ASTM C56-2013 Standard Specification for Structural Clay Nonloadbearing Tile《结构用粘土非承重砖的标准规格》.pdf

1、Designation: C56 12C56 13Standard Specification forStructural Clay Nonloadbearing Tile1This standard is issued under the fixed designation C56; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision.Anumber in pa

2、rentheses indicates the year of last reapproval.Asuperscriptepsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers structural clay nonloadbearing tile

3、partition, fireproofing, and furring).1.2 The property requirements of this specification apply at the time of purchase. The use of results from testing of tile extractedfrom masonry structures for determining conformance or non-conformance to the property requirements (Section 45) of thisstandard

4、is beyond the scope of this specification.1.3 Tile covered by this specification are manufactured from clay, shale, or similar naturally occurring substances and subjectedto a heat treatment at elevated temperatures (firing). The heat treatment must develop sufficient fired bond between the particul

5、ateconstituents to provide the strength and durability requirements of this specification. (See firing and fired bond in TerminologyC1232.)1.4 Fireproofing tile intended for use in load-bearing masonry shall conform to Specification C34.1.5 Tile intended for use in fireproofing structural members sh

6、all be of such sizes and shapes that they can be erected to covercompletely the exposed surfaces of the members.1.6 The text of this specification references notes and footnotes that provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be considere

7、d as requirements of this specification.1.7 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1 This specification is under the jurisdict

8、ion of ASTM Committee C15 on Manufactured Masonry Units and is the direct responsibility of Subcommittee C15.02 on Brickand Structural Clay Tile.Current edition approved Dec. 1, 2012Dec. 1, 2013. Published January 2013December 2013. Originally approved in 1924. Last previous edition approved in 2010

9、2012as C56 10.C56 12. DOI: 10.1520/C0056-12.10.1520/C0056-13.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all cha

10、nges accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Ba

11、rr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States12. Referenced Documents2.1 ASTM Standards:2C34 Specification for Structural Clay Load-Bearing Wall TileC67 Test Methods for Sampling and Testing Brick and Structural Clay TileC1232 Terminology of Masonry3. Terminology3.1 D

12、efinitionsFor definitions relating to structural clay nonload-bearing wall tile, refer to Terminology C1232.4. Classification4.1 One grade of tile is covered, designated Grade NB.4.2 If tile having a particular color (Note 1), texture, or finish are desired, these features shall be specified separat

13、ely by thepurchaser.NOTE 1Color of tile varies with the type of clay used and degree of firing; hence, it cannot be taken as indicative of classification until after it hasbeen related to absorption by actual tests.5. Physical Properties5.1 Structural clay nonloadbearing tile shall conform to the fo

14、llowing requirements for absorption:Absorption by 1-h Boiling,A %Grade Individual MaximumNB 28AThe range in percentage absorption for tile delivered to any one job shall be not more than 12.6. Dimensions and Permissible Variations6.1 No overall dimension shall vary more than 3 % over or under the sp

15、ecified dimension for any form or size of tile. See Note2.NOTE 2Purchasers and designers should ascertain the type and size of tile, modular or non-modular, available in the locality under consideration andshould specify accordingly, stating the size and type represented by the available tile.Modula

16、r sizes are designated by the specified nominal dimensions which are equal to the actual manufactured dimensions plus the thickness of onemortar joint, not to exceed 12 in. (12.7 mm). For example, if the modular, specified, or nominal dimensions of a unit are 4 by 8 by 12 in. (102 by 203by 305 mm) t

17、he actual manufactured dimensions may be 312 by 712 by 1112 in. (114.7 by 215.7 by 317.7 mm).7. Finish and Appearance7.1 All tile shall be reasonably free of laminations and of cracks, blisters, surface roughness, and other defects that wouldinterfere with the proper setting of the tile or impair th

18、e strength or permanence of the construction.7.2 The finish of the outer face or faces of tile shall be plaster-base finish or exposed wall finish as specified in the invitationfor bids.7.3 Surfaces of tile for plaster-base finish shall be smooth, scored, combed, or roughened. When smooth, the tile

19、shall be freeof glaze and the absorption shall be not less than 5 % nor more than 25 %. When scored, each groove shall be not less than 116in. (1.6 mm) nor more than 116 in. (6.4 mm) in depth, and not more than 1 in. (25.4 mm) in width. The area covered by the groovesshall not exceed 50 % of the are

