ASTM B88-2003 Standard Specification for Seamless Copper Water Tube《无缝铜水管标准规范》.pdf

1、Designation: B 88 03Standard Specification forSeamless Copper Water Tube1This standard is issued under the fixed designation B 88; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision. A number in parentheses i

2、ndicates the year of last reapproval. A superscriptepsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers seamless copper water tubesuitable for general pl

3、umbing, similar applications for theconveyance of fluids, and commonly used with solder, flared,or compression-type fittings. The type of copper water tubesuitable for any particular application is determined by theinternal or external fluid pressure, by the installation andservice conditions, and b

4、y local requirements. Means of joiningor bending are also factors which affect the selection of thetype of tube to be used.2NOTE 1Annealed tube is suitable for use with flared or compressionfittings, and with solder-type fittings, provided rounding and sizing of thetube ends is performed where neede

5、d.NOTE 2Drawn temper tube is suitable for use with solder-typefittings. Types K and L tube, in the drawn temper, are suitable for use withcertain types and sizes of compression fittings.NOTE 3A complete metric companion to Specification B 88 has beendevelopedB 88M; therefore, no metric equivalents a

6、re presented in thisspecification.NOTE 4Fittings used for soldered or brazed connections in plumbingsystems are described in ASME B16.18 and ASME B16.22.1.2 The tube shall be produced from the following coppers,and the manufacturer has the option to supply any one of them,unless otherwise specified.

7、CopperUNS No.Previously UsedDesignationDescriptionC10200 OF Oxygen free withoutresidual deoxidantsC12000 DLP Phosphorus deoxidized,low residual phosphorusC12200 DHP Phosphorus deoxidized,high residual phosphorus1.3 The assembly of copper plumbing or fire sprinklersystems by soldering is described in

8、 Practice B 828.1.4 Solders for joining copper potable water or fire sprinklersystems are covered by Specification B32. The requirementsfor acceptable fluxes for these systems are covered by Speci-fication B 813.1.5 The following safety hazards caveat pertains only to thetest methods portion, Sectio

9、n 15, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior

10、to use.2. Referenced Documents2.1 The following documents of the issue in effect on dateof material purchase form a part of this specification to theextent referenced herein:2.2 ASTM Standards:3B32 Specification for Solder MetalB 88M Specification for Seamless Copper Water TubeMetricB 153 Test Metho

11、d for Expansion (Pin Test) of Copper andCopper-Alloy Pipe and TubingB 557 Test Methods for Detection of Cuprous Oxide (Hy-drogen Embrittlement Susceptibility) in CopperB 601 Classification for Temper Designations for Copperand Copper AlloysWrought and CastB 813 Specification for Liquid and Paste Flu

12、xes for Solder-ing Applications of Copper and Copper Alloy TubeB 828 Practice for Making Capillary Joints by Soldering ofCopper and Copper Alloy Tube and FittingsE2 Methods of Preparation of Micrographs of Metals andAlloysE3 Guide for Preparation of Metallographic SpecimensE8 Test Methods for Tensio

13、n Testing of Metallic MaterialsE18 Test Methods for Rockwell Hardness and RockwellSuperficial Hardness of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data to1This specification is under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct respons

14、ibility of Subcommittee B05.04 on Pipeand Tube.Current edition approved Oct. 1, 2003. Published November 2003. Originallyapproved in 1932. Last previous edition approved in 2002 as B 88 02.2The UNS system for copper and copper alloys (see Practice E 527) is a simpleexpansion of the former standard d

15、esignation system accomplished by the additionof a prefix “C” and a suffix “00.” The suffix is permitted to be used to accommodatecomposition variations of the base alloy.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Ann

16、ual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.Determine

17、 Conformance with SpecificationsE53 Test Methods for Determination of Copper in Unal-loyed Copper by GravimetryE62 Test Methods for Chemical Analysis of Copper andCopper Alloys (Photometric Methods)E112 Test Methods for Determining the Average GrainSizeE 243 Practice for Electromagnetic (Eddy-Curren

18、t) Exami-nation of Copper and Copper-Alloy TubesE 255 Practice for Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE 527 Practice for Numbering Metals and Alloys (UNS)2.3 ASME Standards:ASME B16.18 Cast Copper Alloy Solder Joint PressureFittings4ASME B16.22 Wrought Copp

19、er and Copper Alloy SolderJoint Pressure Fittings43. Terminology3.1 Definitions:3.1.1 coil, na length of the product wound into a series ofconnected turns. The unqualified term “coil” as applied to tubeusually refers to a bunched coil.3.1.1.1 bunched, na coil in which the turns are bunchedand held t

20、ogether such that the cross section of the bunchedturns is approximately circular.3.1.1.2 double layer flat, na coil in which the product isspirally wound into two connected disk-like layers such thatone layer is on top of the other. (Sometimes called “doublelayer pancake coil” or “double layer spir

