ASTM B551 B551M-2012 Standard Specification for Zirconium and Zirconium Alloy Strip Sheet and Plate《锆及锆合金板、薄板及带材材标准规格》.pdf

1、Designation:B551/B551M07 Designation: B551/B551M 12Standard Specification forZirconium and Zirconium Alloy Strip, Sheet, and Plate1This standard is issued under the fixed designation B551/B551M; the number immediately following the designation indicates the yearof original adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers five grades of zirconium strip, sheet, and plate.1.2 Unless a single

3、 unit is used, for example corrosion mass gain in mg/dm2, the values stated in either inch-pound or SI unitsare to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore each system mustbe used independently of the other. SI values cannot be mixed w

4、ith inch-pound values.1.3 The following precautionary caveat pertains only to the test method portions of this specification: This standard does notpurport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard toestablish approp

5、riate safety and health practices and determine the applicability of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3E8 Test Methods for Tension Testing of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specificat

6、ionsE290 Test Methods for Bend Testing of Material for Ductility3. Terminology3.1 Definitions:3.1.1 annealed, ndenotes material that exhibits a recrystallized grain structure.3.2 Lot Definition:3.2.1 lot, na lot shall consist of a material of the same size, shape, condition, and finish produced from

7、 the same ingot orpowder blend by the same reduction schedule and the same heat treatment parameters. Unless otherwise agreed betweenmanufacturer and purchaser, a lot shall be limited to the product of an 8 h period for final continuous anneal, or to a single furnaceload for final batch anneal.3.3 F

8、orms:3.3.1 strip, na flat product, may be supplied in coil, less than 6 in. 150 mm in width and from 0.005 in. 0.13 mm to 0.188in. 4.8 mm in thickness.3.3.2 sheet, na flat product 6 in. 150 mm or more in width and from 0.005 in. 0.13 mm to 0.188 in. 4.8 mm in thickness.3.3.3 plate, na flat product m

9、ore than 0.1880.125 in. 4.83.2 mm in thickness.4. Classification4.1 The strip, sheet, or plate is to be furnished in five grades as follows:4.1.1 Grade R60700Low oxygen zirconium.4.1.2 Grade R60702Unalloyed zirconium.4.1.3 Grade R60704Zirconium-tin.4.1.4 Grade R60705Zirconium-niobium.4.1.5 Grade R60

10、706Zirconium-niobium.1This specification is under the jurisdiction of ASTM Committee B10 on Reactive and Refractory Metals and Alloys and is the direct responsibility of SubcommitteeB10.02 on Zirconium and Hafnium.Current edition approved June 1, 2007. Published July 2007. Originally approved in 197

11、1. Last previous edition approved in 2004 as B551/B551M041. DOI:10.1520/B0551_B0551M-07.Current edition approved May 15, 2012. Published June 2012. Originally approved in 1971. Last previous edition approved in 2007 as B551/B551M 07. DOI:10.1520/B0551_B0551M-12.2For ASME Boiler and Pressure Vessel C

12、ode applications, see related Specification SB-551 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page o

13、n the ASTM website.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that use

14、rs consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5. Ordering Information5.1 O

15、rders for material under this specification should include the following information, as applicable:5.1.1 Standard designation and year of issue,5.1.2 Quantity (weight or number of pieces),5.1.3 Lot definition for continuous anneal, if applicable (3.2.1),5.1.4 Form (3.3) and dimensions,5.1.5 Grade (

16、4.1),5.1.6 Metallurgical condition, if not in the recrystallized annealed condition (6.3),5.1.7 Chemical analysis of elements not listed (7.1.4),5.1.8 Product analysis (7.1.3 and 7.3.1),5.1.9 Tensile test temperature (8.1),5.1.10 Material condition and finish (9.1-9.5),5.1.11 Workmanship and appeara

17、nce (11.1 and 11.3),5.1.12 Purchaser inspection (15.1 and 15.2),5.1.13 Rejection and referee (16.2),5.1.14 Product marking, (18.1 and 18.1.1),5.1.15 Packaging and package marking (19.1),5.1.16 Additions to the specification and supplementary requirements, if required, and5.1.17 Additional requiremen

18、ts for explosion cladding, if applicable (Supplementary Requirements S.1).NOTE 1A typical ordering description is as follows: 9000-lb 5000 kg zirconium sheet, 0.098 in. 2.5 mm by 12 in. 300 mm by 144 in.3.5 m, ASTM B551/B551M-07, Grade R60705.6. Materials and Manufacture6.1 Material covered by this

19、specification shall be made from ingots that are produced by vacuum or plasma arc melting,vacuum electron-beam melting, a combination of these three methods or other melting processes conventionally used for reactivemetals. All processes to be done in furnaces usually used for reactive metals.6.2 Th

