ASTM B516-2003(2009) Standard Specification for Welded Nickel-Chromium-Iron Alloy (UNS N06600 UNS N06603 UNS N06025 and UNS N06045 Tubes《焊接镍铬铁合金(UNS N06603、UNS N06025和UNS N06045)管的.pdf

1、Designation: B 516 03 (Reapproved 2009)Standard Specification forWelded Nickel-Chromium-Iron Alloy (UNS N06600, UNSN06603, UNS N06025, and UNS N06045) Tubes1This standard is issued under the fixed designation B 516; the number immediately following the designation indicates the year oforiginal adopt

2、ion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers welded UNS N06600*,N06603, N06025, and N06045 a

3、lloy boiler, heat exchanger,and condenser tubes for general corrosion resisting and low orhigh-temperature service.1.2 This specification covers tubes18 to 5 in. (3.18 to 127mm), inclusive, in outside diameter and 0.015 to 0.500 in. (0.38to 12.70 mm), inclusive, in wall thickness. Table 2 of Specifi

4、-cation B 751 lists the dimensional requirements of these sizes.Tubes having other dimensions may be furnished providedsuch tubing complies with all other requirements of thisspecification.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are ma

5、thematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards in

6、cluding those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:

7、2B 751 Specification for General Requirements for Nickeland Nickel Alloy Welded TubeB 899 Terminology Relating to Non-ferrous Metals andAlloys3. Terminology3.1 Terms defined in Terminology B 899 shall apply unlessdefined otherwise in this standard.4. Ordering Information4.1 It is the responsibility

8、of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not limited to,the following:4.1.1 Quantity (feet or number of lengths),4.1.2 UNS number,4.1.3 Size (out

9、side diameter minimum or average wallthickness),4.1.4 Length (random or specific),4.1.5 Class,4.1.6 ASTM designation,4.1.7 Product AnalysisState if required,4.1.8 CertificationState if a certification or a report of testresults is required, and4.1.9 Purchaser InspectionState which tests or inspec-ti

10、ons are to be witnessed, if any.5. Material and Manufacture5.1 Tube shall be made from flat-rolled alloy by an auto-matic welding process with no addition or filler metal. Subse-quent to welding and prior to final annealing, the material shallbe cold-worked in either the weld metal only or both weld

11、 andbase metal.5.2 Tube shall be furnished with oxide removed. Whenbright annealing is used, descaling is not necessary.6. Chemical Composition6.1 The material shall conform to the composition limitsspecified in Table 1. One test is required for each lot as definedin Specification B 751.1This specif

12、ication is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved April 15, 2009. Published April 2009. Originallyapproved in 1970. Last previous edition

13、 approved in 2003 as B 516 - 03.* New designation established in accordance with ASTM E 527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMSt

14、andards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6.2 If a product analysis is performed, it shall meet thechemistry limits prescribed in Table

15、 1, subject to the analysistolerances specified in Specification B 751.7. Mechanical Properties and Other Requirements7.1 Mechanical PropertiesThe material shall conform tothe mechanical property requirements specified in Table 2. Onetest is required for each lot as defined in Specification B 751.7.

16、2 Flattening TestA flattening test shall be made on eachend of one tube per lot. Superficial ruptures resulting fromsurface imperfections shall not be cause for rejection.7.3 Flange TestA flange test shall be made on each end ofone tube per lot.7.4 Nondestructive Test Requirements:7.4.1 Class 1Each

17、piece in each lot shall be subject to oneof the following four tests: hydrostatic, pneumatic (air under-water), eddy current, or ultrasonic.7.4.2 Class 2Each piece in each lot shall be subjected toa leak test and an electric test as follows:7.4.2.1 Leak TestHydrostatic or pneumatic (air underwa-ter)

18、.7.4.2.2 Electric TestEddy current or ultrasonic.7.5 The manufacturer shall have the option to test to Class1 or Class 2 and select the nondestructive test methods, if notspecified by the purchaser.8. General Requirements8.1 Material furnished under this specification shall con-form to the applicabl

19、e requirements of the current edition ofSpecification B 751 unless otherwise provided herein.9. Keywords9.1 welded tube; N06600; N06603; N06025; N06045ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Use

20、rs of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every

21、 five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technic

22、al committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken

23、, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 1 Chemical RequirementsE

24、lementCompositionLimits,%N06600 N06603 N06025 N06045NickelA72.0 min Bal Bal 45.0 minChromium 14.0 min 24.026.0 24.026.0 26.029.017.0 maxIron 6.0 min 8.011.0 8.011.0 21.025.010.0 maxManganese 1.0 max 0.15 max 0.15 max 1.0 maxCarbon 0.15 max 20.0-40.0 0.150.25 0.050.12Copper 0.5 max 0.50 max 0.10 max

25、0.3 maxSilicon 0.5 max 0.50 max 0.5 max 2.53.0Sulfur 0.015 max 0.010 max 0.010 max 0.010 maxAluminum . 2.4-3.0 1.82.4 .Titanium . 0.010.25 0.10.2 .Phosphorus . 0.020 max 0.02 max 0.02 maxZirconium . 0.010.40 0.010.10 .Yttrium . 0.010.15 0.050.12 .Cerium . . . 0.030.09ANickel shall be determined arit

26、hmetically by difference.TABLE 2 Mechanical Property RequirementsAlloyTensile Strengthmin, psi (MPa)Yield Strength0.2 % Offset, min,psi (MPa)Elongation in 2 in.or 50 mm, min, %N06600 80 000 (550) 35 000 (240) 30N06603 94 000 (650) 43 000 (300) 25N06025 98 000 (680) 39 000 (270) 30N06045 90 000 (620) 35 000 (240) 30B 516 03 (2009)2