ASTM C150 C150M-2016 Standard Specification for Portland Cement《硅酸盐水泥的标准规格》.pdf

1、Designation: C150/C150M 15C150/C150M 16Standard Specification forPortland Cement1This standard is issued under the fixed designation C150/C150M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A number in

2、 parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers ten types of portland cement, as follows (see Note 2):1.1.1 Type IFor use when the special properties specified for a

3、ny other type are not required.1.1.2 Type IAAir-entraining cement for the same uses as Type I, where air-entrainment is desired.1.1.3 Type IIFor general use, more especially when moderate sulfate resistance is desired.1.1.4 Type IIAAir-entraining cement for the same uses as Type II, where air-entrai

4、nment is desired.1.1.5 Type II(MH)For general use, more especially when moderate heat of hydration and moderate sulfate resistance aredesired.1.1.6 Type II(MH)AAir-entraining cement for the same uses as Type II(MH), where air-entrainment is desired.1.1.7 Type IIIFor use when high early strength is d

5、esired.1.1.8 Type IIIAAir-entraining cement for the same use as Type III, where air-entrainment is desired.1.1.9 Type IVFor use when a low heat of hydration is desired.1.1.10 Type VFor use when high sulfate resistance is desired.NOTE 1Some cements are designated with a combined type classification,

6、such as Type I/II, indicating that the cement meets the requirements ofthe indicated types and is being offered as suitable for use when either type is desired.NOTE 2Cement conforming to the requirements for all types are not carried in stock in some areas. In advance of specifying the use of cement

7、 otherthan Type I, determine whether the proposed type of cement is, or can be made, available.1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used in

8、dependently of the other. Combining values from thetwo systems may result in non-conformance with the standard. Values in SI units or inch-pound units shall be obtained bymeasurement in SI units or inch-pound units or by appropriate conversion, using the Rules for Conversion and Rounding givenin IEE

9、E/ASTM SI 10, of measurements made in other units or SI units. Values are stated in only SI units when inch-pound unitsare not used in practice.1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes(excluding those in tables and fig

10、ures) shall not be considered as requirements of the standard.2. Referenced Documents2.1 ASTM Standards:2C33 Specification for Concrete AggregatesC51 Terminology Relating to Lime and Limestone (as used by the Industry)C109/C109M Test Method for Compressive Strength of Hydraulic Cement Mortars (Using

11、 2-in. or 50-mm Cube Specimens)C114 Test Methods for Chemical Analysis of Hydraulic CementC115 Test Method for Fineness of Portland Cement by the TurbidimeterC151 Test Method for Autoclave Expansion of Hydraulic CementC183 Practice for Sampling and the Amount of Testing of Hydraulic CementC185 Test

12、Method for Air Content of Hydraulic Cement MortarC186 Test Method for Heat of Hydration of Hydraulic CementC191 Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle1 This specification is under the jurisdiction of ASTM Committee C01 on Cement and is the direct responsibility of Subco

13、mmittee C01.10 on Hydraulic Cements forGeneral Concrete Construction.Current edition approved July 1, 2015March 15, 2016. Published July 2015April 2016. Originally approved in 1940. Last previous edition approved in 20122015 asC150/C150M 12.C150/C150M 15. DOI: 10.1520/C0150_C0150M-15.10.1520/C0150_C

14、0150M-16.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intende

15、d only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current

16、versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1C204 Test Methods for Fineness of H

17、ydraulic Cement by Air-Permeability ApparatusC219 Terminology Relating to Hydraulic CementC226 Specification for Air-Entraining Additions for Use in the Manufacture of Air-Entraining Hydraulic CementC266 Test Method for Time of Setting of Hydraulic-Cement Paste by Gillmore NeedlesC451 Test Method fo

18、r Early Stiffening of Hydraulic Cement (Paste Method)C452 Test Method for Potential Expansion of Portland-Cement Mortars Exposed to SulfateC465 Specification for Processing Additions for Use in the Manufacture of Hydraulic CementsC563 Test Method for Approximation of Optimum SO3 in Hydraulic Cement

19、Using Compressive StrengthC1038 Test Method for Expansion of Hydraulic Cement Mortar Bars Stored in WaterC1702 Test Method for Measurement of Heat of Hydration of Hydraulic Cementitious Materials Using Isothermal ConductionCalorimetryE29 Practice for Using Significant Digits in Test Data to Determin

20、e Conformance with SpecificationsIEEE/ASTM SI 10 American National Standard for Use of the International System of Units (SI): The Modern Metric System3. Terminology3.1 DefinitionsSee Terminology C219.4. Ordering Information4.1 Orders for material under this specification shall include the following

