1、Designation: C1767 15Standard Specification forStainless Steel Jacketing for Insulation1This standard is issued under the fixed designation C1767; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number

2、in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers stainless steel jacketing forthermal, acoustical, and fire protective insulation operating ateither above or below a

3、mbient temperatures and in both indoorand outdoor locations. It does not cover insulation jacketingmade from other materials such as mastics, fiber reinforcedplastic, PVC, aluminum, or coated carbon steel (for example,aluminum-zinc, galvanized steel, or aluminized steel) nor doesit cover the details

4、 of thermal, acoustical, or fire protectiveinsulation systems.1.2 While not intended to cover use inside the containmentbuildings of nuclear power plants, this standard does notpreclude use of Class E material which does not have amoisture barrier in this containment building application.1.3 This sp

5、ecification provides physical requirements forstainless steel jacketing for thermal and acoustical insulation.Guide C1423 provides guidance in selecting jacketing materi-als and their safe use.1.4 This is a material specification and does not imply anyperformance of the installed system using the ma

6、terials speci-fied herein. For information about installation of stainless steeljacketing, see (1).21.5 The values stated in inch-pound units are to be regardedas standard. No other units of measurement are included in thisstandard.1.6 A version of this standard in SI units is available asSpecificat

7、ion C1767M.1.7 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. R

8、eferenced Documents2.1 ASTM Standards:3A167 Specification for Stainless and Heat-ResistingChromium-Nickel Steel Plate, Sheet, and Strip (With-drawn 2014)4A240/A240M Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for PressureVessels and for General Applications

9、A480/A480M Specification for General Requirements forFlat-Rolled Stainless and Heat-Resisting Steel Plate,Sheet, and StripC168 Terminology Relating to Thermal InsulationC450 Practice for Fabrication of Thermal Insulating FittingCovers for NPS Piping, and Vessel LaggingC585 Practice for Inner and Out

10、er Diameters of ThermalInsulation for Nominal Sizes of Pipe and TubingC835 Test Method for Total Hemispherical Emittance ofSurfaces up to 1400CC1371 Test Method for Determination of Emittance ofMaterials Near Room Temperature Using Portable Emis-sometersC1423 Guide for Selecting Jacketing Materials

11、for ThermalInsulationC1729 Specification for Aluminum Jacketing for InsulationC1785 Test Method for Concentration of Pinhole Detectionsin Moisture Barriers on Metal JacketingE84 Test Method for Surface Burning Characteristics ofBuilding MaterialsF1249 Test Method for Water Vapor Transmission RateThr

12、ough Plastic Film and Sheeting Using a ModulatedInfrared Sensor3. Terminology3.1 DefinitionsDefinitions in Terminology C168 apply toterms used in this specification.3.2 Definitions of Terms Specific to This Standard:1This test method is under the jurisdiction ofASTM Committee C16 on ThermalInsulatio

13、n and is the direct responsibility of Subcommittee C16.40 on InsulationSystems.Current edition approved Nov. 1, 2015. Published November 2015. Originallyapproved in 2012. Last previous edition approved in 2014 as C176714a. DOI:10.1520/C1767-15.2The boldface numbers in parentheses refer to the list o

14、f references at the end ofthis standard.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4The last approved ve

15、rsion of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.2.1 box ribstainless steel sheet formed to have alternat-ing parallel grooves and ridges with a cross section approxi-mat

16、ing a square wave.3.2.2 cladding (as related to insulation jacketing)synonymous with jacketing.3.2.2.1 DiscussionThe three terms “jacketing,” “lagging,”and “cladding” are considered synonymous in most applica-tions and geographies. However, in some cases in the powerindustry in North America the ter

17、m “lagging” has a differentmeaning than “jacketing” or “cladding” and refers specificallyto a heavier gauge of jacketing.3.2.3 crevice corrosion, nin metal jacketing localizedcorrosion of metal jacketing surface at, or immediately adja-cent to an area that is shielded from full exposure to theenviro

18、nment because of close proximity between the metal andthe surface of another material.3.2.4 cross crimpedsynonymous with316 in. corrugated.3.2.5 deep corrugatedstainless steel sheet formed to havealternating parallel grooves and ridges with a cross sectionapproximating a sine wave.3.2.6 gorejacketin

19、g for elbows, fittings, or other non-straight portions of the piping system made from a multitude ofsimilar overlapping pieces.3.2.7 lagging (as related to insulation jacketing)synonymous with jacketing.3.2.7.1 DiscussionThe three terms “jacketing,” “lagging,”and “cladding” are considered synonymous

