ASTM C478-2015a Standard Specification for Circular Precast Reinforced Concrete Manhole Sections《圆形预制钢筋混凝土人孔型材的标准规格》.pdf

1、Designation: C478 15aStandard Specification forCircular Precast Reinforced Concrete Manhole Sections1This standard is issued under the fixed designation C478; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revisio

2、n. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.PART IGENERAL1. Scope1.1 This specification covers the m

3、anufacture and purchaserequirements of products used for the assembly and construc-tion of circular vertical precast reinforced concrete manholesand structures used in sewer, drainage, and water works.1.2 Part I, Sections 111, of this specification presentsgeneral requirements and requirements that

4、are common toeach precast concrete product covered by this specification.1.3 Part II of this specification presents specific require-ments for each manhole product in the following sections:Product SectionGrade Rings 12Flat Slab Tops 13Risers and Conical Tops 14Base Sections 15Steps and Ladders 16NO

5、TE 1Future products will to be included in Part II in a futurerevision of this specification.1.4 This specification is the inch-pound companion toSpecification C478M; therefore, no SI equivalents are pre-sented in the specification.NOTE 2This specification is a manufacturing and purchase specifica-t

6、ion only and does not include requirements for backfill, or the relation-ship between field load conditions and the strength requirements of themanhole products and appurtenances. Experience has shown, however,that the successful performance of this product depends upon the properselection of the pr

7、oduct strength, type of foundation and backfill, and carein the field installation of the manhole products and connecting pipes. Theowner of the project for which these products are specified herein iscautioned to require inspection at the construction site.2. Referenced Documents2.1 ASTM Standards:

8、2A615/A615M Specification for Deformed and Plain Carbon-Steel Bars for Concrete ReinforcementA706/A706M Specification for Deformed and Plain Low-Alloy Steel Bars for Concrete ReinforcementA1064/A1064M Specification for Carbon-Steel Wire andWelded Wire Reinforcement, Plain and Deformed, forConcreteC3

9、3/C33M Specification for Concrete AggregatesC39/C39M Test Method for Compressive Strength of Cylin-drical Concrete SpecimensC150/C150M Specification for Portland CementC260/C260M Specification for Air-Entraining Admixturesfor ConcreteC309 Specification for Liquid Membrane-Forming Com-pounds for Curi

10、ng ConcreteC494/C494M Specification for Chemical Admixtures forConcreteC497 Test Methods for Concrete Pipe, Manhole Sections, orTileC595/C595M Specification for Blended Hydraulic CementsC618 Specification for Coal Fly Ash and Raw or CalcinedNatural Pozzolan for Use in ConcreteC822 Terminology Relati

11、ng to Concrete Pipe and RelatedProductsC989/C989M Specification for Slag Cement for Use inConcrete and MortarsC1017/C1017M Specification for Chemical Admixtures forUse in Producing Flowing ConcreteC1116/C1116M Specification for Fiber-Reinforced ConcreteC1602/C1602M Specification for Mixing Water Use

12、d in theProduction of Hydraulic Cement Concrete2.2 ACI Standard:3318 Building Code, Requirements for Reinforced Concrete1This specification is under the jurisdiction of ASTM Committee C13 onConcrete Pipe and is the direct responsibility of Subcommittee C13.06 on Manholesand Specials.Current edition

13、approved Oct. 15, 2015. Published November 2015. Originallyapproved in 1961. Last previous edition approved in 2015 as C478 15. DOI:10.1520/C0478-15A.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStand

14、ards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from American Concrete Institute (ACI), P.O. Box 9094, FarmingtonHills, MI 48333-9094, http:/www.aci-int.org.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 194

15、28-2959. United States13. Terminology3.1 DefinitionsFor definitions of terms relating to precastreinforced concrete manholes, see Terminology C822.4. Materials and Manufacture4.1 General material requirements for precast reinforcedconcrete manhole products are presented in 4.1.1 4.1.9. Othermaterial

16、s or additional requirements for a product, if any, arecovered in the Part II section for that specific product.4.1.1 Reinforced ConcreteReinforced concrete shall con-sist of cementitious materials, mineral aggregates, admixtures,if used, and water, in which steel reinforcement has beenembedded in s

17、uch a manner so that the steel reinforcement andconcrete act together.4.1.2 Cementitious Materials:4.1.2.1 CementCement shall conform to the requirementsfor portland cement of Specification C150/C150M, or shall beportland blast-furnace slag cement, portland-limestone cement,or portland-pozzolan ceme

