ASTM B464 B464M-2015 Standard Specification for Welded UNS N08020 Alloy Pipe《UNS N08020焊接合金管的标准规格》.pdf

1、Designation: B464 10B464/B464M 15Standard Specification forWelded UNS N08020 Alloy Pipe1This standard is issued under the fixed designation B464;B464/B464M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year of last revision.

2、 A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2 covers welded UNS N08020 alloy pipe for general corrosion-resisting and low- or high-temperatureservice.1.2 The

3、 pipe covered is nominal pipe sizes up to and including NPS 6, 6 168 mm with the nominal wall thicknesses givenas Schedules 5S, 10S, and 40S and nominal pipe sizes up to and including NPS 2, 2 60 mm also including Schedule 80S. Table 2of Specification B775 is based on Table A1 of ANSI B36.19 and giv

4、es the nominal dimensions of these sizes. Table 3 ofSpecification B775 lists the dimensional requirements of these sizes. Pipe having other dimensions may be furnished provided suchpipe complies with all other requirements of this specification.1.3 The values stated in either SI units or inch-pound

5、units are to be regarded separately as standard. The values given inparentheses are mathematical conversions to SI units that are provided for information only and are not considered stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. C

6、ombining values from thetwo systems may result in non-conformance with the standard.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to become familiar with all hazards including those iden

7、tified in the appropriate Material Safety DataSheet (MSDS)(SDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices,and determine the applicability of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3A262 Pract

8、ices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless SteelsB775 Specification for General Requirements for Nickel and Nickel Alloy Welded PipeB899 Terminology Relating to Non-ferrous Metals and Alloys2.2 ANSI Standard:B36.19 Stainless Steel Pipe43. Terminology3.1 Definit

9、ionsDefinitions for terms defined in Terminology B899 shall apply unless otherwise defined by the requirementsof this document.4. General Requirement4.1 Material furnished in accordance with this specification shall conform to the applicable requirements of the current editionof Specification B775 u

10、nless otherwise provided herein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Examples of such requirements include, but are not limited to, the following:1 This specification is under

11、 the jurisdiction ofASTM Committee B02 on Nonferrous Metals andAlloys and is the direct responsibility of Subcommittee B02.07 on RefinedNickel and Cobalt and Their Alloys.Current edition approved June 1, 2010Oct. 1, 2015. Published June 2010November 2015. Originally approved in 1967. Last previous e

12、dition approved in 20092010 asB464 05 (2009).B464 10. DOI: 10.1520/B0464-10.10.1520/B0464_B464M-15.2 For ASME Boiler and Pressure Vessel Code applications, see related Specification SB-464 in Section II of that code.3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM

13、Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standardsstandards Document Summary page on the ASTM website.4 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.This do

14、cument is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions a

15、s appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. Unit

16、ed States15.1.1 Quantity (feet or number of lengths),5.1.2 UNS number,5.1.3 Size (nominal pipe size and schedule),5.1.4 Length (random or specific),5.1.5 ASTM designation,5.1.6 Product AnalysisState if required,5.1.7 CertificationState if a certification or a report of test results is required,5.1.8

17、 Purchaser InspectionState which tests or inspections are to be witnessed, if any, and5.1.9 Supplementary requirements, if any.6. Materials and Manufacture6.1 The pipe shall be made from flat-rolled stock by an automatic welding process with no addition of filler metal.6.2 Heat TreatmentPipe of UNS

18、N08020 alloy shall be furnished in the stabilized-annealed condition.NOTE 1The recommended annealing temperatures are 1800 to 1850F (982982 to 1010C)1010C for UNS N08020.7. Chemical Composition7.1 The material shall conform to the composition limits specified in Table 1. One test is required for eac

19、h lot as defined inSpecification B775.7.2 If a product analysis is performed, it shall meet the chemistry limits prescribed in Table 1, subject to the analysis tolerancesspecified in Specification B775.8. Mechanical Properties and Other Requirements8.1 Mechanical PropertiesThe material shall conform

20、 to the mechanical property requirements specified in Table 2. One testis required for each lot as defined in Specification B775.8.2 Flattening TestA flattening test shall be made on each end of one pipe per lot. Superficial ruptures resulting from surfaceimperfections shall not be cause for rejecti

21、on.8.3 Nondestructive Test RequirementsEach pipe shall be subjected to either a pressure test or a nondestructive electric test atthe manufacturers option. The purchaser may specify which test is to be used.8.4 Transverse Guided Bend TestAt the option of the pipe manufacturer, the transverse guided

22、bend test may be substitutedin lieu of the flattening test. Two bend specimens shall be taken transversely from pipe or the test specimens may be taken froma test plate of the same material and heat as pipe, which is attached to the end of the cylinder and welded as a prolongation of thepipe longitu

23、dinal seam. One test is required for each lot as defined in Specification B775.9. Lengths9.1 Lengths may be ordered as either random lengths (normally 15 to 24 ft (4.64.6 to 8.3 m)m with some agreed uponallowance for shorts) or specific cut lengths.10. Keywords10.1 welded pipe; N08020TABLE 1 Chemica

24、l RequirementsElement Composition,%UNS N08020Carbon, max 0.07Manganese, max 2.00Phosphorus,max0.045Sulfur, max 0.035Silicon, max 1.00Nickel 32.0038.00Chromium 19.0021.00Molybdenum 2.003.00Copper 3.004.00Columbium(Nb) +8 carbon1.00tantalumNitrogen .IronA remainderA By difference.B464/B464M 152SUPPLEM

25、ENTARY REQUIREMENTSThe following supplementary requirements shall be applied only when specified by the purchaserin the inquiry, contract, or order:S1. Corrosion TestsS1.1 One intergranular corrosion test per lot shall be performed by the manufacturer on a sensitized specimen and tested inaccordance

26、 with Practices A262. When this supplementary requirement is specified, the specific practice (Practice B or PracticeE) shall also be specified. If Practice B is specified, the specimen must pass with a rate of less than 0.002 in. (0.05 mm)0.05 mmper month. A lot for intergranular corrosion testing

27、shall be the same as for mechanical testing.S1.1.1 In addition to the anneal recommended in Note 1, the specimen shall be sensitized for 1 h at 1250F (677C)677Cbefore being subjected to corrosion testing.S1.1.2 If any corrosion test specimen fails the test, the material represented by such specimens

28、 may be reheat-treated andresubmitted for test.SUMMARY OF CHANGESCommittee B02 has identified the location of selected changes to this standard since the last issue (B464 - 05(2009)B464)10) that may impact the use of this standard. (Approved JuneOctober 1, 2010.)2015.)(1) Removed N08024 and N08026.U

29、pdated and added metric values.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof i

30、nfringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this stan

31、dard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your v

32、iews known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contac

33、ting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978)

34、646-2600; http:/ 2 Mechanical Property RequirementsTensile Strength,min, ksi (MPa)Yield Strength,min, ksi (MPa)Elongation in 2 in.(50.8 mm), min, %80 (551) 35 (241) 30.0TABLE 2 Mechanical Property RequirementsTensile Strength,min, ksi MPaYield Strength,min, ksi MPaElongation in 2 in.50.8 mm, min, %80 551 35 241 30.0B464/B464M 153