ASTM C836 C836M-2012 Standard Specification for High Solids Content Cold Liquid-Applied Elastomeric Waterproofing Membrane for Use with Separate Wearing Course《与独立磨损层一起使用的高固体含量 应用冷.pdf

1、Designation:C836/C836M11a Designation: C836/C836M 12Standard Specification forHigh Solids Content, Cold Liquid-Applied ElastomericWaterproofing Membrane for Use with Separate WearingCourse1This standard is issued under the fixed designation C836/C836M; the number immediately following the designatio

2、n indicates the yearof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agenc

3、ies of the Department of Defense.1. Scope1.1 This specification describes the required properties and test methods for a cold liquid-applied elastomeric-type membrane,one- or two-component, for waterproofing building decks and walls subject to hydrostatic pressure in building areas to be occupiedby

4、personnel, vehicles, or equipment. This specification applies only to a membrane system that will be covered with a separatewearing course, traffic course, or backfill.NOTE 1See Guide C898 and Guide C1471 for proper application of membrane.1.2 There are no ISO standards similar or equivalent to this

5、 ASTM standard.1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non

6、-conformance with the standard.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations

7、 prior to use.2. Referenced Documents2.1 ASTM Standards:2C717 Terminology of Building Seals and SealantsC794 Test Method for Adhesion-in-Peel of Elastomeric Joint SealantsC898 Guide for Use of High Solids Content, Cold Liquid-Applied Elastomeric Waterproofing Membrane with SeparateWearing CourseC125

8、0 Test Method for Nonvolatile Content of Cold Liquid-Applied Elastomeric Waterproofing MembranesC1305 Test Method for Crack Bridging Ability of Liquid-Applied Waterproofing MembraneC1375 Guide for Substrates Used in Testing Building Seals and SealantsC1471 Guide for the Use of High Solids Content Co

9、ld Liquid-Applied Elastomeric Waterproofing Membrane on VerticalSurfacesC1522 Test Method for Extensibility After Heat Aging of Cold Liquid-Applied Elastomeric Waterproofing MembranesD2240 Test Method for Rubber PropertyDurometer Hardness3. Terminology3.1 DefinitionsRefer to Terminology C717 for def

10、initions of the terms used in this specification.4. Classification4.1 Types:4.1.1 Type IA one-component, cold liquid-applied waterproofing material suitable for immediate application after mixing.Type I products may be used with an accelerator that is beneficial but not essential for curing of the m

11、embrane.1This specification is under the jurisdiction of ASTM Committee D08 on Roofing and Waterproofing and is the direct responsibility of Subcommittee D08.22 onWaterproofing and Dampproofing Systems.Current edition approved JulyMay 1, 2011.2012. Published July 2011.May 2012. Originally approved i

12、n 1976. Last previous edition approved in 2011 asC836/C836M 11a. DOI: 10.1520/C0836_C0836M-11A2.2For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Docum

13、ent Summary page on the ASTM website.1This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM r

14、ecommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.4.1.2 Type

15、 IIAtwo-component, cold liquid-applied waterproofing material. Combining two components is essential for curingof the membrane.5. Physical Requirements5.1 MaterialMembrane materials shall cure, after application by spreading or spraying, to form an elastomeric film capableof maintaining a seal again

16、st liquid water.5.2 The physical, mechanical, and performance properties of the membrane shall conform to the requirements described inTable 1.6. Test Methods6.1 Standard ConditionsStandard conditions for all tests shall be 23 6 2C 73.4 6 3.6F and 50 6 5 % relative humidity.6.2 Conditioning/Mixing:6

17、.2.1 Store all membrane materials to be tested in an unopened container at standard conditions for at least 24 h before any testspecimens are prepared.6.2.2 Follow the manufacturers instructions for mixing and preparing membrane materials for testing. Thoroughly mixone-component samples before using

18、. Mix two-component compounds in the ratio recommended by the manufacturer.6.3 Test SurfacesIn addition to the mortar test surfaces specified, use other test surfaces when required by the specifier.6.4 PrimerWhen required by the manufacturer, use a primer as directed by the manufacturer on all subst

19、rate materials in testassemblies.6.5 Hardness:6.5.1 Following the manufacturers instructions, apply a film of membrane, 1.5 6 0.1 mm 60 6 5 mils thick, on a 100 by150-mm 4 by 6-in. piece of polyethylene film-coated paper and allow the membrane to cure for 14 days at standard conditions.If more than

20、one application is required, the total time for film application shall not exceed 48 h.6.5.2 After curing, strip the film from the coated paper, cut into pieces, and lay the pieces one upon another to provide a testspecimen meeting the requirements of Test Method D2240.6.5.3 Using a Type 00 hardness

