ASTM D517-1998(2003) Standard Specification for Asphalt Plank《沥青厚板材》.pdf

1、Designation: D 517 98 (Reapproved 2003)Standard Specification forAsphalt Plank1This standard is issued under the fixed designation D 517; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parent

2、heses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers asphalt plank used for bridgedecks as well

3、as for industrial floors.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this

4、standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Classification2.1 Type I, aPlain, butt-edge asphalt plank for use as anindustrial flooring.2.2 Type I, bPlain, butt-edge asphalt plank for use on arailroad bridge

5、 as a waterproofing system protection layer.2.3 Type IIShip-lap edge asphalt plank for use on arailroad bridge as a waterproofing system protection layer.3. Ordering Information3.1 The user should state the type and dimensions in thepurchase order. If no type is specified, Type I shall befurnished.4

6、. Materials and Manufacture4.1 Asphalt plank shall be formed from a mixture of asphalt,fibers, modifiers, or a combination thereof, and mineral filler insuch a manner as to produce a uniformly dense mass.4.2 In the case of Type II asphalt plank, the edges of theplanks shall be of a lap joint configu

7、ration.5. Requirements5.1 AsphaltThe asphalt cement shall have such character-istics that when combined with the other ingredients, a plankmeeting the requirements of this specification will result.5.2 FiberThe fibrous material shall consist of finelydivided threads or any natural or synthetic fiber

8、 (exceptasbestos) from free lumps, and when used, shall be in aflocculent condition. The fabric and fibrous material shall befree from all foreign materials.5.3 Mineral FillerThe mineral filler shall consist of finelycrushed slate, limestone, silica, or other aggregate that hasproven suitable for us

9、e with asphalt cement in constructingpavement wearing surfaces.5.4 AbsorptionThe absorption of asphalt plank shall notexceed 1.0 % by weight when tested in accordance with 9.2.5.5 BrittlenessAt least 80 % of the specimens tested ofeach thickness of plank shall not show any detrimentalcracking when t

10、ested in accordance with the method describedin 9.3.5.6 HardnessThe hardness of the plank, when tested inaccordance with the method prescribed in 9.5, shall meet thefollowing requirements:Temperature, Load, Penetration,C (F) kg (lb.) mm (mils)Type I, a 25 (77) 66 (30) 0.889 (35)Type I, b 25 (77) 66

11、(30) 1.651 (65)Type II 25 (77) 66 (30) 1.651 (65)6. Dimensions, Mass, and Permissible Variations6.1 Asphalt plank shall have the dimensions specified orshown on the plans and determined in accordance with 9.4.Tolerances of 61.6 mm (116 in.) in thickness, 63.2 mm (18 in.)in width and 66.4 mm (14 in.)

12、 in length will be permitted.Plank sizes shall be 12 in. in width by either 24 in. or 48 in. inlength. Thickness shall be12 in.,34 in., 1 in., or 1.5 in.6.2 The asphalt plank shall conform to the following massrequirements.Specimen Thickness, Min Mass,mm (in.) kg/m2(lbs/ft2)12.7 (0.5) 0.2 (5)19 (0.7

13、5) 0.3 (7.5)25.4 (1.0) 0.4 (10)37.5 (1.5) 0.6 (15)Specimen Thickness, Min. Mass,mm (in.) kg/m2(lbs/ft2)12.7 (0.5) 0.2 (5)19 (0.75) 0.3 (7.5)1This specification is under the jurisdiction of ASTM Committee D04 on Roadand Paving Materials and is the direct responsibility of Subcommittee D04.34 onPrefor

14、med Joint Fillers, Sealers and Sealing Systems.Current edition approved Dec. 1, 2003. Published January 2004. Originallyapproved in 1938. Last previous edition approved in 1998 as D 517 98.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United Sta

15、tes.25.4 (1.0) 0.4 (10)37.5 (1.5) 0.6 (15)7. Workmanship, Finish, and Appearance7.1 The asphalt plank shall be free from defects affecting itsserviceability and appearance; it shall have straight edges andsquare corners.8. Sampling8.1 For the purpose of testing, three planks shall be selectedat rand