20、 in most applica-tions and geographies. However, in some cases in the powerindustry in North America the term “lagging” has a differentmeaning than “jacketing” or “cladding” and refers specificallyto a heavier gauge of jacketing.3.2.8 mill finishthe appearance of the stainless steel sur-face as supp

21、lied from the metal mill.3.2.9 moisture retarder (moister barrier)a layer of plasticfilm or other material applied to the inner side of metaljacketing to inhibit jacket corrosion by interfering with theformation of a galvanic cell between the dissimilar metals ofthe pipe and jacket or by preventing

22、crevice corrosion.3.2.9.1 DiscussionA moisture retarder is not an insulationsystem water vapor retarder and does not perform the samefunction.3.2.10 polykrafta multilayer composite film used as amoisture retarder on metal jacketing consisting of at least onelayer of minimum 40 lb Kraft paper and one

23、 or more layers ofplastic film, usually polyethylene at a minimum thickness of1.5 mils.3.2.10.1 DiscussionKraft paper is commonly referred toby its basis weight which is the mass per area in units oflbs/3000 ft2. 40 lb Kraft has a basis weight of 40 lbs/3000 ft2.3.2.11 polyfilma multilayer film used

24、 as a moisture re-tarder on metal jacketing consisting of at least one layer ofethylene/methacrylic acid copolymer and one or more layers ofother polymers, usually polyethylene.3.2.12 safety edgean edge of metal jacketing that has beende-burred or rounded by a rolling operation.3.2.13 safety hema ro

25、unded edge of metal jacketing cre-ated by folding the edge of sheet jacketing completely backupon itself using a roll former or a brake.3.2.13.1 Discussionthe fold is typically made toward theunderside of the jacketing so that the original edge is hiddenand the external appearance of the jacketing i

26、s preserved3.2.14 splice rollmetal jacketing sold in roll form wherethe package contains two separate pieces of metal jacketingrolled approximately end to end.3.2.14.1 DiscussionA splice roll occurs when the metalcoil being used to form the roll jacketing reaches its end beforethe required roll leng

27、th is obtained.3.2.15 split rollsynonymous with splice roll.3.2.16 surface finish (as related to insulation jacketing)the final texture of the stainless steel jacketing surface.4. Significance and Use4.1 This specification is used to specify material by physicalproperty requirements that address the

28、 prerequisites in Sections6 to 10. The designer of an insulation system, after determiningthe system requirements, shall use this specification to specifythe appropriate stainless steel jacketing.5. Classification5.1 Classification of stainless steel jacketing is based onthree factors:5.1.1 Outer Su

29、rface Treatment and Emittance ():5.1.1.1 Type I = Bare surface, = 0.35.1.2 Alloy and Temper per Specification A240/A240M:5.1.2.1 Grade 1 = Alloy T-304/T-304L, annealed temper5.1.2.2 Grade 2 = Alloy T-316/T-316L, annealed temperNOTE 1The four allowable alloys shown in 5.1.2 are of the austenitictype

30、of stainless steel.NOTE 2The “L” in the alloy is an indication of low carbon content.Since the low carbon alloy will avoid corrosion problems caused bywelding, a low carbon alloy is required on those rare occasions when thestainless steel jacketing will be subjected to direct welding or the heatfrom

31、 welding nearby metal. The low carbon and standard alloys areconsidered interchangeable for use as insulation jacketing.5.1.3 Moisture Retarder:5.1.3.1 Class A = polyfilm, 3 mil thick5.1.3.2 Class C = polykraft per section 3.2.105.1.3.3 ClassE=nomoisture retarderNOTE 3ClassesB straight pipe, pipe el

32、bows/fittings,and vessels/equipment. The requirements for each of theseapplications differ.10.3 Stainless Steel Jacketing on Straight Pipe:10.3.1 At the point of application, stainless steel jacketingused on straight pipe will consist of a multitude of pre-curvedpieces with dimensions per 8.2.10.3.2

33、 The thickness (gauge) used for the stainless steeljacketing on straight pipe varies with jacket diameter as shownin this section and in Table 1.10.3.2.1 For straight pipe up to a jacket diameter of 24 in.,the minimum allowable thickness is 0.010 in. and Grade 1 orGrade 2 stainless steel shall be us

34、ed.10.3.2.2 For straight pipe with jacket diameter greater than24 in. up to 36 in., the minimum allowable thickness is 0.016in. and Grade 1 or Grade 2 stainless steel shall be used.10.3.2.3 For straight pipe with a jacket diameter greater than36 in., the minimum allowable thickness is 0.020 in. and