18、nt conforming to the requirementsof Specification C595/C595M, except that the pozzolan con-stituent of the Type IP portland-pozzolan cement shall be flyash.4.1.2.2 Fly AshFly ash shall conform to the requirementsof Class F or Class C of Specification C618.4.1.2.3 Slag CementSlag cement shall conform

19、 to therequirements of Grade 100 or 120 of Specification C989/C989M.4.1.3 Allowable Combinations of Cementitious MaterialsThe combination of cementitious materials used in the concreteshall be one of the following:4.1.3.1 Portland cement only,4.1.3.2 Portland blast-furnace slag cement only,4.1.3.3 P

20、ortland-pozzolan cement only,4.1.3.4 Portland-limestone cement only,4.1.3.5 A combination of portland cement or portland-limestone cement and slag cement,4.1.3.6 A combination of portland cement or portland-limestone cement, and fly ash, or4.1.3.7 A combination of portland cement or portland-limesto

21、ne cement, slag cement, and fly ash, or4.1.3.8 A combination of portland-pozzolan cement and flyash.4.1.4 AggregatesAggregates shall conform to Specifica-tion C33/C33M, except that the requirements for gradationshall not apply.4.1.5 AdmixturesThe following admixtures and blends areallowable:4.1.5.1

22、Air-entraining admixture conforming to Specifica-tion C260/C260M;4.1.5.2 Chemical admixture conforming to SpecificationC494/C494M;4.1.5.3 Chemical admixture for use in producing flowingconcrete conforming to Specification C1017/C1017M;4.1.5.4 Chemical admixture or blend approved by theowner.4.1.6 St

23、eel ReinforcementReinforcement shall consist ofwire and welded wire conforming to Specification A1064/A1064M or of bars conforming to Specification A615/A615M,Grade 40 or 60, or Specification A706/A706M, Grade 60.4.1.7 WaterWater used in the production of concrete shallbe potable or non-potable wate

24、r that meets the requirements ofSpecification C1602/C1602M.4.1.8 FiberSynthetic fibers and nonsynthetic fibers shallbe allowed to be used, at the manufacturers option, in concretemanholes as a nonstructural manufacturing material. Syntheticfibers (Type II and Type III) and nonsynthetic fiber (Type 1

25、)designed and manufactured specifically for use in concrete andconforming to the requirements of Specification C1116/C1116M shall be accepted.4.1.9 Other MaterialsOther materials required for a prod-uct and not covered in Section 4 will be covered in the Part IIsection for that specific product.5. D

26、esign5.1 Design requirements for a product are prescribed in thespecific Part II section for that product.5.1.1 The minimum compressive strength of concrete man-hole products covered by this specification shall be 4000 psiunless specified otherwise in Part II of this specification.5.2 Modified or Sp

27、ecial Design5.2.1 Manufacturers are not prohibited from submitting tothe owner, for approval prior to manufacture, designs otherthan those prescribed in the specific section for a product. Ifsuch approval is obtained, then the product shall meet all thetests and performance requirements specified by

28、 the owner inaccordance with the appropriate sections on manufacture andphysical requirements.5.2.2 If permitted by the owner, the manufacturer is notprohibited from requesting approval of designs of specialsections, such as reducers, tees, and bases.6. Reinforcement6.1 This section presents require

29、ments for reinforcementcover, continuity, laps, welds, and splices. Other reinforcementrequirements are presented in Section 4, and any additionalrequirements are given in the Part II section for a specificproduct.6.2 CoverThe exposure of the ends of reinforcement,stirrups or spacers used to positio

30、n the reinforcement duringplacement of the concrete shall not be cause for rejection.6.3 ContinuityThe continuity of the circumferential rein-forcement shall not be destroyed during the manufacture of theproduct, except when lift holes or pipe openings are providedin the product.6.4 Welded Steel Cag

31、e Laps, Welds, and Splices:6.4.1 If splices are not welded, the reinforcement shall belapped not less than 20 diameters for deformed bars, and 40diameters for plain bars and cold-drawn wire. In addition,where lapped cages of welded wire fabric are used withoutwelding, the lap shall contain a longitu

32、dinal wire.6.4.2 When splices are welded and are not lapped to theminimum requirements in 6.4.1, there shall be a minimum lapof 2 in. and a weld of sufficient length such that pull tests ofrepresentative specimens shall develop at least 50 % of theC478 15a2minimum specified tensile strength of the s

33、teel. For buttwelded splices in bars or wire, permitted only with helicallywound cages, pull tests of representative specimens shalldevelop at least 75 % of the minimum specified tensile strengthof the steel.6.5 Steel Hoop SplicesWhen splices are welded and arenot lapped to the minimum requirements