20、e various mill products covered by this specification shall be formed with the conventional extrusion, forging, or rollingequipment normally found in primary ferrous and nonferrous plants.6.3 The strip, sheet, and plate shall be supplied in the recrystallized annealed condition unless otherwise spec

21、ified in thepurchase order.7. Chemical Composition7.1 The material covered by this specification shall conform to the chemical composition requirements prescribed in Table 1.7.1.1 The elements listed in Table 1 are intentional alloy additions or elements which are inherent to the manufacture of spon

22、ge,ingot or mill product.7.1.2 Elements intentionally added to the melt must be identified, analyzed, and reported in the chemical analysis.7.1.3 Elements other than those listed in Table 1 are deemed to be capable of occurring in the grades listed in Table 1 by andonly by way of unregulated or unan

23、alyzed scrap additions to the ingot melt. Therefore, product analysis for elements not listed inTable 1 shall not be required unless specified and shall be considered to be in excess of the intent of this specification.7.1.4 When agreed upon by producer and purchaser and requested by the purchaser i

24、n his written purchase order, chemicalanalysis shall be completed for specific residual elements not listed in this specification.7.2 The manufacturers ingot analysis shall be considered the chemical analysis for strip, sheet, and plate, except for hydrogenand nitrogen, which shall be determined on

25、the finished product.7.2.1 The ingot shall be sampled in sufficient places along the side wall so that the top sample is within 5 in. 125 mm of thetop face. A minimum of three samples per ingot is required.TABLE 1 Chemical RequirementsAElementComposition, %GradesR60700 R60702 R60704 R60705 R60706Zir

26、conium + hafnium, min 99.2 99.2 97.5 95.5 95.5Hafnium, max 4.5 4.5 4.5 4.5 4.5Iron + chromium 0.2 max 0.2 max 0.2 to 0.4 0.2 max 0.2 maxTin . . 1.0to2.0 . .Hydrogen, max 0.005 0.005 0.005 0.005 0.005Nitrogen, max 0.025 0.025 0.025 0.025 0.025Carbon, max 0.05 0.05 0.05 0.05 0.05Niobium . . . . . . .

27、2.0 to 3.0 2.0 to 3.0Oxygen, max 0.10 0.16 0.18 0.18 0.16ABy agreement between the purchaser and the manufacturer, analysis may be required and limits established for elements and compounds not specified in the tableof chemical composition (see 7.1.1).B551/B551M 1227.2.2 These samples shall be analy

28、zed for the alloying and impurity elements given in Table 1.7.2.3 Alternatively, the manufacturer may sample an intermediate or final size during processing with the same frequency andin the same positions relative to the ingot as specified in 7.2.1 to determine the composition, except for hydrogen

29、and nitrogen,which shall be determined on the finished product.7.3 Check Analysis:7.3.1 Check analysis is an analysis made by the purchaser or the manufacturer of the metal after it has been processed intofinished mill forms, and is either for the purpose of verifying the composition of a heat or lo

30、t or to determine variations in thecomposition within a heat or lot. Acceptance or rejection of a lot of material may be made by the purchaser on the basis of thischeck analysis. When requested by the purchaser and stated in the purchase order, a product check analysis for any elements listedin Tabl

31、e 1 shall be made on the finished product.7.3.2 Check analysis limits shall be as specified in Table 2. These limits are the amounts an individual result for a given elementmay vary under or over the specified limits shown in Table 1.7.3.3 Check analysis tolerances do not broaden the specified heat

32、analysis requirements but cover variations betweenlaboratories in the measurement of chemical content.7.3.4 The manufacturer shall not ship material that is outside the limits specified in Table 1 for the applicable grade.8. Mechanical Properties8.1 The material, as represented by the test specimens

33、, shall conform to the tensile properties prescribed in Table 3 for roomtemperature mechanical properties.8.2 For strip and sheet, the bend test specimen shall stand being bent at ambient temperature through an angle of 105 withoutfracture in the outside of the bent portion. The bend shall be made a

34、round a mandrel having a radius equal to that shown in Table3 for the applicable grade. Bend testing shall be performed in accordance with Test Methods E290.9. Condition and Finish9.1 Sheet, strip, or plate shall be furnished in one of the following conditions as designated on the purchase order:For

35、m ConditionStrip hot-rolledhot-rolled, annealedcold-rolledcold-rolled, annealedcold-rolled, annealed,followed by a final lightcold-rolled pass,generally on polished rollsSheet hot-rolledhot-rolled, annealedcold-rolled, annealedcold-rolled, annealed,followed by a final lightcold-rolled pass,generally

36、 on polished rollsPlate hot-rolledhot-rolled, annealed9.2 Hot-rolled sheet, strip, or plate shall be furnished with one of the following finishes as designated in the purchase order:9.2.1 Not descaled,9.2.2 Mechanically descaled,9.2.3 Mechanically descaled and pickled,9.2.4 As-ground.TABLE 2 Permiss