21、ally wound coil.”)3.1.1.3 level or traverse wound, na coil in which the turnsare wound into layers parallel to the axis of the coil such thatsuccessive turns in a given layer are next to one another.(Sometimes called “helical coil.”)3.1.1.4 single layer flat, na coil in which the product isspirally

22、wound into a single disk-like layer. (Sometimes called“pancake coil” or “single layer spirally wound coil.”)3.1.2 lengths, nstraight pieces of the product.3.1.2.1 standard, nuniform lengths recommended in asimplified practice recommendation or established as a com-mercial standard.3.1.3 tube, seamle

23、ss, na tube produced with a continuousperiphery in all stages of the operations.3.1.3.1 tube, copper service, na bendable copper watertube for underground water service.3.1.3.2 tube, copper water, na seamless copper tubeconforming to the particular dimensions commercially knownas Copper Water Tube a

24、nd designated as Types K, L, and M.3.2 Definitions of Terms Specific to This Standard:3.2.1 capable ofthe test need not be performed by theproducer of the material. However, if subsequent testing by thepurchaser establishes that the material does not meet theserequirements, the material shall be sub

25、ject to rejection.4. Ordering Information4.1 Include the following information for material orderedunder this specification.4.1.1 ASTM designation and year of issue (for example,B 88 03),4Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave.,

26、 New York, NY 10016-5990.TABLE 1 Dimensions, Weights, and Tolerances in Diameter and Wall Thickness for Nominal or Standard Copper Water Tube Sizes(All tolerances are plus and minus except as otherwise indicated)Nominal orStandard Size,in.OutsideDiameter,in.Average OutsideDiameterATolerance, in.Wall

27、 Thickness and Tolerances, in.Theoretical Weight, lb/ftType K Type L Type MAnnealed DrawnWallThicknessToler-anceBWallThicknessToler-anceBWallThicknessToler-anceBType K Type L Type M14 0.375 0.002 0.001 0.035 0.0035 0.030 0.003CC0.145 0.126C38 0.500 0.0025 0.001 0.049 0.005 0.035 0.004 0.025 0.002 0.

28、269 0.198 0.14512 0.625 0.0025 0.001 0.049 0.005 0.040 0.004 0.028 0.003 0.344 0.285 0.20458 0.750 0.0025 0.001 0.049 0.005 0.042 0.004CC0.418 0.362C34 0.875 0.003 0.001 0.065 0.006 0.045 0.004 0.032 0.003 0.641 0.455 0.3281 1.125 0.0035 0.0015 0.065 0.006 0.050 0.005 0.035 0.004 0.839 0.655 0.46511

29、4 1.375 0.004 0.0015 0.065 0.006 0.055 0.006 0.042 0.004 1.04 0.884 0.682112 1.625 0.0045 0.002 0.072 0.007 0.060 0.006 0.049 0.005 1.36 1.14 0.9402 2.125 0.005 0.002 0.083 0.008 0.070 0.007 0.058 0.006 2.06 1.75 1.46212 2.625 0.005 0.002 0.095 0.010 0.080 0.008 0.065 0.006 2.93 2.48 2.033 3.125 0.0

30、05 0.002 0.109 0.011 0.090 0.009 0.072 0.007 4.00 3.33 2.68312 3.625 0.005 0.002 0.120 0.012 0.100 0.010 0.083 0.008 5.12 4.29 3.584 4.125 0.005 0.002 0.134 0.013 0.110 0.011 0.095 0.010 6.51 5.38 4.665 5.125 0.005 0.002 0.160 0.016 0.125 0.012 0.109 0.011 9.67 7.61 6.666 6.125 0.005 0.002 0.192 0.0

31、19 0.140 0.014 0.122 0.012 13.9 10.2 8.928 8.125 0.006 + 0.002 0.271 0.027 0.200 0.020 0.170 0.017 25.9 19.3 16.50.00410 10.125 0.008 + 0.002 0.338 0.034 0.250 0.025 0.212 0.021 40.3 30.1 25.60.00612 12.125 0.008 + 0.002 0.405 0.040 0.280 0.028 0.254 0.025 57.8 40.4 36.70.006AThe average outside dia

32、meter of a tube is the average of the maximum and minimum outside diameter, as determined at any one cross section of the tube.BMaximum deviation at any one point.CIndicates that the material is not generally available or that no tolerance has been established.B880324.1.2 Copper UNS No. (not necessa

33、ry unless a specificcopper is desired),4.1.3 Nominal or standard size (Column 1 of Table 1) andwhether Type K, L, or M (Sections 3 and 11),4.1.4 Temper (Sections 5 and 7),4.1.5 Length (see 11.5),4.1.6 How furnished: straight or coils, and4.1.7 Quantity (pieces) of each size and type.4.1.8 In additio

