ASTM B865-2004(2010) Standard Specification for Precipitation Hardening Nickel-Copper-Aluminum Alloy (UNS N05500) Bar Rod Wire Forgings and Forging Stock《沉淀硬化镍铜铝合金(UNS N05500)棒材 杆材.pdf

1、Designation: B865 04 (Reapproved 2010)Standard Specification forPrecipitation Hardening Nickel-Copper-Aluminum Alloy(UNS N05500) Bar, Rod, Wire, Forgings, and Forging Stock1This standard is issued under the fixed designation B865; the number immediately following the designation indicates the year o

2、foriginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers nickel-copper-aluminum alloy(UNS

3、 N05500) in the form of rounds, squares, hexagons, orrectangles, and forgings and forging stock, manufactured eitherby hot working or cold working, and cold-worked wire.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversion

4、s to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identi

5、fied in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2E8 Test Methods for

6、 Tension Testing of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE112 Test Methods for Determining Average Grain SizeE140 Hardness Conversion Tables for Metals Relation

7、shipAmong Brinell Hardness, Vickers Hardness, RockwellHardness, Superficial Hardness, Knoop Hardness, andScleroscope HardnessE602 Test Method for Sharp-Notch Tension Testing withCylindrical SpecimensE1473 Test Methods for Chemical Analysis of Nickel,Cobalt, and High-Temperature Alloys2.2 Federal Sta

8、ndards:Fed. Std. No. 102 Preservation, Packaging, and PackingLevelsFed. Std. No. 123 Marking for Shipment (Civil Agencies)Fed. Std. No. 182 Continuous Identification Marking ofNickel and Nickel-Base Alloys2.3 Military Standards:MIL-STD-129 Marking for Shipment and StorageMIL-STD-271 Nondestructive T

9、esting Requirements forMetals3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 bar, nmaterial of rectangular (flats), hexagonal, orsquare solid section up to and including 10 in. (254 mm) inwidth and18 in. (3.2 mm) and over in thickness in straightlengths.3.1.2 rod, nmaterial of

10、 round solid section furnished instraight lengths.3.1.3 wire, na cold-worked solid product of uniformround cross section along its whole length, supplied in coilform.4. Ordering Information4.1 Orders for material to this specification should includethe following information:4.1.1 ASTM designation an

11、d year of issue,4.1.2 Alloy name or UNS number (see Table 1),4.1.3 Shaperod (round) or bar (square, hexagonal, orrectangular),4.1.3.1 Forging (sketch or drawing),4.1.4 Dimensions, including length, (see Tables 2 and 3),4.1.5 Condition (see Table 4, Table 5, and Table 6),4.1.6 Forging stockSpecify if

12、 material is stock for reforg-ing,4.1.7 Finish,1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Oct. 1, 2010. Published Octo

13、ber 2010. Originallyapproved in 1995. Last previous edition approved in 2004 as B865 04. DOI:10.1520/B0865-04R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the

14、 standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.8 Quantityfeet or number of pieces, and4.1.9 CertificationState if certification or a report of testresults is required (Section

15、15),4.1.10 Samples for product (check) analysisState whethersamples for product (check) analysis should be furnished, and4.1.11 Purchaser inspectionIf purchaser wishes to witnesstests or inspection of material at place of manufacture, thepurchase order must so state indicating which test or inspec-t

16、ions are to be witnessed.5. Chemical Composition5.1 The material shall conform to the composition limitsspecified in Table 1.5.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations in Table 1.6. Mechanical Properties6.1 Mec

17、hanical PropertiesThe material in the unagedcondition shall conform to the mechanical properties specifiedin Table 4. After aging the material shall conform to themechanical properties specified in Table 5 and Table 6.7. Dimensions and Permissible Variations7.1 Diameter, Thickness, or WidthThe permi

18、ssible varia-tions from the specified dimensions as measured on thediameter or between parallel surfaces of cold-worked rod andbar shall be as prescribed in Table 7; of hot-worked rod and baras prescribed in Table 2; and of wire as prescribed in Table 7.7.2 Out-of-RoundHot-worked rods and cold-worke