37、ible Variation in Check Analysis BetweenDifferent LaboratoriesElementPermissible Variation inProduct Analysis, %Hydrogen 0.002Nitrogen 0.01Carbon 0.01Hafnium 0.1Iron + chromium 0.025Tin 0.05Niobium 0.05Oxygen 0.02B551/B551M 1239.3 Cold-rolled sheet or strip shall be furnished with one of the followi

38、ng finishes as designated in the purchase order:9.3.1 Bright cold-rolled,9.3.2 Ground 32 in. 0.8 m rms or better, or9.3.3 Pickled.9.4 Hot-Rolled StripThe following types of edges can be furnished on hot-rolled strip when specified in the purchase order:9.4.1 Mill edge,9.4.2 Split edge, or9.4.3 Shear

39、ed edge.9.5 Cold-Rolled StripAslit edge is normally furnished on cold-rolled strip.Amachined edge is available for weld preparationwhen specified in the purchase order.9.6 Sheet and PlateBoth hot- and cold-rolled sheet and plate are furnished with a sheared edge.10. Permissible Variations in Dimensi

40、ons and Weights10.1 ThicknessThe variations in thickness of strip, sheet, and plate are given in the following tables:10.1.1 Hot-rolled strip, Table 4.10.1.2 Cold-rolled strip, Table 5.10.1.3 Hot- and cold-rolled sheet, Table 6.10.1.4 Plate, Table 7.10.2 WidthThe variations in width are given in the

41、 following tables:10.2.1 Hot-rolled strip, Table 8.10.2.2 Cold-rolled strip, Table 9.10.2.3 Hot- and cold-rolled sheet, Table 10.10.2.4 Plate, Table 11.10.3 LengthThe variations in length are given in the following tables:10.3.1 Hot- and cold-rolled strip, Table 12.10.3.2 Hot- and cold-rolled sheet,

42、 Table 13.10.3.3 Plate, Table 11.10.4 Crown TolerancesThe variations in crown tolerances are given in the following tables:10.4.1 Hot-rolled strip, Table 14.10.4.2 Cold-rolled strip, Table 15.10.4.3 Hot-rolled sheet, Table 16.10.4.4 Cold-rolled sheet, Table 17.10.5 Camber TolerancesThe variations in

43、 camber tolerances are given in the following tables.10.5.1 Hot- and cold-rolled strip, Table 18.10.5.2 Hot- and cold-rolled sheet, Table 19.10.5.3 Plate, Table 20.10.6 DiameterThe variation in diameter tolerance for circular plates is given in Table 21.TABLE 3 Tensile RequirementsGradesR60700 R6070

44、2 R60704 R60705 R60706Tensile strength, min, ksi MPa . 55 380 60 415 80 550 74 510Yield strength, min, ksi MPa . 30 205 35 240 55 380 50 345Tensile strength, max, ksi MPa 55 380 . . . .Yield strength, max, ksi MPa 44 305 . . . .Elongation in 2 in. or 50 mm, min, %A20 16 14 16 14Bend test radiusB5T 5

45、T 5T 3T 2.5TAWhen a sub-size specimen is used, the gage length shall be as specified in Test Methods E8 for that specimen.BT equals the thickness of the bend test specimen. Bend tests are not applicable to material over 0.187 in. 4.8 mm in thickness.TABLE 4 Permissible Variations in Thickness of Hot

46、-RolledZirconium StripASpecified Width, in. mmVariation from Specified Thicknessfor Widths Given, Over andUnder, in mm0.0830.118 2.13.0 Over 0.1180.1883.04.78To 312 90, incl 0.005 0.13 0.006 0.15Over 312 90 6 150, incl 0.006 0.15 0.007 0.18AThickness measurements are taken at least38 in. 10 mm from

47、edge.B551/B551M 12410.7 FlatnessThe permissible variation from a flat surface for plate is given in Table 22.10.8 WeightThe actual shipping weight of any one item of an ordered thickness and width in any finish may exceed estimatedweight by as much as 10 %.11. Workmanship and Appearance11.1 Cracks,

48、seams, slivers, blisters, burrs, and other injurious imperfections shall not exceed standards of acceptability agreedupon by the manufacturer and the purchaser.11.2 The finished strip, sheet, or plate shall be visibly free of oxide, grease, oil, residual lubricants, and other extraneousmaterials.TAB

49、LE 5 Permissible Variations in Thickness of Cold-Rolled Zirconium StripNOTE 1For thickness under 0.010 in. 0.25 mm in width to 6 in. 150 mm a tolerance of 610 % of the thickness shall apply.NOTE 2Thickness measurements shall be taken38 in. 10 mm in from edge of the strip, except on widths less than 1 in. 2.5 mm where thetolerances are applicable for measurements at all locations.Specified Thickness, in. mmPermissible Variations in Thickness, for Widt