1、Designation: C 1247 09Standard Test Method forDurability of Sealants Exposed to Continuous Immersion inLiquids1This standard is issued under the fixed designation C 1247; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of
2、last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers a laboratory procedure thatassists in determining the durability of a sealant and itsadhesion
3、to a substrate while continuously immersed in aliquid. This test method tests the influence of a liquid on thesealant and its adhesion to a substrate. It does not test the addedinfluence of constant stress from hydrostatic pressure that isoften present with sealants used in submerged and below-grade
4、applications, nor does it test the added influence of stress fromjoint movement while immersed. This test method also doesnot (in its standard form) test the added influence of acids orcaustics or other materials that may be in the liquid, in manyapplications.1.2 The values stated in SI units are to
5、 be regarded as thestandard. The inch-pound given in parentheses are provided forinformation only.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health
6、 practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C33 Specification for Concrete AggregatesC 109/C 109M Test Method for Compressive Strength ofHydraulic Cement Mortars (Using 2-in. or 50-mm CubeSpecimens)C 150 Specification
7、for Portland CementC 717 Terminology of Building Seals and SealantsC 719 Test Method for Adhesion and Cohesion of Elasto-meric Joint Sealants Under Cyclic Movement (HockmanCycle)2.2 ISO StandardsISO 13638 Building Construction-Sealants-Determinationof Resistance of Prolonged Exposure to Water33. Ter
8、minology3.1 Definitions:3.1.1 Definitions of the following terms used in this testmethod are found in Terminology C 717: adhesive failure;cohesive failure; compound; cure; hydrostatic pressure; joints;primer; sealant; self-leveling sealant ; and substrate.4. Summary of Test Method4.1 Specimens are p
9、repared and the sealant is cured. Thespecimens are immersed in a hot liquid at 50 6 2C (122 63.6F) for six weeks. At the end of the six weeks, thespecimens are placed into a compression/extension machine, asdescribed in Test Method C 719, and cycled through themovement range appropriate to the test
10、sealant or its applica-tion, or both.4.2 If after three movement cycles at 3.2 mm/h (18 in./h)adhesive or cohesive failure is not noted, the specimens areagain placed in the hot liquid for an additional four weeks andthen retested.4.3 This test method consists of six weeks of immersionfollowed by th
11、ree extension and compression cycles. This canbe followed by four weeks of further immersion and a repeat ofthe three extension and compression cycles. The four weeks ofimmersion and subsequent extension and compression testingcan be repeated as many times as required for the application.5. Signific
12、ance and Use5.1 This test method uses elevated temperature to acceleratethe degradation of a sealant and its adhesion to a substrate. Thistest method is an accelerated method and will only be apredictor of long-term durability if the actual service tempera-ture is significantly lower than the elevat
13、ed test temperature.5.2 This test method can be used as an indicator of longevitybut direct correlation to actual use will be difficult for manyapplications.5.3 The correlation of data from this test method to appli-cations where the sealant joint will have wet and dry cycles1This test method is und
14、er the jurisdiction ofASTM Committee C24 on BuildingSeals and Sealants and is the direct responsibility of Subcommittee C24.30 onAdhesion.Current edition approved Jan. 1, 2009. Published February 2009. Originallyapproved in 1993. Last previous edition approved in 2004 as C 124798(2004).2For referenc
15、ed ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute, 11 W. 42nd Street,
16、13thFloor, New York, NY 10036.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.will be difficult since, with some sealants on some substrates,adhesion that is lost during wet periods is regained during dryperiods.5.4 This test method
17、is performed in a hot liquid and may beconsidered an acceleration of deterioration of the sealant or thesealants adhesion to a substrate. Compared to how the sealantwill be used in some applications, in some cases, this test maybe less severe than the actual application. The benefit from theuse of t
18、his test method will depend on the comparison of theconditions of this test to the actual conditions of use (tempera-ture, duration, nature of substrate, composition of the liquid).5.5 To determine the ability of a sealant to perform in agiven application; modification of this procedure will often b