19、d rods(except “forging quality”) of all sizes, in straight lengths, shallnot be out-of-round by more than one half the total permissiblevariations in diameter shown in Table 2 and Table 7, except forhot-worked rods12 in. (12.7 mm) in diameter and under, whichmay be cut-of-round by the total permissi

20、ble variations indiameter shown in Table 2. Cold-worked wire shall not beout-of-round by more than one-half the total permissiblevariations in diameter shown in Table 7.7.3 EdgesSquare, rectangular, and hexagonal bar and rodshall have angles and corners consistent with commercialpractice.TABLE 1 Che

21、mical RequirementsElement Composition Limits, %Product (check) analysisvariations, under min orover max, of the specifiedlimit of element, %NickelA63.0 min 0.45Aluminum 2.303.15 0.20Carbon 0.18 max 0.01Iron 2.0 max 0.05Manganese 1.5 max 0.04Silicon 0.50 max 0.03Titanium 0.350.85 0.03 min0.04 maxSulf

22、ur 0.010 max 0.003Copper 27.033.0 0.15 min0.20 maxAThe nickel content shall be determined arithmetically by difference.TABLE 2 Permissible Variations in Diameter or DistanceBetween Parallel Surfaces of Hot-Worked Rod and BarASpecified Dimension,Bin. (mm)Permissible Variations fromSpecified Dimension

23、s, in. (mm)Plus MinusRod and bar, hot worked:1 (25.4) and under 0.016 (0.41) 0.016 (0.41)Over 1 (25.4) to 2 (50.8), incl 0.031 (0.79) 0.016 (0.41)Over 2 (50.8) to 4 (101.6), incl 0.047 (1.19) 0.031 (0.79)Over 4 (101.6) 0.125 (3.18) 0.063 (1.60)Rod, rough-turned or ground:Under 1 (25.4) 0.005 (0.13)

24、0.005 (0.13)1 (25.4) and over 0.031 (0.79) 0Round rod, semi-smooth, machined:Over 312 (88.9) 0.031 (0.79) 0Round rod, smooth finished, machined:Over 312 (88.9) 0 0.005 (0.13)Forging quality bolt stock (rounds only):14 (6.4),516 (7.9) 0 0.0062 (0.16)38 (9.5),716 (11.1),12 (12.7) 0 0.0066 (0.17)916 (1

25、4.3),58 (7.9),1116 (17.5),34(19.1),1316 (20.6),78 (22.2)0 0.0082 (0.21)516 (7.9), 1 (25.4) 0 0.0098 (0.25)1116 to 112 (27.0 to 38.1), in116 (1.6)increments0 0.0112 (0.28)ANot applicable to forging stock.BDimensions apply to diameter of rods, to distance between parallel surfaces ofhexagons and squar

26、es, and separately to width and thickness of rectangles.TABLE 3 Permissible Variations in Straightness of PrecisionStraightened Cold-Worked ShaftingSpecified Dimension,in. (mm)Standard DistanceBetween Supports,in. (mm)Permissible VariationsThrow In One RevolutionFrom Straightness,in. (mm)12 (12.7) t

27、o1516 (23.8),incl42 (1070) 0.005 (0.13)Over1516 (23.8) to 11516(49.2), incl42 (1070) 0.006 (0.15)Over 11516 (49.2) to 212(63.5), incl42 (1070) 0.007 (0.18)Over 212 (63.5) to 4(101.6), incl42 (1070) 0.008 (0.20)34 (19.0) to1516 (23.8),inclSpecified lengths of 3 to 10ft (0.91 to 3.05 m)0.004 (0.10) pl

28、us 0.0025(0.064) for each foot, orfraction thereof, in excessof 3 ft (0.91 m)Over1516 (23.8) to 4(101.6), inclSpecified lengths of 20 ft(6.10 m) and less0.005 (0.13) plus 0.0015(0.038) for each foot, orfraction thereof, in excessof 3 ft (0.91 m)TABLE 4 Mechanical PropertiesUnagedA(Bar, Rod, Forgings

29、)Form ConditionHardnessBrinell3000 kg, maxRockwell, maxRounds,Bhexagons,squares, rectangles, andforgingsHot-worked 245 C23Hexagons Cold-worked 260 C26Rounds:14 (6.4 mm) to 1 in.(25.4 mm), inclCold-worked 280 C29Over 1 (25.4 mm) to 3in. (76.2 mm), inclCold-worked 260 C26Over 3 (76.2 mm) to 4in. (101.

