1、Designation: D 1817 05Standard Test Method forRubber ChemicalsDensity1This standard is issued under the fixed designation D 1817; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses in

2、dicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the densityof solid chemicals used as rubber additives during processingand manufacture. It is intended for deter

3、mining the density ofthe rubber chemical itself and not for the determination of theeffective density of the chemical in a rubber.1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 This standard does not purport to address

4、all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2E1 Specification f

5、or ASTM Liquid-in-Glass ThermometersE 300 Practice for Sampling Industrial Chemicals3. Summary of Test Method3.1 The density of the test specimen is obtained via wetpycnometry.4. Significance and Use4.1 The density of a rubber chemical is used for calculatingthe rubber compound volume, which is used

6、 to determine thecost of a rubber product. The density may also be used as a rawmaterial control tool.5. Apparatus5.1 Pycnometer, 50-cm3capacity.NOTE 1The weld type with the cap seal on the outside of the neck ofthe bottle is preferred because there is less danger of trapping air justunder the capil

7、lary tube than with types having the ground seal on theinside of the neck. The stopper may contain a thermometer. However, thecontrol of the temperature is through the adjustment of the water bathrather than by this thermometer.5.2 Water Bath, maintained at 23 6 0.5C and equippedwith a stirring devi

8、ce.5.3 Pressure MeterA gage or manometer that is accurateto 0.2 kPa, is required to measure the differential pressurebetween the outside and inside of the system.5.3.1 Alternatively, a device for measuring the absolutepressure inside the system can be used. The range of themeasuring device should be

9、 at least 100 kPa for differentialpressure meters and at least 10 kPa for absolute pressuremeters.5.4 DesiccatorA glass desiccator constructed with heavywalls to withstand a differential pressure of 100 kPa and withan opening at the side or top. The desiccator should be enclosedin a sturdy box or sh

10、ield to prevent possible injury to theoperator.5.5 Vacuum PumpAn oil-filled, motor-driven pump, ca-pable of reducing the absolute pressure of the system to 2 kPa.5.6 Thermometer, having a minimum range from 10 to 30Cand graduated in 0.1C divisions. ASTM Solidification PointThermometer having a range

11、 from 0 to 30C and conformingto the requirements for Thermometer 90C as prescribed inSpecification E1, may be used.5.7 Weighing BottleA wide-mouth, cylindrical, glassweighing bottle (about 30 mm in height and 70 mm indiameter) provided with a ground-glass stopper.6. Sampling6.1 Select a representati

12、ve sample of the chemical to betested in accordance with the appropriate section of PracticeE 300.1This test method is under the jurisdiction of ASTM Committee D11 on Rubberand is the direct responsibility of Subcommittee D11.11 on Chemical Analysis.Current edition approved Dec. 1, 2005. Published J

13、anuary 2006. Originallyapproved in 1961. Last previous edition approved in 2001 as D 1817 01e1.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Documen

14、t Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6.2 Mesh SizeRubber chemicals are generally in the formof powders that require no further treatment. Grind any lumps,pellets, and so forth, to pass a 1

15、49-m sieve prior to thedetermination.6.3 DryingIt is not necessary to dry rubber chemicals,unless it is known that they contain sufficient water to interferewith an accurate density measurement. If necessary, dry toconstant mass at least 10C below the melting pointing but notabove 110C.7. Immersion

16、Liquid7.1 An immersion liquid should be chosen in which noportion of the rubber chemical (major component, impurity, oradded component) is soluble and which will not react with anyportion of the rubber chemical. Refined white kerosene ofnarrow boiling range and low evaporation rate may sometimesbe u

17、sed. Other immersion liquids such as ethylene glycol,tetrahydronaphthalene, and so forth, may be suitable. If animmersion liquid cannot be found that meets these solubilityrequirements, an immersion liquid saturated with the solublecomponents of the sample shall be used.8. Standardization of Pycnome

