ASTM B709-2017 Standard Specification for Iron-Nickel-Chromium-Molybdenum Alloy (UNS N08028) Plate Sheet and Strip《铁-镍-铬-钼合金(UNS N08028)厚板材 薄板材和带材的标准规格》.pdf

1、Designation: B709 04 (Reapproved 2014)B709 17Standard Specification forIron-Nickel-Chromium-Molybdenum Alloy (UNS N08028)Plate, Sheet, and Strip1This standard is issued under the fixed designation B709; the number immediately following the designation indicates the year oforiginal adoption or, in th

2、e case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers iron-nickel-chromium-molybdenum alloy (UNS N08028)2 plate, s

3、heet, and strip in thesolution-annealed condition.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.3 This standard does not purpor

4、t to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety DataSheet (MSDS)(SDS) for this product/material as provided by the manufact

5、urer, to establish appropriate safety and health practices,and determine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the Decision on Principles for the

6、 Development of International Standards, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3B880 Specification for General Requirements for Chemical Check Analysis Limits for Nickel, Nickel Alloys an

7、d Cobalt AlloysB906 Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE8/E8M Test Methods for Tension Testing of Metallic Materials3. Ordering Information3.1 It is the responsibility of the purchaser to specify all requirements that are necessary

8、for material ordered under thisspecification. Examples of such requirements include, but are not limited to those specified in Ordering Information Section inSpecification B906.4. General Requirements4.1 Material furnished under this specification shall conform to the applicable requirements of the

9、current edition ofSpecification B906, unless otherwise specified herein.5. Materials and Manufacture5.1 Heat TreatmentThe final heat treatment shall be a solution-anneal. Minor cold working such as flattening or temper rollingmay be performed after the final solution annealing treatment.NOTE 1This r

10、ecommended solution-anneal consists of heating to a minimum temperature of 1975F (1080C) and cooling rapidly to roomtemperature.1 This specification is under the jurisdiction ofASTM Committee B02 on Nonferrous Metals andAlloys and is the direct responsibility of Subcommittee B02.07 on RefinedNickel

11、and Cobalt and Their Alloys.Current edition approved Oct. 1, 2014April 1, 2017. Published October 2014April 2017. Originally approved in 1982. Last previous edition approved in 20092014 asB709 04 (2009). 04 (2014). DOI: 10.1520/B0709-04R14. 10.1520/B0709-17.2 New designation in accordance with ASTM

12、E527 and SAE J1086, Practice for Numbering Metals and Alloys (UNS).3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM we

13、bsite.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult pri

14、or editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Chemical Composition6.1 The material sa

15、mpled in accordance with 10.2 shall conform to the composition limits prescribed in Table 1.6.2 If a product analysis is subsequently made, the material shall conform to the composition limits with the product analysisvariation prescribed Specification B880.7. Mechanical Properties7.1 The material s

16、hall conform to the requirements as to the mechanical property prescribed in Table 2.8. Dimensions and Permissible Variations8.1 SheetMaterial furnished under this specification shall conform to the applicable requirements of the current edition ofSpecification B906, except as specified in Table 3 a

17、nd Table 4.8.2 Cold-Rolled StripMaterial furnished under this specification shall conform to the applicable requirements of the currentedition of Specification B906, except as specified in Tables 5-7.8.3 PlateMaterial furnished under this specification shall conform to the applicable requirements of

18、 the current edition ofSpecification B906.9. Sampling9.1 Sampling for Chemical Analysis, Mechanical Testing, and Corrosion Testing shall be performed in accordance withSpecification B906, except as specified herein:9.1.1 PlateAlot of plate for testing and inspection purposes shall consist of the pro

19、ducts resulting from the rolling of one heatof material in the same condition and specified thickness, solution annealed by the same practice, but in no case more than 25 000lb (11 340 kg).9.1.2 Sheet and StripA lot of sheet or strip for testing and inspection purposes shall consist of material from

20、 one heat in thesame form (sheet or strip), condition, finish, and specified thickness, solution-annealed by the same practice but in no case morethan 25 000 lb (11 340 kg).9.2 Sampling for Mechanical Tests:9.2.1 When samples are to be taken after delivery, the purchaser of material ordered to cut l

21、engths may request on the purchaseorder additional material of adequate size to provide sample coupons for inspection purposes.10. Number of Tests and Retests10.1 In the case of sheet or strip supplied in coil form, two or more tension tests (one from each end of each coil), and one ormore hardness

22、tests shall be made on specimens taken from each end of the coil. When material is supplied in flatsheet, flat strip,or plate, one tension and one or more hardness tests shall be made on each 100 or less sheets, strips, or plates of the same lot. Whenspecified, one corrosion test shall be conducted

