ASTM B688-1996(2009) Standard Specification for Chromium-Nickel-Molybdenum-Iron (UNS N08366 and UNS N08367) Plate Sheet and Strip《铬-镍-钼-铁(UNS N08366和UNS N08367)厚板材、薄板材和带材用标准规范》.pdf

1、Designation: B 688 96 (Reapproved 2009)Standard Specification forChromium-Nickel-Molybdenum-Iron (UNS N08366 and UNSN08367) Plate, Sheet, and Strip1This standard is issued under the fixed designation B 688; the number immediately following the designation indicates the year oforiginal adoption or, i

2、n the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers chromium-nickel-molybdenum-iron UNS N08366 and UNS N0836

3、7* plate,sheet, and strip for use in corrosive service and heat-resistingapplications.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard

4、.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materiala

5、s provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2E 8/E 8M Test Methods for Tension Testing of MetallicMaterialsE10 Test Method for Brinell Hardness of

6、Metallic Materi-alsE18 Test Methods for Rockwell Hardness of MetallicMaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE38 Methods for Chemical Analysis of Nickel-Chromiumand Nickel-Chromium-Iron Alloys3E 140 Hardness Conversion Tables for Met

7、als RelationshipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, andScleroscope HardnessE 354 Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron,Nickel, and Cobalt Alloys3. Terminology3.1 Definitions o

8、f Terms Specific to This Standard:3.1.1 sheet, nmaterial under316 in. (5 mm) in thicknessand 24 in. (610 mm) and over in width.3.1.2 strip, nmaterial under316 in. (5 mm) in thicknessand under 24 in. (610 mm) in width.3.1.3 plate, nmaterial316 in. (5 mm) and over in thicknessand over 10 in. (254 mm)

9、in width.4. Ordering Information4.1 Orders for material under this specification shall includethe following information, as required:4.1.1 Quantity (feet, metres, or number of pieces),4.1.2 Alloy name or UNS number,4.1.3 Finish (hot-rolled or cold-rolled),4.1.4 Dimensions (thickness, width, and leng

10、th if cut-length),4.1.5 Certification, if required,4.1.6 Purchasers inspection, if required,4.1.7 ASTM designation and year of issue, and4.1.8 Samples for product analysis, if required.5. Chemical Composition5.1 The material shall conform to the composition limitsspecified in Table 1.5.2 If a produc

11、t (check) analysis is made by the purchaser,the material shall conform to the permissible variations forproduct (check) analysis in Table 1.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Ref

12、ined Nickel and Cobalt and Their Alloys.Current edition approved April 15, 2009. Published April 2009. Originallyapproved in 1981. Last previous edition approved in 2004 as B 688 96 (2004).* New designation established in accordance with ASTM E 527 and SAE J1086,Practice for Numbering Metals and All

13、oys (UNS).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Withdrawn.1Copyright ASTM International, 100 Barr

14、Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Mechanical Properties and Other Requirements6.1 The material shall conform to the mechanical propertyrequirements specified in Table 2.7. Dimensions and Permissible Variations7.1 SheetMaterial shall conform to the variatio

15、ns speci-fied in Tables 3-9, inclusive. There will be no flatness require-ments for non-stretcher leveled sheet.7.2 StripMaterial shall conform to the variations specifiedin Tables 10-13, inclusive. Note that strip of all sizes may beordered to cut lengths in which case a variation of12 in. (13mm) o

16、ver the specified length shall be permitted. There shall beno flatness requirements for non-stretcher leveled strip.7.3 PlateMaterial shall conform to the variations speci-fied in Tables 14-20, inclusive. Specially flattened plate, whenso specified, shall have permissible variations in flatness asag

17、reed upon between the manufacturer and purchaser.8. Workmanship, Finish and Appearance8.1 The material shall be uniform in quality and condition,smooth, commercially straight or flat, and free of injuriousimperfections.9. Sampling9.1 Lot for Chemical Analysis and Mechanical Testing:9.1.1 A lot for c

18、hemical analysis shall consist of one heat.TABLE 1 Chemical RequirementsElementComposition Limits, %Product (Check)Analysis Varia-tions, under minor over max, ofthe SpecifiedLimit of Ele-ment, %N08366 N08367Carbon 0.035 max 0.030 max 0.005Manganese 2.00 max 2.00 max 0.04Silicon 1.00 max 1.00 max 0.0

