ASTM B710-2004 Standard Specification for Nickel-Iron-Chromium-Silicon Alloy Welded Pipe《镍铁铬硅合金焊接管标准规范》.pdf

1、Designation: B 710 04Standard Specification forNickel-Iron-Chromium-Silicon Alloy Welded Pipe1This standard is issued under the fixed designation B 710; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A n

2、umber in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers alloys UNS N08330 and UNSN08332 in the form of welded pipe intended for heat-resistingapplications and genera

3、l-corrosive service.1.2 The pipe covered is nominal pipe sizes up to andincluding size 12, with the nominal wall thicknesses given asSchedules 5S, 10S, 40S, and 80S. Table 2 of SpecificationB 775 is based on Table A1 of ANSI B36.19 and gives thenominal dimension of these sizes. Table 3 of Specificat

4、ionB 775 lists the dimensional requirements of these sizes. Pipehaving other dimensions may be furnished provided such pipecomplies with all other requirements of this specification.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forin

5、formation only.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet for this product/ma

6、terial as pro-vided by the manufacturer, to establish appropriate safety andhealth practices, and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 536 Specification for Nickel-Iron-Chromium-Silicon Al-loy (UNS N08330 and N08332) Plate, Sh

7、eet, and StripB 775 Specification for General Requirements for Nickeland Nickel Alloy Welded PipeB 899 Terminology Relating to Non-ferrous Metals andAlloys2.2 ANSI Standard:4ANSI B36.19 Stainless Steel Pipe3. Terminology3.1 Definitions:3.1.1 Definitions for terms defined in Terminology B 899shall ap

8、ply unless otherwise defined by the requirements of thisdocument.4. General Requirement4.1 Material furnished in accordance with this specificationshall conform to the applicable requirements of the currentedition of Specification B 775 unless otherwise providedherein.5. Ordering Information5.1 It i

9、s the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Examples of such requirements include, but arenot limited to, the following:5.1.1 Quantity (feet or number of lengths),5.1.2 UNS number,5.1.3 Size (nominal pipe size and

10、schedule),5.1.4 Length (random or specific),5.1.5 ASTM designation,1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Feb. 1,

11、2004. Published February 2004. Originallyapproved in 1982. Last previous edition approved in 1999 as B 710 99.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SB710 in Section 11 of that code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orco

12、ntact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from American National Standards Institute, 11 West 42nd St., 13thFloor, New York, NY 10036.TABLE 1 Chemical RequirementsEle

13、ment Composition Limits, %C .AMn 2.00 maxP 0.03 maxS 0.03 maxSi 0.751.50Cr 17.020.0Ni 34.037.0Cu 1.00 maxPb 0.005 maxSn 0.025 maxFe remainderBAAlloy UNS N08330: 0.08 max. Alloy UNS N08332: 0.050.10.Blement shall be determined arithmetically by difference.1Copyright ASTM International, 100 Barr Harbo

14、r Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.6 Product Analysis State if required.5.1.7 Certification State if a certification or report of testresults is required,5.1.8 Purchaser InspectionState which tests or inspec-tions are to be witnessed, if any, and5.1.9 Supplemen

15、tary requirements, if any.6. Materials and Manufacture6.1 The pipe shall be made from flat-rolled alloy conform-ing to Specification B 536, by an automatic welding processwith no addition of filler metal. Subsequent to welding andprior to final heat treatment, the material shall be cold workedeither

16、 in both weld and base metal or in weld metal only.6.2 Heat Treatment Pipe of UNS N08330 alloy shall beannealed at 1900F (1040C), minimum. Pipe of UNS N08332alloy shall be annealed at 2100F (1150C), minimum.7. Chemical Composition7.1 The material shall conform to the composition limitsspecified in T

17、able 1. One test is required for each lot as definedin Specification B 775.7.2 If a product analysis is performed, it shall meet thechemistry limits prescribed in Table 1, subject to the analysistolerances specified in Table 1 of Specification B 775.8. Mechanical Properties and Other Requirements8.1

18、 Mechanical PropertiesThe material shall conform tothe mechanical property requirements specified in Table 2. Onetest is required for each lot as defined in Specification B 775.8.2 Flattening Test A flattening test shall be made on eachend of one pipe per lot. Superficial ruptures resulting fromsurf

19、ace imperfections shall not be cause for rejection.8.3 Nondestructive Test RequirementsEach pipe shall besubjected to either a pressure test or a nondestructive electrictest at the manufacturers option. The purchaser may specifywhich test is to be used.8.4 Grain SizeAnnealed alloy UNS N08332 shall c

20、on-form to an average grain size of ASTM No. 5 or coarser.9. Lengths9.1 Lengths may be ordered as either random lengths(normally 15 to 24 ft (4.6 to 8.3 m), with some agreed uponallowance for shorts) or specific cut lengths.10. Keywords10.1 high-temperature alloy; welded pipeASTM International takes

21、 no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own resp

22、onsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addresse

23、d to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the

24、address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phon

25、e), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 2 Mechanical PropertiesAlloy ConditionTensile Strength, min,psi (MPa)Yield Strength, 0.2 %offset, min, psi (MPa)Elongation in 2 in. or50 mm, or 4D, min,%HardnessAUNS N08330 annealed 70 000 (483) 30 000 (207) 30 70 to 90 HRBUNS N08332 annealed 67 000 (462) 27 000 (186) 30 65 to 88 HRBAHardness values are informative only and not to be construed as the basis for acceptance.B710042