ASTM B862-2014 Standard Specification for Titanium and Titanium Alloy Welded Pipe《钛和钛合金焊接管的标准规格》.pdf

1、Designation: B862 13aB862 14Standard Specification forTitanium and Titanium Alloy Welded Pipe1This standard is issued under the fixed designation B862; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A nu

2、mber in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers the requirements for 33

3、grades of titanium and titanium alloy welded pipe intended for generalcorrosion resisting and elevated temperature service as follows:1.1.1 Grade 1UNS R50250. Unalloyed titanium, low oxygen,1.1.2 Grade 2UNS R50400. Unalloyed titanium, standard oxygen,1.1.2.1 Grade 2HUNS R50400. Unalloyed titanium (G

4、rade 2 with 58 ksi (400 MPa) minimum UTS),1.1.3 Grade 3UNS R50550. Unalloyed titanium, medium oxygen,1.1.4 Grade 5UNS R56400. Titanium alloy (6 % aluminum, 4 % vanadium),1.1.5 Grade 7UNS R52400. Unalloyed titanium plus 0.12 to 0.25 % palladium, standard oxygen,1.1.5.1 Grade 7HUNS R52400. Unalloyed t

5、itanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi (400 MPa) minimumUTS),1.1.6 Grade 9UNS R56320. Titanium alloy (3 % aluminum, 2.5 % vanadium),1.1.7 Grade 11UNS R52250. Unalloyed titanium plus 0.12 to 0.25 % palladium, low oxygen,1.1.8 Grade 12UNS R53400. Titanium alloy (0.3 % molybdenum, 0

6、.8 % nickel),1.1.9 Grade 13UNS R53413. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), low oxygen,1.1.10 Grade 14UNS R53414. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), standard oxygen,1.1.11 Grade 15UNS R53415. Titanium alloy (0.5 % nickel, 0.05 % ruthenium), medium oxygen,1.1.12 Grade 16UNS

7、R52402. Unalloyed titanium plus 0.04 to 0.08 % palladium, standard oxygen,1.1.12.1 Grade 16HUNS R52402. Unalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi (400 MPa)minimum UTS),1.1.13 Grade 17UNS R52252. Unalloyed titanium plus 0.04 to 0.08 % palladium, low oxygen,1.1.14 Grade 18

8、UNS R56322. Titanium alloy (3 % aluminum, 2.5 % vanadium plus 0.04 to 0.08 % palladium),1.1.15 Grade 19UNS R58640. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 %molybdenum),1.1.16 Grade 20UNS R58645. Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconiu

9、m, 4 %molybdenum) plus 0.04 to 0.08 % palladium,1.1.17 Grade 21UNS R58210. Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),1.1.18 Grade 23UNS R56407. Titanium alloy (6 % aluminum, 4 % vanadium, extra low interstitial, ELI),1.1.19 Grade 24UNS R56405. Titanium alloy (6 %

10、aluminum, 4 % vanadium) plus 0.04 to 0.08 % palladium,1.1.20 Grade 25UNS R56403. Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 to 0.8 % nickel and 0.04 to 0.08 %palladium,1.1.21 Grade 26UNS R52404. Unalloyed titanium plus 0.08 to 0.14 % ruthenium,1.1.21.1 Grade 26HUNS R52404. Unalloyed titani

11、um plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi (400 MPa)minimum UTS),1.1.22 Grade 27UNS R52254. Unalloyed titanium plus 0.08 to 0.14 % ruthenium,1.1.23 Grade 28UNS R56323. Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,1.1.24 Grade 29UNS R56404. Titanium alloy (6

12、 % aluminum, 4 % vanadium with extra low interstitial elements (ELI) plus0.08 to 0.14 % ruthenium,1.1.25 Grade 33UNS R53442. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),1 This specification is under the jurisdiction of ASTM Committee B10 on Reactive and Refra

13、ctory Metals and Alloys and is the direct responsibility of SubcommitteeB10.01 on Titanium.Current edition approved July 1, 2013Nov. 1, 2014. Published August 2013November 2014. Originally approved in 1995. Last previous edition approved in 2013 asB862 13.B862 13a. DOI: 10.1520/B0862-13A.10.1520/B08

14、62-14.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult pri

15、or editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 194

16、28-2959. United States11.1.26 Grade 34UNS R53445. Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),1.1.27 Grade 35UNS R56340. Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 %silicon),1.1.28 Grade 37UNS R52815. Titanium alloy (1.5 %

