ASTM B704-2003(2014) Standard Specification for Welded UNS N06625 UNS N06219 and UNS N08825 Alloy Tubes《焊接UNS N06625 UNS N06219和UNS N08825合金管的标准规格》.pdf

1、Designation: B704 03 (Reapproved 2014)Standard Specification forWelded UNS N06625, UNS N06219 and UNS N08825 AlloyTubes1This standard is issued under the fixed designation B704; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the y

2、ear of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers welded UNS N06625, UNSN06219 and UNS N08825 alloy boiler, heat exchanger, andcondense

3、r tubes for general corrosion resisting and low orhigh-temperature service.1.2 This specification covers tubes18 to 5 in. (3.18 to 127mm), inclusive, in outside diameter and 0.015 to 0.500 in. (0.38to 12.70 mm), inclusive, in wall thickness. Specification B751lists the dimensional requirements of th

4、ese sizes. Tubes havingother dimensions may be furnished provided such tubingcomplies with all other requirements of this specification.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided f

5、or information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial S

6、afety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B751 Specification for General Requirements for Nick

7、el andNickel Alloy Welded TubeE8 Test Methods for Tension Testing of Metallic Materials3. Ordering Information3.1 Orders for material to this specification should includethe following information:3.1.1 Quantity (feet or number of lengths),3.1.2 UNS number,3.1.3 Size (outsize diameter, minimum or ave

8、rage wallthickness),3.1.4 Length (random or specific),3.1.5 Class, and3.1.6 Grade if UNS N06625 is specified. If neither grade ofN06625 is specified, grade 1 will be supplied.3.1.7 ASTM designation.3.1.8 Product AnalysisState if required.3.1.9 CertificationState if a certification or a report of tes

9、tresults is required.3.1.10 Purchaser InspectionState which tests or inspec-tions are to be witnessed, if any.4. Materials and Manufacture4.1 Tube shall be made from flat-rolled alloy by an auto-matic welding process with no addition or filler metal. Subse-quent to welding and prior to final anneali

10、ng, the material shallbe cold-worked in either the weld metal only or both weld andbase metal.4.2 Tube shall be furnished with oxide removed. Whenbright annealing is used, descaling is not necessary.5. Chemical Composition5.1 The material shall conform to the composition limitsspecified in Table 1.

11、One test is required for each lot as definedin Specification B751.5.2 If a product analysis is performed, it shall meet thechemistry limits prescribed in Table 1, subject to the analysistolerances of Specification B751.6. Mechanical and Other Properties6.1 Mechanical PropertiesThe material shall con

12、form tothe mechanical property requirements specified in Table 2. Onetest is required for each lot as defined in Specification B751.6.2 Flattening TestA flattening test shall be made on eachend of one tube per lot. Superficial ruptures resulting fromsurface imperfections shall not be cause for rejec

13、tion.6.3 Flange TestA flange test shall be made on each end ofone tube per lot.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition appro

14、ved Oct. 1, 2014. Published October 2014. Originallyapproved in 1982. Last previous edition approved in 2009 as B704 03 (2009).DOI: 10.1520/B0704-03R14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMSta

15、ndards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16.4 Nondestructive Test Requirements:6.4.1 Class 1Each piece in each lot shall be subject to on

16、eof the following four tests: hydrostatic, pneumatic (airunderwater), eddy current, or ultrasonic.6.4.2 Class 2Each piece in each lot shall be subjected toa leak test and an electric test as follows:6.4.2.1 Leak TestHydrostatic or pneumatic (air underwa-ter).6.4.2.2 Electric TestEddy current or ultr

17、asonic.6.5 The manufacturer shall have the option to test to Class1 or 2 and select the nondestructive test methods, if notspecified by the purchaser.7. General Requirements7.1 Material furnished under this specification shall con-form to the applicable requirements of the current edition ofSpecific

18、ation B751 unless otherwise provided herein.8. Product Marking8.1 In addition to the requirements of Specification B751,UNS N06625 tubes shall be marked with grade information.9. Keywords9.1 UNS N06219; UNS N06625; UNS N08825; weldedtubeASTM International takes no position respecting the validity of

19、 any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to

20、revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Y

21、our comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is co

22、pyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.

23、org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Chemical RequirementsComposition Limits, %UNSN06625UNSN06219UNSN08825Ni 58

24、.0 minABal 38.046.0Cr 20.023.0 18.0-22.0 19.523.5Fe 5.0 max 2.0-4.0 22.0 minAMo 8.010.0 7.0-9.0 2.5 3.5Cb + Ta 3.154.15 . .C 0.10 max 0.05 max 0.05 maxMn 0.50 max 0.50 max 1.0 maxSi 0.5 max 0.70-1.10 0.5 maxP 0.015 max 0.020 max .S 0.015 max 0.010 max 0.03 maxAl 0.4 max 0.50 max 0.2 maxTi 0.40 max 0

25、.50 max 0.61.2Co (if determined) 1.0 max 1.0 max .Cu . 0.50 max 1.53.0AElement may be determined arithmetically by difference.TABLE 2 Mechanical Property RequirementsAlloy GradeTensileStrengthmin, psi (MPa)Yield StrengthA0.2 % Offset,min, psi (MPa)Elonga-tionin2in.or50mm, min,%UNS N06625 1 (annealed

26、) 120 000 (827) 60 000 (414) 30UNS N06625 2 (solutionannealed)B100 000 (690) 40 000 (276) 30UNS N06219 . 96 000 (660) 39 000 (270) 30UNS N08825 . 85 000 (586) 35 000 (240) 30AYield strength shall be determined by the offset method at 0.2 % limitingpermanent set in accordance with Test Methods E8.BSolution annealed at 2000F (1093C) minimum, with or without subsequentstabilization anneal at 1800F (982C) minimum to increase resistance tosensitization.B704 03 (2014)2