19、erequired and is permissible, as mutually agreed upon bypurchaser and seller.6. Apparatus6.1 Water Bath, equipped with a heater to maintain the testbath at 50 6 2C (122 6 3.6F).6.2 Compression/Extension Machine,4designed to auto-matically compress the joint width of the test specimen from 12mm (12 i
20、n.) to the maximum extension desired at a constantrate of 3.2 mm/h (18 in./h). The machine shall be equipped withgrips of sufficient strength to withstand, without bending, theresistance of high-tensile-strength sealants.6.3 “C” Clamps, or other devices for specimen preparation.6.4 Casting Spacers,
21、for specimen preparation.6.5 Liquid, appropriate to the application for the test bath.NOTE 1The precision and bias statement for this test method is basedon the use of distilled water for the test bath.7. Test Specimens7.1 Standard substrates for this test method shall be portlandcement mortar and a
22、luminum alloy.NOTE 2The precision and bias statement of this test method is basedon standard substrates of mortar and aluminum. When requested, only oneor two of the standard substrates may be tested with the sealant. Likewise,other substrates such as brick, marble, etc., may be specified by thepurc
23、haser in place of or in addition to the standard substrates for test withthe sealant sample.7.1.1 Mortar Block5Prepare cement mortar blocks, each75 by 25 by 25 mm (3 by 1 by 1 in.) in size, using one part ofhigh early strength portland cement conforming to Type III ofSpecification C 150, to two part
24、s by weight of clean uniformlygraded, concrete fine aggregate (sand) conforming to Specifi-cation C33. Use sufficient water to produce a flow of 100 6 5when tested in accordance with the procedure for the determi-nation of consistency of cement mortar described in TestMethod C 109. After curing one
25、day in moist air and six daysin saturated lime water at 23 6 2C (73 6 3.6F), prepare thesurface of one face, 25 by 76 mm (1 by 3 in.) of each block bywet grinding either with a belt sander using No. 60 aluminumcarbide sanding belt or using an iron lap with No. 60 siliconcarbide (or aluminum oxide) g
26、rain, until the aggregate isuniformly exposed. Return blocks to saturated lime waterstorage until needed.7.1.2 Blocks may be prepared and shipped to other locationsfor use. The blocks may be shipped dry and returned to limewater storage on arrival until needed.7.1.3 Prior to use, wet grind the previ
27、ously ground face toremove any laitance, rinse thoroughly under running tap waterand dry the blocks overnight at 105 to 110C (220 to 230F).Clean the blocks of film or powder by vigorous brushing witha stiff-bristled fiber brush. Condition the blocks at standardconditions for not less than one nor mo
28、re than seven days.7.1.4 AluminumThe aluminum plates shall be 75 by 25 by6mm(3by1by14 in.) aluminum alloy, 6063-T5 or 6061-T6with anodizing process AA-MIOC22A31. Prior to use cleanthe aluminum by wiping the surface with methyl ethyl ketoneor similar solvent. Then dip the surface in a detergent solut
29、ion.This should be a 0.04 % solution of alcohol ethoxy sulfate. Analternative would be a 0.1 % solution of a clear hand dishwash-ing detergent. These solutions should be made up in distilledwater. Rinse the surface (without touching it) in distilled waterand allow it to air dry.NOTE 3Methyl ethyl ke
30、tone and similar solvents are both toxic andflammable and should be handled with caution in a well-ventilated hood.NOTE 4At the request of the sealant producer, the detergent cleaningstep shall be omitted.7.2 PrimersWhere the use of a primer(s) is recommendedby the sealant manufacturer, prime substr
31、ate materials with therecommended primer or primers.7.3 Preparation of Test Specimens:7.3.1 Standard conditions of temperature and relative hu-midity for this test method are defined as 23 6 2C (73.4 63.6F) and 50 6 5 % respectively.7.3.2 Multicomponent SealantsPrepare three test speci-mens for each
32、 substrate that is to be used in the test. Aftermaintaining the unopened sample for at least 24 h at standardconditions, mix thoroughly for 5 min at least 250 g of basecompound with the appropriate amount of curing agent. Applya bead of sealant 12 by 12 by 50 mm (12 by12 by 2 in.)between parallel 25
33、 by 76 mm (1 by 3 in.) faces of similarblocks or plates (see Fig. 1). Use appropriate casting spacer toform the proper size sealant bead. Use non-adhering castingspacers or apply polyethylene adhesive tape or any othersuitable inert release agent to the inside surface of the spacersto prevent adhesi
34、on of the spacers to the sealant after cure. Useadhesive tape, rubber bands, or clamps to hold the testassembly together before and after filling it with the sealant.For self-leveling sealants, use masking or any other suitabletape to retain the sealant.7.3.3 Single-Component SealantsPrepare three t
