ASTM B757-2000(2011) Standard Specification for Nickel-Chromium-Molybdenum-Tungsten-Alloys (UNS N06110) Welded Pipe《镍铬钼钨合金(UNS N06110)焊接管标准规格》.pdf

1、Designation: B757 00 (Reapproved 2011)Standard Specification forNickel-Chromium-Molybdenum-Tungsten-Alloys(UNS N06110) Welded Pipe1This standard is issued under the fixed designation B757; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revi

2、sion, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers welded UNS N061102pipe inthe annealed condition (temper) for general corro

3、sion applica-tions.1.2 This specification covers pipe sizes in schedules shownin Table 1.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered stand

4、ard.1.4 The following precautionary caveat pertains only to thetest method portion, Section 13, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to become familiar with all

5、 hazards includingthose identified in the appropriate Material Safety Data Sheet(MSDS) for this product/material as provided by the manufac-turer, to establish appropriate safety and health practices, anddetermine the applicability of regulatory limitations prior touse.2. Referenced Documents2.1 AST

6、M Standards:3E8 Test Methods for Tension Testing of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE38 Methods for Chemical Analysis of Nickel-Chromiumand Nickel-Chromium-Iron Alloys4E213 Practice for Ultrasonic Testing of Metal Pi

7、pe andTubingE354 Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron,Nickel, and Cobalt AlloysE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)E571 Practice for Electromagnetic (Eddy-Current) Exami-nation of Nickel and

8、 Nickel Alloy Tubular Products2.2 ANSI Standards:B2.1 Pipe Threads5B36.19 Stainless Steel Pipe53. Classification3.1 Class 1Welded, cold-worked, annealed, and nonde-structively tested in accordance with 11.4.1.3.2 Class 2Welded, cold-worked, annealed, and nonde-structively tested in accordance with 1

9、1.4.2.4. Ordering Information4.1 Orders for material to this specification shall include thefollowing information:4.1.1 Alloy Name or UNS number.4.1.2 ASTM Designation.4.1.3 Dimensions:4.1.3.1 Pipe size (see Table 1).4.1.3.2 Length (specific or random).4.1.4 Class (see 11.4).4.1.5 Quantity (feet or

10、number of pieces).4.1.6 CertificationState if certification is required (seeSection 16).4.1.7 Samples for Product (Check) AnalysisState whethersamples for product (check) analysis should be furnished(10.2).4.1.8 Purchaser InspectionIf purchaser wishes to witnesstests or inspection of material at pla

11、ce of manufacture, thepurchase order must so state indicating which tests or inspec-tions are to be witnessed (see Section 14).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel a

12、nd Cobalt and Their Alloys.Current edition approved Oct. 1, 2011. Published October 2011. Originallyapproved in 1990. Last previous edition approved in 2006 as B757 - 00 (2006).DOI: 10.1520/B0757-00R11.2New designation established in accordance with Practice E527 and SAEJ 1086,Recommended Practice f

13、or Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Withdrawn. The last app

14、roved version of this historical standard is referencedon www.astm.org.5Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, U

15、nited States.5. Materials and Manufacture5.1 Pipe shall be made from flat-rolled alloy by an auto-matic welding process with no addition of filler metal. Subse-quent to welding and prior to final annealing, the material shallbe cold-worked in either the weld metal only or both weld andbase metal.5.2

16、 Pipe shall be furnished with oxide removed. Whenbright annealing is used, descaling is not necessary.6. Chemical Composition6.1 The material shall conform to the composition limitsspecified in Table 2.6.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the

17、product (check)analysis variations in Table 3.7. Mechanical and Other Requirements7.1 Mechanical PropertiesThe material shall conform tothe mechanical properties specified in Table 4.7.2 Flattening TestA section of pipe not less than 4 in.(102 mm) in length shall be capable of withstanding, withoutc

18、racking, flattening under a load applied gradually at roomtemperature until the distance between the platens is five timesthe wall thickness. The weld shall be positioned 90 from thedirection of the applied flattening force.7.2.1 Superficial ruptures resulting from surface imperfec-tions shall not b

19、e a cause for rejection.7.3 Nondestructive Test RequirementsTube shall be sub-jected to a pressure test or nondestructive electric test at themanufacturers option (see 13.2).TABLE 1 Dimensions of Welded PipeANOTE 1The following table is a partial reprint of Table 1 of the American National Standard

20、for Stainless Steel Pipe (ANSI B36.19).NOTE 2The decimal thicknesses for the respective pipe sizes represent their nominal wall dimensions.Nominal PipeSize in.Outside Diameterin. (mm)Nominal Wall Thickness, in. (mm)Schedule5SASchedule10SSchedule40S18 0.405 (10.29) . 0.049 (1.25) 0.068 (1.73)14 0.540

