ASTM C326-2009(2018) Standard Test Method for Drying and Firing Shrinkages of Ceramic Whiteware Clays.pdf

1、Designation: C326 09 (Reapproved 2018)Standard Test Method forDrying and Firing Shrinkages of Ceramic Whiteware Clays1This standard is issued under the fixed designation C326; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the yea

2、r of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This test method covers the determination of linearshrinkage of ceramic whiteware clays, both unfired and fired.

3、1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, asso

4、ciated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally re

5、cognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Significance and Use2.1 The purpose of this test is to obt

6、ain values of shrinkageafter drying and firing of clays or bodies or both, under variousprocessing conditions to enable designers to determine theproper size of mold or die so as to produce a predeterminedsize of fired ware.3. Test Specimens3.1 Test specimens shall be round bars approximately0.75 in

7、. (19 mm) in diameter by 5 in. (127 mm) in length.3.2 Test specimens may be prepared either by casting orplastic forming, as circumstances require. At least ten speci-mens shall be prepared. For cast specimens the molds may beeither one-piece, or two- or more-part molds; in either instancesufficient

8、 space shall be provided to allow solid casting withoutpiping. Where plastic-forming is employed, the clay-watermass shall be brought to a consistency that permits the makingof specimens rigid enough to allow careful handling withoutdistortion immediately after the test specimen is made. Plastic-for

9、med test specimens shall be made either by extrusion or bypressing in a suitable metal mold. Where a vacuum pugmill isused, a vacuum of not less than 25 in. (635 mm) Hg shall bemaintained during the forming operation. Where no vacuumattachment is used, the plastic clay shall be thoroughly hand-wedge

10、d to eliminate entrapped air as a preliminary to formingtest pieces.3.3 The test specimens, cast or plastic-formed, shall besuitably identified and marked with shrinkage reference lines4 in. (102 mm) apart on the long axis of the specimen. Theshrinkage reference lines may conveniently be made with a

11、gage with knife edges at zero and 4 in. (102 mm) and markingmust be done as soon as the bars can be handled withoutdistortion.3.4 The marked specimens shall then be placed on a lightlyoiled pallet with semi-circular grooves 0.40 in. (10.2 mm) indiameter and allowed to dry at 68 to 100F (20 to 40C) f

12、or24 h. The purpose of the semi-circular (half round) grooves isto maintain straightness of the bars during drying. During thispreliminary drying period, the bars shall be turned 90 severaltimes at 2-h intervals to eliminate possible warping in thevertical direction. After the initial drying period,

13、 the specimensshall be placed in a drying oven at 200 to 230F (100 to 110C)and further dried for 24 h.3.5 The drying shrinkage of the test specimens should bedetermined in accordance with Sections 4 and 5. The speci-mens can now be fired according to a suitable firing scheduleto the desired temperat

14、ure and the procedures of Sections 4 and5 applied to determine the total shrinkage.3.6 The test bars must be clearly identified as to whetherthey were cast or extruded, and shrinkage data likewiseidentified because of slight differences in shrinkage betweencast and extruded bars.4. Shrinkage Measure

15、ment4.1 Measure the distance between shrinkage referencemarks on dried or fired specimens to the closest 0.004 in.(0.1 mm) with calipers of suitable accuracy. Record the aver-age of at least ten measurements (one measurement on each ofthe group of ten or more specimens).1This test method is under th

16、e jurisdiction ofASTM Committee C21 on CeramicWhitewares and Related Products and is the direct responsibility of SubcommitteeC21.04 on Raw Materials.Current edition approved Oct. 1, 2018. Published October 2018. Originallyapproved in 1953. Last previous edition approved in 2014 as C326 09 (2014).DO

17、I: 10.1520/C0326-09R18.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles

18、on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.15. Calculation5.1 Calculate the linear drying shrinkage as a percentage ofplastic

19、 length, as follows:Sd5Lp2 LdLp3100 (1)where:Sd= linear drying shrinkage, %,Lp= plastic length of test specimen, andLd= dry length of test specimen.5.2 Calculate the total linear shrinkage after drying andfiring of clay shrinkage specimens as a percentage of plasticlength, as follows:St5Lp2 LfLp3100

20、 (2)where:St= total linear shrinkage after drying and firing, %,Lp= plastic length of test specimen, andLf= fired length of test specimen.5.3 When desired, volume shrinkage may be calculatedfrom linear shrinkage, as follows:Volume shrinkage, % 5 1 2 1 2 S/100!3# 100 (3)where:S = linear shrinkage, %.

21、5.4 The shrinkage factor is used to convert fired sizes toplastic sizes or mold sizes. Calculate as follows:Shrinkage factor 5 Lp/Lf(4)where:Lp= plastic length of test specimen, andLf= fired length of test specimen.6. Precision and Bias6.1 The direction of flow in forming influences the orienta-tion

22、 of the clay particles and the shrinkage. The shrinkagevalue should be related to the method of forming as well as thedimension of the ware.6.2 When the original reference points are 100 mm apart,the precision of the shrinkage measurement is 60.1 %.6.3 Measurements of drying shrinkage on one dimensi

23、on ofspecimens all formed by the same method should yield astandard deviation of 0.1 % or less.6.4 Measurement of total linear shrinkage after drying andfiring on one dimension of specimens should yield a standarddeviation of 0.25 % or less.7. Keywords7.1 clay; drying shrinkage; firing shrinkageSUMM

24、ARY OF CHANGESCommittee C21 has identified the location of selected changes to this standard since the last issue (C326 03)that may impact the use of this standard. (Approved Jan. 1, 2009.)(1) Addition of 1.2 describing the use of units in this testmethod, with renumbering of the subsequent subsecti

25、on of theScope.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of s

26、uch rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for add

27、itional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to t

28、he ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at th

29、e aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 09 (2018)2