ASTM B673-2005(2011) Standard Specification for UNS N08925 UNS N08354 and UNS N08926 Welded Pipe《UNS N08925 UNS N08354和UNS N08926焊接管的标准规格》.pdf

1、Designation: B673 05 (Reapproved 2011)Standard Specification forUNS N08925, UNS N08354, and UNS N08926 Welded Pipe1This standard is issued under the fixed designation B673; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year o

2、f last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers UNS N08925, UNS N08354,and UNS N08926* welded pipe for general corrosion applica-tions.1.2

3、 This specification covers pipe sizes in schedules shownin Table 1.1.3 ASTM International has adopted definitions wherebysome grades, such as UNS N08904, previously in this speci-fication were recognized as stainless steels, because thosegrades have iron as the largest element by mass percent. Suchg

4、rades are under the oversight of ASTM Committee A01 andits subcommittees. The products of N08904 previously coveredin this specification are now covered by Specification A312/A312M.1.4 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematic

5、alconversions to SI units that are provided for information onlyand are not considered standard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including

6、those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2A312/A3

7、12M Specification for Seamless, Welded, andHeavily Cold Worked Austenitic Stainless Steel PipesB775 Specification for General Requirements for Nickeland Nickel Alloy Welded PipeE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 ANSI Standards:3B2.1 Pipe ThreadsB31.

8、10 Power PipingB36.10 Welded and Seamless Wrought Steel PipeB36.19 Stainless Steel Pipe33. Classification3.1 Class 1Welded, cold worked, solution treated, andnondestructively tested in accordance with 8.3.1.3.2 Class 2Welded, cold worked, solution treated, andnondestructively tested in accordance wi

9、th 8.3.2.3.3 Class 3As welded, solution treated, and nondestruc-tively tested in accordance with 8.3.1.4. General Requirement4.1 Material furnished under this specification shall con-form to the applicable requirements of Specification B775unless otherwise provided herein.5. Ordering Information5.1

10、Orders for material under this specification shouldinclude the following information:5.1.1 Alloy name or UNS number,5.1.2 Class,5.1.3 Quantity (feet or number of lengths),5.1.4 Size (nominal size or outside diameter and schedulenumber or average wall thickness),5.1.5 LengthSpecify cut length or rand

11、om,5.1.6 CertificationState if certification or a report of testresults is required,5.1.7 Purchaser InspectionState which tests or inspec-tions are to be witnessed,1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of S

12、ubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved May 1, 2011. Published May 2011. Originallyapproved in 1980. Last previous edition approved in 2005 as B673 051. DOI:10.1520/B0673-05R11.* New designation established in accordance with ASTM E527 and SAE J1086,P

13、ractice for Numbering Metals and Alloys (UNS).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from

14、 American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.8 EndsPlain ends cut and deburred will be furnished,unless otherwise

15、specified, and5.1.9 Samples for Product (Check) AnalysisState whethersamples shall be furnished.6. Materials and Manufacture6.1 Pipe shall be made from flat-rolled alloy by an auto-matic welding process with no addition of filler metal. Subse-quent to welding and before final solution treatment, Cla

16、ss 1and Class 2 material shall be cold worked either in both weldand base metal or in weld metal only.NOTE 1The recommended heat treatment shall consist of heating to atemperature of 1975 to 2150F (1080 to 1180C) for UNS N08354, or2010 to 2100F (1100 to 1150C) for UNS N08925 and UNS N08926,followed

17、by quenching in water or rapid cooling by other means.6.2 Pipe shall be furnished with oxide removed. Whensolution treatment is performed in a protective atmosphere,descaling is not necessary.NOTE 2Pipe produced with the addition of filler metal is available.The manufacturer must be consulted for ap

18、plicable requirements.7. Chemical Composition7.1 The material shall conform to the requirements as tochemical composition prescribed in Table 2.7.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations prescribed in Specifica

19、tion B775.8. Mechanical Properties and Other Requirements8.1 Tension TestThe tensile properties of the material atroom temperature shall conform to those shown in Table 3.TABLE 1 Dimensions of Welded PipeNOTE 1The following table is a partial reprint of Table 1 of ANSI B36.19.NOTE 2The decimal thick

20、nesses listed for the respective pipe sizes represent their nominal wall dimensions.NOTE 31 in. = 25.4 mm.NominalPipe Size,in.Outside DiameterNominal Wall Thickness, in.Schedule 5SASchedule 10SASchedule 40S Schedule 80S Schedule 160S18 0.405 10.29 . . 0.049 1.25 0.068 1.73 0.095 2.41 . .14 0.540 13.

