ASTM B836-2000(2011) Standard Specification for Compact Round Stranded Aluminum Conductors Using Single Input Wire Construction《通过单输入线路构造的紧压圆形绞合铝导线的标准规格》.pdf

1、Designation: B836 00 (Reapproved 2011)Standard Specification forCompact Round Stranded Aluminum Conductors UsingSingle Input Wire Construction1This standard is issued under the fixed designation B836; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers aluminum/single input wire(SIW) stranded conductors made from

3、round or shaped wiresfor use in covered or insulated electrical wires or cables. Theseconductors shall be composed of one or more roller or diecompacted layers of helically applied wires (Explanatory Note1, Explanatory Note 2, and Explanatory Note 3).1.2 The values stated in inch-pound units are to

4、be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.2.1 For density, resistivity, and temperature, the valuesstated in SI units are to be regarded as standard.NOTE 1The aluminum and te

5、mper designations conform toANSI H35.1.Aluminum 1350 andAluminum-Alloy 8XXX correspond toUnified Numbering System A91350 and A98XXX, in accordance withPractice E527.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of th

6、e user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on dateof material purchase form a part of this specification to theextent r

7、eferenced herein.2.2 ASTM Standards:2B230/B230M Specification for Aluminum 1350H19 Wirefor Electrical PurposesB263 Test Method for Determination of Cross-SectionalArea of Stranded ConductorsB354 Terminology Relating to Uninsulated Metallic Elec-trical ConductorsB400 Specification for Compact Round C

8、oncentric-Lay-Stranded Aluminum 1350 ConductorsB609/B609M Specification for Aluminum 1350 RoundWire, Annealed and Intermediate Tempers, for ElectricalPurposesB800 Specification for 8000 Series Aluminum Alloy Wirefor Electrical PurposesAnnealed and Intermediate Tem-persB801 Specification for Concentr

9、ic-Lay-Stranded Conduc-tors of 8000 Series Aluminum Alloy for SubsequentCovering or InsulationB830 Specification for Uniform Test Methods and Fre-quencyE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE527 Practice for Numbering Metals and Alloys in t

10、heUnified Numbering System (UNS)2.3 ANSI Standard:ANSI H35.1 Alloy and Temper Designation Systems forAluminum32.4 NIST Standard:Handbook 100 Copper Wire Tables NBS43. Classification3.1 The conductors described in this specification are in-tended for subsequent insulation or covering. The classificat

11、ionof these conductors is SIW Compact.4. Ordering Information4.1 Orders for material in accordance with this specificationshall include the following information:4.1.1 Quantity of each size and class (Table 1);4.1.2 Conductor size, circular-mil area orAWG (Section 7);4.1.3 Temper (Section 12);4.1.4

12、Lay direction, if nonstandard (see 6.2 and 6.3);1This specification is under the jurisdiction of ASTM Committee B01 onElectrical Conductors and is the direct responsibility of Subcommittee B01.07 onConductors of Light Metals.Current edition approved April 1, 2011. Published September 2011. Originall

13、yapproved in 1993. Last previous edition approved in 2005 as B836 00 (2005).DOI: 10.1520/B0836-00R11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards D

14、ocument Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.4Available from National Institute of Standards and Technology (NIST), 100Bureau Dr., Stop 3460, Gaithersburg, MD 20899-3460.1Copyright ASTM Internationa

15、l, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.5 Special tension test, if required (see 16.2);4.1.6 Place of inspection (Section 17);4.1.7 Packaging and package marking (Section 18), and4.1.8 Material for conductor.5. Joints5.1 Joints may be made in any of

16、 the wires of any strandingby electric-butt welding, cold-pressure welding, or electric-butt, cold-upset welding.5.1.1 Joints in the individual wires in a finished conductorshall not be closer together than 1 ft (0.3 m) for conductors of19 wires or less, or closer than 1 ft (0.3 m) in a layer forcon

17、ductors of more than 19 wires.5.2 No joint or splice shall be made in a stranded conductoras a whole.6. Lay6.1 The length of lay of each layer for SIW conductors shallnot be less than 8 or more than 17.5 times the outside diameterof the finished conductor.6.2 The direction of lay of the outer layer

18、shall be left-handand may be reversed or unidirectional in successive layers.6.3 Other lay requirements may be furnished upon specialagreement between the manufacturer and the purchaser.7. Construction7.1 The construction of the conductors shall be as given inTable 1.7.2 Wire used in the fabrication

19、 of conductors shall be ofsuch dimensions as to produce a finished conductor as pre-scribed in Table 1.8. Rated Strength of Conductor8.1 The rated strength of SIW conductors made from anyand all alloys and tempers covered in this specification shall betaken as the percentage, indicated in Table 2, o