19、5Phosphorus 0.040 max 0.040 max 0.005Sulfur 0.030 max 0.030 max 0.005Chromium 20.00 to 22.00 20.00 to 22.00 0.25Nickel 23.50 to 25.50 23.50 to 25.50 0.20Molybdenum 6.00 to 7.00 6.00 to 7.00 0.15Nitrogen . 0.18 to 0.25 0.01IronAremainder remainder .Copper . 0.75 max 0.04AIron shall be determined arit

20、hmetically by difference.TABLE 2 Mechanical Properties for Plate, Sheet, and StripN08366 N08367Yield strength, 0.2 % offset, min, ksi(MPa)35 (240) 45 (310)Tensile strength, min, ksi (MPa)#316 in. (4.8 mm) thick 75 (515) 100 (690)316 75 (515) 95 (655)Elongation in 2 in. or 50 mm or 4D,min, %30A30AHar

21、dness,Bmax#316 in. (4.8 mm) thick 95 HRB 100 HRB316 212 HBN 240 HBNANot applicable for thickness under 0.015 in. (0.40 mm).BHardness values (Brinell, Rockwell, or equivalent) are informative only and arenot to be construed as the basis for acceptance or rejection.TABLE 3 Permissible Variations in Th

22、ickness for Hot-Rolled Sheets in Cut Lengths, Cold-Rolled Sheets in CutLengths and CoilsSpecified Thickness,Ain. (mm)PermissibleVariations, Plusand Minusin. mmOver 0.145 (3.68) to less than316 (4.76) 0.014 0.36Over 0.130 (3.30) to 0.145 (3.68), incl 0.012 0.30Over 0.114 (2.90) to 0.130 (3.30), incl

23、0.010 0.25Over 0.098 (2.49) to 0.114 (2.90), incl 0.009 0.23Over 0.083 (2.11) to 0.098 (2.49), incl 0.008 0.20Over 0.072 (1.83) to 0.083 (2.11), incl 0.007 0.18Over 0.058 (1.47) to 0.072 (1.83), incl 0.006 0.15Over 0.040 (1.02) to 0.058 (1.47), incl 0.005 0.13Over 0.026 (0.66) to 0.040 (1.02), incl

24、0.004 0.10Over 0.016 (0.41) to 0.026 (0.66), incl 0.003 0.08Over 0.007 (0.18) to 0.016 (0.41), incl 0.002 0.05Over 0.005 (0.13) to 0.007 (0.18), incl 0.0015 0.040.005 (0.13) 0.001 0.03AThickness measurements are taken at least38 in. (9.52 mm) from the edge ofthe sheet.TABLE 4 Permissible Variations

25、in Width and Lengthfor Hot-Rolled and Cold-Rolled Resquared Sheets(Stretcher Leveled Standard of Flatness)Specified Dimensions, in. (mm)TolerancesPlusMinusin. mmFor thickness under 0.131 (3.33):Widths up to 48 (1219) excl116 20Widths 48 (1219) and over18 30Lengths up to 120 (3048) excl116 20Lengths

26、120 (3048) and over18 30For thicknesses 0.131 (3.33) and over:All widths and lengths14 60TABLE 5 Permissible Variations in Width for Hot-Rolled andCold-Rolled Sheets not Resquared and Cold-Rolled CoilsSpecified Thickness, in.(mm)Tolerances for SpecifiedWidth, in. (mm)24 (610) to 48(1219), excl48 (12

27、19) andOverLess than316 (4.76)116 (2) plus0 minus18 (3) plus0 minusTABLE 6 Permissible Variations in Camber for Hot-Rolledand Cold-Rolled Sheets Not Required and Cold-Rolled CoilsASpecified Width, in. (mm)Tolerance perUnit Length ofAny 8 ft (2438 mm),in. (mm)24 (610) to 36 (914), incl18 (3)Over 36 (

