ASTM C1443-1999(2010) Standard Specification for Glasses Portlight Circular Fully Tempered《完全回火的环形港口灯玻璃的标准规范》.pdf

1、Designation: C1443 99 (Reapproved 2010)Standard Specification forGlasses, Portlight, Circular, Fully Tempered1This standard is issued under the fixed designation C1443; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of la

2、st revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the requirements for circular,fully tempered, high clarity, flat glasses used for portlightapp

3、lications.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 The following safety hazard caveat pertains only to thetest method port

4、ion, Section 11, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-t

5、ions prior to use.2. Referenced Documents2.1 ASTM Standards:2C162 Terminology of Glass and Glass ProductsC1036 Specification for Flat GlassC1048 Specification for Heat-Treated Flat GlassKind HS,Kind FT Coated and Uncoated GlassC1279 Test Method for Non-Destructive Photoelastic Mea-surement of Edge a

6、nd Surface Stresses in Annealed,Heat-Strengthened, and Fully Tempered Flat Glass2.2 ANSI Standard:ANSI Z1.4 Sampling Procedures and Tables for Inspectionby Attributes (DOD Adopted)33. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology C162 and also S

7、pecificationsC1036 and C1048 and Test Method C1279.4. Classification4.1 Glasses covered by this specification shall be of thefollowing types, as specified (see 5.1):4.1.1 Type 1Plain edges, both faces polished,4.1.2 Type IIPlain edge, one face polished, opposite facefrosted,4.1.3 Type IIIRabbeted ed

8、ge, both faces polished, or4.1.4 Type IVRabbeted edge, one face polished, oppositeface frosted.5. Ordering Information5.1 Purchasers should select the preferred options permittedin this specification, and include the following information inprocurement documents:5.1.1 Title, number, and date of this

9、 specification,5.1.2 Type of portlight glasses, as requested (see 4.1),5.1.3 Dimensions of portlight glasses (see 8.1 and 9.3), and5.1.4 Type, class, and quality of glass (see SpecificationC1036) and heat treatment (see Specification C1048).5.2 SamplesIf samples are to be supplied with bids, theysho

10、uld be specifically requested in the invitation for bids andthe particular purpose to be served by the bid sample should beclearly stated.6. Materials and Manufacture6.1 MaterialThe glass used shall be glazing quality, floatglass in accordance with the requirements for SpecificationC1036, Type I, Cl

11、ass 1, quality q3or higher, if required, andheat-treated Specification C1048, kind FT.6.2 MarkingSpecimens shall exhibit the words “fullytempered” approximately12 in. (12.7 mm) from the edge bymeans of etching or sand blasting. Marking shall be donebefore heat treating.7. Other Requirements7.1 Break

12、ing StrengthGlasses shall exhibit satisfactoryresistance to breakage (see 11.1.2.1).7.2 Surface and Edge CompressionType I and III glassesshall have a surface compression of not less than 10 000 psi oran edge compression of not less than 9700 psi (see 11.1.1.2).7.3 ClarityWhen glasses are tested (se

13、e 11.1.2.3), blackand white lines of the clarity target shall be definitely distin-guishable for all parts of the critical area.1This specification is under the jurisdiction of ASTM CommitteeC14 on Glassand Glass Products and is the direct responsibility of Subcommittee C14.08 on FlatGlass.Current e

14、dition approved March 1, 2010. Published March 2010. Originallyapproved in 1999. Last previous edition approved in 2005 as C144399(2005). DOI:10.1520/C1443-99R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book

15、of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West C

16、onshohocken, PA 19428-2959, United States.7.4 WarpageGlasses shall not exhibit more than132 in.(0.8 mm) warpage along any line on either face (see 11.1.2.3).8. Dimensions8.1 The dimensions of the specimens shall be as specified in5.1. The thickness of a circular glass specimen shall not varymore tha

17、n132 in. (0.8 mm) between any two points on itsperiphery. Dimensional tolerances for circular cut glasses shallnot exceed values specified in Table 1 and Specification C1036.9. Finish and Appearance9.1 FinishGlasses shall be finished by grinding to thetolerances specified in 8.1. Edges shall be grou

18、nd, with cornerschamfered116 in. (1.6 mm).9.2 Types II and IVThe designated faces of the glassesshall be uniformly frosted by sand blasting or etching.9.3 Types III and IVThe edges of the glasses shall berabbeted. The depth of the rabbet in the horizontal directionand in the vertical direction shall

19、 be specified by the purchaser(see 5.1.3). Depth dimensions for the rabbet shall be accurateto within132 in. (0.8 mm) when measured from the edge andfrom the face of the glass. One edge of the rabbet shall beperpendicular to the face of the glass and the other edge of therabbet shall be perpendicula

20、r to the edge of the glass such thatthe angle formed by the faces of the rabbet is 90 6 2.10. Sampling10.1 Inspection LotFor purposes of inspection, a lot shallconsist of not more than 1000 specimens which shall be of asingle thickness, produced in a single plant and offered fordelivery at one time.

