1、Designation: C 1603 05aStandard Test Method forMeasurement of Solids in Water1This standard is issued under the fixed designation C 1603; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parent
2、heses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the measurement of the solidscontent in water for use as mixing water in ready-mixedconcrete and the measurement of its densit
3、y. Solids content isexpressed in terms of parts per million (ppm) or in terms ofpercent by mass of the water sample.1.2 The values stated in SI units are to be regarded asstandard; inch-pound units are shown in parenthesis for infor-mation only.1.3 The text of this standard references notes and foot
4、notesthat provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be consideredas requirements of the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the use
5、r of this standard to establish appro-priate safety and health practices and to determine theapplicability of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C 29/ C 29M Test Method for Bulk Density (“Unit Weight”)and Voids in AggregateC 670 Practice for Preparing Prec
6、ision and Bias Statementsfor Test Methods for Construction MaterialsC 1602/C 1602M Standard Specification for Mixing WaterUsed in the Production of Hydraulic Cement Concrete3. Significance and Use3.1 This test method is used to determine the solids contentof mixing water used to produce concrete whe
7、n one or more ofthe water sources is wash water from concrete productionoperations or water that contains solids when batched asmixing water in concrete.3.2 The test method provides a means to determine therelationship between the density and solids content of water forcompliance with solids content
8、 limits of mixing water such asin Specification C 1602/C 1602M.3.3 During production of concrete, the water property mea-sured is its density, which can then be used to estimate thesolids content from procedures described in this test method.3.4 To develop a correlation between the density and solid
9、scontent of water, water samples should be tested that cover therange of solids concentrations anticipated during production.4. Apparatus4.1 Density Measure: A cylindrical container (Note 1) witha volume of 200 6 25 mL (7 6 1 fl. oz.) with a glass or hardplastic plate that is placed over it. The gla
10、ss or plastic plateshall be at least 6 mm (14 in.) thick and 40 mm (112-in.) largerthan the outer diameter of the measure. The top of the densitymeasure shall be flat such that it does not leak when the plateis placed over it.NOTE 1Acommonly available smaller size mason jar with top groundsmooth is
11、acceptable.4.2 The volume of the density measure shall be determinedto nearest 0.1 mL in accordance with procedures used forcalibrating air or density measures, as in Test Method C 29/C 29M.4.3 A microwave oven with at least 900 W of powercapacity.4.4 Amicrowave-safe glass dish large enough to conta
12、in thewater sample and fiberglass cloth (See Note 2).NOTE 2A 450 3 450 3 25 mm (9 3 9 3 1 in.) dish is acceptable.Fiberglass cloth commonly used with fiberglass resin for boat or auto bodyrepair is found in most hardware stores.4.5 A balance or scale with a minimum capacity of 2000 gaccurate to 0.1
13、g4.6 A rubber syringe5. Measurement of Density5.1 Obtain the mass of the empty density measure and plateto the nearest 0.1g.1This test method is under the jurisdiction of ASTM Committee C09 onConcrete and Concrete Aggregates and is the direct responsibility of SubcommitteeC09.40 on Ready-Mixed Concr
14、ete.Current edition approved July 1, 2005. Published August 2005. Originallyapproved in 2004. Last previous edition approved in 2005 as C 1603 05.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards
15、 volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2 If the water contains solids in suspension, ensure that thewater is sampled while the water sour
16、ce is being agitated. Takea representative sample of water and fill the density measure tooverflowing. Slide the cover plate over the measure ensuringthat there are no air bubbles. Wipe the outside of the plate andmeasure dry and obtain the mass of the filled density measurecovered with the plate.5.
17、3 Calculate the density of the water sample to 0.001 g/mLDW5MWV(1)Where:DW= Density of the water, g/mL,MW= Net mass of water in the density measure, g, andV = Volume of the density measure, mL.6. Measurement of Solids Content6.1 Obtain the mass of the empty dish and a piece of fiberglass cloth about
18、 500 mm (20 in.) square to the nearest 0.1 g.6.2 Keep the glass plate over the density measure and shakethe water suspension. Pour the water sample into the glass dish.Using the rubber syringe, wash solids adhered in the measureinto the dish using a minimum amount of water. Cover thewater with the f
19、iberglass cloth to prevent loss of solids duringdrying.6.3 Place the dish in a microwave oven and heat it forapproximately 20 min or until the water has evaporated.Determine the mass of the dish and place it back in themicrowave oven for 2 min increments until the mass deter-mined in two subsequent
20、determinations do not differ by morethan 0.5 g.6.4 Determine the mass of the dish and cloth with the driedsolids.6.5 Calculate the percent solids in terms of percent by massto the nearest 0.1 % and in ppm to the nearest 1000 ppm.SW,% 5MsMW3 100 (2)Sppm5 SW3 10 000 (3)Where:Ms= Mass of dry solids,MW=
21、 Mass of water with solids,SW= Solids content in water, in percent, andSppm= Solids content in water, in ppm.6.6 Repeat these measurements for water with differentsolids content. Test water at 4 or more different levels of solidscontent.7. Relationship Between Density and Solids Content7.1 Establish
22、 a relationship using linear regression analysis(See Note 3) between the measured density and solids contentof water sample measurements for a range of solid concentra-tions that cover the anticipated range in the production facility.NOTE 3The linear regression analysis can be performed using spread
23、-sheet software.7.1.1 Express the relationship between the density of thewater and the solids content as follows, such that the measureddensity on a particular production day can be used to determinethe solids content of the water.Sppm5 A 1 B 3 DW(4)Where: A and B are regression constantsNOTE 4Eq 4
