ASTM C515-2013(2018) Standard Specification for Chemical-Resistant Ceramic Tower Packings.pdf

1、Designation: C515 13 (Reapproved 2018)Standard Specification forChemical-Resistant Ceramic Tower Packings1This standard is issued under the fixed designation C515; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last re

2、vision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers fired ceramic shapes formedfrom naturally occurring clays and from compounded bodiesthat are used a

3、s packing in tower installations. These ceramicunits are designed primarily for use in process equipment forthe chemical or allied industries.1.2 The physical and chemical properties that affect qualityof packing materials are covered in this specification. Proper-ties that affect actual operational

4、 efficiency or characteristics ofprocessing towers are not covered.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.4 The following precautionary statement pertains to thetest method portion only, Section 7, of thi

5、s standard. Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to establish appropriate safety, health, andenvironmental practices and determine the applicability ofregulatory limitations prior to

6、use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarrier

7、s to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2C279 Specification for Chemical-Resistant Masonry UnitsC373 Test Methods for Determination of Water Absorptionand Associated Properties by Vacuum Method for PressedCeramic Tiles and Glass Tiles and Boil Method forExtruded Ceramic

8、Tiles and Non-tile Fired CeramicWhiteware ProductsE4 Practices for Force Verification of Testing Machines3. Terminology3.1 Definitions:3.1.1 tower packinga term covering variously shapedceramic pieces such as spheres, cylindrical rings with eithernormal or angular ends, rings with included obstructi

9、ons,perforated cylinders, and curved saddles. These shapes areused within columns or towers to provide inert surfaces forpromotion of energy transfer or chemical reaction betweenliquids and liquids, gases and liquids, and gases and gases.3.1.1.1 DiscussionClay: An earthy or stony mineral ag-gregate

10、consisting, essentially of hydrous silicates of alumina,plastic when sufficiently pulverized and wetted, rigid when dry,and vitreous when fired at a sufficiently high temperature.3.1.2 chemical stoneware tower packingpieces manufac-tured from specially compounded bodies consisting of claysand other

11、minerals, of natural origin.3.1.3 chemical porcelain tower packingpieces manufac-tured from specially compounded bodies, consisting of refinedclays and other naturally occurring minerals. These pieces arecharacteristically smooth-textured, vitreous, and white or lightgray in color.4. Shapes, Sizes,

12、and Quantities4.1 The number of dumped pieces of cylindrical-type pack-ing per cubic foot shall conform to the requirements for eachsize of rings, packings, and saddles as specified in Table 1,Table 2, and Table 3 or as negotiated between customer andsupplier.5. Tolerances for Rings5.1 Dimensional A

13、ccuracyThe average outside diameterand average length shall be within 65 % of specified size for80 % of a lot, and within 610 % of specified size for 100 % ofa lot.5.2 Measurement of the ring shall be made with calipers,avoiding flashes, protrusions, and obviously defective areas.The average outside

14、 diameter shall be determined as one halfthe sum of the maximum and minimum outside diameters. The1This specification is under the jurisdiction of ASTM Committee D32 onCatalysts and is the direct responsibility of Subcommittee D32.02 on Physical-Mechanical Properties.Current edition approved May 1,

15、2018. Published May 2018. Originallyapproved in 1963. Last previous edition approved in 2013 as C515 13. DOI:10.1520/C0515-13R18.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume informati

16、on, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization e

17、stablished in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1average length shall be determined as one half the sum of themaximum and minimum lengths.5.3 Ovalness

18、The difference between maximum and mini-mum outside diameters of any ring in a lot shall not exceed10 % of the specified size.5.4 InspectionThe sample plan and procedure shall be asagreed upon by the supplier and purchaser at time of purchase.NOTE 1See Table 2 for piece size counts of saddles which

19、define sizetolerances.6. Chemical Composition6.1 The appearance of iron or other leachable impurities onthe surfaces may be cause for rejection if this is a matter ofconcern to the purchaser.6.2 The presence of undesirable trace elements such asboron is to be considered as a special case and will be

20、 treatedas such by the purchaser and the manufacturer.7. Test Methods7.1 Crushing TestsMake crushing tests on any standardmachine conforming to the requirements of Practice E4. Breakten or more specimens between18-in. (3.2-mm) thick squaresof a metal that is oil-hardened to HR C60, with cushions of0

21、022-in. (0.56-mm) blotting paper between the hardened plateand the specimen as shown in Fig. 1. The loading rate shall bebetween 0.2 to 1.0 in. (5 to 25 mm)/min, or between 100 to 500lbf/min (445 to 2224 N/min). The report shall include theaverage load causing failure, calculated in pounds-force pe

22、rlinear inch (or newtons per metre) and the loading rate used.8. Physical Requirements8.1 Crushing StrengthCeramic tower packing in the formof rings must withstand a load of at least 25 lbf/linear in. (4.4kN) when the load is applied (distributed) along a full elementTABLE 1 Requirements For Shapes,

23、 Sizes, and Quantitiesof RingsRaschig RingsSize,Ain. (mm)Nominal WallThickness, in. (mm)ApproximateNumber perCubic FootB(0.03 m3)14 (6.4)132 to116 (0.8 to 1.6) 79 200516 (7.9)116 (1.6) 36 00038 (9.5)332 to116C(2.4 to 1.6) 22 50012 (12.7)332 (2.4) 9 96058 (15.9)332 to18C(2.4 to 3.2) 5 36034 (19.1)332