21、 (13.72) . 0.065 (1.65) 0.088 (2.24)38 0.675 (17.15) . 0.065 (1.65) 0.091 (2.31)12 0.840 (21.34) 0.065 (1.65) 0.083 (2.11) 0.109 (2.77)34 1.050 (26.67) 0.065 (1.65) 0.083 (2.11) 0.113 (2.87)1 1.315 (33.40) 0.065 (1.65) 0.109 (2.77) 0.133 (3.38)114 1.660 (42.16) 0.065 (1.65) 0.109 (2.77) 0.140 (3.56)

22、112 1.900 (48.26) 0.065 (1.65) 0.109 (2.77) 0.145 (3.68)2 2.375 (60.33) 0.065 (1.65) 0.109 (2.77) 0.154 (3.91)212 2.875 (73.03) 0.083 (2.11) 0.120 (3.05) .3 3.500 (88.90) 0.083 (2.11) 0.120 (3.05) .312 4.000 (101.6) 0.083 (2.11) 0.120 (3.05) .4 4,500 (114.3) 0.083 (2.11) 0.120 (3.05) 0.237 (6.02)5 5

23、.563 (141.3) 0.109 (2.77) 0.134 (3.40) .6 6.625 (168.3) 0.109 (2.77) 0.134 (3.40) .ASchedules 5S and 10S wall thicknesses do not permit threading in accordance with the American National Standard for Pipe Threads (ANSI B2.1).TABLE 2 Chemical RequirementsAComposition Limits,%UNSN06110Ni 51.0 minCr 28

24、.033.0Fe 1.0 maxMo 9.012.0W 1.04.0C 0.15 maxMn 1.0 maxSi 1.0 maxP 0.015 maxS 0.015 maxAl 1.0 maxTi 1.0 maxCu 0.5 maxCb 1.0 maxAElement may be determined arithmetically by difference.TABLE 3 Product (Check) Analysis Chemical CompositionVariationsElementSpecified Limit ofElement, % inclVariation Under

25、 min orOver max of theSpecifiedLimit of ElementsNi over 40.0 to 60.0 0.35Cr over 25.0 to 35.0 0.25Fe up to 1.0 0.05Mo over 9.0 to 12.0 0.15W over 1.0 to 4.0 0.07C over 0.0 to 0.20 0.01Mn up to 1.0 0.05Si over 0.25 to 1.0 0.05P upto0.04 0.005S upto0.02 0.003over 0.02 to 0.06 0.005Al over 0.10 to 1.0

26、0.05Ti over 0.10 to 0.50 0.03over 0.50 to 1.0 0.04over 1.0 to 2.0 0.05Cb over 0.1 to 1.0 0.04Cu up to 0.50 0.03TABLE 4 Mechanical Property RequirementsAlloyTensile strengthmin, psi (MPa)Yield strength0.2 % offsetmin, psi(MPa)Elongationin 2 in. or50 mm,min, %UNS N06110 95000 (655) 45000 (310) 60B757

27、00 (2011)27.3.1 Acceptance and RejectionMaterial producing a sig-nal equal to or greater than the calibration imperfection shall besubject to rejection.7.3.1.1 Test signals produced by imperfections that cannotbe identified or produced by cracks or crack-like imperfectionsshall result in rejection o

28、f the pipe, subject to rework and retest.To be accepted, the material shall pass the same electric test towhich it was originally subjected provided that the dimensionalrequirements are met.7.3.1.2 If the imperfection is judged as injurious, the pipeshall be rejected but may be reconditioned and ret

29、estedproviding the dimensional requirements are met. To be ac-cepted, retested material shall meet the original electric testrequirements.7.3.1.3 If the imperfection is explored to the extent that itcan be identified as noninjurious, the material may be acceptedwithout further test provided the impe

30、rfection does not en-croach on the minimum wall thickness.8. Dimensions and Permissible Variations8.1 Diameter and Wall ThicknessOutside diameter andnominal wall thickness shall not exceed the permissible varia-tions prescribed in Table 5.8.1.1 Material having a specified wall thickness that is 3 %o

31、r less of the outside diameter cannot be straightened properlywithout a certain amount of ovality resulting in the diameter.The limits to this ovality are stated in Footnote C to Table 5.8.2 Straightness Material shall be reasonably straight andfree of bends or kinks.8.3 LengthVariations from the sp

32、ecified length shall notexceed the amounts prescribed in Table 6.9. Workmanship, Finish and Appearance9.1 The material shall be uniform in quality and temper,smooth, commercially straight, and free of injurious imperfec-tions.10. Sampling10.1 Lot Definition:10.1.1 A lot for chemical analysis shall c

33、onsist of one heat.10.1.2 Alot for mechanical properties and flattening testing,shall consist of all material from the same heat, nominal size(excepting length), and condition (temper).10.2 Test Material Selection:10.2.1 Chemical AnalysisRepresentative samples fromeach lot shall be taken during pour

34、ing or subsequent process-ing.10.2.1.1 Product (check) analysis shall be wholly the re-sponsibility of the purchaser.10.2.2 Mechanical Properties and Flattening TestingSamples of the material to provide test specimens shall betaken from such locations in each lot as to be representative ofthat lot.1