20、f the sum of thestrengths of the component wires, calculated on the basis of theequivalent diameter of these wires and the specified minimumaverage tensile strengths given in Specifications B230/B230M,B609/B609M, and B800.8.2 Rated-strength and breaking-strength values shall berounded to three signi

21、ficant figures, in the final value only, inaccordance with the rounding method of Practice E29.8.3 Rated strengths of conductors are given in Table 3 ofSpecification B400 for conductors made of Aluminum 1350 inall tempers.8.4 Rated strengths of conductors made from any and alltempers of 8000 series

22、aluminum alloys are given in Table 3 ofSpecification B801.9. Density9.1 For the purpose of calculating mass, cross-sections, andso forth, the density of Aluminum 1350 shall be taken as 2705kg/m3(0.0975 lb/in.3) at 20C, and the density of 8000 seriesaluminum alloys shall be taken as 2710 kg/m3(0.098

23、lb/in.3)at 20C.TABLE 1 Construction of Compact Round, Concentric-Lay-Stranded Aluminum ConductorsConductor SizeMinimumNumber ofWiresNominal Compact ConductorDiameterNominalMass/1000ft,AlbNominalMass/km, kgNominal dc Resistance at 20CCircular, mils AWG mm2in. mm V/1000 ft V/km1 000 000 . 507 53 1.060

24、 26.9 937 1394 0.0173 0.0563900 000 . 456 53 0.999 25.4 844 1257 0.0193 0.0632800 000 . 405 53 0.938 23.8 750 1116 0.0217 0.0712750 000 . 380 53 0.908 23.1 703 1046 0.0231 0.0759700 000 . 355 34 0.877 22.3 656 976 0.0248 0.0813650 000 . 329 34 0.845 21.5 609 906 0.0267 0.0875600 000 . 304 34 0.813 2

25、0.7 563 838 0.0289 0.0948550 000 . 279 34 0.775 19.7 516 768 0.0315 0.103500 000 . 253 30 0.736 18.7 468 696 0.0347 0.114450 000 . 228 30 0.700 17.8 422 628 0.0385 0.126400 000 . 203 24 0.659 16.7 375 558 0.0434 0.142350 000 . 177 24 0.616 15.6 328 488 0.0495 0.162300 000 . 152 18 0.570 14.5 281 418

26、 0.0578 0.190250 000 . 127 18 0.520 13.2 234 348 0.0694 0.228211 600 0000 107 17 0.475 12.1 198 295 0.0820 0.269167 800 000 85.0 15 0.423 10.7 157 234 0.103 0.338133 100 00 67.4 12 0.376 9.55 125 186 0.130 0.428105 600 0 53.5 7 0.336 8.53 98.9 147 0.164 0.53983 690 1 42.4 7 0.299 7.59 78.4 117 0.207

27、 0.68066 360 2 33.6 6 0.268 6.81 62.2 92.6 0.261 0.85752 620 3 26.7 6 0.238 6.05 49.3 73.3 0.330 1.0841 740 4 21.2 6 0.213 5.41 39.1 58.2 0.416 1.3626 240 6 13.3 6 0.169 4.29 24.6 36.6 0.661 2.1716 510 8 8.37 6 0.134 3.40 15.5 23.1 1.05 3.44AWeights are based on Aluminum 1350 with a density of 0.097

28、5 lb/in.3TABLE 2 Rating FactorsStrandingNumber of LayersRating Factor, %196293391490B836 00 (2011)210. Mass and Resistance10.1 The mass and electrical resistance of a unit length ofstranded conductor is a function of the length of lay. Theapproximate weight and electrical resistance may be deter-min

29、ed using an increment of 2 %. When greater accuracy isdesired, the increment based on the specific lay of the conduc-tor may be calculated (Explanatory Note 4).10.2 The maximum electrical resistance of a unit length ofstranded conductor shall not exceed the nominal dc resistance(Table 1), plus 2 %.1

30、0.2.1 When the dc resistance is measured at other than20C, it is to be corrected by using the multiplying factor givenin Table 3.10.3 For conductors to be used in covered or insulated wiresor cables, dc resistance measurement may be used instead ofthe method outlined in Section 13, to determine comp

31、liancewith this specification; however, the referee method shall bethat outlined in Section 13.11. Workmanship, Finish, and Appearance11.1 The conductor shall be clean and free of imperfectionsnot consistent with good commercial practice.12. Requirements of Wires12.1 Before stranding and compacting,

32、 the round input wireused shall meet the requirements of Specifications B230/B230M, B609/B609M,orB800, whichever is applicable.12.2 Wire shaped before stranding shall meet the require-ments of the appropriate specification listed in 12.1 except fortensile and elongation requirements and diameter tol

33、erance.For the 1350-H19 temper, the minimum tensile and elongationrequirements shall be 96 % of those for round wire of the samenominal area, provided the completed conductor is capable ofmeeting the requirements of Sections 8 and 16.12.3 For conductors made from all other alloys and temperscovered

