ASTM C56-2013(2017) Standard Specification for Structural Clay Nonloadbearing Tile《结构粘土非承重砖标准规范》.pdf

1、Designation: C56 13 (Reapproved 2017)Standard Specification forStructural Clay Nonloadbearing Tile1This standard is issued under the fixed designation C56; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the year of last revision.

2、A number in parentheses indicates the year of last reapproval. A superscriptepsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification covers structural clay nonlo

3、adbearingtile (partition, fireproofing, and furring).1.2 The property requirements of this specification apply atthe time of purchase. The use of results from testing of tileextracted from masonry structures for determining confor-mance or non-conformance to the property requirements (Sec-tion 5) of

4、 this standard is beyond the scope of this specification.1.3 Tile covered by this specification are manufactured fromclay, shale, or similar naturally occurring substances andsubjected to a heat treatment at elevated temperatures (firing).The heat treatment must develop sufficient fired bond between

5、the particulate constituents to provide the strength and dura-bility requirements of this specification. (See firing and firedbond in Terminology C1232.)1.4 Fireproofing tile intended for use in load-bearing ma-sonry shall conform to Specification C34.1.5 Tile intended for use in fireproofing struct

6、ural membersshall be of such sizes and shapes that they can be erected tocover completely the exposed surfaces of the members.1.6 The text of this specification references notes andfootnotes that provide explanatory material. These notes andfootnotes (excluding those in tables and figures) shall not

7、 beconsidered as requirements of this specification.1.7 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.8 This international standard w

8、as developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referen

9、ced Documents2.1 ASTM Standards:2C34 Specification for Structural Clay Loadbearing Wall TileC67 Test Methods for Sampling and Testing Brick andStructural Clay TileC1232 Terminology for Masonry3. Terminology3.1 DefinitionsFor definitions relating to structural claynonload-bearing wall tile, refer to

10、Terminology C1232.4. Classification4.1 One grade of tile is covered, designated Grade NB.4.2 If tile having a particular color (Note 1), texture, orfinish are desired, these features shall be specified separatelyby the purchaser.NOTE 1Color of tile varies with the type of clay used and degree offiri

11、ng; hence, it cannot be taken as indicative of classification until after ithas been related to absorption by actual tests.5. Physical Properties5.1 Structural clay nonloadbearing tile shall conform to thefollowing requirements for absorption:Absorption by 1-h Boiling,A%Grade Individual MaximumNB 28

12、AThe range in percentage absorption for tile delivered to any one job shall be notmore than 12.6. Dimensions and Permissible Variations6.1 No overall dimension shall vary more than 3 % over orunder the specified dimension for any form or size of tile. SeeNote 2.NOTE 2Purchasers and designers should

13、ascertain the type and size oftile, modular or non-modular, available in the locality under consideration1This specification is under the jurisdiction of ASTM Committee C15 onManufactured Masonry Units and is the direct responsibility of SubcommitteeC15.02 on Brick and Structural Clay Tile.Current e

14、dition approved Dec. 1, 2017. Published January 2018. Originallyapproved in 1924. Last previous edition approved in 2013 as C56 13. DOI:10.1520/C0056-13R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of AST

15、MStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard

16、 was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1and shoul

17、d specify accordingly, stating the size and type represented bythe available tile.Modular sizes are designated by the specified nominal dimensionswhich are equal to the actual manufactured dimensions plus the thicknessof one mortar joint, not to exceed12 in. (12.7 mm). For example, if themodular, sp

18、ecified, or nominal dimensions of a unit are 4 by 8 by 12 in.(102 by 203 by 305 mm) the actual manufactured dimensions may be 312by 712 by 1112 in. (114.7 by 215.7 by 317.7 mm).7. Finish and Appearance7.1 All tile shall be reasonably free of laminations and ofcracks, blisters, surface roughness, and

19、 other defects thatwould interfere with the proper setting of the tile or impair thestrength or permanence of the construction.7.2 The finish of the outer face or faces of tile shall beplaster-base finish or exposed wall finish as specified in theinvitation for bids.7.3 Surfaces of tile for plaster-