34、in 6.4.1, there shall bea minimum lap of 2 in. and a weld of sufficient length such thatpull tests from representative specimens shall develop at least50 % of the minimum specified tensile strength of the steel. Forbutt welded splices, pull tests from representative specimensshall develop at least 7

35、5 % of the minimum specified tensilestrength of the steel.7. Precast Concrete Manufacture7.1 MixtureThe aggregates shall be sized, graded,proportioned, and mixed with such proportions of cementitiousmaterials and water as will produce a thoroughly-mixedconcrete of such quality that the products will

36、 conform to thetest and design requirements of this specification. All concreteshall have a water-cementitious ratio not exceeding 0.53 byweight. Cementitious materials shall be as specified in 4.1.2and shall be added to the mix in a proportion not less than 470lb/yd3, unless mix designs with a lowe

37、r cementitious materialscontent demonstrate that the quality and performance of theproduct meet the requirements of this specification.7.2 CuringConcrete products shall be subjected to anyone of the methods of curing prescribed in 7.2.1 7.2.4 or toany other method or combination of methods approved

38、by theowner that will give satisfactory results.7.2.1 Steam CuringConcrete products are placed in acuring chamber, free of outside drafts, and cured in a moistatmosphere maintained by the injection of steam for such timeand such temperatures as needed to enable the products to meetthe strength requi

39、rements. The curing chamber shall be soconstructed as to allow full circulation of the steam around theentire product.7.2.2 Water CuringConcrete products are water-cured bycovering with water-saturated material, or by a system ofperforated pipes, mechanical sprinklers, porous hose, or by anyother ap

40、proved method that will keep the products moist duringthe curing period.7.2.3 Sealing MembraneA sealing membrane conformingto the requirements of Specification C309 is applied and shallbe left intact until the required concrete strength requirementsare met. The concrete at the time of application of

41、 themembrane shall be within 10F of the atmospheric tempera-ture. All concrete surfaces shall be kept moist prior to theapplication of the membrane and shall be damp when themembrane is applied.7.2.4 The manufacturer is not prohibited from combiningthe methods prescribed in 7.2.1 7.2.3 provided the

42、requiredconcrete compressive strength is attained.8. Acceptance8.1 Acceptance Procedures:8.1.1 Unless otherwise designated by the owner at the timeof, or before, placing an order, acceptance procedures forprecast reinforced concrete manhole products shall be asspecified in the Part II section for a

43、particular product, and shallnot be prohibited from consisting of one or more of thefollowing:8.1.1.1 Acceptance of a product on the basis of tests ofmaterials, including concrete compressive strength and absorp-tion.8.1.1.2 Acceptance of a product on the basis of inspection ofthe finished product,

44、including amount and placement ofreinforcement to determine conformance with the designprescribed under this specification, and freedom from defects.8.2 Test Methods:8.2.1 Concrete Compressive Strength Test:8.2.1.1 Type of SpecimenCompression tests for satisfyingthe minimum specified concrete streng

45、th requirement shall bemade on either concrete cylinders or, at the option of themanufacturer, on cores cut from the concrete manhole product.8.2.1.2 Compression Testing of CylindersCylinders shallbe made in accordance with Test Methods C497, and shall betested in accordance with Test Method C39/C39

46、M. For man-hole products, an owner shall not be prohibited from requiringconcrete compressive tests on cylinder specimens numberingin the amount of 5 % of the total order of a manhole product,but not to exceed two cylinders for each days production. Theaverage compressive strength of all cylinders t

47、ested shall beequal to or greater than the specified strength of the concrete.Not more than 10 % of the cylinders tested shall fall below thespecified strength of the concrete. In no case shall any cylindertested fall below 80 % of the specified strength of the concrete.8.2.1.3 Compression Testing o

48、f CoresCores shall be cutfrom the concrete manhole product and tested in accordancewith Test Methods C497, except that the requirements formoisture conditioning shall not apply. One core shall be takenfrom a manhole product selected at random from each daysproduction run of a single concrete strengt

49、h. When the concretecompressive strength of the core is equal to or greater than80 % of the specified strength of the concrete, the concretestrength of the production run is acceptable. If the core doesnot meet the preceding concrete strength requirement, anothercore from the same manhole product shall be taken and tested.8.2.1.4 If the concrete compressive strength of the recore isequal to or greater than 80 % of the specified strength of theconcrete, the concrete strength of the production run is accept-able. If the recore does not meet the pr