ASTM C196-2000(2016) Standard Specification for Expanded or Exfoliated Vermiculite Thermal Insulating Cement《扩大或膨胀的蛭石隔热水泥的标准规格》.pdf

1、Designation: C196 00 (Reapproved 2016)Standard Specification forExpanded or Exfoliated Vermiculite Thermal InsulatingCement1This standard is issued under the fixed designation C196; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, t

2、he year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification co

3、vers expanded or exfoliated ver-miculite thermal insulating material in the form of dry cementor plaster, intended to be mixed with a suitable proportion ofwater, applied as a plastic mass, and dried in place, for use asinsulation on surfaces operating at temperatures between100F (38C) and 1800F (98

4、2C). The cement shall not beused where it will be exposed to combustion conditions, suchas the hot face lining of a furnace.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for informati

5、on onlyand are not considered standard.1.3 The following safety hazards caveat pertains only to thetest method portion, Section 10, of this specification. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this

6、standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.1.4 When the installation or use of thermal insulationmaterials, accessories and systems, may pose safety or healthproblems, the manufacturer shall provide the user wi

7、th appro-priate current information regarding any known problemsassociated with the recommended use of the companysproducts. The manufacturer shall also recommend protectivemeasures to be employed in the safe utilization of saidproducts.2. Referenced Documents2.1 ASTM Standards:2C163 Practice for Mi

8、xing Thermal Insulating CementSamplesC166 Test Method for Covering Capacity and VolumeChange Upon Drying of Thermal Insulating CementC168 Terminology Relating to Thermal InsulationC177 Test Method for Steady-State Heat Flux Measure-ments and Thermal Transmission Properties by Means ofthe Guarded-Hot

9、-Plate ApparatusC353 Test Method forAdhesion of Dried Thermal Insulatingor Finishing Cement (Withdrawn 2002)3C354 Test Method for Compressive Strength of ThermalInsulating or Finishing Cement (Withdrawn 2002)3C356 Test Method for Linear Shrinkage of Preformed High-Temperature Thermal Insulation Subj

10、ected to SoakingHeatC390 Practice for Sampling and Acceptance of ThermalInsulation LotsC405 Practice for Estimating Consistency of Wet-MixedThermal Insulating Cement (Withdrawn 2006)3C518 Test Method for Steady-State Thermal TransmissionProperties by Means of the Heat Flow Meter ApparatusC1058 Pract

11、ice for Selecting Temperatures for Evaluatingand Reporting Thermal Properties of Thermal Insulation3. Terminology3.1 Definitions:3.2 Terminology C168 shall be considered as applying tothe terms used in this specification.4. Materials and Manufacture4.1 The cement shall be composed predominantly of e

12、x-panded or exfoliated vermiculite, with a suitable proportion ofheat-resistant binder. Asbestos shall not be used as an ingredi-ent or component part of the product.5. Other Requirements5.1 The cement shall conform to the requirements given inTable 1. Conformance shall be based on results of tests

13、on1This specification is under the jurisdiction of ASTM Committee C16 onThermal Insulation and is the direct responsibility of Subcommittee C16.20 onHomogeneous Inorganic Thermal Insulations.Current edition approved March 1, 2016. Published March 2016. Originallyapproved in 1944. Last previous editi

14、on approved in 2010 as C196 00 (2010).DOI: 10.1520/C0196-00R16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM websit

15、e.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1specimens first mixed with water, according to the ratio forproper troweling consistency determined

16、in accordance withSection 10.6. Qualification Requirements6.1 The following requirements are employed for purposesof initial material or product qualification:6.1.1 Consistency,6.1.2 Compressive strength,6.1.3 Linear shrinkage,6.1.4 Apparent thermal conductivity, and6.1.5 Dry adhesion to steel.7. Sa

17、mpling7.1 The cement shall be sampled, for the purpose of testsusing one of the following procedures.7.1.1 Inspection Requirements:7.1.1.1 Use Practice C390. Each bag shall represent a unit.7.1.1.2 In a single sampling plan by attributes the accept-ability of a lot will be determined by the number o

18、f units ofproduct in the sample that do not conform to the specifications.The acceptable quality level (AQL) and limiting quality level(LQL) of an acceptance sampling plan, expressed as percent-ages of the units nonconforming, are characteristics of thesampling plan and are not to be viewed as produ

19、ct specifica-tions.7.1.2 Qualification Requirements:7.1.2.1 Use the average of the test data from the number oftest specimens required by the appropriate test method torepresent the average for the entire lot.7.2 The specimen for test is to be taken from the middle ofa bag, so as to be representativ

20、e of material from the entire bag.8. Number of Tests and Retests8.1 If the average of the test data obtained using 7.1.2.1 failsto conform to the requirements of this specification, a secondsample shall be taken from the lot. Average the results of theretest with the results of the original test to