17、 aluminum),1.1.29 Grade 38UNS R54250. Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron), and1.1.30 Grade 39UNS R53390. Titanium alloy (0.25 % iron, 0.4 % silicon).NOTE 1H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaran

18、teed minimumUTS, and may always be certified as meeting the requirements of its corresponding numeric grade. Grades 2H, 7H, 16H, and 26H are intended primarilyfor pressure vessel use.1.2 Pipe 8 in. NPS (nominal pipe size) and larger is most frequently custom made for an order. In such cases, the pur

19、chasercarefully should consider the applicability of this specification. Since the pipe is custom made, the purchaser may choose a wallthickness other than those in Table 1 to meet specific operating conditions. The purchaser may also be better served to specify onlythe portions of this specificatio

20、n that are required to meet the operating conditions (for example, annealing, flattening test,chemistry, properties, etc.).1.3 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. Thesesupplementary requirements may be invoked by the purchaser, when

21、 desired, by specifying in the order.1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.2. Referenced Documents2.1 ASTM Standards:2A37

22、0 Test Methods and Definitions for Mechanical Testing of Steel ProductsB600 Guide for Descaling and Cleaning Titanium and Titanium Alloy SurfacesE8 Test Methods for Tension Testing of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specification

23、sE539 Test Method for Analysis of Titanium Alloys by X-Ray Fluorescence SpectrometryE1409 Test Method for Determination of Oxygen and Nitrogen in Titanium and Titanium Alloys by Inert Gas FusionE1417 Practice for Liquid Penetrant TestingE1447 Test Method for Determination of Hydrogen in Titanium and

24、 Titanium Alloys by Inert Gas Fusion ThermalConductivity/Infrared Detection MethodE1941 Test Method for Determination of Carbon in Refractory and Reactive Metals and Their Alloys by Combustion AnalysisE2371 Test Method for Analysis of Titanium and Titanium Alloys by Direct Current Plasma and Inducti

25、vely Coupled PlasmaAtomic Emission Spectrometry (Performance-Based Test Methodology)E2626 Guide for Spectrometric Analysis of Reactive and Refractory Metals2.2 ANSI/ASME Standards:3B.1.20.1 Pipe Threads, General Purpose (Inch)B 36.10 Carbon, Alloy and Stainless Steel PipesB 36.19M-1985 Stainless Ste

26、el PipeASME Boiler and Pressure Vessel Code Section VIII2.3 AWS Standard:4AWS A5.16A5.16M-2007 Specification for Titanium and Titanium Alloy Welding Electrodes and Rods3. Terminology3.1 Definitions:3.1.1 lot, na number of pieces of pipe of the same nominal size and wall thickness manufactured by the

27、 same process froma single heat of titanium or titanium alloy and heat treated by the same furnace parameters in the same furnace.3.1.2 welded pipe, na hollow tubular product produced by forming flat-rolled product and seam welding to make a rightcircular cylinder.4. Ordering Information4.1 Orders f

28、or materials under this specification shall include the following information as required:4.1.1 Quantity,4.1.2 Grade number (Section 1 and Table 2),2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standar

29、dsvolume information, refer to the standardsstandards Document Summary page on the ASTM website.3 Available from American National Standards Institute (ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.4 Available from American Welding Society (AWS), 550 NW LeJeune Rd., Miami,

30、 FL 33126, http:/www.aws.org.B862 142TABLE 1 Dimensions of PipeNOTE 1Schedule sizes conform to ANSI/ASME B 36.19M-1985 (for “S” sizes) or B 36.10 (for non-S sizes).NOTE 2The decimal thickness listed for the respective pipe sizes represent their nominal wall dimensions.NPSDesig.Outside Dia. Nominal W

31、all ThicknessSchedule 5SA Schedule 5A Schedule 10SA Schedule 10A Schedule 40S Schedule 40 Schedule 80S Schedule 80in mm in mm in mm in mm in mm in mm in mm in mm in mm18 0.405 10.29 x x x x 0.049 1.24 0.049 1.24 0.068 1.73 0.068 1.73 0.095 2.41 0.095 2.4114 0.540 13.72 x x x x 0.065 1.65 0.065 1.65

32、0.088 2.24 0.088 2.24 0.119 3.02 0.119 3.0238 0.675 17.15 x x x x 0.065 1.65 0.065 1.65 0.091 2.31 0.091 2.31 0.126 3.20 0.126 3.2012 0.840 21.34 0.065 1.65 0.065 1.65 0.083 2.11 0.083 2.11 0.109 2.77 0.109 2.77 0.147 3.73 0.147 3.7334 1.050 26.67 0.065 1.65 0.065 1.65 0.083 2.11 0.083 2.11 0.113 2.