20、base finish shall be smooth,scored, combed, or roughened. When smooth, the tile shall befree of glaze and the absorption shall be not less than 5 % normore than 25 %. When scored, each groove shall be not lessthan116 in. (1.6 mm) nor more than116 in. (6.4 mm) in depth,and not more than 1 in. (25.4 m

21、m) in width. The area coveredby the grooves shall not exceed 50 % of the area of the scoredfaces. When combed, the tile shall be scratched or scarifiedprior to firing by mechanical means which shall make scratchesor scarifications on the surface of the tile not less than116 in.nor more than18 in. (3

22、.2 mm) in depth, and not more than14in. apart. When roughened, the die skin on the face of the tileshall be entirely broken by mechanical means, such as wirecutting or wire brushing. (The die skin may be observed withinthe cells of the tile.)7.4 Surfaces of tile with exposed finish shall be smooth,c

23、ombed, or roughened. Combed or roughened tile surfacesshall conform to the requirements for these finishes given in7.3.8. Number of Cells and Weights8.1 Partition and split furring tile shall conform to therequirements prescribed in Table 1 for total number of cells,number of cells in the direction

24、of wall thickness, and weightper unit area.8.2 The requirements for minimum weight per unit area ofstructural clay nonloadbearing tile shall be waived if theoverall thickness of the shells, measured between the inner andextreme outer surfaces of scored tile, is not less than58 in.(15.9 mm) and the m

25、ean shell thickness of unscored tile is notless than12 in. (12.7 mm). Thickness of webs shall be not lessthan12 in. (12.7 mm).9. Sampling and Testing9.1 The purchaser or his authorized representative shall beaccorded proper facilities for sampling and inspection of unitsboth at the place of manufact

26、ure and at the site of the work. Atleast 10 days from the time of sampling should be allowed forcompletion of the tests.9.2 Tile shall be sampled and tested in accordance with TestMethods C67.NOTE 3Unless otherwise specified in the purchase order, the cost oftests is typically borne as follows: If t

27、he results of the tests show that thetile do not conform to the requirements of this specification, the cost istypically borne by the seller. If the results of the test show that the tile doconform to the requirements of this specification, the cost is typicallyborne by the purchaser.10. Rejection10

28、.1 In case the shipment fails to conform to therequirements, the manufacturer is permitted to sort it, and newspecimens shall be selected by the purchaser from the retainedlot and tested at the expense of the manufacturer. In case thesecond set of specimens fails to meet the requirements, theentire

29、lot shall be rejected.TABLE 1 Number of Cells and Weight of TileDimensions, in. (mm)Minimum Number of Cells Minimum Weight per Unit AreaA, lb/ft2(kg/m2)In UnitIn Directionof WallThicknessAverage IndividualPartition Tile2 by 12 by 12 51 by 305 by 305) 3 1 14 (68) 13 (63)3 by 12 by 12 (76 by 305 by 30

30、5) 3 1 15 (73) 14 (68)4 by 12 by 12 (102 by 305 by305)3 1 16 (78) 15 (73)6 by 12 by 12 (152 by 305 by305)3 1 22 (107) 21 (102)6 by 12 by 12 (152 by 305 by305)4 2 25 (112) 24 (117)8 by 12 by 12 (203 by 305 by305)4 2 30 (146) 28 (137)10 by 12 by 12 (254 by 305 by305)4 2 35 (161) 33 (161)12 by 12 by 12

31、 (305 by 305 by305)4 2 40 (195) 38 (185)Split Furring Tile112 by 12 by 12 (38 by 305 by 305) 3 . 712 (37) 7 (34)2 by 12 by 12 (51 by 305 by 305) 3 . 8 (39) 712 (37)AThe weights given in the table are for scored tile. If any of the faces are unscored, the weights shall be increased 0.5 lb/ft2(2.4 kg/

32、m2) of unscored area.C56 13 (2017)211. Keywords11.1 clay; masonry construction; nonloadbearing tile; physi-cal properties; shale; tileASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standa

33、rd are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif

34、 not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, whi

35、ch you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,U

36、nited States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 13 (2017)3