21、determine compli-ance with this specification.9. Specimen Preparation9.1 Mix specimens for testing in accordance with PracticeC163.9.2 The amount of water to be used in preparing samples forall tests shall be that amount which results in the specifiedconsistency, determined in accordance with Practi

22、ce C405.10. Test Methods10.1 Consistency Practice C405.10.2 Dry Covering CapacityTest Method C166.10.3 Volume Change upon DryingTest Method C166.10.4 Compressive StrengthTest Method C354.10.5 Linear Shrinkage Test Method C356.10.6 Apparent Thermal ConductivityTest Method C177 orTest Method C518, exc

23、ept prepare the test specimens asfollows:10.6.1 Mold test specimens in a mold of suitable size andshape for the equipment to be used and 112 in. (38 mm) indepth. The cement shall be mixed with water in accordancewith Practice C163. Place the mold in a horizontal position ona piece of glass 14 in. (3

24、56 mm) or 15 in. (381 mm) square, orslightly larger than the specimen required. Place the mixedcement in the mold, trowel the top surface of the cementsmooth, and place a sheet of ordinary writing paper on top ofthe cement. Place a18 in. (3 mm) thick steel plate 14 in. (356mm) or 15 in. (381 mm) squ

25、are, or slightly larger than thespecimen required, having nine equally spaced holes316 in. (5mm) in diameter in the central area 10 in. (254 mm) indiameter, on top of the mold and use a pointed pin to puncturethe paper immediately under the holes in the steel plate. Invertthis entire assembly and re

26、move the glass plate, trowel thesurface of the cement smooth and flush with the top of themold, and then carefully remove the mold. Place the perforatedplate with the molded cement on an open shelf of an ovenhaving a volume at least 50 times that of the specimens to bedried. The oven chamber shall b

27、e adequately vented in such amanner as to ensure complete circulation of the atmosphere ofthe entire oven chamber preferably by fan or other forcedcirculation method. The test specimens shall remain in theoven for at least 48 h at a temperature of 215F (102C) to250F (121C). Upon removal from the ove

28、n, the surfaces ofthe specimens shall be made plane and parallel by cutting,sandpapering, or rubbing, or by a combination of thesemethods. The lateral dimensions of the specimens shall begoverned by the size of the apparatus.10.6.2 Temperature of test shall be in accordance withPractice C1058.10.7 D

29、ry Adhesion to SteelTest Method C353.11. Inspection11.1 The following requirements are employed for purposesof acceptance sampling of lots or shipments of qualifiedcement:11.1.1 Dry Covering Capacity.11.1.2 Volume Change Upon Drying.12. Rejection and Rehearing12.1 Material that fails to conform to t

30、he requirements ofthis specification may be rejected. Rejection should be reportedTABLE 1 Other RequirementsConsistencyMethod A, %Method B, in. (mm)35 to 457 (178) to 9 (229)Dry covering capacity, min, ft2, 1 in. in thickness per100 lb of dry cement (m2, 1 cm. in thickness per100 kg of dry cement)50

31、 (26)Volume change upon drying, max,% 20Compressive strength, min, psi (kPa) at 5 % defor-mation5 (34.5)Linear shrinkage max % 24 h at 1800F (980C) 5Apparent thermal conductivity, max, Btuin./hft2F (W/mK)At mean temperatures of:200F (95C) 0.95 (0.137)500F (260C) 1.10 (0.159)700F (370C) 1.20 (0.173)D

32、ry adhesion to steel, min, psi(kPa) 3.5 (24.2)C196 00 (2016)2to the manufacturer or supplier promptly and in writing. In caseof dissatisfaction with the results of the test, the manufactureror supplier may make claim for a rehearing.12.2 In case of rejection, the manufacturer or supplier shallhave t

33、he right to reinspect the rejected shipment and resubmitthe lot after removal of that portion not conforming to thespecified requirements.13. Certification13.1 When specified in the purchase order or contract, thepurchaser shall be furnished certification that samples repre-senting each lot have bee

34、n either tested or inspected as directedin this specification and the requirements have been met. Whenspecified in the purchase order or contract, a report of the testresults shall be furnished.14. Packaging14.1 Unless otherwise specified or agreed upon between thepurchaser and the manufacturer or s

35、upplier, the cement shall bepackaged in the manufacturers standard commercial contain-ers.15. Keywords15.1 cement-thermal insulating; expanded/exfoliated ver-miculite thermal insulating cement; sampling-thermalinsulating-thermal insulating materials; thermal conductivity;thermal insulating materials

36、-cementASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such righ

37、ts, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional

38、standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM

39、Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the abovea

40、ddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 00 (2016)3