30、6 mm), inclCold-worked 240 C22Rounds, hexagons,squares, rectangles, andforgingsHot-worked or cold-worked and annealed185 B90ANo tensile tests are required except as provided for in 9.2.3.BRounds over 414 in. (108.0 mm) in diameter shall have hardness of 260 BHN,max.B865 04 (2010)27.4 Machining Allow

31、ances for Hot-Worked MaterialsWhen the surfaces of hot-worked products are to be machined,the allowances prescribed in Table 8 are recommended fornormal machining operations.7.5 LengthThe permissible variations in length of cold-worked and hot-worked rod and bar shall be as prescribed inTable 9.7.5.

32、1 Rods and bars ordered to random or nominal lengthswill be furnished with either cropped or saw-cut ends; materialordered to cut lengths will be furnished with square, saw-cut,or machined ends.7.6 Straightness:7.6.1 The permissible variations in straightness ofprecision-straightened cold-worked rod

33、 and bar as determinedby the departure from straightness shall be as specified in Table3.7.6.2 The permissible variations in straightness of hot-worked, cold-worked, rough-turned, and machined rod and baras determined by the departure from straightness shall be asspecified in Table 10.7.6.2.1 In det

34、ermining straightness in the standard 42-in.(1.07-mm) distance between supports or, when specified, inTABLE 5 Mechanical PropertiesAge-HardenedA(Bar, Rod, and Forgings)Form ConditionMaximum SectionThickness, in. (mm)TensileStrength, min,ksi (MPa)Yield StrengthB,0.2 % offset,min, ksi (MPa)ElongationB

35、in 2 in. or 4D,min,%HardnessCBrinell 3000kg, minRockwellC, minRounds,Dhexagons, squares,rectangles, and forgingsEHot-worked and age-hardenedAll sizes 140 (965) 100 (690) 20.0 265 27Rounds Cold-worked and14 (6.4) to 1 (25.4), incl 145 (1000) 110 (760) 15.0 300 32age-hardened over 1 (25.4) to 3(76.2),

36、 incl140 (965) 100 (690) 17.0 280 29over 3 (76.2) to 4(101.6), incl135 (930) 95 (655) 20.0 255 25Hexagons Cold-worked and age-hardened14 (6.4) to 2 (50.8), incl 140 (965) 100 (690) 15.0 265 27Rounds, hexagons, squares, Annealed and age- Up to 1 (25.4) 130 (895) 90 (620) 20.0 250 24rectangles, and fo

37、rgings hardenedF1 (25.4) and over 130 (895) 85 (585) 20.0 250 24AAge hardening heat treatment:Age hardening shall be accomplished by holding at an aim temperature of 1100F (595C) for 8 to 16 h followed by furnace cooling to 900F (480C) at a rate of 15to 25F (10 to 15C) per hour and then air cooling.

38、 An alternate procedure consists of holding at 1100F (595C) for up to 16 h, furnace cooling to 1000F (540C), holdingfor approximately 6 h, furnace cooling to 900F (480C), holding for approximately 8 h, and air cooling to room temperature.(Mill age-hardened products have been precipitation heat treat

39、ed by the manufacturer and further thermal treatment normally is not required. Hot-worked, cold-worked,or annealed material is normally age hardened by the purchaser after forming or machining.)BNot applicable to subsize tensile specimens less than 0.250 in. (6.4 mm) in diameter.CHardness values are

