ASTM C1186-2007 Standard Specification for Flat Non-Asbestos Fiber-Cement Sheets《平面无石棉的纤维水泥薄板的标准规范》.pdf

1、Designation: C 1186 07Standard Specification forFlat Non-Asbestos Fiber-Cement Sheets1This standard is issued under the fixed designation C 1186; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number i

2、n parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers either untextured or surfacetextured non-asbestos fiber-cement flat sheets intended forexterior applications such as

3、 claddings, facades, curtain walls,soffits, and so forth.1.2 This specification is not applicable to asbestos-cementflat sheets (Specification C 220), gypsum-based boards (Speci-fications C 1396/C 1396M, C 1177/C 1177M, C 1178/C 1178M), or particle boards (Terminology D 1554) discretenon-asbestos fi

4、ber-cement interior substrate sheets (Specifica-tion C 1288), fiber-mat reinforced non-asbestos cement interiorsubstrate sheets (Specification C 1325), or cement-bondedparticleboards (Specification BS 5669: Part 4) and (ISO 8335).1.3 The values stated in inch-pound units are to be regardedas the sta

5、ndard. The values given in parentheses are providedfor information only.1.4 The text of this standard references notes and footnoteswhich provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be consideredas requirements of the standard.2. Reference

6、d Documents2.1 ASTM Standards:2C 220 Specification for Flat Asbestos-Cement SheetsC 1154 Terminology for Non-Asbestos Fiber-ReinforcedCement ProductsC 1177/C 1177M Specification for Glass Mat Gypsum Sub-strate for Use as SheathingC 1178/C 1178M Specification for Coated Glass MatWater-Resistant Gypsu

7、m Backing PanelC 1185 Test Methods for Sampling and Testing Non-Asbestos Fiber-Cement Flat Sheet, Roofing and SidingShingles, and ClapboardsC 1288 Specification for Discrete Non-Asbestos Fiber-Cement Interior Substrate SheetsC 1325 Specification for Non-Asbestos Fiber-Mat Rein-forced Cement Substrat

8、e SheetsC 1396/C 1396M Specification for Gypsum BoardD 1554 Terminology Relating to Wood-Base Fiber andParticle Panel MaterialsE84 Test Method for Surface Burning Characteristics ofBuilding Materials2.2 British Standards:3BS 5669: Part 4 Specification for Cement Bonded Particle-board2.3 Internationa

9、l Standards:3ISO 8335 Cement-bonded ParticleboardsBoards of Port-land or Equivalent Cement Reinforced with Fibrous WoodParticles3. Terminology3.1 DefinitionsRefer to Terminology C 1154.4. Classification4.1 Flat sheets covered by this specification are divided intotwo types, according to their intend

10、ed application.4.2 Type ASheets are intended for exterior applications,subjected to the direct action of sun, rain, or snow. They aresupplied coated or uncoated.4.3 Type BSheets are intended for exterior applications,not subjected to the direct action of sun, rain, or snow.NOTE 1If sheets of Type B

11、are used in an exterior application, wherethey are directly exposed to the weather, but are protected by impregnationor coatings, the weather resistance of the product may be altered by thequality of the protection. Specification of this protection, as well as themethod for control and test, are out

12、side the scope of this specification.4.4 The sheets are further classified into four grades accord-ing to their flexural strengths. The manufacturer shall declarethe type and grade of a given product in the literature for thatproduct.5. Composition and Manufacture5.1 CompositionThis specification is

13、 applicable to fiber-reinforced cement flat sheets consisting essentially of an1This specification is under the jurisdiction of ASTM Committee C17 onFiber-Reinforced Cement Products and is the direct responsibility of SubcommitteeC17.02 on Non-Asbestos Fiber Cement Products.Current edition approved

14、June 1, 2007. Published June 2007. Originallyapproved in 1991. Last previous edition approved in 2002 as C 1186 02.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to t

15、he standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.inor

16、ganic hydraulic binder or a calcium silicate binder formedby the chemical reaction of a siliceous material and a calcar-eous material reinforced by organic fibers, inorganic non-asbestos fibers, or both. Process aids, fillers, and pigments thatare compatible with fiber-reinforced cement are not proh

17、ibitedfrom being added.5.2 ManufactureThese products are formed either with orwithout pressure and cured, either under natural or acceleratedconditions, to meet the physical requirements of this specifi-cation.6. Mechanical and Physical Requirements6.1 Mechanical and physical properties shall be det

18、erminedon uncoated product wherever practical. Where products aresupplied coated, this material shall also be tested with theresults identified as applying to coated material.6.1.1 Sampling and inspection for mechanical and physicalproperties shall be conducted in accordance with Test MethodC 1185.6

