ASTM B573-2006(2016) Standard Specification for Nickel-Molybdenum-Chromium-Iron Alloys (UNS N10003 N10242) Rod《钼镍铬铁合金 (UNS N10003 N10242) 杆材的标准规格》.pdf

1、Designation: B573 06 (Reapproved 2016)Standard Specification forNickel-Molybdenum-Chromium-Iron Alloys (UNS N10003,N10242) Rod1This standard is issued under the fixed designation B573; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision

2、, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers nickel-molybdenum-chromium-iron alloys (UNS N10003 and UNS N10242)3rodfor use

3、in general corrosive service.1.2 The following products are covered under this specifi-cation:1.2.1 Rods516 to34 in. (7.94 to 19.05 mm) excl in diameter,hot or cold finished, annealed, and pickled or mechanicallydescaled.1.2.2 Rods34 to 312 in. (19.05 to 88.9 mm) incl in diameter,hot or cold finishe

4、d, annealed, ground, or turned.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.4 This standard does not purport to address all of t

5、hesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateSafety Data Sheet (SDS) for this product/material as providedby the manufacturer, to establish appropriate safety a

6、nd healthpractices, and determine the applicability of regulatory limi-tations prior to use.2. Referenced Documents2.1 ASTM Standards:4B880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys andCobalt AlloysE8 Test Methods for Tension Testing of Metall

7、ic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE1473 Test Methods for Chemical Analysis of Nickel, Co-balt and High-Temperature Alloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 rod, na product of round solid s

8、ection furnished instraight lengths.4. Ordering Information4.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include but are not limited tothe

9、 following:4.1.1 DimensionsNominal diameter and length. Theshortest usable multiple length shall be specified (Table 1).4.1.2 CertificationState if certification or a report of testresults is required (Section 15).4.1.3 Purchaser InspectionState which tests or inspec-tions are to be witnessed (Secti

10、on 13).4.1.4 Samples for Product (Check) AnalysisState whethersamples shall be furnished (9.2.2).5. Chemical Composition5.1 The material shall conform to the requirements as tochemical composition prescribed in Table 2.5.2 If a product (check) analysis is made by the purchaser,the material shall con

11、form to the requirements specified inTable 2 subject to the permissible tolerances in SpecificationB880.6. Mechanical Properties and Other Requirements6.1 The mechanical properties of the material at roomtemperature shall conform to those shown in Table 3.7. Dimensions and Permissible Variations7.1

12、DiameterThe permissible variations from the speci-fied diameter shall be as prescribed in Table 4.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Cu

13、rrent edition approved June 1, 2016. Published June 2016. Originallyapproved in 1972. Last previous edition approved in 2011 as B573 06 (2011).DOI: 10.1520/B0573-06R16.2For ASME Boiler and Pressure Vessel Code applications see SpecificationSB-573 in Section II of that Code.3New designation establish

14、ed in accordance with Practice E527 and SAE J1086,Recommended Practice for Numbering Metals and Alloys (UNS).4For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the sta

15、ndards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States17.2 Out-of-RoundnessThe permissible variation in round-ness shall be as prescribed in Table 4.7.3 Machining AllowancesWhen the surfaces of

16、 finishedmaterial are to be machined, the following allowances aresuggested for normal machining operations:7.3.1 As-finished (Annealed and Descaled)For diametersof516 to1116 in. (7.94 to 17.46 mm) incl, an allowance of116in. (1.59 mm) on the diameter should be made for finishmachining.7.4 Length:7.

17、4.1 Unless multiple, nominal, or cut lengths are specified,random mill lengths shall be furnished.7.4.2 The permissible variations in length of multiple,nominal, or cut length rod shall be as prescribed in Table 1.Where rods are ordered in multiple lengths,14 in. (6.35 mm)length addition shall be al

18、lowed for each uncut multiple length.7.5 Ends:7.5.1 Rods ordered to random or nominal lengths shall befurnished with either cropped or sawed ends.7.5.2 Rods ordered to cut lengths shall be furnished withsquare saw cut or machined ends.7.6 WeightFor calculation of mass or weight, the follow-ing densi

19、ties shall be used:Alloy lb/in3g/cm3N10003 0.317 8.78N10242 0.327 9.057.7 StraightnessThe maximum curvature (depth of chord)shall not exceed 0.050 in. multiplied by the length of the chordin feet (0.04 mm multiplied by the length in centimetres).8. Workmanship, Finish, and Appearance8.1 The material

20、 shall be uniform in quality and condition,smooth, and free of injurious imperfections.9. Sampling9.1 Lots for Chemical Analysis and Mechanical Testing:9.1.1 A lot for chemical analysis shall consist of one heat.9.1.2 A lot of bar for mechanical testing shall be defined asthe material from one heat

21、in the same condition and specifieddiameter.9.2 Sampling for Chemical Analysis:9.2.1 A representative sample shall be obtained from eachheat during pouring or subsequent processing.9.2.2 Product (check) analysis shall be wholly the respon-sibility of the purchaser.9.3 Sampling for Mechanical Testing

22、A representativesample shall be taken from each lot of finished material.10. Number of Tests and Retests10.1 Chemical AnalysisOne test per heat.10.2 Tension TestsOne test per lot.10.3 RetestsIf the specimen used in the mechanical test ofany lot fails to meet the specified requirements, two additiona