35、est speci-mens as described in 7.3.2 except that no mixing of compo-nents is required. Condition the sealed sealant cartridge or bulkcontainer at standard conditions at least 24 h before use.8. Conditioning8.1 Cure specimens made with multicomponent sealants for14 days at standard conditions. During
36、 the second week of the4Series 520 Sealing Compound Tester, manufactured by Applied Test Systems,Inc., 348 New Castle Road, Butler, PA 16001 has been found suitable for thispurpose.5Prepared concrete blocks are available from Masonry Test Block Company,6389 Lawdale Road, Saginaw, MI 48604.C1247092cu
37、ring period, make attempts to free the sealant from thecasting spacers at the ends and bottom without damaging thesealant bead.8.2 Cure specimens made with single-component sealantsfor a total of 21 days as follows: (a) seven days at standardconditions; (b) seven days at 37.8 6 2C (100 6 3.6F) and 9
38、56 5 % relative humidity; and (c) seven days at standardconditions. Separate the casting spacers from the sealant assoon as practical during the curing period without damagingthe sealant.9. Procedure9.1 Remove the spacers and place the cured test specimensinto the 506 2C (122 6 3.6F) test bath, tota
39、lly immersingthem and maintaining them at this condition for six weeks. Usea 3.8 L(1 gal) size container containing 1.9 L(2 qt) of test bath.Mortar and aluminum specimens should be separated andconditioned in separate containers.9.2 After six weeks immersion, remove the specimens fromthe test bath,
40、place them immediately into the compression andextension machine and start cycling with the compressionmode, using the movement range appropriate to the test sealantor its application, or both. The test is to be conducted atstandard conditions.9.3 Cycle the specimens through three compression andthr
41、ee extension cycles.9.4 Remove the specimens, hand flex the specimens tocheck sealant adhesion by rotating them 60, and examinethem for adhesive or cohesive failure. Measure the amount ofadhesive or cohesive failure in square millimetres (squareinches) and record these results on the report form. No
42、te alsoany apparent swelling or change in appearance or contour ofthe sealant.9.5 Return the specimens to the 50 6 2C (1226 3.6F) testbath for four weeks. After immersion, remove the specimensfrom the test bath. Place them immediately into the compres-sion and extension machine and start cycling wit
43、h the com-pression mode.9.6 Repeat 9.3 and 9.4. If there is not total adhesive orcohesive failure and, if required for the application, repeat9.5,9.3, and 9.4 in that order.10. Report10.1 Report the test results and observations on the formshown in Fig. 2. Report total square millimetres (square inc
44、hes)of adhesion and cohesive failure for all three samples of eachsubstrate tested.10.2 Report the following additional information:10.2.1 Techniques used in substrate preparation includingthe solvent, primers, or other materials used for cleaning. Ifother than the standard substrates or different p
45、reparationtechniques are used, describe them completely,10.2.2 Other pertinent observations on the condition of thesealant or its adhesion or other characteristics, and10.2.3 Any variation in test procedure or cure cycle used.11. Precision and Bias611.1 Polyurethane Sealant, Six and Ten Weeks of Wat
46、erImmersion on Aluminum and Concrete Substrates:11.1.1 Repeatability I(r)The repeatability (within a givenlaboratory) interval for four test parameters tested by fourlaboratories is 0.0 mm2(0.0 in.2). In future use of this testmethod, the difference between two test results obtained in thesame labor
47、atory on the same material will be expected toexceed 0.0 mm2(0.0 in.2) only about 5 % of the time.11.1.2 Reproducibility I(R)The reproducibility (betweengiven laboratories) interval for four test parameters tested byfour laboratories is 0.0 mm2(0.0 in.2). In future use of this testmethod, the differ
48、ence between two test results obtained in adifferent laboratory on the same material will be expected toexceed 0.0 mm2(0.0 in.2) only about 5 % of the time.11.2 Polysulfide Sealant, Six and Ten Weeks of WaterImmersion on Aluminum and Concrete Substrates:11.2.1 Repeatability I(r)The repeatability (wi
49、thin a givenlaboratory) interval for four test parameters tested by four6Supporting data have been filed at ASTM Headquarters. Request RR: C24-1043.FIG. 1 Test SpecimenC1247093laboratories is 26.5 cm2(4.1 in.2). In future use of this testmethod, the difference between two test results obtained in thesame laboratory on the same material will be expected toexceed 26.5 cm2only about 5 % of the time.11.2.2 Reproducibility I(R)The reproducibility (betweengiven laboratories) interval for four test parameters tested byfour laboratories is 43.9 cm2(6.8