21、72 . . 0.065 1.65 0.088 2.24 0.119 3.02 . .38 0.675 17.15 . . 0.065 1.65 0.091 2.31 0.126 3.20 . .12 0.840 21.34 0.065 1.65 0.083 2.11 0.109 2.77 0.147 3.73 0.187 4.7534 1.050 26.67 0.065 1.65 0.083 2.11 0.113 2.87 0.154 3.91 0.218 5.541 1.315 33.40 0.065 1.65 0.109 2.77 0.133 3.38 0.179 4.46 0.250

22、6.35114 1.660 42.16 0.065 1.65 0.109 2.77 0.140 3.56 0.191 4.85 0.250 6.35112 1.900 48.26 0.065 1.65 0.109 2.77 0.145 3.68 0.200 5.08 0.281 7.142 2.375 60.33 0.065 1.65 0.109 2.77 0.154 3.91 0.218 5.54 0.343 8.71212 2.875 73.03 0.083 2.11 0.120 3.05 0.203 5.16 0.276 7.01 0.375 9.523 3.500 88.90 0.08

23、3 2.11 0.120 3.05 0.216 5.49 0.300 7.62 0.438 11.12312 4.000 101.60 0.083 2.11 0.120 3.05 0.226 5.74 0.318 8.08 . .4 4.500 114.30 0.083 2.11 0.120 3.05 0.237 6.02 0.337 8.56 0.581 13.415 5.563 141.30 0.109 2.77 0.134 3.40 0.258 6.55 0.375 9.52 0.625 15.886 6.625 168.30 0.109 2.77 0.134 3.40 0.280 7.

24、11 0.432 10.97 0.718 18.248 8.625 219.07 0.109 2.77 0.148 3.76 0.322 8.18 0.500 12.70 0.906 23.0110 10.750 273.05 0.134 3.40 0.165 4.19 0.365 9.27 0.500B12.70B1.125 28.5812 12.75 323.85 0.156 3.96 0.180 4.57 0.375 9.52 0.500B12.70B1.312 33.3214 14.00 355.60 0.156C3.96 0.188 4.78 0.375 9.52 0.500 12.

25、70 . .16 16.00 406.40 0.165C4.19 0.188 4.78 0.375 9.52 0.500 12.70 . .18 18.00 457.20 0.165C4.19 0.188 4.78 0.375 9.52 0.500 12.70 . .20 20.00 508.00 0.188C4.78 0.218C5.54 0.375 9.52 0.500 12.70 . .22 22.00 558.80 0.188C4.78 0.218C5.54 0.375 9.52 0.500 12.70 . .24 24.00 609.60 0.218C5.54 0.250 6.35

26、0.375 9.52 0.500 12.70 . .30 30.00 762.00 0.250C6.35 0.312 7.92 0.375 9.52 0.500 12.70 . .ASchedule 5S and 10S wall thicknesses do not permit threading in accordance with ANSI B2.1.BThese do not conform to ANSI B31.10.CThese do not conform to ANSI for Welded and Seamless Wrought Steel Pipe (ANSI B36

27、.10).TABLE 2 Chemical RequirementsElementUNSN08925 UNN08354UNSN08926Carbon, max 0.020 0.030 0.020Manganese, max 1.0 1.00 2.00Phosphorus, max 0.045 0.030 0.03Sulfur, max 0.030 0.010 0.01Silicon, max 0.50 1.00 0.5Nickel 24.0 to 26.0 34.0 to 36.0 24.00 to 26.00Chromium 19.0 to 21.0 22.0 to 24.0 19.00 t

28、o 21.00Molybdenum 6.0 to 7.0 7.0 to 8.0 6.0 to 7.0Copper 0.8 to 1.5 . 0.5 to 1.5Nitrogen 0.1 to 0.2 0.17 to 0.24 0.15 to 0.25IronAbalance balance balanceAIron shall be determined arithmetically by difference. UNS N08925 was editorially corrected.TABLE 3 Mechanical PropertiesAlloy TemperTensileStreng

29、th,min, psi(MPa)YieldStrength,0.2 %offset, min,psi (MPa)Elongationin 2 in. or50 mm, (or4D), min,%UNS N08925 solution annealed 87 (600) 43 (300) 40UNS N08354 solution annealed 93 (640) 43 (295) 40UNS N08926 solution annealed 94 (650) 43 (295) 35B673 05 (2011)28.1.1 One tension test shall be made on e

30、ach lot of pipe.8.2 Flattening TestOne flattening test shall be made on aspecimen from one end of one pipe from each lot.8.3 Nondestructive Tests:8.3.1 Class 1 and Class 3Each piece in each lot shall besubjected to one of the following four tests: hydrostatic,pneumatic (air underwater), eddy-current

31、, or ultrasonic.8.3.2 Class 2Each piece in each lot shall be subjected toa leak test and an electric test as follows:8.3.2.1 Leak TestHydrostatic or pneumatic (air underwa-ter).8.3.2.2 Electric TestEddy-current or ultrasonic.8.3.3 The manufacturer shall have the option to test Class 1or Class 2 and

32、select the nondestructive test methods, if notspecified by the purchaser.9. Dimensions and Permissible Variations9.1 The outside diameter and nominal wall thickness shallnot exceed the permissible variations prescribed in Specifica-tion B775.10. Keywords10.1 UNS N08925; UNS N08354; UNS N08926; welde

33、dpipeASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights

34、, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional st

35、andardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Co

36、mmittee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).B673 05 (2011)3