33、87 0.113 2.87 0.154 3.91 0.154 3.911 1.315 33.40 0.065 1.65 0.065 1.65 0.109 2.77 0.109 2.77 0.133 3.38 0.133 3.38 0.179 4.55 0.179 4.551-14 1.660 42.16 0.065 1.65 0.065 1.65 0.109 2.77 0.109 2.77 0.140 3.56 0.140 3.56 0.191 4.85 0.191 4.851-12 1.900 48.26 0.065 1.65 0.065 1.65 0.109 2.77 0.109 2.77

34、 0.145 3.68 0.145 3.68 0.200 5.08 0.200 5.082 2.375 60.32 0.065 1.65 0.065 1.65 0.109 2.77 0.109 2.77 0.154 3.91 0.154 3.91 0.218 5.54 0.218 5.542-12 2.875 73.02 0.083 2.11 0.083 2.11 0.120 3.05 0.120 3.05 0.203 5.16 0.203 5.16 0.276 7.01 0.276 7.013 3.500 88.90 0.083 2.11 0.083 2.11 0.120 3.05 0.12

35、0 3.05 0.216 5.49 0.216 5.49 0.300 7.62 0.300 7.623-12 4.000 101.60 0.083 2.11 0.083 2.11 0.120 3.05 0.120 3.05 0.226 5.74 0.226 5.74 0.318 8.08 0.318 8.084 4.500 114.30 0.083 2.11 0.083 2.11 0.120 3.05 0.120 3.05 0.237 6.02 0.237 6.02 0.337 8.56 0.337 8.565 5.563 141.30 0.109 2.77 0.109 2.77 0.134

36、3.40 0.134 3.40 0.258 6.55 0.258 6.55 0.375 9.53 0.375 9.536 6.625 168.27 0.109 2.77 0.109 2.77 0.134 3.40 0.134 3.40 0.280 7.11 0.280 7.11 0.432 10.97 0.432 10.978 8.625 219.07 0.109 2.77 0.109 2.77 0.148 3.76 0.148 3.76 0.322 8.18 0.322 8.18 0.500 12.70 0.500 12.7010 10.75 273.05 0.134 3.40 0.134

37、3.40 0.165 4.19 0.165 4.19 0.365 9.27 0.365 9.27 0.500 12.70 0.594 15.0912 12.75 323.85 0.156 3.96 0.156 3.96 0.180 4.57 0.180 4.57 0.375 9.53 0.406 10.31 0.500 12.70 0.688 17.4814 14.00 355.60 0.156 3.96 0.156 3.96 0.188 4.78 0.250 6.35 x x 0.438 11.13 x x 0.750 19.0516 16.00 406.40 0.165 4.19 0.16

38、5 4.19 0.188 4.78 0.250 6.35 x x 0.500 12.70 x x 0.844 21.4418 18.00 457.20 0.165 4.19 0.165 4.19 0.188 4.78 0.250 6.35 x x 0.562 14.27 x x 0.938 23.8320 20.00 508.00 0.188 4.78 0.188 4.78 0.218 5.54 0.250 6.35 x x 0.594 15.09 x x 1.031 26.1922 22.00 558.80 0.188 4.78 0.188 4.78 0.218 5.54 0.250 6.3

39、5 x x x x x x 1.125 28.5824 24.00 609.60 0.218 5.54 0.218 5.54 0.250 6.35 0.250 6.35 x x 0.688 17.48 x x 1.219 30.9626 26.00 660.40 x x x x x x 0.312 7.92 x x x x x x x x28 28.00 711.20 x x x x x x 0.312 7.92 x x x x x x x x30 30.00 762.00 0.250 6.35 0.250 6.35 0.312 7.92 0.312 7.92 x x x x x x x x3

40、2 32.00 812.80 x x x x x x 0.312 7.92 x x 0.688 17.48 x x x x34 34.00 863.60 x x x x x x 0.312 7.92 x x 0.688 17.48 x x x x36 36.00 914.40 x x x x x x 0.312 7.92 x x 0.750 19.05 x x x xA Threading not permitted in accordance with ANSI B.1.20.1.B862143TABLE 2 Chemical RequirementsComposition, Weight

