, andN08811Nickel 35.0 min 40.0 min 30.0 min39.0 max 45.0 max 35.0 maxChromium 23.0 min 23.5 min 19.0 mi

29、n27.0 max 28.5 max 23.0 maxIron remainderAremainder 39.5 minAManganese, max 1.5 1.5 1.5Carbon 0.02 min 0.06 minB0.10 max 0.14 max .Copper, max 0.50 0.75 0.75Silicon, max 1.0 1.0 min 1.0. 2.0 max .Sulfur, max 0.03 0.015 0.015AluminumC0.40 max 0.05 min 0.15 min. 0.60 max 0.60 maxTitaniumC0.20 max 0.15

30、 min 0.15 min. 0.60 max 0.60 maxColumbium 0.4 min . .0.9 max . .Molybdenum 2.50 max 1.0 min . 2.0 max .Niobium . 0.2 min . 1.0 max .Tantalum . 0.10 min . 0.60 max .Phosphorus 0.040 max . .Tungsten 2.50 max . .Cobalt, max 3.0 . .Nitrogen 0.15 min . .0.30 max . .Boron 0.010 max . .AIron shall be deter

31、mined arithmetically by difference.BAlloy UNS N08800: 0.10 max.Alloy UNS N08810: 0.050.10.Alloy UNS N08811: 0.060.10.CAlloy UNS N08811: Al + Ti, 0.851.20.B409 06 (2016)29.2.2 Sheet and StripThe permissible variations in widthfor sheet and strip shall be as prescribed in Table A3.6 inSpecification B9

32、06.9.3 Length:9.3.1 Sheet and strip of all sizes may be ordered to cutlengths, in which case a variation of18 in. (3.18 mm) over thespecified length shall be permitted.9.3.2 Permissible variations in length of rectangular plateshall be as prescribed in Table A3.7 in Specification B906.9.4 Straightne

33、ss:9.4.1 The edgewise curvature (depth of chord) of flat sheet,strip, and plate shall not exceed 0.05 in. multiplied by thelength in feet (0.04 mm multiplied by the length in centime-tres).9.4.2 Straightness for coiled strip material is subject toagreement between the manufacturer and the purchaser.

34、9.5 Edges:9.5.1 When finished edges of strip are specified in thecontract or order, the following descriptions shall apply:9.5.1.1 Square-edge strip shall be supplied with finishededges, with sharp, square corners, without bevel or rounding.TABLE 3 Mechanical Properties for Plate, Sheet, and Strip(A

35、ll thicknesses and sizes unless otherwise indicated)Alloy ConditionTensile Strength, min, psi(MPa)Yield StrengthA(0.2 %offset), min, psi (MPa)Elongation in 2 in. or50 mm (or 4D), min,%Hot-Rolled PlateUNS N08120 Annealed 90 000 (621) 40 000 (276) 30UNS N08800 Annealed 75 000 (520) 30 000 (205) 30UNS

36、N08800 As-rolledBC80 000 (550) 35 000 (240) 25UNS N08810 Annealed 65 000 (450) 25 000 (170) 30UNS N08811 Annealed 65 000 (450) 25 000 (170) 30UNS N08890 Annealed 75 000 (520) 30 000 (205) 35Hot-Rolled SheetUNS N08120 Annealed 90 000 (621) 40 000 (276) 30UNS N08800 Annealed 75 000 (520) 30 000 (205)

37、30UNS N08810DAnnealed 65 000 (450) 25 000 (170) 30UNS N08811DAnnealed 65 000 (450) 25 000 (170) 30UNS N08890 Annealed 75 000 (520) 30 000 (205) 35Cold-Rolled SheetUNS N08120 Annealed 90 000 (621) 40 000 (276) 30UNS N08800 Annealed 75 000 (520) 30 000 (205) 30UNS N08810DAnnealed 65 000 (450) 25 000 (