35、1. Number of Tests11.1 Chemical AnalysisOne test per lot.11.2 Mechanical PropertiesOne test per lot.11.3 FlatteningOne test per lot.11.4 Nondestructive:11.4.1 Class 1Each piece in each lot shall be subjected toone of the following four tests, hydrostatic, pneumatic (airunderwater), eddy current, or

36、ultrasonic.11.4.2 Class 2Each piece in each lot shall be subjected toa leak test and an electric test as follows:11.4.2.1 Leak TestHydrostatic or pneumatic (air underwa-ter).11.4.2.2 Electric TestEddy current or ultrasonic.11.4.3 The manufacturer shall have the option to test toClass 1 or 2 and sele

37、ct the nondestructive test methods, if notspecified by the purchaser.12. Specimen Preparation12.1 Tension test specimens shall be taken from material inthe final condition (temper) and tested in the direction offabrication.12.1.1 Whenever possible, all material shall be tested in fulltubular size. W

38、hen testing in full tubular size is not possible,longitudinal strip specimens shall be used. In the event ofdisagreement when full tubular testing is not possible, alongitudinal strip specimen with reduced gage length ascontained in Test Methods E8 shall be used.TABLE 5 Permissible Variations in Out

39、side DiameterAand WallThicknessBIPSPermissible Variations in OutsideDiameter, in. (mm)C+18 0.005(0.13) 0.005(0.13)14 0.005(0.13) 0.005(0.13)38 0.0075(0.19) 0.0075(0.19)12 0.0075(0.19) 0.0075(0.19)34 0.010(0.25) 0.0075(0.19)1 0.010(0.25) 0.0075(0.19)114 0.010(0.25) 0.010(0.25)112 0.015(0.38) 0.010(0.

40、25)2 0.018(0.46) 0.010(0.25)212 0.018(0.46) 0.010(0.25)3 0.025(0.64) 0.010(0.25)312 0.025(0.64) 0.015(0.38)4 0.025(0.64) 0.015(0.38)5 0.025(0.64) 0.020(0.51)6 0.025(0.64) 0.030(0.76)AThese permissible variations in outside diameter apply only to material asfinished at the mill before subsequent swag

41、ing, expanding, bending, polishing, orother fabricating operations.BWall thickness variation shall not exceed 612 % of the nominal wall thickness.COvality is the difference between maximum and minimum outside diametermeasured at any one cross section. There is no additional tolerance for ovality onm

42、aterial having a nominal wall thickness of more than 3 % of the outside diameter.On this material, the average of maximum and minimum outside diametermeasurements will fall within the outside diameter tolerance shown in the tableabove. An additional ovality allowance of twice the outside diameter to

43、lerancespreads shown above, applied one half plus and one half minus, is allowed formaterial having nominal wall thickness of 3 % or less of nominal outside diameter.TABLE 6 Permissible Variations in LengthsAOutside diameter in.(mm)Cut length, in. (mm)Over UnderUnder 2 (50.8)18 (3) 02 (50.8) and ove

44、r316 (5) 0AThese permissible variations in length apply to pipe before bending. Theyapply to cut lengths up to and including 24 ft (7.3 m). For lengths over 24 ft, anadditional over-tolerance of18 in. (3 mm) for each 10 ft (3.0 m) or fraction thereofshall be permissible up to a maximum additional ov

45、er-tolerance of12 in. (12.7 mm).B757 00 (2011)313. Test Methods13.1 The chemical composition, mechanical, and otherproperties of the material as enumerated in this specificationshall be determined, in case of disagreement, in accordancewith the following methods:Test ASTM DesignationChemical analysi

46、s E38, E354ATension E8Rounding procedure E29AMethods E38 is to be used only for elements not covered by Test MethodsE354.13.2 Nondestructive Tests:13.2.1 Hydrostatic TestTest each piece at a pressure notexceeding 1000 psi (6.9 MPa), calculated as follows:P 5 2St/D, or (1)S 5 PD/2t (2)where:P = hydro

47、static test pressure, psi or MPa;S = allowable fiber stress as follows: UNS N06110-35000psi (242 MPa);t = specified wall thickness, in. or mm; andD = specified outside diameter, in. or mm.13.2.1.1 Hold the test pressure for a minimum of 5 s.13.2.1.2 Make visual examination when the material isunder

48、pressure. Examine the full length of material for leaks. Ifany pipe shows leaks during the hydrostatic test, reject it.13.2.2 Pneumatic (Air Underwater) TestTest each pieceat a pressure of 150 psi (1.05 MPa).13.2.2.1 Hold the test pressure for a minimum of 5 s.13.2.2.2 Make visual examination when t

49、he material issubmerged and is under pressure. Examine the full length ofmaterial for leaks. If any piece shows leaks during the test,reject it.13.2.3 Electric TestGive each pipe an electric test inaccordance with either Practice E213 or Practice E571. Foreddy-current testing, the calibration pipe shall contain, at theoption of the producer, any one of the following discontinuitiesto establish a minimum sensitivity level for rejection. Thediscontinuity shall be placed in the weld if visible.13.2.3.1 Drill HoleDrill a hole, not