ASTM B952 B952M-2014 Standard Specification for Zinc Alloys in Ingot Form for Spin Casting《旋转铸造用锭锌合金的标准规格》.pdf

1、Designation: B952/B952M 13B952/B952M 14Standard Specification forZinc Alloys in Ingot Form for Spin Casting1This standard is issued under the fixed designation B952/B952M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of

2、 last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers zinc alloys in ingot form for remelting for the manufacture of Spin Castings as specified

3、anddesignated, as shown in Table 1. Seven alloy compositions are specified, designated as follows:Common Traditional UNSSpin Casting Alloy SC-A . Z35550Spin Casting Alloy SC-B . Z35551Spin Casting Alloy SC-C . Z35534Spin Casting Alloy SC-D HJ10 Z35547Spin Casting Alloy SC-E HJ20 Z35548Spin Casting A

4、lloy SC-F HJ40 Z35552ZA-73 . Z365001.2 Zinc alloys #2, #3, #5, and ZA-8 specified in Specification B240 are also used in the spin casting process.1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may not be exact e

5、quivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the

6、user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety DataSheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, anddetermine the applicability of regulatory limit

7、ations prior to use.2. Referenced Documents2.1 The following documents of the issue in effect on date of order acceptance form a part of this specification to the extentreferenced herein:2.2 ASTM Standards:2B240 Specification for Zinc and Zinc-Aluminum (ZA) Alloys in Ingot Form for Foundry and Die C

8、astingsB899 Terminology Relating to Non-ferrous Metals and AlloysB908 Practice for the Use of Color Codes for Zinc Casting Alloy IngotB949 Specification for General Requirements for Zinc and Zinc Alloy ProductsE29 Practice for Using Significant Digits in Test Data to Determine Conformance with Speci

9、ficationsE88 Practice for Sampling Nonferrous Metals and Alloys in Cast Form for Determination of Chemical CompositionE536 Test Methods for Chemical Analysis of Zinc and Zinc AlloysE634 Practice for Sampling of Zinc and Zinc Alloys by Spark Atomic Emission Spectrometry2.3 ISO Standards:3ISO 3815-1 Z

10、inc and zinc alloysPart 1: Analysis of solid samples by optical emission spectrometryISO 3815-2 Zinc and zinc alloysPart 2: Analysis by inductively coupled plasma optical emission1 This specification is under the jurisdiction of ASTM Committee B02 on Nonferrous Metals and Alloys and is the direct re

11、sponsibility of Subcommittee B02.04 on Zincand Cadmium.Current edition approved Feb. 1, 2013Oct. 1, 2014. Published March 2013October 2014. Originally approved in 2007. Last previous edition approved in 20122013 asB952/B952M 12.B952/B952M 13. DOI: 10.1520/B0952_B0952M-13.10.1520/B0952_B0952M-14.2 Fo

12、r referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standardsstandards Document Summary page on the ASTM website.3 Available from American National Standards Institute (

13、ANSI), 25 W. 43rd St., 4th Floor, New York, NY 10036, http:/www.ansi.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately de

14、pict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM Internati

15、onal, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13. Terminology3.1 Terms shall be defined in accordance with Terminology B899.3.2 Definitions of Terms Specific to This Standard:3.2.1 spin casting, na casting process in which molten metal is poured into a rubb

16、er, polymer, graphite or metal mold and spuncentrifugally until solidified, also a product produced by such a process.4. Ordering Information4.1 Orders for zinc alloy ingot under this specification shall include information as specified in Specification B949, Section 4.5. Materials and Manufacture5.

17、1 The alloys may be made by any approved process.5.2 The material covered by this specification shall be of uniform quality and shall be free from dross or other harmfulcontamination.6. Chemical Requirements6.1 LimitsThe alloy shall conform to the requirements as to chemical composition prescribed i

18、n Table 1.6.2 Chemical requirement procedures shall be in compliance with the provisions of Specification B949, Section 5.2.6.3 Methods of SamplingSampling procedures shall be in compliance with the provisions of Specification B949, Section 6.6.4 Method of AnalysisApproved methods include: Test Meth