38、170) 30UNS N08811DAnnealed 65 000 (450) 25 000 (170) 30UNS N08890 Annealed 75 000 (520) 30 000 (205) 35Cold-Rolled StripUNS N08120 Annealed 90 000 (621) 40 000 (276) 30UNS N08800 Annealed 75 000 (520) 30 000 (205) 30EUNS N08810DAnnealed 65 000 (450) 25 000 (170) 30UNS N08811DAnnealed 65 000 (450) 25

39、 000 (170) 30UNS N08890 Annealed 75 000 (520) 30 000 (205) 35AYield strength requirements do not apply to material under 0.020 in. (0.51 mm) in thickness.BAs-rolled plate may be given a stress-relieving heat treatment subsequent to final rolling.CAs-rolled plate specified “suitable for hot forming”

40、shall be furnished from heats of known good hot-malleability characteristics (see X1.1.1.2). The purchaser must specifyAlloy UNS N08800 or UNS N08810. There are no applicable tensile or hardness requirements for such material.DAvailable only in thicknesses 0.115 in. (2.92 mm) and over.ENot applicabl

41、e for thickness under 0.010 in. (0.25 mm).TABLE 4 Grain Size and Hardness for Alloy UNS N08800 Cold-Rolled, Deep-Drawing, and Spinning Quality Sheet and StripThicknessCalculated Diameter of AverageGrain Section, max, in. (mm)CorrespondingASTM Micro-Grain Size No.Rockwell BABHardness, maxSheet (56 in

42、. (1.42 m) Wide and Under)0.050 (1.3) and less 0.0030 (0.075) 4.5 86Over 0.050 to 0.250 (1.3 to 6.4), incl 0.0043 (0.110) 3.5 86Strip (12 in. (305 mm) Wide and Under)C0.005Dto 0.010 (0.13 to 0.25), incl 0.0009 (0.022) 8E88EOver 0.010 to 0.125 (0.25 to 3.2), incl 0.0030 (0.075) 4.5 86AFor Rockwell or

43、 equivalent hardness conversions see Hardness Conversion Tables E140.BCaution should be observed in using the Rockwell test on thin material, as the results may be affected by specimen thickness. For thicknesses under 0.050 in. (1.3 mm),the use of the Rockwell superficial or the Vickers hardness tes

44、t is suggested.CSheet requirements (above) apply to strip thicknesses over 0.125 in. (3.2 mm), and for all thicknesses of strip over 12 in. (305 mm) in width.DFor ductility evaluations for strip under 0.005 in. (0.13 mm) in thickness, the spring-back test such as described in Test Method F155, is of

45、ten used and the manufacturershould be consulted.EAccurate grain size and hardness determinations are difficult to make on strip under 0.005 in. (0.13 mm) in thickness and are not recommended.B409 06 (2016)39.5.1.2 Round-edge strip shall be supplied with finishededges, semicircular in form, the diam

46、eter of the circle formingthe edge being equal to the strip thickness.9.5.1.3 When no description of any required form of stripedge is given, it shall be understood that edges such as thoseresulting from slitting or shearing will be acceptable.9.5.1.4 Sheet shall have sheared or slit edges.9.5.1.5 P

47、late shall have sheared or cut (machined, abrasive-cut, powder-cut, or inert arc-cut) edges, as specified.9.6 Squareness (Sheet):9.6.1 For sheets of all thicknesses, the angle betweenadjacent sides shall be 90 6 0.15 (116 in. in 24 in.) (1.59 mmin 610 mm).9.7 Flatness:9.7.1 There shall be no flatnes

48、s requirements for “deep-drawing quality” and “spinning quality” sheet and strip (seeX1.1.3).9.7.2 Standard flatness tolerances for plate shall conform tothe requirements of Table 5. “Specially-flattened” plate whenso specified, shall have permissible variations in flatness asagreed upon between the

49、 manufacturer and the purchaser.10. Test Methods10.1 The chemical composition, mechanical, and otherproperties of the material as enumerated in this specificationshall be determined, in case of disagreement, in accordancewith the methods in Specification B906.10.2 The measurement of average grain size may be carriedout by the planimetric method, the comparison method, or theintercept method described in Specification B906. In case ofdispute, the “referee” method for determining average grainsize shall be the planimetric method.10.3