21、10.1.1 Sampling for Visual and DimensionalExaminationsSamples shall be selected in accordance withthe procedures of ANSI Z1.4 at inspection Level II for exami-nation in accordance with 11.1.1.1.10.1.2 Sampling for Surface and Edge StressSamplesshall be selected at random in accordance with Table 2 f

22、orexamination in accordance with 11.1.1.2. When a lot containsfewer than seven glasses, or when a special use (see 5.1)requires protection against defects, the sample shall consist ofall specimens in the lot. Where the lot consists of between 7and 50 glasses, the sample shall consist of 6 specimens.

23、 Wherethe lot consists of between 51 and 100 glasses, the sample shallconsist of 14 specimens. Lots containing more than 100 glassesshall be evaluated by means of a sample of 10 specimens.Samples from lots consisting of more than 6 glasses shallcontain a representative variety of types and diameters

24、.10.1.3 Sampling for TestSampling for all tests to beperformed on specimens shall be in accordance with 10.1.2.11. Inspection, Acceptance and Rejection11.1 ResponsibilityThe supplier is responsible for inspec-tion of cut specimens unless otherwise specified in the contractor purchase order. Two form

25、s of inspection are required:examination and test.11.1.1 ExaminationInspection by examination shall con-sist of determining compliance with visual and dimensionalrequirements.11.1.1.1 Visual and Dimensional ExaminationsAll speci-mens of a sample size selected in accordance with 10.1.1 shallbe examin

26、ed to verify conformance to all of the requirementswhich do not involve tests or polariscopic examination. The lotshall be accepted if all of the specimens in the sample (see10.1.1) conform to visual requirements of Section 6.2 andSection 9 and dimensional requirements of Section 8. The lotshall be

27、rejected if any of the specimens in the sample fail toconform to these requirements. If the lot is rejected on the basisof visual and dimensional examination, the supplier may at hisoption examine all remaining specimens of the lot to determineconformance with visual and dimensional requirements. An

28、yof the specimens of the lot that comply with the visual anddimensional requirements shall be considered acceptable, sub-ject to conformance with polariscopic examination require-ments and test requirements.11.1.1.2 Surface and Edge Stresses, (Type I and Type IIIGlasses)All specimens of a sample siz

29、e selected in accor-dance with 10.1.2 shall be subjected to surface or edge stressexamination (see 7.2) to determine if they are fully tempered.It is suggested that Type III glasses be tested for surface stress.Test Method C1279 is recommended for testing edge andsurface stresses. If any glass speci

30、men from a sample under-going surface and edge stress examination does not meet therequired values (see 7.2), the lot shall be rejected in accordancewith criteria given in Table 2.11.1.2 Test Acceptance or RejectionInspection by testshall consist of load, clarity, and warpage tests.11.1.2.1 Load Tes

31、tAll specimens of a sample size selectedin accordance with 10.1.3 shall be tested under a load appliedwithout shock using the jig illustrated in Fig. 1. Each of thespecimens shall be placed centrally between the upper andlower steel beams which should be perpendicular as shown inTABLE 1 Permitted To

32、lerancesDimension Tolerance, 6 in. (6 mm)Diameter116 (1.6)Depth of rabbet132 (0.8)TABLE 2 Sampling for Surface and Edge Stress Examinationand TestsLot SizeSampleSizeAllowable Number ofFailures for Surface andEdge Stress ExaminationAllowable Number ofFailures for Tests (Load,Clarity, Warpage)1-6 all

33、none none7-50.51-1006.14noneloadAclarity: noneBwarpage: noneC101-1000 10 noneloadAclarity: noneBwarpage: noneCASee 11.1.2.1.BSupplier may, at his option, test all remaining glasses in the lot for clarity inaccordance with 11.1.2.2 and all glasses that pass shall be considered acceptable.CSupplier ma

34、y, at his option, test all remaining glasses in the lot for warpage inaccordance with 11.1.2.3 and all glasses that pass shall be considered acceptable.C1443 99 (2010)2side and end views, respectively. The steel bearings supportingthe specimen shall be spaced on Dimension A so that thespecimen has a

35、 clearance of116 in. (1.6 mm) at either side.Each bearing shall have a leather insert approximately18 in.(3.2 mm) thick over the entire surface between steel and glass.Type III and IV specimens shall be tested with the largediameter down, and the bearings against the bottom face shallextend approxim