20、a of the scored faces. When combed, the tile shall be scratched or scarified prior to firing bymechanical means which shall make scratches or scarifications on the surface of the tile not less than 116 in. nor more than 18 in.(3.2 mm) in depth, and not more than 14 in. apart. When roughened, the die

21、 skin on the face of the tile shall be entirely brokenby mechanical means, such as wire cutting or wire brushing. (The die skin may be observed within the cells of the tile.)7.4 Surfaces of tile with exposed finish shall be smooth, combed, or roughened. Combed or roughened tile surfaces shallconform

22、 to the requirements for these finishes given in 6.37.3.8. Number of Cells and Weights8.1 Partition and split furring tile shall conform to the requirements prescribed in Table 1 for total number of cells, number ofcells in the direction of wall thickness, and weight per unit area.2 For referencedAS

23、TM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.C56 1328.2 The requirements for minimum weight per unit area of structural clay

24、 nonloadbearing tile shall be waived if the overallthickness of the shells, measured between the inner and extreme outer surfaces of scored tile, is not less than 58 in. (15.9 mm) andthe mean shell thickness of unscored tile is not less than 12 in. (12.7 mm). Thickness of webs shall be not less than

25、 12 in. (12.7mm).9. Sampling and Testing9.1 The purchaser or his authorized representative shall be accorded proper facilities for sampling and inspection of units bothat the place of manufacture and at the site of the work.At least 10 days from the time of sampling should be allowed for completiono

26、f the tests.9.2 Tile shall be sampled and tested in accordance with Test Methods C67.NOTE 3Unless otherwise specified in the purchase order, the cost of tests is typically borne as follows: If the results of the tests show that the tiledo not conform to the requirements of this specification, the co

27、st is typically borne by the seller. If the results of the test show that the tile do conformto the requirements of this specification, the cost is typically borne by the purchaser.10. Rejection10.1 In case the shipment fails to conform to the requirements, the manufacturer is permitted to sort it,

28、and new specimens shallbe selected by the purchaser from the retained lot and tested at the expense of the manufacturer. In case the second set of specimensfails to meet the requirements, the entire lot shall be rejected.11. Keywords11.1 clay; masonry construction; nonloadbearing tile; physical prop

29、erties; shale; tileSUMMARY OF CHANGESCommittee C15 has identified the location of selected changes to this standard since the last issue (C56 12)that may impact the use of this standard. (December 1, 2013)(1) Added Terminology section (Section 3) and renumbered subsequent sections.SUMMARY OF CHANGES

30、Committee C15 has identified the location of selected changes to this standard since the last issue (C56 10)that may impact the use of this standard. (Approved Dec. 1, 2012.)(1) Selected sections within the standard were reorganized using the ASTM Form and Style manual as a guide.TABLE 1 Number of C

31、ells and Weight of TileDimensions, in. (mm)Minimum Number of Cells Minimum Weight per Unit AreaA , lb/ft2 (kg/m2)In UnitIn Directionof WallThicknessAverage IndividualPartition Tile2 by 12 by 12 51 by 305 by 305) 3 1 14 (68) 13 (63)3 by 12 by 12 (76 by 305 by 305) 3 1 15 (73) 14 (68)4 by 12 by 12 (10

32、2 by 305 by305)3 1 16 (78) 15 (73)6 by 12 by 12 (152 by 305 by305)3 1 22 (107) 21 (102)6 by 12 by 12 (152 by 305 by305)4 2 25 (112) 24 (117)8 by 12 by 12 (203 by 305 by305)4 2 30 (146) 28 (137)10 by 12 by 12 (254 by 305 by305)4 2 35 (161) 33 (161)12 by 12 by 12 (305 by 305 by305)4 2 40 (195) 38 (185

33、)Split Furring Tile112 by 12 by 12 (38 by 305 by 305) 3 . 712 (37) 7 (34)2 by 12 by 12 (51 by 305 by 305) 3 . 8 (39) 712 (37)A The weights given in the table are for scored tile. If any of the faces are unscored, the weights shall be increased 0.5 lb/ft2 (2.4 kg/m2) of unscored area.C56 133ASTM Inte

34、rnational takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely

35、 their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand shou

36、ld be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Stan

37、dards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C56 134