21、:4.1.1 This specification number and date,4.1.2 Type or types allowable. If no type is specified,Type I shall be supplied,4.1.3 Any optional chemical requirements from Table 2, if desired, and4.1.4 Any optional physical requirements from Table 4, if desired.5. Ingredients5.1 The cement covered by th

22、is specification shall contain no ingredients except as follows:5.1.1 Portland cement clinker.TABLE 1 Standard Composition RequirementsCement TypeAApplicableTestMethodI andIAII andIIAII(MH)andII(MH)AIII andIIIA IV VAluminum oxide (Al2O3), max, % C114 . 6.0 6.0 . . .Ferric oxide (Fe2O3), max, % C114

23、. 6.0B 6.0B,C . 6.5 .Magnesium oxide (MgO), max, % C114 6.0 6.0 6.0 6.0 6.0 6.0Sulfur trioxide (SO3),D max, % C114When (C3A)E is 8 % or less 3.0 3.0 3.0 3.5 2.3 2.3When (C3A)E is more than 8 % 3.5 F F 4.5 F FLoss on ignition, max, % C114 3.0 3.0 3.0 3.0 2.5 3.0Loss on ignition, max, % C114When limes

24、tone is not an ingredient 3.0 3.0 3.0 3.0 2.5 3.0When limestone is an ingredient 3.5 3.5 3.5 3.5 3.5 3.5Insoluble residue, max, % C114 0.75 0.75 0.75 0.75 0.75 0.75Insoluble residue, max, % C114 1.5 1.5 1.5 1.5 1.5 1.5Tricalcium silicate (C3S)E , max, % See Annex A1 . . . . 35C .Dicalcium silicate (

25、C2S)E , min, % See Annex A1 . . . . 40C .Tricalcium aluminate (C3A)E , max, % See Annex A1 . 8 8 15 7C 5BSum of C3S + 4.75C3AG , max, % See Annex A1 . . 100C,H . . .Tetracalcium aluminoferrite plus twice thetricalcium aluminate (C4AF + 2(C3A),or solid solution (C4AF + C2F), asapplicable, max, %See A

26、nnex A1 . . . . . 25BA See Note 2.B Does not apply when the sulfate resistance limit in Table 4 is specified.C Does not apply when the heat of hydration limit in Table 4 is specified.D It is permissible to exceed the values in the table for SO3 content, provided it has been demonstrated by Test Meth

27、od C1038 that the cement with the increased SO3will not develop expansion exceeding 0.020 % at 14 days. When the manufacturer supplies cement under this provision, supporting data shall be supplied to the purchaser.See Note 6.E See Annex A1 for calculation.F Not applicable.G See Note 5.H In addition

28、, three-day heat of hydration testing by Test Method C1702 shall be conducted at least once every six months. Such testing shall not be used for acceptanceor rejection of the cement, but results shall be reported for informational purposes.C150/C150M 1625.1.2 Water or calcium sulfate, or both. The a

29、mounts shall be such that the limits shown in Table 1 for sulfur trioxide andloss-on-ignition are not exceeded.5.1.3 Limestone. The amount shall not be more than 5.0 % by mass such that the chemical and physical requirements of thisstandard are met (see Note 3). The limestone, defined in Terminology

30、 C51, shall be naturally occurring and consist of at least 70 %by mass of one or more of the mineral forms of calcium carbonate. If limestone is used, the manufacturer shall report the amountused, expressed as a percentage of cement mass, as determined using AnnexA2, along with the oxide composition

31、 of the limestone.NOTE 3The standard permits up to 5 % by mass of the final cement product to be naturally occurring, finely ground limestone, but does not requirethat limestone be added to the cement. Cement without ground limestone can be specified in the contract or order.5.1.4 Inorganic processi

32、ng additions. The amount shall be not more than 5.0 % by mass of cement. Not more than one inorganicprocessing addition shall be used at a time. For amounts greater than 1.0 %, they shall have been shown to meet the requirementsof Specification C465 for the inorganic processing addition in the amoun

33、t used or greater. If an inorganic processing addition isused, the manufacturer shall report the amount (or range) used, expressed as a percentage of cement mass, along with the oxidecomposition of the processing addition. See Note 4.NOTE 4These requirements are based on data and recommendations by

34、Taylor.35.1.5 Organic Processing additions. They shall have been shown to meet the requirements of Specification C465 in the amountsused or greater and the total amount of organic processing additions used shall not exceed 1.0 % by mass of cement.5.1.6 Air-entraining addition (for air-entraining por

35、tland cement only). The interground addition shall conform to therequirements of Specification C226.6. Chemical Composition6.1 Portland cement of each of the ten types shown in Section 1 shall conform to the respective standard chemical requirementsprescribed in Table 1. In addition, optional chemic