23、for each lot.10.2 If any specimens selected to represent any lot fail to meet any of the test requirements, the material represented by suchspecimens may be retested. If there is valid reason to believe the result is not representative, the material may be re-reannealedand retested.11. Specimen Prep

24、aration11.1 Tension test specimens from material under 12 in. (12.7 mm) in thickness shall be of the full thickness of the material andmachined to the form and dimensions shown for the sheet-type specimen in Test Methods E8/E8M. Tension test specimens frommaterial 12 in. (12.7 mm) and over shall be

25、of the full thickness of the material, machined to the form and dimensions shown forTABLE 1 Chemical RequirementsElement Composition, %Ni 29.5 to 32.5Ni 30.0 to 34.0Fe remainderACr 26.0 to 28.0Mo 3.0 to 4.0C, max 0.030Si, max 1.00Mn, max 2.50P, max 0.030S, max 0.030Cu 0.6 to 1.4A Determined arithmet

26、ically by difference.B709 172the plate-type specimen in Test Methods E8/E8M. Tension test specimens shall be taken from material after final heat treatmentand shall be selected in the transverse direction unless prohibited by width.12. Keywords12.1 N08028; plate; sheetstripTABLE 2 Mechanical Propert

27、y RequirementsFormTensileStrength,min, ksi(MPa)YieldStrength(0.2 % off-off-set),set), min,ksi (MPa)Elonga-Elongationtion in 2in. in.or 5050 mm,or4D, min,%RockwellHardness (or(or equivalent)ASheet 73 (500) 31 (214) 40 7090 HRBStrip 73 (500) 31 (214) 40 7090 HRBPlate 73 (500) 31 (214) 40 7090 HRBA Har

28、dness values are shown for information only and shall not constitute a basis for acceptance or rejection as long as the other mechanical properties are met.TABLE 3 Flatness Tolerances for Hot-Rolled and Cold-Rolled SheetsSheets not Specified to Stretcher Leveled Standard of FlatnessSpecified Thickne

29、ss, in. (mm) Width, in. (mm)Flatness Tolerance (maxDeviation from a HorizontalFlat Surface), in. (mm)0.062 (1.57) and over to 60 (1524), inclover 60 to 72 (1524 to 1829), incl12 (12.7)34 (19.1)over 72 (1829) 1 (25.4)Under 0.062 (1.57) to 36 (914), inclover 36 to 60 (914 to 1524), incl12 (12.7)34 (19

30、1)over 60 (1524) 1 (25.4)TABLE 4 Weight Tolerances for Hot-Rolled and Cold-Rolled SheetsIt is not practicable to produce hot-rolled and cold-rolled sheets to exact theoretical weight. Sheets of any one item of a specified thicknessand size in any finish may be overweight to the following extent:(1)

31、 An item of five sheets or less, or an item estimated to weigh 200 lb (90.7 kg) or less, may actually weigh as much as 10 % over thetheoretical weight.(2) An item of more than five sheets and estimated to weigh more than 200 lb (90.7 kg) may actually weigh as much as 712 % over thetheoretical weight

32、3) The underweight variations for sheets are limited by the under thickness tolerances shown in Table 3 of Specification B906.For determining theoretical weight, the factor 42 lb/ft2in. (0.0008 kg/cm2mm) thickness may be used.B709 173TABLE 5 Thickness ToleranceA,B,C for Cold-Rolled Strip for the T

33、hicknesses and Widths Given, Over and UnderSpecified ThicknessWidth, in.0.187 to 1,inclOver 1 to3, inclOver 3 to6, inclOver 6 to9, inclOver 9 to12, inclOver 12 to16, inclOver 16 to20, inclOver 20 to24, inclThickness Tolerance, in.Over 0.160 to less than 0.002 0.003 0.004 0.004 0.004 0.005 0.006 0.00

34、60.187Over 0.099 to 0.160, incl 0.002 0.002 0.003 0.003 0.004 0.004 0.005 0.005Over 0.068 to 0.099, incl 0.002 0.002 0.003 0.003 0.003 0.004 0.004 0.004Over 0.049 to 0.068, incl 0.002 0.002 0.003 0.003 0.003 0.003 0.004 0.004Over 0.039 to 0.049, incl 0.002 0.002 0.0025 0.003 0.003 0.003 0.004 0.004O

35、ver 0.034 to 0.039, incl 0.002 0.002 0.0025 0.0025 0.003 0.003 0.003 0.003Over 0.028 to 0.034, incl 0.0015 0.0015 0.002 0.002 0.0025 0.0025 0.003 0.003Over 0.025 to 0.028, incl 0.001 0.0015 0.0015 0.002 0.002 0.002 0.0025 0.003Over 0.019 to 0.025, incl 0.001 0.001 0.0015 0.0015 0.002 0.002 0.0025 0.