28、914)116 (2)ACamber is the greatest deviation of a side edge from a straight line andmeasurement is taken by placing an 8-ft (2438-mm) straightedge on the concaveside and measuring the greatest distance between the sheet edge and thestraightedge.TABLE 7 Permissible Variations in Length for Hot-Rolled

29、 and Cold-Rolled Sheets Not ResquaredLength, ft (mm) Tolerances, in. (mm)Up to 10 (3048), incl14 (6) plus 0 minusOver 10 (3048) to 20 (6096), incl12 (13) plus 0 minusB 688 96 (2009)29.1.2 Lots for mechanical testing shall consist of the mate-rial from one heat, in the same condition, and of the same

30、nominal thickness.9.2 Test Material Selection:9.2.1 Chemical Analysis:9.2.1.1 An analysis of each lot shall be made by themanufacturer from a representative sample obtained during thepouring of the heat or subsequent processing.9.2.1.2 If samples for product (check) analysis are specified,a represen

31、tative sample shall be taken from each lot (see 9.1.1)of finished material.9.2.2 Sampling for Mechanical PropertiesSamples of thematerial to provide test specimens for mechanical testing shallbe taken from such locations in each lot (see 9.1.2)astoberepresentative of that lot.10. Number of Tests10.1

32、 Chemical AnalysisOne test per lot.10.2 Mechanical TestsOne test per lot.10.3 RetestsIf the specimen used in the mechanical test ofany lot fails to meet the specified requirements, two additionalspecimens shall be taken from different sample pieces andTABLE 8 Permissible Variations in Flatness for H

33、ot-Rolled and Cold-Rolled Sheets Specified to Stretcher-LeveledStandard of FlatnessSpecified Thickness, in. (mm) Width, in. (mm) Length, in. (mm) Flatness Tolerance,Ain. (mm)Under316 (4.76) to 48 (1219), incl to 96 (2438), incl18 (3)Under316 (4.76) to 48 (1219), incl over 96 (2438)14 (6)Under316 (4.

34、76) over 48 (1219) to 96 (2438), incl14 (6)Under316 (4.76) over 48 (1219) over 96 (2438)14 (6)TABLE 9 Permissible Variations in Diameter for Hot-Rolled and Cold-Rolled Sheets, Sheared CirclesSpecified Thickness, in. (mm)Tolerance Over Specified Diameter (No Tolerance Under), in.(mm)Diameters Under 3

35、0in. (762)Diameters 30 (762)to 48 in. (1219)Diameters Over 48in. (1219)0.0972 (2.46) and thicker18 (3)316 (5)14 (6)0.0971 (2.46) to 0.0568 (1.45), incl332 (2)532 (4)732 (6)0.0567 (1.45) and thinner116 (2)18 (3)316 (5)TABLE 10 Permissible Variations in Thickness for Cold-Rolled Strip in Coils and Cut

36、 LengthsNOTE 1Thickness measurements are taken at least38 in. (9.52 mm) in from the edge of the strip, except that on widths less than 1 in. (25.4 mm),the tolerances are applicable for measurements at all locations. The tolerances in this table include crown tolerances.Specified Thickness, in. (mm)T

37、hickness Tolerances, for the Thickness and Widths Given, Plus and Minus, in. (mm)Width, in. (mm)316 (4.76) to 6 (152),inclOver 6 (152) to 12(305), inclOver 12 (305) to 24(610), exclThickness TolerancesA0.005 (0.13) to 0.010 (0.25), incl 10 % 10 % 10 %Over 0.010 (0.25) to 0.011 (0.28), incl 0.0015 (0

38、.04) 0.0015 (0.04) 0.0015 (0.04)Over 0.011 (0.28) to 0.013 (0.33), incl 0.0015 (0.04) 0.0015 (0.04) 0.002 (0.05)Over 0.013 (0.33) to 0.017 (0.43), incl 0.0015 (0.04) 0.002 (0.05) 0.002 (0.05)Over 0.017 (0.43) to 0.020 (0.51), incl 0.0015 (0.04) 0.002 (0.05) 0.0025 (0.06)Over 0.020 (0.51) to 0.029 (0