36、al requirements are shown in Table 2.NOTE 5The limit on the sum, C3S + 4.75C3A, in Table 1 provides control on the heat of hydration of the cement and is consistent with a Test MethodC186 seven-day heat of hydration limit of 335 kJ/kg 80 cal/g, or a Test Method C1702 three-day heat of hydration limi

37、t of 315 kJ/kg 75 cal g.NOTE 6There are cases where performance of a cement is improved with SO3 in excess of the Table 1 limits in this specification. Test Method C563is one of several methods a manufacturer can use to evaluate the effect of sulfate content on cement characteristics. Whenever SO3 c

38、ontent of a cementexceeds Table 1 limits, Test Method C1038 results provide evidence that excessive expansion does not occur at this higher sulfate content.7. Physical Properties7.1 Portland cement of each of the ten types shown in Section 1 shall conform to the respective standard physical requirem

39、entsprescribed in Table 3. In addition, optional physical requirements are shown in Table 4.3 Taylor, P., “Specifications and Protocols for Acceptance Tests on Processing Additions in Cement Manufacturing,” NCHRP Report 607, Transportation Research Board,Washington, DC 20008, 96 pp. Available at www

40、.trb.org.TABLE 2 Optional Composition RequirementsACement TypeApplicableTestMethodI andIAII andIIAII(MH) andII(MH)AIII andIIIA IV V RemarksTricalcium aluminate(C3A)B , max, %See Annex A1 . . . 8 . . for moderatesulfate resistanceTricalcium aluminate(C3A)B , max, %See Annex A1 . . . 5 . . for high su

41、lfateresistanceEquivalent alkalies(Na2O + 0.658K2O), max, %C114 0.60C 0.60C 0.60C 0.60C 0.60C 0.60C low-alkali cementTABLE 2 Optional Composition RequirementsACement Type Applicable TestMethod I and IA II and IIA II(MH) andII(MH)A III and IIIA IV V RemarksTricalcium aluminate(C3A)B , max, % See Anne

42、x A1 . . . 8 . .for moderatesulfate resistanceTricalcium aluminate(C3A)B , max, % See Annex A1 . . . 5 . .for high sulfateresistanceEquivalent alkalies(Na2O + 0.658K2O), max, % C114 0.60C 0.60C 0.60C 0.60C 0.60C 0.60C low-alkali cementA These optional requirements apply only when specifically reques

43、ted. Verify availability before ordering. See Note 2.B See Annex A1 for calculation.C Specify this limit when the cement is to be used in concrete with aggregates that are potentially reactive and no other provisions have been made to protect the concretefrom deleteriously reactive aggregates. Refer

44、 to Specification C33 for information on potential reactivity of aggregates.C150/C150M 163TABLE 3 Standard Physical RequirementsCement TypeAApplicableTestMethodI IA II IIA II(MH) II(MH)A III IIIA IV VAir content of mortar,B volume %: C185max 12 22 12 22 12 22 12 22 12 12min . 16 . 16 . 16 . 16 . .Fi

45、neness, specific surface, m2/kgAir permeability test C204min 260 260 260 260 260 260 . . 260 260max . . . . 430C 430C . . 430 .Autoclave expansion, max, % C151 0.80 0.80 0.80 0.80 0.80 0.80 0.80 0.80 0.80 0.80Strength, not less than the values shown for the agesindicated as follows:DCompressive stre

46、ngth, MPa psi: C109/C109M1 day . . . . . . 12.0174010.01450. .3 days 12.0174010.0145010.014508.0116010.014507.0E1020E8.011606.0E870E24.0348019.02760. 8.011607 days 19.0276016.0232017.0247014.0203017.0247012.0E1740E14.020309.0E1310E. . 7.0102015.0218028 days . . . . . . . . 17.0247021.03050Time of se

47、tting; Vicat test:F C191Time of setting, min, not less than 45 45 45 45 45 45 45 45 45 45Time of setting, min, not more than 375 375 375 375 375 375 375 375 375 375A See Note 2.B Compliance with the requirements of this specification does not necessarily ensure that the desired air content will be o

48、btained in concrete.C Maximum fineness limits do not apply if the sum of C3S + 4.75C3A is less than or equal to 90.D The strength at any specified test age shall be not less than that attained at any previous specified test age.E When the optional heat of hydration in Table 4 is specified.F The time

49、 of setting is that described as initial setting time in Test Method C191.C150/C150M1648. Sampling8.1 When the purchaser desires that the cement be sampled and tested to verify compliance with this specification, performsampling and testing in accordance with Practice C183.8.2 Practice C183 is not designed for manufacturing quality control and is not required for manufacturers certification.9. Test Methods9.1 Determine the applicable properties enumerated in this specification in accordance wi