34、in this specification with shaped wires, the tensilerequirements for the wires shall be the same as those for roundinput wires of equal nominal area. The area tolerances forshaped wire of all alloys and tempers shall be such that thefinished conductor conforms to Section 13.13. Variation in Area13.1

35、 The cross-sectional area of the conductor shall not beless than 98 % of the cross-sectional area as specified inColumn 1 of Table 1.13.2 The manufacturer shall determine the cross-sectionalarea by Test Method B263. In applying this test method, theincrement in weight resulting from stranding may be

36、 theapplicable value specified in 10.1, or it may be calculated fromthe measured dimensions of the sample under test. In case of aquestion regarding area compliance, the actual weight incre-ment due to stranding shall be calculated.NOTE 2The term “weight” is used in this specification because ofesta

37、blished trade usage in place of the technically correct term “mass.”14. Variation in Diameter14.1 The average diameter of the conductor shall vary bynot more than plus 1 % and minus 2 % from the diameterspecified in Table 1.15. Sampling15.1 The aluminum cross-sectional area (Section 13) anddiameter

38、(Section 14) shall be measured on a sample ofcompleted conductor. At least one sample shall be tested oneach size of conductor on each order of quantities from 5000 to100 000 ft (1500 to 30 000 m), and one additional sample shallbe tested from each 100 000 ft (30 000 m) thereafter.15.2 In addition o

39、r instead of the acceptance testing outlinedin 15.1, the sampling may be in accordance with SpecificationB830 (see Explanatory Note 5).16. Mechanical and Electrical Tests of SIW Conductors16.1 Tests for the mechanical and electrical properties ofwire composing the conductor shall be made before, but

40、 notafter, stranding unless otherwise agreed upon by the manufac-turer and the purchaser as provided in 16.2 (Explanatory Note6).16.2 At the option of the purchaser, at the time of placingthe order, tensile and elongation tests of wire before strandingmay be waived, and the completed conductor may b

41、e tested asa unit. The minimum breaking strength of the conductors sotested shall not be less than the rated strength of the conductor(per Section 8 of this specification) if failure occurs in the freelength at least 1 in. (25 mm) beyond the end of either grippingdevice, or it shall not be less than

42、 95 % of the rated strength iffailure occurs inside, or within, 1 in. (25 mm) of the end ofeither gripping device. The maximum breaking strength fortempers other than -H19 shall not be greater than theirmaximum rated strengths as provided in Section 9 of thisspecification and in Table 3 of Specifica

43、tion B400 and Table 3of Specification B801. The free length between grips of the testspecimen shall not be less than 24 in. (600 mm), and care shallbe taken to ensure that the wires in the conductor are grippedevenly during the test (Section 8 and Explanatory Note 7).TABLE 3 Temperature Correction F

44、actors for ConductorResistanceTemperature, C Multiplying Factor for Conversion to 20C0 1.0885 1.06410 1.04215 1.02020 1.00025 0.98030 0.96135 0.94340 0.92545 0.90850 0.89255 0.87660 0.85165 0.84670 0.83275 0.81880 0.80585 0.79290 0.780B836 00 (2011)317. Inspection17.1 Unless otherwise specified in t

45、he contract or purchaseorder, the manufacturer shall be responsible for the perfor-mance of all inspection and test requirements specified.17.2 All inspections and tests shall be made at the place ofmanufacture unless otherwise especially agreed upon betweenthe manufacturer and the purchaser at the

46、time of the purchase.17.3 The manufacturer shall afford the inspector represent-ing the purchaser all reasonable facilities to satisfy him that thematerial is being furnished in accordance with this specifica-tion.18. Packaging and Package Marking18.1 Package sizes for conductors shall be agreed upo

47、n bythe manufacturer and the purchaser during the placing ofindividual orders.18.2 The conductors shall be protected from damage duringordinary handling and shipping.18.3 There shall be only one length of conductor on a reelunless otherwise agreed upon by the manufacturer and pur-chaser at the time

48、of placing the order.18.4 The net weight, length (and number of lengths, if morethan one length is included in the package), size, kind ofconductor, and purchase order shall be marked on a tagattached to the end of the conductor inside of the package. Thesame information, together with the manufactu

49、rers serialnumber (if any) and all shipping marks required by thepurchaser, shall appear on the outside of each package.19. Keywords19.1 aluminum; aluminum stranded conductors; compact;concentric lay stranded conductors; electrical conductors; re-verse concentric; Single Input Wire; SIW; SIW Compact;unidirectional; unilayEXPLANATORY NOTESNOTE 1In this specification, only compact round/SIW conductorconstructions are specifically designated. Constructions not included inthis specification should be specifically agreed upon by the manufacturerand the purchaser when placin