35、Grade1 or Grade 2 stainless steel shall be used.10.3.3 When expected physical abuse is severe, consider-ation shall be given to using thickness of 0.024 in. or greater.Grade 1 or Grade 2 stainless steel shall be used.10.3.4 Stainless steel jacketing on straight pipe requires theuse of a moisture ret

36、arder so only Classes A or C shall be used.10.4 Stainless Steel Jacketing on Pipe Elbow/Fittings:10.4.1 Stainless steel jacketing applied to insulation on pipeelbows/fittings shall take the form of 2-piece (pressed),C1767 1544-piece, or gores all of which shall be pre-formed or pre-rolledto fit arou

37、nd the insulation. For outer insulation diameters of 20in. or larger, the use of 8-piece sections on pipe elbows/fittingsis acceptable.10.4.1.1 For 2-piece (pressed) elbows, the overlaps at theheel and throat shall comply with the minimum values in Table4 when the insulation outer diameter conforms

38、to the targetvalues in Practices C585 or C450.NOTE 10When the insulation outer diameter is smaller or larger thanthat specified in Practices C585 or C450, the heel and throat overlaps willbe larger or smaller than58 in. With 2-piece (pressed) elbows, deviationsin insulation outer diameter from that

39、specified in Practices C585 or C450causes, in some cases, undesirable gaps in the joint at the heel or throat.10.4.2 Stainless steel jacketing used shall be Grade 2(T-316/T316L annealed), 0.016 in. thick.10.5 Stainless Steel Jacketing on Equipment and Vessels:10.5.1 Except for the thickness, finish,

40、 and Grade require-ments in 10.5.2 to 10.5.4, stainless steel jacketing applied toequipment and vessels shall be of any size and shape agreedupon by purchaser and seller.10.5.2 The minimum allowable stainless steel jacketingthickness shall be as listed in Table 1.10.5.3 For horizontal vessels, only

41、smooth or stucco em-bossed finish shall be used (no deep corrugated sheet or316 in.corrugated finish).NOTE 11When deep corrugated or316 in. corrugated sheet is used onhorizontal vessels, there is a tendency for water to pond in the corruga-tions on the top of the vessel resulting in an increase in j

42、acket corrosion,more dirt collection, poorer aesthetics, and an increased likelihood ofwater penetrating the jacket and entering the insulation system.10.5.4 For vertical vessels and equipment less than 8 ftdiameter, any finish of stainless steel jacketing or stainless steeldeep corrugated sheet is

43、acceptable. For vertical vessels andequipment 8 ft diameter and greater, deep corrugated stainlesssteel sheet jacketing shall be used.10.6 The purchaser shall be aware that Grade 1 (T-304/T-304L alloy) is normally used in most applications except themost corrosive areas, where Grade 2 (T-316/T-316L)

44、 is recom-mended.11. Test Methods11.1 Outer Jacket Surface EmittanceTest in accordancewith Test Method C835 or C1371.11.2 Surface Burning CharacteristicsTest in accordancewith Test Method E84 with outer surface of jacketing exposedto the flames.11.3 Metal Sheet ThicknessTest in accordance with Speci

45、-fication A480/A480M.11.4 Pinhole Detections in Moisture RetarderTest in ac-cordance with Test Method C1785.11.4.1 Pass CriteriaThe moisture retarder is consideredacceptable when no more than 5 pinhole detections,collectively, are detected in the 10 wetted test areas.11.5 Water Vapor Transmission Ra

46、te of the MoistureRetarderTest in accordance with Test Method F1249 at 73Fand 100 % relative humidity with results normalized to 1atmosphere of pressure.12. Sampling, Inspection, and Rejection of DefectiveMaterial12.1 A lot of material shall be considered to be the largestquantity of a specific stai

47、nless steel jacketing received by thepurchaser under one order, or, when so designated by themanufacturer, that quantity of products identified as the par-ticular lot.12.2 Aunit of material shall be considered to be the smallestpackaged quantity of stainless steel jacketing within a lot, thatis, one

48、 roll in a lot of rolls or one bundle of sheets in a lot ofsheeted material.12.3 Inspection shall consist of any tests for specificationconformance the user deems necessary. Due to the impracti-cality of performing some tests on an inspection basis, whendeemed necessary, the user shall request certi

49、fication to spe-cific test requirements.12.4 Incoming lots shall be sampled at a minimum rate of5 % of units received for inspection.12.5 When any nonconformance to specification is detectedwithin the 5 % sample, increase sampling to 10 % of the lot.12.6 When 50 % or more of the 10 % sampled units isdetermined to be defective, the lot shall be considered unac-ceptable.12.7 It shall be left to the discretion of the user whether tocontinue sampling for acceptable material. In any case, unitsfound defective shall be considered unacceptable and