ASTM B540-1997(2012) Standard Specification for Palladium Electrical Contact Alloy《电触点用钯合金标准规格》.pdf

1、Designation: B540 97 (Reapproved 2012)Standard Specification forPalladium Electrical Contact Alloy1This standard is issued under the fixed designation B540; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.

2、 A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers an alloy containing palla

3、dium,silver, copper, gold, platinum, and zinc in the form of wire, rod,and strip for electrical contacts.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not

4、considered standard.1.3 The following safety hazard caveat pertains only to thetest methods portion, Section 6 of this specification. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to become fa

5、miliar with all hazards includingthose identified in the appropriate Material Safety Data Sheet(MSDS) for this product/material as provided by themanufacturer, to establish appropriate safety and healthpractices, and determine the applicability of regulatory limi-tations prior to use.1.4 It is the r

6、esponsibility of the user to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer.2. Referenced Documents2.1 ASTM Standards:2B476 Specification for General Requirements for WroughtPreci

7、ous Metal Electrical Contact MaterialsE8 Test Methods for Tension Testing of Metallic MaterialsE384 Test Method for Knoop and Vickers Hardness ofMaterials3. Materials and Manufacture3.1 Raw materials shall be of such quality and purity thatthe finished product will have the properties and characteri

8、sticsprescribed in this specification.3.2 The material shall be finished by such operations (coldworking, heat treating, annealing, turning, grinding, pickling)as are required to produce the prescribed properties.4. Chemical Composition4.1 Material produced under the specification shall meet therequ

9、irements of chemical composition shown in Table 1.5. Mechanical Properties5.1 The contract or order may specify ultimate tensilestrength, elongation, mirohardness (Knoop or Vickers), or acombination of these mechanical properties (as listed in Table2, Table 3, and Table 4) as temper criterion. If th

10、e contract ororder does not specify a temper criterion, then the criterion fortemper designation will be ultimate tensile strength and elon-gation.6. Test Methods6.1 Test methods shall be in accordance with SpecificationB476.6.1.1 Knoop hardness tests shall be in accordance with TestMethod E384. Mat

11、erial 0.005 in. (0.13 mm) in thickness(diameter) and larger shall be tested using a 100-g indenterload. Material less than 0.005 in. (0.13 mm) in thickness(diameter) shall be tested using a 50-g indenter load. Aminimum of five hardness indentations shall be made on eachspecimen. All indentations sha

12、ll be made so that the long axisof the indenter is parallel to the rolling or drawing direction ofthe material. The hardness value reported shall be the averageof the five indentations.6.1.2 All tension test specimens shall be full cross-sectionsize when practical (see Test Methods E8).6.1.3 All tes

13、ts shall be conducted in room temperature, 65 to85F (18.3 to 29.4C).6.2 Chemical analysis shall be performed by spectrochemi-cal or wet analysis methods.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of Subcommittee

14、B02.05 on Precious Metals and Electrical Contact Materials.Current edition approved Nov. 1, 2012. Published November 2012. Originallyapproved in 1970. Last previous edition approved in 2008 as B540 97 (2008)1.DOI: 10.1520/B0540-97R12.2For referenced ASTM standards, visit the ASTM website, www.astm.o

15、rg, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States17. Inspection

16、 and Testing7.1 Material furnished under this specification shall beinspected and tested by the manufacturer as listed below:7.1.1 Visual inspection at 10 magnification,7.1.2 Tension or hardness tests, or both, for temperverification,7.1.3 Dimensional inspection, andTABLE 1 Chemical RequirementsElem

17、entComposition,weight %Palladium 34.036.0Silver 29.031.0Copper 13.514.5Gold 9.510.5Platinum 9.510.5Zinc 0.81.2Total platinum group metal impurities(iridium, osmium, rhodium, ruthenium)0.1 maxTotal base metal impurities 0.2 maxTABLE 2 Mechanical Properties of WireA(0.004 to 0.020 in. (0.1 to 0.5 mm)

18、diameter)PropertyTemperSolution-AnnealedStress-RelievedDuctileHeat-TreatedAge-HardenedHeat TreatedAge-HardenedTensile strength, ksi 110130 140170 160190 160200Tensile strength, MPa 760900 9701170 11001310 11001380Elongation, % in 2 in. (51 mm) 20 min 1020 818 110Hardness, KnoopB200260 280340 320370

19、350410Hardness, Vickers, 100-g load (50-g 190250 265340 320380 330400under 0.005-diameter)AThe limits to all properties apply only to the sizes specified.BSee 6.1.1.TABLE 3 Mechanical Properties of WireA(Over 0.020 to 0.040 in. (0.5 to 1.0 mm) diameter)PropertyTemperSolution-Annealed Stress-Relieved

20、 Ductile-Hardened Age-HardenedTensile strength, ksi 105130 130170 155180 160200Tensile strength, MPa 720860 9001170 10701240 11001380Elongation, % in 2 in. (51 mm) 15 min 825 825 110Hardness, KnoopB200260 280340 310360 340400Hardness, Vickers: 190250 265340 320380 330400100-g loadAThe limits to all

21、properties apply only to the sizes specified.BSee 6.1.1.TABLE 4 Mechanical Properties of StripA(0.003 to 0.020 in. (0.075 to 0.5 mm) thick)PropertyTemperSolution-Annealed Stress-Relieved Ductile-Hardened Age-HardenedTensile strength, ksi 110135 135160 150185 160200Tensile strength, MPa 760930 930110

22、0 10301280 11001380Elongation, % in 2 in. (51 mm) 12 min 825 825 110Hardness, KnoopB200260 280340 300360 340400Hardness, Vickers 100-g load (50-g load under0.005 thick)185255 265340 320380 330400AThe limits to all properties apply only to the sizes specified.BSee 6.1.1.B540 97 (2012)27.1.4 Chemical

23、analysis when indicated by the purchaseorder.8. Keywords8.1 contact; electrical contact material; palladium alloy;precious metalAPPENDIX(Nonmandatory Information)X1. REFERENCE PROPERTIES OF PALLADIUM ALLOY ELECTRICAL CONTACT MATERIALX1.1 Table X1.1 provides a list of typical property valueswhich are

24、 useful for engineering calculations in electricalcontact design and application.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the va

25、lidity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your co

26、mments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments hav

27、e not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple

28、 copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org

29、/COPYRIGHT/).TABLE X1.1 Typical Physical PropertiesSolution-AnnealedStress-RelievedDuctile-HardenedAge-HardenedResistivity, cm 34.9 33.2 31.6 31.6Density, Mg/m311.8 11.8 11.8 11.8Solidus temperature, C 1015 1015 1015 1015Linear coefficient of thermal expansion/C (23-100C) 13.5 10613.5 10613.5 10613.

30、5 106Thermal emf versus platinum (0-100C), V/C 10 9 8 8Softening voltage, mV 220 220 220 220Melting voltage, mV 385 . 400 400Fatigue strength (rotating-bending)at 108cycles:ksi 50 50 50 50MPa 345 345 345 345Modulus of elasticity in tension:ksi 17 103171031710317103MPa 117 103117103117103117103Proportional limit:ksi 90 135 135 145MPa 620 930 930 1000B540 97 (2012)3