ASTM C1511-2015 Standard Test Method for Determining the Water Retention (Repellency) Characteristics of Fibrous Glass Insulation (Aircraft Type)《测定玻璃纤维绝缘材料保水 (斥水性) 特征的标准试验方法 (航空用).pdf

1、Designation: C1511 15Standard Test Method forDetermining the Water Retention (Repellency)Characteristics of Fibrous Glass Insulation (Aircraft Type)1This standard is issued under the fixed designation C1511; the number immediately following the designation indicates the year oforiginal adoption or,

2、in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers a laboratory procedure forevaluating the water absorption

3、 potential of blanket insulationfor aircraft, thereby providing a measure of potential weightincrease due to water retention in an aircraft.1.2 The water repellency (or retention) characteristics ofmaterials can be affected by conditions such as contaminationor temperature of the water. Values obtai

4、ned as a result of thistest method does not adequately describe the water repellencycharacteristics of materials subject to these conditions.1.3 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provi

5、ded for information onlyand are not considered standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bilit

6、y of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C168 Terminology Relating to Thermal InsulationC390 Practice for Sampling and Acceptance of ThermalInsulation LotsC800 Specification for Fibrous Glass Blanket Insulation(Aircraft Type)E691 Practice for Conducting an

7、Interlaboratory Study toDetermine the Precision of a Test Method3. Terminology3.1 DefinitionsTerminology C168 shall be considered asapplying to the terms used in this specification.4. Summary of Test Method4.1 The insulation is weighed then submerged in de-ionized(or distilled) water for 15 min; it

8、is drained for 60 s andreweighed. The amount of water retained is the difference inspecimen weights and is expressed in grams.5. Significance and Use5.1 The water retention of the insulation can result in anincrease in weight and a resultant potential degradation in theproperties of the insulation.6

9、. Apparatus6.1 The water repellency test apparatus is shown in Fig. 1.6.2 Scale, accurate to 0.1 g.7. Sampling, Test Specimens, and Test Units7.1 Three specimens shall be tested, taken from across thewidth of a representative package. Sampling techniques shallbe in accordance with Practice C390.7.2

10、The specimens shall be 10- by 10-in. (254- by 254-mm)by full sample thickness; samples shall be no thicker than 4-in.(100-mm)7.3 The insulation shall be tested without facing or jacket-ing.8. Conditioning8.1 No conditioning of the specimen is required.9. Procedure9.1 Weigh each specimen to the neare

11、st 0.1 g.9.2 Float each specimen on the surface of a vat of de-ionized (or distilled) water at 70 6 4F (21 6 2C). Lay a0.25-in. (6.4-mm) mesh rigid screen on top of each specimenand slowly submerge it to a level that is 5 in. (127 mm) belowthe surface of the water. Fix the screen in position as show

12、n inFig. 1. After 15 6 1 min, release the screen and raise thespecimens slowly until they float. Remove the screen. Gripeach specimen on one corner with a spring clamp and hang itin a vertical position for 60 6 5 s. Reweigh each specimen andrecord.1This test method is under the jurisdiction ofASTM C

13、ommittee C16 on ThermalInsulation and is the direct responsibility of Subcommittee C16.33 on InsulationFinishes and Moisture.Current edition approved March 1, 2015. Published June 2015. Originallyapproved in 2001. Last previous edition approved in 2009 as C1511 04(2009).DOI: 10.1520/C1511-15.2For re

14、ferenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, We

15、st Conshohocken, PA 19428-2959. United States110. Calculation or Interpretation of Results10.1 Determine water retained by each specimen by sub-tracting the original specimen weight from the final specimenweight. Calculate water repellency by averaging the results ofthe three specimens.11. Report11.

16、1 The report shall include the following:11.2 Name and any additional identification of the materialtested,11.3 Thickness of the material,11.4 Number of specimens tests, and11.5 Average weight gain of the specimens.12. Precision and Bias12.1 Interlaboratory Test ProgramAn interlaboratorycomparison w

17、as run in which randomly selected test specimensof one material were tested for water repellency. Four labora-tories participated, with each laboratory testing three speci-mens. Practice E691 was followed for the design and analysisof the data. All of the test specimens were provided by a singlelabo

18、ratory. The details are given in ASTM Research Report:C16-1017.312.2 Test ResultsThe following information on precision,in units of measurement noted, is for the comparison of onematerial and is based on an average of three tests.12.3 PrecisionWater repellency interlaboratory compari-son statistical

19、 results using Practice E691:x 13.0 gsx2.1sr4.1sR4.1r11.5R112.4 BiasThere is no accepted reference material suitablefor determining the bias for this procedure. Bias has not beendetermined.13. Keywords13.1 aircraft; aircraft insulation; fibrous glass insulation;water repellencyASTM International tak

20、es no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own re

21、sponsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addres

22、sed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at th

23、e address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (ph

24、one), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ from ASTM Headquarters, request RR:C16-1017.FIG. 1 Water Repellency Test ApparatusC1511 152