23、lspecimens shall be taken from different sample pieces andtested. The results of the tests on both of these specimens shallmeet the specified requirements.11. Specimen Preparation11.1 Tension test specimens shall be taken from materialafter final heat-treatment and tested in the direction of fabri-c

24、ation.11.2 Tension test specimens shall be any of the standard orsubsized specimens shown in Test Methods E8.11.3 In the event of disagreement, the referee specimenshall be the largest possible round specimen shown in TestMethods E8.12. Test Methods12.1 The chemical composition and mechanical proper

25、tiesof the material as enumerated in this specification shall bedetermined, in case of disagreement, in accordance with thefollowing ASTM methods:12.1.1 Chemical AnalysisTest Methods E1473.12.1.2 Tension TestTest Methods E8.12.1.3 Determining Significant PlacesPractice E29.TABLE 1 Permissible Variat

26、ions in Length of RodsRandom milllengths2 to 12 ft (610 to 3660 mm) long with not more than25 weight % under 4 ft (1.22 m).MultiplelengthsFurnished in multiples of a specified unit length,within the length limits indicated above. For eachmultiple, an allowance of14 in. (6.35 mm) shallbe made for cut

27、ting, unless otherwise specified. Atthe manufacturers option, individual specified unitlengths may be furnished.NominallengthsSpecified nominal lengths having a range of not lessthan 2 ft (610 mm) with no short lengths allowed.Cut lengths A specified length to which all rods shall be cut witha permi

28、ssible variation of +18 in. (3.17mm) 0.TABLE 2 Chemical RequirementsElementComposition, %UNS N10242 UNS N10003Chromium 7.0-9.0 6.08.0Iron, max 2.0 5.0Carbon 0.03 max 0.040.08Silicon, max 0.80 1.00Cobalt, max 1.00 0.20Manganese, max 0.80 1.00Tungsten, max . 0.50Vanadium, max . 0.50Molybdenum 24.0-26.

29、0 15.018.0Phosphorus, max 0.030 0.015Sulfur, max 0.015 0.020Aluminum plus titanium, max . 0.50Copper, max 0.50 0.35Boron, max 0.006 0.010Nickel remainder remainderAluminum, max 0.50 .TABLE 3 Mechanical Property RequirementsUNSTensile Strength,min,ksi (MPa)Yield Strength (0.2% Offset), min, ksi(MPa)E

30、longation in 2 in.(50.8 mm) or 4DAmin, %N10003 100 000(690) 40 000(280) 35N10242 105 000(725) 45 000(310) 40A4D D refers to the diameter of the tension specimen.B573 06 (2016)212.2 For purposes of determining compliance with thelimits in this specification, an observed value or a calculatedvalue sha

31、ll be rounded in accordance with the rounding methodof Practice E29:RequirementsRounded Unit for Observed orCalculated ValueChemical composition and tolerance nearest unit in the last right-hand placeof figures of the specified limitTensile strength and yield strength nearest 1000 psi (7 MPa)Elongat

32、ion nearest 1 %13. Inspection13.1 Inspection of the material shall be made as agreed uponbetween the manufacturer and the purchaser as part of thepurchase contract.14. Rejection and Rehearing14.1 Material tested by the purchaser that fails to conform tothe requirements of this specification may be r

33、ejected. Rejec-tion should be reported to the producer or supplier promptlyand in writing. In case of dissatisfaction with the results of thetest, the producer or supplier may make claim for a rehearing.15. Certification15.1 When specified in the purchase order or contract, amanufacturers certificat

34、ion shall be furnished to the purchaserstating that material has been manufactured, tested, and in-spected in accordance with this specification, and that the testresults on representative samples meet specification require-ments. When specified in the purchase order or contract, areport of the test

35、 results shall be furnished.16. Product Marking16.1 Each piece of material12 in. (12.7 mm) and over indiameter shall be marked with this specification number, nameof the material, and size of the product.16.2 Each bundle or shipping container shall be markedwith the name of the material; this specif

36、ication number; thesize; gross, tare, and net weight; consignor and consigneeaddress; contract or order number; and such other informationas may be defined in the contract or order.17. Keywords17.1 rod; UNS N10003; UNS N10242APPENDIX(Nonmandatory Information)X1. HEAT TREATMENTX1.1 Proper heat treatm

37、ent during or subsequent to fabrica-tion is necessary for optimum performance, and the manufac-turer shall be consulted for details.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard

38、 are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif n

39、ot revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which

40、 you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,Uni

41、ted States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may

42、also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 4 Permissible Variations in Diameter and Out-of-Roundness of Finished RodsSpecified Diameter, in. (mm)Permissible Variations, in. (mm)DiameterOut of Roundness, maxPlus MinusHot-Fini

43、shed, Annealed, and Descaled Rods516 to716 (7.94 to 11.11), incl 0.012 (0.30) 0.012 (0.30) 0.018 (0.46)Over716 to58 (11.11 to 15.87), incl 0.014 (0.36) 0.014 (0.36) 0.020 (0.51)Over58 to34 (15.87 to 19.05), excl 0.016 (0.41) 0.016 (0.41) 0.024 (0.61)Hot-Finished, Annealed, and Ground or Turned Rods34 to 312 (19.0588.9), incl 0.010 (0.25) 0 0.008 (0.20)B573 06 (2016)3