36、ately12 in. (12.7 mm) within the circle of thesmaller diameter. The rate of loading shall be 0.1 6 0.0005 in.(2.54 6 0.0127 mm) per min. When all specimens in a lot areto be tested, each specimen shall be loaded to the value shownin Table 3. (Other values may be obtained, if needed, by linearinterpo

37、lation between the nearest values shown in the table.)Specimens not damaged shall be accepted. Each specimen inthe sample size selected in accordance with 10.1.3 shall be loadtested to the corresponding value shown in Table 3.Ifnospecimen breaks, the lot shall be accepted. If one of thespecimens bre

38、aks the entire lot shall be load tested by themethod specified above and specimens not damaged by thattest will be accepted. Lots containing more than 100 specimensshall be evaluated by testing a sample of 10 specimens selectedin accordance with 10.1.3. The sample shall be evaluated bydetermining wh

39、ether the breaking load of each specimen in thesample falls above or below the corresponding values shown inTable 4. (Other values may be obtained, if needed, by linearinterpolation between the nearest values shown in the table.) Ifthe breaking loads of the specimens are greater than or equal tothe

40、specified value, the lot shall be accepted. If the breakingload of the specimens is less than the specified value, the lotshall be rejected, but the manufacturer shall have the option oftesting such sample of the lot by the method specified aboveand samples not damaged in that test shall be accepted

41、.Appendix X1 provides rationale for proof load testing.11.1.2.2 Clarity Test (Type I and Type III Glasses)Allspecimens of a sample selected in accordance with 10.1.3 shallbe tested for clarity. The deterioration of the clarity of targetlines due to placing the sample in a light path shall be observe

42、dthrough a suitable telescope. The target shall consist of two setsFIG. 1 Load Apparatus (see 11.1.2.1)TABLE 3 Load When All Samples in a Lot Are to be TestedDiameterLoad, lb (kg) for Given Thickness, in. (mm)14 (6.4)38 (9.5)12 (12.7)58 (15.9)34 (19.1)78 (22.2) 1 (25.4) 114 (31.8)6 (152.4) 790 (358.

43、3) 1720 (780.2) 2980 (1351.7) 4570 (613.1) 6480 (2939.3) 8690 (3941.7) 11 220 (5089.3) 17 190 (7797.3)812 (215.9) 710 (322.1) 1550 (703.1) 2690 (1220.2) 4120 (553.5) 5840 (2649.0) 7830 (3551.6) 10 110 (4585.8) 15 490 (7026.1)1212 (317.5) 600 (272.2) 1310 (594.2) 2280 (1034.2) 3490 (469.1) 4940 (2240

44、.7) 6640 (3011.9) 8570 (3887.3) 13 120 (5951.1)16 (406.4) 520 (235.9) 1140 (517.1) 1970 (893.6) 3020 (405.3) 4280 (1941.4) 5740 (2603.6) 7410 (3361.1) 11 350 (5148.3)20 (508) 440 (199.6) 960 (435.4) 1670 (757.5) 2560 (343.6) 3620 (1642.0) 4860 (2204.5) 6270 (2844.0) 9610 (4359.0)2512 (647.7) 350 (15

45、8.8) 770 (349.3) 1330 (603.3) 2030 (273.6) 2880 (1306.3) 3870 (1755.4) 4990 (2263.4) 7650 (3470.0)C1443 99 (2010)3of alternating black and white lines of equal width oriented sothat the lines of the two sets are mutually perpendicular. Thetarget to telescope distance shall be at least 20 ft (6.1 m).

46、 Thetelescope shall have a magnifying power of at least 10X, andthe test aperture shall be $12 in. (12.7 mm) diameter. If thewidth of any of the lines is greater than 0.001 75 in. multipliedby the distance in feet between the target and the objective ofthe telescope, the lot shall be rejected in acc

47、ordance withcriteria given in Table 2. For example, if the distance betweenthe target and the objective of the telescope is 20.0 ft (6.10 m)the width of any line shall not exceed 0.035 in. (0.889 mm).The sample shall be held normal to the axis of the line of sightof the telescope, and shall be locat

48、ed immediately in front ofthe telescope objective. The sample shall be moved within theplane defined by the two parallel surfaces separated by thethickness of the glass so as to survey the critical area, coveringat least 30 % of this area. The critical area is the central portionof the glass, exclus

49、ive of a rim area which extends inward 1 in.(25.4 mm) from the edge for specimens not over 10 in. (254.0mm) diameter, and exclusive of areas which extend inward 112in. (38.1 mm) in any direction from tong marks, if tong marksare present.11.1.2.3 Warpage TestAll specimens of a sample selectedin accordance with 10.1.3 shall be tested for warpage. Theannular ring method shall be used to determine warpage. Thetesting apparatus shall consist of an upper and lower annularring, whose outside diameter shall exceed the diameter of theglass