19、.2 Mechanical Requirements:6.2.1 Flexural StrengthWhen tested in accordance withTest Method C 1185, the flexural strength shall not be less thanthe corresponding value for the appropriate grade in Table 1.Where manufacturers state minimum product strength, thisshall be at the 4 % acceptable quality

20、level (AQL) as are thevalues of Table 1.6.2.2 Type A sheets for exterior applications shall be testedand specified in both the wet and equilibrium conditions. TypeA sheets shall meet the minimum wet and minimum equilib-rium flexural strength requirements for the appropriate gradespecified in Table 1

21、. In addition, the average wet flexuralstrength of the sample shall not be less than 50 % of the meanequilibrium strength of the sample.6.2.3 Type B sheets shall be specified and tested in theequilibrium condition only.NOTE 2When sampling from continuous production, these tests maybe conducted on dr

22、y, equilibrium, or saturated specimens, provided arelationship can be established between this testing and the specifiedvalues.6.3 Physical Requirements:6.3.1 DensityNominal values and tolerances for densityshall be stated by the manufacturer for each product. Whentested in accordance with the metho

23、d specified in Test MethodC 1185, the value for density shall comply with the value statedby the manufacturer.7. Dimensions and Tolerances7.1 Method of MeasurementThe method of measurementshall be in accordance with Test Method C 1185.7.2 Nominal Length and WidthFiber-cement sheets aretypically supp

24、lied in nominal lengths of 96 in. (2438 mm), 120in. (3048 mm) and nominal width of 48 in. (1219 mm). Greateror lesser nominal lengths and widths are not prohibited frombeing supplied.7.3 Nominal ThicknessFiber-cement sheets are normallyavailable in thickness of18 in. (3.5 mm) to 1 in. (25 mm),althou

25、gh thickness outside of this range is not prohibited frombeing supplied. Refer to Table 2.7.4 Length and Width ToleranceThe tolerance from thenominal shall be 60.5 % with a maximum variation of 614 in.(6 mm). A tolerance of 618 in. is acceptable for dimensionsless than 24 in. (609 mm).7.5 Thickness

26、ToleranceThe maximum difference be-tween extreme values of the thickness measurement within asheet shall not exceed 15 % of the maximum measured value.Thickness variation from sheet to sheet shall not exceed thetolerances shown in Table 2.7.6 Squareness ToleranceThe length of the diagonalsshall not

27、vary by more than132 in./ft (2.6 mm/m) of the lengthof the sheet. Opposite sides of the sheet shall not vary in lengthby more than132 in./ft (2.6 mm/m).7.7 Edge Straightness ToleranceThe sheet edges shall bestraight within132 in./ft (2.6 mm/m) of length or width.8. Workmanship, Finish, and Appearanc

28、e8.1 WorkmanshipSheets shall have a commercially uni-form surface on one side, and be free of major defects that willimpair appearance, erection, use, or serviceability.8.2 FinishThe surface of the sheet to be exposed shall besmooth, granular, or otherwise textured.8.3 ColorThe surface of the sheet

29、shall be the naturalcolor of the product or colored by the addition of mineralpigments, chemical impregnation, pigmented coating, veneer,or embedded mineral granules.9. Inspection9.1 Inspection of material shall be made at the point ofshipment. The inspector representing the purchaser shall havefree

30、 access to the carriers being loaded for shipment to thepurchaser. The purchaser shall be afforded all reasonable andavailable facilities at the point of shipment for sampling andinspection of the material, which shall be conducted as not tointerfere unnecessarily with the loading of the carriers.9.

31、2 Third party certification, either continuous or at regularintervals, shall be recognized as an alternative to batch inspec-tion.10. Rejection10.1 If the sampling fails to conform to any one of therequirements of this specification, a second sample from theTABLE 1 Flexural Strength RequirementsNOTE

32、The values of Table 1 are lower limit values based on anacceptable quality level (AQL) of 4 % at a 90 % confidence level.GradeWet Strength, psi (MPa)minEquilibrium Strength, psi (MPa)minI 580 (4) 580 (4)II 1015 (7) 1450 (10)III 1885 (13) 2320 (16)IV 2610 (18) 3190 (22)TABLE 2 Thickness RequirementsN

33、ominal Thickness, in.(mm)Tolerance, in.(mm)18 316 (3.55) 60.02 (0.5)316 38 (510) 60.04 (1.0)38 58 (1016) 60.05 (1.3)58 34 (1620) 60.06 (1.5)34 (20) 610 % thicknessC1186072same lot shall be prepared and tested. The results of the retestshall be combined with the results of the original test, accord-i