39、.74), incl 0.002 (0.05) 0.0025 (0.06) 0.0025 (0.06)Over 0.029 (0.74) to 0.035 (0.89), incl 0.002 (0.05) 0.003 (0.08) 0.003 (0.08)Over 0.035 (0.89) to 0.050 (1.27), incl 0.0025 (0.06) 0.0035 (0.09) 0.0035 (0.09)Over 0.050 (1.27) to 0.069 (1.75), incl 0.003 (0.08) 0.0035 (0.09) 0.0035 (0.09)Over 0.069

40、 (1.75) to 0.100 (2.54), incl 0.003 (0.08) 0.004 (0.10) 0.005 (0.13)Over 0.100 (2.54) to 0.125 (2.98), incl 0.004 (0.10) 0.0045 (0.11) 0.005 (0.13)Over 0.125 (2.98) to 0.161 (4.09), incl 0.0045 (0.11) 0.0045 (0.11) 0.005 (0.13)Over 0.161 (4.09) to under316 (4.76) 0.005 (0.13) 0.005 (0.13) 0.006 (0.1

41、5)AThickness tolerances given in in. (mm) unless otherwise indicated.TABLE 11 Permissible Variations in Width for Cold-Rolled Strip in Coils and Cut Lengths for Edge Nos. 1 and 5Specified EdgeNo.Width, in. (mm) Thickness, in. (mm)Width Tolerance for Thicknessand Width Given, in. (mm)Plus Minus1 and

42、5332 (7.14) and under116 (1.59) and under 0.005 (0.13) 0.005 (0.13)1 and 5 over332 (7.14) to34 (19.05), incl332 (2.38) and under 0.005 (0.13) 0.005 (0.13)1 and 5 over34 (19.05) to 5 (127), incl18 (3.18) and under 0.005 (0.13) 0.005 (0.13)5 over 5 (127.00) to 9 (228.60), incl18 (3.18) to 0.008 (0.20)

43、, incl 0.010 (0.25) 0.010 (0.25)5 over 9 (228.60) to 20 (508.00), incl 0.105 (2.67) to 0.015 (0.38) 0.010 (0.25) 0.010 (0.25)5 over 20 (508.00) 0.080 (2.03) to 0.023 (0.58) 0.015 (0.38) 0.015 (0.38)B 688 96 (2009)3tested. The results of the tests on both of these specimens shallmeet the specified re

44、quirements.11. Specimen Preparation11.1 Tension test specimens shall be taken from material inthe final condition and tested transverse to the direction ofrolling when width permits.11.2 Tension test specimens shall be any of the standard orsub-size specimens shown in Test Methods E 8/E 8M. Thelarge

45、st possible size specimen of Test Methods E 8/E 8M shallbe used.11.3 In the event of disagreement, referee specimens shallbe as follows:11.3.1 Full thickness of the material machined to the formand dimensions shown for the sheet-type specimen in TestMethods E 8/E 8M for material under12 in. (13 mm)

46、inthickness.11.3.2 The largest possible round specimen shown in TestMethods E 8/E 8M for material12 in. (13 mm) and over inthickness.12. Test Methods12.1 Determine the chemical composition and mechanicalproperties of the material, as enumerated in this specification,in the case of disagreement, in a

47、ccordance with the followingASTM methods:12.1.1 Chemical AnalysisMethods E38and Test MethodsE 354.12.1.1.1 Methods E38shall be used only for elements notcovered by Test Methods E 354.12.2 Tension TestTest Methods E 8/E 8M.12.3 Hardness TestTest Method E10 or Test MethodsE18, as applicable.12.4 Hardn

48、ess ConversionHardness Conversion TablesE 140.12.5 Determination of Significant PlacesFor purposes ofdetermining compliance with the specified limits for therequirements of the properties listed in the following table,round an observed or a calculated value as indicated, inaccordance with the roundi

49、ng methods of Practice E29.Requirements rounded unit for observed orcalculated valueChemical composition nearest unit in the last right-hand place of figures of thespecified limitTensile strength and yieldstrengthnearest 1000 psi (7 MPa)Elongation nearest 1 %Brinell hardness tabular valueARockwell hardness 1 Rockwell numberARound the mean diameter of the Brinell impression to the nearest 0.05 mmand report the corresponding hardness number read from the table without furtherrounding.13. Inspection13.1 Inspection o