41、PercentA,B,C,D,EGradeUNSNumberCarbon,max.Oxygenrangeor max.Nitrogen,max.Hydrogen,max.Ironrangeor max. Aluminum Vanadium Palladium Ruthenium Nickel MolybdenumChromium Cobalt Zirconium Niobium Tin SiliconOtherElements,max.eachOtherElements,max.total- - 0.1 0.41 R50250 0.08 0.18 0.03 0.015 0.20 - - - -

42、 - - - - - - - - - - - - - - - - - - - - 0.1 0.42/2H R50400 0.08 0.25 0.03 0.015 0.30 - - - - - - - - - - - - - - - - - - - - - - - - 0.1 0.43 R50550 0.08 0.35 0.05 0.015 0.30 - - - - - - - - - - - - - - - - - - - - - - - - - - - - 0.1 0.45 R56400 0.08 0.20 0.05 0.015 0.40 5.5-6.753.5-4.5- - - - - -

43、 - - - - - - - - - - - - - - - - - - 0.1 0.47/7H R52400 0.08 0.25 0.03 0.015 0.30 - - - - 0.12-0.25- - - - - - - - - - - - - - - - - - 0.1 0.49 R56320 0.08 0.15 0.03 0.015 0.25 2.5-3.52.0-3.0- - - - - - - - - - - - - - - - - - - - 0.1 0.411 R52250 0.08 0.18 0.03 0.015 0.20 - - - - 0.12-0.25- - - - -

44、 - - - - - - - - - - - - - 0.1 0.412 R53400 0.08 0.25 0.03 0.015 0.30 - - - - - - - - 0.6-0.90.2-0.4- - - - - - - - - - - - 0.1 0.413 R53413 0.08 0.10 0.03 0.015 0.20 - - - - - - 0.04-0.060.4-0.6- - - - - - - - - - - - - - 0.1 0.414 R53414 0.08 0.15 0.03 0.015 0.30 - - - - - - 0.04-0.060.4-0.6- - -

45、- - - - - - - - - - - 0.1 0.415 R53415 0.08 0.25 0.05 0.015 0.30 - - - - - - 0.04-0.060.4-0.6- - - - - - - - - - - - - - 0.1 0.416/16H R52402 0.08 0.25 0.03 0.015 0.30 - - - - 0.04-0.08- - - - - - - - - - - - - - - - - - 0.1 0.417 R52252 0.08 0.18 0.03 0.015 0.20 - - - - 0.04-0.08- - - - - - - - - -

46、 - - - - - - - - 0.1 0.418 R56322 0.08 0.15 0.03 0.015 0.25 2.5-3.52.0-3.00.04-0.08- - - - - - - - - - - - - - - - - - 0.1 0.419 R58640 0.05 0.12 0.03 0.02 0.30 3.0-4.07.5-8.5- - - - - - 3.5-4.55.5-6.5- - 3.5-4.5- - - - - - 0.15 0.420 R58645 0.05 0.12 0.03 0.02 0.30 3.0-4.07.5-8.50.04-0.08- - - - 3.

47、5-4.55.5-6.5- - 3.5-4.5- - - - - - 0.15 0.421 R58210 0.05 0.17 0.03 0.015 0.40 2.5-3.5- - - - - - - - 14.0-16.0- - - - - - 2.2-3.2- - 0.15-0.250.1 0.423 R56407 0.08 0.13 0.03 0.0125 0.25 5.5-6.53.5-4.5- - - - - - - - - - - - - - - - - - - - 0.1 0.424 R56405 0.08 0.20 0.05 0.015 0.40 5.5-6.753.5-4.50

48、.04-0.08- - - - - - - - - - - - - - - - - - 0.1 0.425 R56403 0.08 0.20 0.05 0.015 0.40 5.5-6.753.5-4.50.04-0.08- - 0.3-0.8- - - - - - - - - - - - - - 0.1 0.426/26H R52404 0.08 0.25 0.03 0.015 0.30 - - - - - - 0.08-0.14- - - - - - - - - - - - - - - - 0.1 0.427 R52254 0.08 0.18 0.03 0.015 0.20 - - - -

49、 - - 0.08-0.14- - - - - - - - - - - - - - - - 0.1 0.428 R56323 0.08 0.15 0.03 0.015 0.25 2.5-3.52.0-3.0- - 0.08-0.14- - - - - - - - - - - - - - - - 0.1 0.429 R56404 0.08 0.13 0.03 0.0125 0.25 5.5-6.53.5-4.5- - 0.08-0.14- - - - - - - - - - - - - - - - 0.1 0.4 - - - - - - - - - - - -33 R53442 0.08 0.25 0.03 0.015 0.30 - - - - 0.01-0.020.02-0.040.35-0.55- -