40、 given for information only and are not the basis for acceptance or rejection.DRounds over 414 in. (108.0 mm) in diameter shall have an elongation in 2 in. (50.8 mm) or 4D of 17 %, min.EWhen specified, for forged rings and discs, hardness measurements may be utilized in lieu of tensile test.FApplica

41、ble to both hot-worked and cold-worked material.TABLE 6 Tensile Strength of Cold-Drawn Wire in CoilsCondition and Size, in. (mm)Tensile Strength, min,ksi (MPa)Cold-worked, as-worked, all sizes 110155 (7601070)ACold-worked and annealed, all sizes 110 (760)BCold-worked, spring temper, as-drawn 0.057 (

42、1.45)and lessC165 (1140)Over 0.057 to 0.114 (1.45 to 2.90), incl 155 (1070)Over 0.114 to 0.229 (2.90 to 5.82), incl 150 (1035)Over 0.229 to 0.312 (5.82 to 7.92), incl 145 (1000)Over 0.312 to 0.375 (7.92 to 9.52), incl 135 (930)Over 0.375 to 0.437 (9.52 to 11.10), incl 125 (860)Over 0.437 to 0.563 (1

43、1.10 to 14.30), incl 120 (825)Cold-worked, annealed, and age-hardened,Dall sizes 130 (895)Cold-worked, as drawn, age-hardened,Dall sizes 155 (1070)Cold-worked, spring temper, and age-hardenedDUp to 0.114 (2.90), incl 180 (1240)Over 0.114 to 0.375 (2.90 to 9.52), incl 170 (1170)Over 0.375 to 0.563 (9

44、.52 to 14.30), incl 160 (1105)AMaximum and minimum.BMaximum.CApplicable to material in coil. For material in straightened and cut lengths,deduct 15 ksi (105 MPa) from above values.DAge hardening heat treatment:Age hardening shall be accomplished by holding at an aim temperature of1100F (595C) for 8

45、to 16 h followed by furnace cooling to 900F (480C) at a rateof 15 to 25F (10 to 15C) per hour and then air cooling. An alternate procedureconsists of holding at 1100F (595C) for up to 16 h, furnace cooling to 1000F(540C), holding for approximately 6 h, furnace cooling to 900F (480C), holdingfor appr

46、oximately 8 h, and air cooling to room temperature.(Mill age-hardened products have been precipitation heat treated by themanufacturer and further thermal treatment is not normally required. Hot-worked,cold-worked, or annealed material is normally age hardened by the purchaser afterforming or machin

47、ing.)TABLE 7 Permissible Variations in Diameter or DistanceBetween Parallel Surfaces of Cold-Worked Rod and BarSpecified Dimension,Ain. (mm)Permissible Variations FromSpecified Dimension, in. (mm)Plus MinusRounds:116 (1.6) to316 (4.8), excl 0 0.002 (0.05)316 (4.8) to12 (12.7), excl 0 0.003 (0.08)12

48、(12.7) to1516 (23.8), incl 0 0.002 (0.05)BOver1516 (23.8) to 11516 (49.2), incl 0 0.003 (0.08)BOver 11516 (49.2) to 212 (63.5), incl 0 0.004 (0.10)BOver 212 (63.5) to 3 (76.2), incl 0 0.005 (0.13)BOver 3 (76.2) to 312 (88.9), incl 0 0.006 (0.15)BOver 312 (88.9) to 4 (101.6), incl 0 0.007 (0.18)BHexa

49、gons, squares, rectangles:12 (12.7) and less 0 0.004 (0.10)Over12 (12.7) to78 (22.2), incl 0 0.005 (0.13)Over78 (22.2) to 114 (31.8), incl 0 0.007 (0.18)Over 114 (31.8) to 2 (50.8), incl 0 0.009 (0.23)ADimensions apply to diameter of rounds, to distance between parallel surfacesof hexagons and squares, and separately to width and thickness of rectangles.BFor cold-worked, age-hardened, bright finish shafting, an additional minus0.002 (0.05) tolerance will be permitted.B865 04 (2010)3d