19、ods E536, ISO 3815-1, or ISO 3815-2.NOTE 1Test Methods E536 is directly applicable in an unmodified form, only to alloys 3, 5, and 7. ISO 3815-1 and ISO 3815-2 are generic methodsapplied to zinc and zinc alloys. Each of the methods may be modified and formatted for the alloy to be assayed. An experi

20、enced chemist, using suitableand/or traceable standards along with valid quality assurance techniques, will be able to perform and validate the methods and demonstrate acceptableprecision and accuracy.7. Source Inspection7.1 Source inspection shall be in compliance with the provisions of Specificati

21、on B949, Section 7.8. Rejection and Rehearing8.1 Claims to be considered in accordance with the provisions of Specification B949, Section 8.9. Investigation of Claims9.1 Claims shall be investigated in accordance with the provisions of Specification B949, Section 8.10. Settlement of Claims10.1 Claim

22、s shall be settled in accordance with the provisions of Specification B949, Section 8.11. Product Identification Marking and Packaging11.1 Each slab, block, jumbo or ingot shall be marked for identification in accordance with the provisions of Specification B949,Section 10.TABLE 1 Chemical and North

23、 American Color Code RequirementsAlloy SC-A Alloy SC-B Alloy SC-C ZA-73C Alloy SC-D Alloy SC-E Alloy SC-FUNS Z35550 Z35551 Z35534 Z56500 Z35547 Z35548 Z35552Color CodeAColor CodeA Green/Black Green/Purple Green/Yellow Blue/Orange Green/Blue Green/Red Green/OrangeElementBAluminum 3.94.3 3.94.3 3.44.6

24、 7.78.0 3.23.8 3.2-3.8 3.25-3.75Magnesium 0.10.2 0.40.6 0.40.43 0.020.03 0.15-0.30 0.45-0.75 0.45-4.75Magnesium 0.10.2 0.40.6 0.40.43 0.020.03 0.15-0.30 0.45-0.75 0.45-0.75Copper 2.62.9 2.73.3 1.31.4 3.03.3 1.2-1.8 2.5-3.25 4.25-4.75Iron, max 0.035 0.035 0.10 0.075 0.035 0.075 0.035Lead, max 0.004 0

25、.004 0.015 0.005 0.004 0.005 0.004Cadmium, max 0.0030 0.0030 0.005 0.003 0.003 0.003 0.003Tin, max 0.0015 0.0015 0.005 0.002 0.002 0.003 0.002Nickel, max . . 0.02 . . . . 0.02 . . .Zinc Remainder Remainder Remainder Remainder Remainder Remainder RemainderA Per Practice B908.B For purposes of accepta

26、nce and rejection, the observed value or calculated value obtained from analysis should be rounded to the nearest unit in the last right-handplace of figures, used in expressing the specific limit in accordance with the rounding procedure prescribed in Practice E29.C ZA-73 is also often used as a pr

27、essure die casting alloy.B952/B952M 14212. Preparation for Delivery12.1 PackagingUnless otherwise specified, the ingot shall be packaged to provide adequate protection during normal handlingand transportation. Each package shall contain only one alloy unless otherwise agreed upon.13. Keywords13.1 ca

28、sting; casting alloys; centrifugical casting; prototyping; rubber mold; SC-A; SC-B; SC-C; silicon mold; spin casting; ZAalloys; Zamak; ZA-73; zinc; zinc-aluminum alloysSUMMARY OF CHANGESCommittee B02 has identified the location of selected changes to this standard since the last issue(B952/B952M 12)

29、 13) that may impact the use of this standard. (Approved FebruaryOctober 1, 2013.)2014.)(1) UNS numbers were added.Added color codes to Table 1.(2) Added footnote C for ZA-73 in Table 1.(3) Corrected magnesium range for Alloy SC-F.Committee B02 has identified the location of selected changes to this

30、 standard since the last issue(B952/B952M 10) that may impact the use of this standard. (Approved May 1, 2012.)(1) Revisions have been made to Sections 2, 4, 6, 7, 8, 9, 10, and 11 to reference Specification B949 and delete certain portionsof these sections formerly a part of this standard.(2) The t

31、itles of Sections 7 and 9 have been revised to be in agreement with a standard format for Subcommittee B02.04 standards.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are express

32、ly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,

33、either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may atte

34、nd. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. I

35、ndividual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 143