16、om by the purchaser or his representative for each 1000planks or fraction thereof for each thickness included in theshipment.9. Test Methods9.1 ScopeThe four test methods listed in this section areintended to measure those attributes necessary to measure theability of asphalt plank to provide a reas

17、onably long andsatisfactory service. They are listed as follows:Test Method SectionAbsorption 9.2Brittleness 9.3Dimensions 9.4Hardness 9.59.2 Absorption:9.2.1 ScopeThis test method covers the determination ofwater absorption of asphalt plank.9.2.2 Significance and UseThe ability of the plank towiths

18、tand significant water absorption is a measure of itsporosity and therefore its ability to withstand freezing andthawing conditions. It is a measure of its density.9.2.3 ProcedureA specimen 50.8 by 152.4 mm (2 by 6in.) shall be cut from the asphalt plank in such a manner that alledges are freshly cu

19、t. The mass of the specimen shall beaccurately determined to the nearest 0.10 g, immersed in waterfor 24 h, removed, and the surface water wiped off with aslightly dampened cloth. The mass of the specimen shall thenbe determined to the nearest 0.10 g and the percent absorptiondetermined. The time el

20、apsing between the removal of thespecimen from the bath and its weighing shall not exceed 1min.9.3 Brittleness:9.3.1 ScopeThis test method covers the determination ofbrittleness of asphalt plank.9.3.2 Significance and UseThis test measures the abilityof the plank to function in cold temperatures wit

21、hout detrimen-tal cracking.9.3.3 ProcedureTwo 152.4 by 152.4 mm (6 by 6 in.)specimens shall be cut from each of the three sample planksselected in accordance with Section 8. Five of those specimensshall be tested as follows: The specimens shall be conditionedand maintained at a temperature of 0C (32

22、F) for not less than3 h, and then tested immediately. A 0.9-kg (2-lb) weightdropped from a height of 508 mm (20 in.) onto a 5.7 mm(0.225 in.) diameter cylindrical pin shall not cause a crack toextend more than 37.5 mm (1.5 in.) from the point of impact.The point of impact shall be as close to the ce

23、nter of the sampleas possible.9.4 Dimensions:9.4.1 ScopeThis test method covers the measurement ofdimensions to determine if the sample complies with the planor specification requirements.9.4.2 Significance and UseThis test method will ensurethat the finished product in place will afford an even, un

24、iformbearing surface for subsequent construction.9.4.3 ProcedurePlank from each lot shall be examined forappearance, straightness of edges, and squareness of corners,and measured for width and length to an accuracy required inSection 6. They shall also be calipered at four scattered pointseach, with

25、 a micrometer having flat bearing surfaces at bothcontact points of not less than 6.4 mm (14 in.) in diameter. Theaverage of the readings shall be considered the thickness of theplank.9.5 Hardness:9.5.1 ScopeThis test method covers the determination ofhardness of asphalt plank.9.5.2 Significance and

26、 UseThis test method measures theability of the asphalt plank to withstand serviceable loads andto ensure that the grade of asphalt used is proper to serve underwarm temperature without excessive deformation.9.5.3 ProcedureThe hardness of the plank shall be deter-mined by means of a McBurney penetro

27、meter in which the pinin contact with the plank during the test is a hemispherical pin5.7 mm (0.225 in.) in diameter. The specimen shall be keptsubmerged in water maintained at the temperature specified fora time sufficient to ensure that the specimen has attained thistemperature throughout. The tes

28、t shall be made with thespecimen supported on a smooth, solid support. The tests shallbe performed upon samples at least 152.4 mm (6 in.) in lengthand of the full width of the plank. In each case the requiredload shall be applied for a period of 60 s, and the contact pinof the penetrometer shall be

29、applied to the specimen at points37.5 mm (1.5 in.) or more from the edge of the specimen.9.6 Precision and Bias:9.6.1 PrecisionAttempts are being made to determine theprecision of the two tests in this standard that result in anumerical value.9.6.2 BiasNo statement can be made on the bias of thetest

30、s in this standard because no material having an acceptedreference value is available.10. Keywords10.1 asphalt plank; bridge deck waterproofing; protectioncourse; industrial flooringD 517 98 (2003)2ASTM International takes no position respecting the validity of any patent rights asserted in connecti

31、on with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible

32、 technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consi

33、deration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Ba

34、rr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 517 98 (2003)3