24、 to18C(2.4 to 3.2) 2 8901 (25.4)18 (3.2) 1 260114 (31.8)316 (4.8) 640112 (38.1)14 (6.4) 3602 (50.8)316 to14C(4.8 to 6.4) 1553 (76.2)38 (9.5) 64 to 744 (101.6)12 (12.7) 27 to 316 (152.4)58 (15.9) 8 to 9Lessing RingsSize,Ain. (mm)Nominal WallThickness, in. (mm)ApproximateNumber perCubic FootB(0.03 m3)

25、1 (25.4)18 (3.2) 1220114 (31.8)316 (4.8) 620112 (38.1)14 (6.4) 3302 (50.8)14 (6.4) to (9.5)C1423516 (7.9) to38 (9.5)C44438 (9.5) to12 (12.7)C22Cross Partition RingsSize,Ain. (mm)Nominal WallThickness, in. (mm)Number perCubic Foot(0.03 m3)SquareSetStaggerSet3 (76.2)516 (7.9) to38 (9.5) 64 744 (101.6)

26、38 (9.5) to12 (12.7) 27 316 (152.4)12 (12.7) 8 9AThis dimension describes both the specified length and the specified outsidediameter, and is intended as a guide rather than as an acceptance criterion.BDumped, except for values assigned to 3 in. (76.2 mm) of larger rings, which areusually stacked in

27、 square or stagger set. These numbers are to be considered asguides rather than as acceptance criteria.CRepresentative of different manufacturers practices.TABLE 2 Requirements for Sizes and Quantities of SaddlesSaddlesSaddleDesignationApproximateNumber perCubic FootA(0.03 m3)B14 115 00038 50 00012

28、17 00034 6 2001 2 100112 6502 240350AAs randomly dumped.B1 in. = 25.4 mm.TABLE 3 Requirements for Shapes, Sizes, andQuantities of SaddlesABerl SaddlesBSquare Cut SaddlesCSize, in.(mm)DMinimumNumber perCubic FootE(0.03 m3)Size, in.(mm)DMinimumNumber perCubic FootE(0.03 m3)1-4 96 05014 99 45012 15 840

29、12 18 63034 4 70034 61101 2 070 1 2 240112 630 112 6752 238 2 257ASaddle shapes and piece count shall conform to samples previously approved bythe consumer.BSee United States Patent 1,796,501. This saddle is disclosed in an expiredpatent. Interested parties are invited to submit information regardin

30、g the identifi-cation of an alternative(s) to this item to ASTM International Headquarters. Yourcomments will receive careful consideration at a meeting of the responsibletechnical committee,1which you may attend.CSee United States Patent 2,639,909. This saddle is disclosed in an expiredpatent. Inte

31、rested parties are invited to submit information regarding the identifi-cation of an alternative(s) to this item to ASTM International Headquarters. Yourcomments will receive careful consideration at a meeting of the responsibletechnical committee,1which you may attend.D1 in. = 25.4 mm.ESee Footnote

32、 B to Table 1.C515 13 (2018)2of the cylinder which lies in a longitudinal plane containing thecylinder axis. In the case of cross-partition rings, the load mustbe distributed along an element in a longitudinal plane con-taining the cylinder axis and midway between the partitions.8.2 Water Absorption

33、8.2.1 Porcelain packing shall absorb no more than 0.5weight percent water as determined in accordance with TestMethod C373.8.2.2 Stoneware packing shall absorb no more than 3 weightpercent water as determined in accordance with Test MethodC373.8.3 Acid-Resisting Properties.NOTE 2Ceramic tower packi

34、ngs are used in acidic or chemicallyneutral solutions and as heat transfer media.8.3.1 Porcelain packing shall lose no more than 4 % of itsoriginal weight when determined in accordance with Section 7of Specification C279.8.3.2 Stoneware packing shall lose no more than 10 % of itsoriginal weight as d

35、etermined in accordance with SpecificationC279.NOTE 3In preparing samples no attempt shall be made to remove theskin surface of the units and a significant random sample should be takenfor use in Specification C279.9. Precision and Bias9.1 The determination of water absorption by Test MethodC373 is

36、accurate to 60.2 % water absorption in interlaboratorytesting when the average value recorded by all laboratories isassumed to be the true water absorption. The precision isapproximately 60.1 % water absorption on measurementsmade by a single experienced operator.9.2 The original data on acid weight

37、 loss on eight (8)different types of cross partition rings run by four different labsin accordance with Specification C279 gave the followingstandard deviations:Type of Ring Standard Deviation1-in. porcelain 0.363-in. porcelain 0.421-in. Stoneware 0.483-in. Stoneware 0.923-in. Clay 3.2210. Keywords1

38、0.1 acid resistance; ceramic; chemical-resistant; crushingstrength; low absorption; porcelain; rings; saddles; stoneware;tower packingASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standa

39、rd are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif

40、 not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, whi

41、ch you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,U

42、nited States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Arrangement of Apparatus for Crushing TestC515 13 (2018)3