18、ter8.1 Fill the pycnometer with freshly boiled distilled water at20 to 22C; gradually bring to 23 6 0.5C in the water bath,and then remove, dry, and weigh it as described in 9.1. Emptythe pycnometer, then clean, dry, and reweigh it. Next, fill thepycnometer with the immersion liquid at 22C or less,

19、andbring to 23 6 0.5C in the water bath. Remove from the bath,dry, and weigh as before. Calculate the density of the immer-sion liquid as follows:Density at 23C, Mg/m35 A/B! 3 0.997 (1)where:A = mass of immersion liquid, andB = mass of water,0.9976 = density of water at 23C, Mg/m3.9. Procedure9.1 We

20、ighingTransfer a sufficient amount of the testspecimen to a clean, dry, weighed pycnometer to form a layerapproximately 19 mm (34 in.) deep and reweigh. Weigh rubberchemicals of a hygroscopic nature from a weighing bottle.9.2 Addition of Immersion LiquidAdd sufficient immer-sion liquid to the pycnom

21、eter to form a thin layer above therubber chemical. When necessary, swirl the contents of thepycnometer by hand, to wet the sample.9.3 Removal of Occluded AirPlace the pycnometer in thedesiccator, close, and attach to the pump for the removal of air.Take care not to decrease the pressure too quickly

22、, otherwisesome of the sample may be lost due to the sudden removal ofthe entrapped air. A pinch-cock may be used to control the rateof evacuation. The pressure meter is used to indicate whetherthe oil pump is giving the proper vacuum, which is an absolutepressure of 0.2 kPa. Bubbles of air rise fro

23、m the sample rapidlyat first, then decrease and finally stop. The time required forcomplete removal of air may vary from 30 min to 24 h. Whenno more bubbles can be seen, it may be assumed that occludedair has been removed and the rubber chemical is thoroughlywet with immersion liquid. Slowly readmit

24、 air to the desicca-tor.NOTE 2If an immersion liquid is used whose vapor pressure is greaterthan 0.2 kPa at room temperature, the liquid will evaporate, often with“bumping.” Therefore it is necessary to adjust the vacuum to a higherpressure with some loss in effectiveness of air removal. The use of

25、suchimmersion liquids should be limited to those cases in which no low vaporpressure liquid can be used. In no case should a mixed liquid be used inwhich any component has an appreciable vapor pressure.9.4 Final AdjustmentRemove the pycnometer from thedesiccator, fill with immersion liquid at 22C or

26、 less, takingcare to add a sufficient quantity to prevent air bubbles remain-ing in the pycnometer when closed. Insert the stopper, beingcareful not to trap any air bubbles. Place the pycnometer in thewater bath and permit it to come to constant temperature at 236 0.5C. Remove from the water bath, w

27、ipe the end of thecapillary with lint-free toweling or lens paper, making sure notto suck any liquid from the capillary. Cap the capillary. Dip thepycnometer (up to the side arm) in a beaker of alcohol toremove any residual immersion liquid. Thoroughly dry theoutside of the pycnometer and weigh.9.5

28、Number of SpecimensMake duplicate tests on allspecimens.10. Calculation10.1 Calculate the density of the rubber chemical as fol-lows:Density at 23C, Mg/m35 PS/P 1 K! 2 F (2)where:P = mass of rubber chemical used,S = density of the immersion liquid,K = mass of the pycnometer filled with immersion liq

29、uid,andF = final mass of the pycnometer with rubber chemicaland immersion liquid.11. Report11.1 Report the following information:11.1.1 Sample identification11.1.2 Density at 23C, Mg/m3, and11.1.3 Immersion liquid used.12. Precision and Bias12.1 PrecisionThis test method has not been tested forrepro

30、ducibility or repeatability, but duplicate determinations onthe same sample should not differ by more than 0.02 Mg/m3at23C.12.2 BiasNo statement about bias is being made at thistime.13. Keywords13.1 density; rubber chemicalsD1817052ASTM International takes no position respecting the validity of any

31、patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revis

32、ion at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your c

33、omments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrig

34、hted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D1817053