21、 gauge, obtain an instantaneous reading of the film hardness as specified in Test Method D2240.6.6 Weight Loss:6.6.1 Test in compliance with the requirements of Test Method C1250.6.7 Low-Temperature Crack Bridging:6.7.1 Test in compliance with the requirements of Test Method C1305.6.8 Film Thickness

22、 on Vertical Surface:6.8.1 Prepare mortar test blocks 152 by 76 by 25 mm 6 by 3 by 1 in. as described in Guide C1375.6.8.2 Prepare the test assembly by covering one cut face of a mortar slab with a film of membrane material 1.5 6 0.1 mm 606 5 mils in thickness, mixed and applied in accordance with t

23、he manufacturers directions. Install the film in one applicationunless manufacturers application instructions require application in several coats. If applied in several coats, the test substrate shallbe set in a vertical position between applications, and the complete film thickness shall be accomp

24、lished in 48 h in accordance withthe manufacturers instructions.6.8.3 Immediately after applying the film, place the coated slab on its end, in a vertical position, and let remain in this positionfor 24 h at standard conditions.6.8.4 Using a vernier caliper, measure the thickness of the total assemb

25、ly at five points within 25 mm 1 in. of the top end ofthe slab. Cover the film at each point of measurement with a 25-mm 1 in. square piece of aluminum, 0.5 mm 0.002 in. thick,to prevent point indentation on the film.6.8.5 Cut a 25-mm 1-in. wide band of film from across the top of the mortar strip.

26、Measure the thickness of the test mortarin approximately the same five locations that measurements were made in 6.8.4. Determine the average.6.8.6 Determine the film thickness by subtracting the average test mortar thickness from the average total assembly thickness(test mortar and film).TABLE 1 Hig

27、h Solids Content, Cold Liquid-Applied Elastomeric Waterproofing Membrane Physical RequirementsProperty Requirement Test MethodHardness, Type 00, min 50 D2240 as modified in section 6.5 ofthis specificationWeight loss, max, % 20 C1250Nonvolatile, min, % 80Low temperature crack bridging no cracking C1

28、305Film thickness (vertical surface),min, mm mils1.5 6 0.1 60 6 5 See section 6.8 of this specificationAAdhesion-in-Peel after waterimmersion, N lbf4.4 1 C794 as modified in section 6.9 ofthis specificationExtensibility after heat aging, min,mm in.6.4 14 , no cracking C1522Stability, min, months 6 S

29、ee section 6.11 of this specifcation.ANumbers refer to portions of the Test Methods section, Section 6, of this specification.C836/C836M 1226.9 Adhesion-in-Peel After Water Immersion:6.9.1 Perform the test as specified in Test Method C794 with the following qualifications:6.9.1.1 Mortar shall be the

30、 test substrate. Other substrates may be tested when specified.6.9.1.2 The cure conditions shall be 14 days at standard conditions, followed by 7 days at 70 6 2C 158 6 3.6F.6.9.1.3 After the specimen has cured for about 7 days, coat the cloth with a layer of the compound about 2.5 mm 0.1 in. thickto

31、 help minimize cloth failure.6.10 Extensibility After Heat Aging:6.10.1 Test in compliance with the requirements of Test Method C1522.6.11 StabilityWhen stored at a temperature not exceeding 27C 80F in a dry environment, or kept protected from moisture,or both, the membrane material shall be capable

32、 of meeting the requirements of this specification for at least 6 months from thetime of delivery.7. Precision and Bias7.1 PrecisionThe precision of the procedure in No information is presented about either the precision or bias of theprocedure in 6.8 for measuring film thickness on a vertical surfa

33、ce is being determined. for measuring film thickness on a verticalsurface.8. Rejection and Resubmittal8.1 Failure to conform to any one of the requirements prescribed in this specification shall constitute grounds for rejection. Theseller shall have the right to reinspect the rejected shipment and r

34、esubmit the lot after removal of those packages not conformingto the specified requirements.9. Packaging and Product Marking9.1 Shipping containers shall be labeled to indicate compliance with this specification including classification.9.2 The date of production shall be marked on each package.9.3

35、The material shall be packaged in standard commercial containers constructed so as to ensure acceptance by common orother carrier for safe transportation to the point of delivery. Shipping containers shall be marked with the name, type, and quantityof the material contained therein, as defined by th

36、e contract or order under which the shipments are made.10. Keywords10.1 crack bridging; membrane; waterproofingASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advise

37、d that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either re

38、approved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If y

39、ou feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individua

40、l reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).C836/C836M 123