34、ng to the sampling procedure, to determine compliance withthis specification.10.2 Failure to conform to any one of the requirements ofthis specification, upon retest as prescribed above, shall con-stitute grounds for rejection.11. Product Marking11.1 IdentificationProduct marking shall include trade

35、-mark or other means of identification that ensures that themanufacturer and product category can be identified. Themethod of marking shall be stated in the manufacturerscatalog.12. Packaging and Storage12.1 Commercial PackagingFlat sheets shall be soshipped as to ensure acceptance by common carrier

36、. There is nostandard package. The material is usually in bulk or cratedwhen so specified by the purchaser.12.2 StorageFlat sheets must be piled on sufficient firmsupports that will keep the sheets level and flat. The sheetsmust be piled with the edges square and flush and covered toprovide protecti

37、on from the weather until used.13. Keywords13.1 air cured; appearance; autoclaved cured; cellulosefiber; density; edge straightness; exterior application; finish;flexural strength; frost resistance; heat/rain resistance; inspec-tion; length and width tolerance; mechanical properties; mini-mum equili

38、brium strength; minimum wet strength; moisturecontent; moisture movement; nominal length; nominal thick-ness; nominal width; non-asbestos fiber; packaging; physicalproperties; polyethylene fiber; polyvinyl alcohol fiber; pressurecured; rejection; sampling; sheet grading; shipping; squarenesstoleranc

39、e; storage; supplementary requirements; supplemen-tary tests; surface burning characteristics; thickness require-ments; thickness tolerance; third party certification; tolerance;Type A; Type B; type tests; warm water resistance; waterabsorption; water tightness; workmanshipSUPPLEMENTARY REQUIREMENTS

40、S1. Supplementary requirements for Type A and B sheetsshall consist of once only supplementary test, with the manu-facturers statement of results provided upon customers re-quest. Fundamental changes in formulation or methods ofmanufacture, or both, shall require the subsequent retesting ofthe suppl

41、ementary tests.S1.1 The following supplementary tests shall be requiredfor Type A and B sheets:Supplementary Test Type A Type BMoisture Movement yes yesWater Absorption yes yesMoisture Content yes yesWater Tightness yes noSurface Burning Characteristics yes yesFrost Resistance yes noWarm Water Resis

42、tance yes noHeat/Rain Resistance yes noS1.2 Supplementary requirements shall be determined onuncoated product wherever practical. Where products aresupplied coated, this material shall also be tested with theresults identified as applying to coated material.S2. Moisture MovementThe linear variation

43、with changein moisture content shall be stated as the percentage change inlength based on a relative humidity change from 30 to 90 % inaccordance with Test Method C 1185.S3. Water AbsorptionCalculate the amount of water ab-sorbed from the increase in weight of the dried specimenduring submersion for

44、 a period of 48 h. Express the waterabsorptions as the percentage by weight when tested inaccordance with Test Method C 1185.S4. Moisture ContentState the percentage of moisturecontent of the fiber-cement sheet when conditioned at 50 65 % relative humidity and a temperature of 73 6 4F (23 62C) in ac

45、cordance with Test Method C 1185.S5. Water TightnessThe specimens, when tested in accor-dance with Test Method C 1185, are not prohibited fromshowing traces of moisture on the underside of the sheet, but inno instance shall there be any formation of drops of water.S6. Surface Burning Characteristics

46、Fiber cement sheetsof14 in. (6 mm) shall have a reported flame spread index of0 and a smoke developed index of not more than 5, when testedin accordance with Test Method E84. Sheets of thicknessgreater than14 in. (6 mm) shall meet this specification or shallbe formed at14 in. (6 mm) thickness with t

47、he sameformulation for test purposes.S7. Frost Resistance (Freeze/Thaw)The specimens, whentested in accordance with Test Method C 1185 (Section 12 onFreeze/ThawCladding Products), for 50 cycles, shall notshow visible cracks or structural alteration such as to affecttheir performance in use. The rati

48、o of retained strength ascalculated from the test results shall be at least 80 %.S8. Warm Water ResistanceThe specimens, when testedin accordance with Test Method C 1185, shall not show visiblecracks or structural alteration, such as to affect their perfor-mance in use. The ratio of strengths as cal

49、culated from testresults shall be reported.S9. Heat/Rain ResistanceThe specimens, when tested inaccordance with Test Method C 1185 (Section 14 on Heat/RainWall Structures), for 25 cycles, shall not show visiblecracks or structural alteration of the sheets and frame assemblysuch as to affect their performance in use.C1186073ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that det