34、n, when material is purchased for agencies ofthe U.S. Government, it shall conform to the SupplementaryRequirements as defined herein when specified in the contractor purchase order.4.2 The following options are available and shall be speci-fied in the contract or purchase order when required:4.2.1

35、Tension test (Section 8),4.2.2 Grain size determination (Section 8),4.2.3 Expansion test (9.1), and4.2.4 Microscopical Examination for Hydrogen Embrittle-ment, Procedure B (9.3.2).5. Materials and Manufacture5.1 The material shall be of such quality and purity that thefinished product shall have the

36、 properties and characteristicsprescribed in this specification, and shall be cold drawn to size.5.2 The tube shall be finished by such cold-working andannealing operations as are necessary to produce the requiredtemper and surface finish.5.3 Tube when furnished in coils shall be annealed aftercoili

37、ng.5.4 Tube when furnished in straight lengths shall normallybe in the drawn temper. Upon agreement between the manu-facturer or supplier and the purchaser, the manufacturer shallhave the option to supply annealed straight length tubing.6. Chemical Composition6.1 The material shall conform to the ch

38、emical requirementsin Table 2 for the specific type of copper.6.2 These specification limits do not preclude the presenceof other elements. When included in the contract or purchaseorder, and agreed upon by the manufacturer or supplier and thepurchaser, limits shall be established and analysis requi

39、red forunnamed elements.7. Temper7.1 Seamless copper water tube shall be furnished in thetempers designated below. Current designations as defined inClassification B 601 are shown.AnnealedODrawnH8. Mechanical Properties8.1 The tube shall conform to the mechanical propertyrequirements prescribed in T

40、able 3. Tension tests and grainsizedeterminations need not be made except when indicated by thepurchaser at the time of placing the order.Aconvenient methodof indicating that these tests are to be made is to state that “TestProcedure T is required” (see 4.2.1). Where agreement on theRockwell hardnes

41、s tests cannot be reached, the tensile strengthand grain-size requirements of Table 3 shall be the basis foracceptance or rejection.9. Performance Requirements9.1 Expansion Test:9.1.1 The annealed (O) tube shall be capable of beingexpanded in accordance with Test Method B 153 with anexpansion of the

42、 outside diameter in the following amount:Nominal orStandard Size, in.Expansion ofOutside Diameter, %58 and under 40Over58 30The expanded tube shall show no cracking or rupture visibleto the unaided eye.9.2 Flattening Test:9.2.1 As an alternative to the expansion test for tubestandard sizes 4 in. an

43、d over in the annealed condition, asection 4 in. in length shall be cut from the end of one of thelengths for a flattening test. This 4-in. test specimen shall beflattened so that a gage set at three times the wall thickness willpass over the tube freely throughout the flattened part. The tubeso tes

44、ted shall develop no cracks or flaws visible to the unaidedeye as a result of this test. In making the flattening test theelements shall be slowly flattened by one stroke of the press.9.3 Microscopical Examination for Susceptibility to Hydro-gen Embrittlement:9.3.1 Tubes furnished in Copper UNS No.

45、C10200 andC12000 shall be essentially free of cuprous oxide as deter-mined by Procedure A of Test Methods B 577. When CopperUNS No. C12200 is supplied, examination is not required. Incase of a dispute, Procedure C of Test Methods B 577 shall beused as the referee method.9.3.2 Tubes furnished in all

46、coppers shall be capable ofpassing the embrittlement test specified in Procedure B of TestMethods B 577. The actual performance of the test is notrequired unless specifically requested in the ordering docu-ment. In case of a dispute, Procedure C of Test Methods B 577shall be used as the referee meth

47、od.10. Nondestructive Testing10.1 Each tube up to and including 318 in. in outsidediameter shall be subjected to an eddy-current test. Testingshall follow the procedures of Practice E 243, except for thedetermination of “end effect.” Tubes shall be passed through aneddy-current test unit adjusted to

48、 provide information on thesuitability of the tube for the intended application.10.1.1 Notch-depth standards, rounded to the nearest 0.001in., shall be 22 % of the wall thickness. The notch-depthtolerance shall be plus and minus 0.0005 in. Alternatively, atTABLE 2 Chemical CompositionWeight %Element

49、 Copper UNS No.C10200AC12000 C12200Copper,Bmin 99.95 99.90 99.9Phosphorus . 0.0040.012 0.0150.040AOxygen shall be 10 ppm max.BCopper + silver.B88033the option of the manufacturer using speed insensitive eddy-current units that are equipped to select a fraction of themaximum unbalance signal, the following percent maximumunbalance signals shall be used:Nominal or StandardTube Size, in.Unbalance SignalMagnitude, max %Up to38 , incl 0.212 to 2, incl 0.3Over 2 to 3, incl 0.410.1.2 Tubes that do not actuate the signalling device of theeddy-curr