24、provides an approximate linear relationship betweensolids content and measured density. The relationship between solidscontent and density is non-linear (see Eq 5) and Eq 4 should not be usedto estimate the solids content of water outside the range of values used toestablish the relationship in Eq 4
25、.NOTE 5During concrete production, a producer might choose tomonitor the density of a water source using a hydrometer. It is recom-mended that the density of the water using a hydrometer be determined onthe water at the time of this density measurement to obtain a relationship,if needed, or to calib
26、rate the hydrometer. The water sample should beplaced in a transparent volumetric measuring flask. The hydrometermeasurement should be taken within 10 s after filling the water in theflask. This is to ensure that significant settlement of solids has not occurredbefore the measurement is taken as tha
27、t will affect the measured density.7.2 When the relationship between density and solids con-tent is not determined by testing, calculate the solids content ofthe water in ppm from the measured density using thefollowing:Sppm5SDW2 1DS2 1D3DSDW3 1 000 000 (5)where:DS= Density of solids in the water, g
28、/mL7.2.1 When the density of solids in the water is unknown,assume it to be 2.6 g/mL, and determine the solids content ofthe water in ppm from the measured density using thesimplified form of Eq 5 as follows:Sppm5 1 625 000 3S11DWD(6)NOTE 6Guidance for blending two sources of water with differentsol
29、ids content is provided in Appendix X1.8. Report8.1 For the water samples tested to establish the relationshipof water density to solids content, maintain a record of thedensity of water to the nearest 0.001 g/mL; and the solidscontent of the same water sample in ppm to the nearest 1000ppm or percen
30、t by mass of water to the nearest 0.1 %. Includethe dates of these tests and maintain a record of the regressionequation used to establish the relationship of water density tosolids content.8.2 For tests of water samples during production of concreteor to calibrate automated measuring devices, maint
31、ain a recordof water density tests to the nearest 0.001 g/mL or solidscontent to the nearest 1000 ppm. Include the date and time ofthese tests. Record the calculated solids content of the testedwater sample and the method (7.1 or 7.2) used to determine thesolids content.9. Precision and Bias9.1 Prec
32、isionThe estimates of precision for this testmethod are based on results from tests on wash water sampleswith a range of solids content between 25 000 and 140 000ppm. Four operators tested the same water samples in triplicatefor the density and in duplicate for solids content.C 1603 05a29.1.1 Single
33、 Operator PrecisionThe single-operator stan-dard deviation (1s) is shown in Table 1 by average density andsolids content; therefore, results of two properly conductedtests on the same sample by the same operator are not expectedto differ by more than the d2s values listed in Table 1.9.1.2 Multi-Oper
34、ator PrecisionThe multi-operator stan-dard deviation (1s) is shown in Table 1 by average density andsolids content; therefore, results of two properly conductedtests on the same sample by two different operators are notexpected to differ by more than the d2s values listed in Table1.9.2 BiasSince the
35、re is no accepted reference material fordetermining the bias of the results from this test method, nostatement on bias is made.10. Keywords10.1 concrete mixing water; density; recycled water; solidsAPPENDIX(Nonmandatory Information)X1. Determination of Blending Percentages of Combined WaterX1.1 Use
36、the following relationships to determine themixing percentage (Note X1.1) of each of two water sources tobe blended to ensure that the added mixing water to concrete isat a target limit of solids content or the respective targetdensity.X1.1.1 When the solids content of the two sources of wateris kno
37、wn and water is batched by mass or by volume, use EqX1.1:P15ST S2S1 S23 100 (X1.1)X1.1.2 When the density of the two sources of water isknown, use Eq X1.2 when water is batched by mass and EqX1.3 when water is batched by volume:P15DT D2D1 D23D1DT3 100 (X1.2)P15DT D2D1 D23 100 (X1.3)Where:P1= Percent
38、age of water from source 1 in theblended mixing water,STand DT= Target solids content in ppm and density ing/mL of the blended mixing water,S1and D1= Solids content in ppm and density in g/mL ofthe water from source 1, andS2and D2= Solids content in ppm and density in g/mL ofthe water from source 2.
39、NOTE X1.1The target solids content may be a limit established in aspecification or one that the quality control function of the ready mixedconcrete producer establishes. The solids content, typically dissolved, ofmunicipal water may be considered to be 0 ppm and the density may beconsidered to be 1.
40、0 g/mL, to simplify this calculation.X1.2 When wash water from concrete production is used ata higher percentage of solids content, there will be necessarycorrections in the quantity of mixing water and the volume ofsolids to account for the solids content in the total mixingwater.TABLE 1 Table Prec
41、isionStandardDeviation (1s)AAcceptable Range ofTwo Results (d2s)ASingle Operator PrecisionDensity, g/mL1.016 0.0005 0.00151.033 0.0010 0.00301.052 0.0017 0.00471.101 0.0014 0.0039Solids Content, ppm22,300 740 2,10046,600 970 2,70071,500 600 1,700134,500 2,300 6,300Multi-Operator PrecisionDensity, g/
42、mL1.016 0.0009 0.00261.033 0.0018 0.00501.052 0.0025 0.00691.101 0.0020 0.0056Solids Content, ppm22,300 1,080 3,00046,600 1,110 3,10071,500 2,250 6,300134,500 2,530 7,100AThese numbers represent, respectively, the (1s) and (d2s) limits as describedin Practice C 670C 1603 05a3ASTM International takes
43、 no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own resp
44、onsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addresse
45、d to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the
46、address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).C 1603 05a4