36、0025Over 0.016 to 0.019, incl 0.001 0.001 0.001 0.0015 0.0015 0.002 0.002 0.002Over 0.012 to 0.016, incl 0.001 0.001 0.001 0.001 0.0015 0.0015 0.002 0.002Over 0.011 to 0.012, incl 0.001 0.001 0.001 0.001 0.0015 0.0015 0.0015 0.0015Over 0.010 to 0.011, incl 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015

37、 0.00150.010 0.001 0.001 0.001 0.001 0.001 0.001 0.0015 0.0015Specified Thickness, mmWidth, mm4.76 to25.4, inclOver25.4to 76.2,inclOver 76.2to 152.4,inclOver152.4 to228.6,inclOver228.6 to304.8, inclOver304.8 to406.4,inclOver406.4 to508, inclOver 508to 609.6,inclThickness Tolerance, mmOver 4.06 to le

38、ss than 0.05 0.08 0.10 0.10 0.10 0.13 0.15 0.154.76Over 2.51 to 4.06, incl 0.05 0.05 0.08 0.08 0.10 0.10 0.13 0.13Over 1.73 to 2.51, incl 0.05 0.05 0.08 0.08 0.08 0.10 0.10 0.10Over 1.25 to 1.73, incl 0.05 0.05 0.08 0.08 0.08 0.08 0.10 0.10Over 0.99 to 1.24, incl 0.05 0.05 0.06 0.08 0.08 0.08 0.10 0

39、10Over 0.86 to 0.99, incl 0.05 0.05 0.06 0.06 0.08 0.08 0.08 0.08Over 0.71 to 0.86, incl 0.04 0.04 0.05 0.05 0.06 0.06 0.08 0.08Over 0.64 to 0.71, incl 0.02 0.04 0.04 0.05 0.05 0.05 0.06 0.08Over 0.48 to 0.64, incl 0.02 0.02 0.04 0.04 0.05 0.05 0.06 0.06Over 0.41 to 0.48, incl 0.02 0.02 0.02 0.04 0

40、04 0.05 0.05 0.05Over 0.38 to 0.41, incl 0.02 0.02 0.02 0.02 0.04 0.04 0.05 0.05Over 0.28 to 0.30, incl 0.02 0.02 0.02 0.02 0.04 0.04 0.04 0.04Over 0.25 to 0.28, incl 0.02 0.02 0.02 0.02 0.02 0.04 0.04 0.040.25 0.02 0.02 0.02 0.02 0.02 0.02 0.04 0.04A For thickness under 0.010 to 0.005 in. (0.254 t

41、o 0.127 mm), inclusive, in widths up to and including 16 in. (406 mm), a tolerance of 10 % of the thickness applies. Forthicknesses under 0.010 to 0.005 in. (0.254 to 0.127 mm), inclusive, in widths over 16 to 24 in. (406 to 610 mm), exclusive, a tolerance of 15 % of the thickness applies.For thickn

42、ess tolerances on thicknesses under 0.005 in. (0.127 mm) in widths up to 24 in. (610 mm), exclusive, the producer should be consulted.B Thickness measurements are taken 38 in. (9.5 mm) in from the edge of the strip, except that on widths less than 1 in. (25.4 mm) the tolerances are applicable formea

43、surements at all locations.C The tolerances in this table do not include crown tolerances.TABLE 6 Crown Tolerances for Cold-Rolled StripSpecified Thickness, in. (mm)Additional Thickness, at Middle of Strip over That Shown in Table 5 forEdge Measurement, for Widths and Thicknesses Given, in. (mm)Widt

44、h, in. (mm)To 5 (127), incl Over 5 to 12 (127 to305), incl Over 12 to 24 (305 to610), excl0.005 to 0.010 (0.127 to 0.254), incl 0.0075 (0.19) 0.001 (0.02) 0.0015 (0.04)Over 0.010 to 0.025 (0.254 to 0.635), incl 0.001 (0.02) 0.0015 (0.04) 0.002 (0.05)Over 0.025 to 0.065 (0.635 to 1.65), incl 0.0015 (

45、0.04) 0.002 (0.05) 0.0025 (0.06)Over 0.065 to 0.187 (1.65 to 4.76), excl 0.002 (0.05) 0.0025 (0.06) 0.003 (0.08)B709 174ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are express

46、ly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,

47、either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may atte

48、nd. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. I

49、ndividual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 7 Length and Camber Tolerances for Cold-Rolled StripLength TolerancesSpecified Length, ft (mm)Tolerance OverSpecifiedLength (No